CN109895487A - A kind of fire-retardant sound-absorbing hot melt adhesive decoration material and its production technology - Google Patents
A kind of fire-retardant sound-absorbing hot melt adhesive decoration material and its production technology Download PDFInfo
- Publication number
- CN109895487A CN109895487A CN201711299603.6A CN201711299603A CN109895487A CN 109895487 A CN109895487 A CN 109895487A CN 201711299603 A CN201711299603 A CN 201711299603A CN 109895487 A CN109895487 A CN 109895487A
- Authority
- CN
- China
- Prior art keywords
- retardant
- fire
- melt adhesive
- hot
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to decoration materials and its technical field of producing more particularly to a kind of fire-retardant sound-absorbing hot melt adhesive decoration material and its production technologies.A kind of fire-retardant sound-absorbing hot melt adhesive decoration material of the present invention, it includes flame-retardant foam layer, hot-melt adhesive membrane and the fire retardant set gradually from the bottom to top, the flame-retardant foam layer, hot-melt adhesive membrane and fire retardant are integrated by calendering or curtain coating or hot synthetic type, with multi-layer fire-retarded and sound absorption, its flame retardant effect, sound insulating and absorbing significant effect, it is fire-retardant during will not generate be to human body and the harmful toxic gas of environment novel environment friendly fire-fighting one of optimal selection.
Description
Technical field
The present invention relates to decoration materials and its technical field of producing more particularly to a kind of fire-retardant sound-absorbing hot melt adhesive decorations
Material and its production technology.
Background technique
In the industries such as furniture, automobile, building materials, building, especially in cinema, music hall, museum, exhibition center, books
Shop, hearing room, gallery, auction hall, gymnasium, Conference Hall, multifunctional hall, hotel lobby, hospital, market, school, qin room, meeting
Discuss room, studio, recording studio, KTV private room, bar, industrial premises, computer room, family's noise reduction etc. it is more demanding to acoustic enviroment and
The place of top grade decoration, it is often necessary to use the material with fire-retardant sound-absorbing effect.
Existing fire-retardant sound-absorbing material, flame retardant effect, sound insulating and absorbing effect are often not ideal enough, can generate pair during fire-retardant
Human body and the harmful toxic gas of environment, are not the optimal selections of environmentally friendly fire-fighting.
Summary of the invention
The purpose of the present invention is to solve the shortcomings of the prior art and provide a kind of fire-retardant sound-absorbing hot melt adhesive decoration material and its
Production technology, flame retardant effect, sound insulating and absorbing significant effect will not generate harmful to human body and environment toxic during fire-retardant
Gas is one of the optimal selection of novel environment friendly fire-fighting.
To achieve the above object, the present invention adopts the following technical scheme: a kind of fire-retardant sound-absorbing hot melt adhesive decoration material, it includes under
Supreme flame-retardant foam layer, hot-melt adhesive membrane and the fire retardant set gradually, the flame-retardant foam layer, hot-melt adhesive membrane and fire retardant
By rolling or being cast or hot synthetic type is integrated.
The flame-retardant foam layer is foaming melamine.
The hot-melt adhesive membrane is TPU flame-retardant hot-melt adhesive film or EVA flame-retardant hot-melt adhesive film.
The fire retardant is polyacrylonitrile fire retardant.
The upper layer heat seal of the fire retardant has flame-retardant layer.
The flame-retardant layer is fire-retardant TPU film.
The fire retardant or flame-retardant layer may be provided with embossing or printing layer.
A kind of production technology of fire-retardant sound-absorbing hot melt adhesive decoration material, it the following steps are included:
Step A makes hot-melt adhesive membrane:
Hot melt adhesive and fire retardant are first pressed (30% ~ 99.9%): the weight ratio of (0.1% ~ 70%) mixes, and will mix at normal temperature
Object is closed to stir to being mixed thoroughly；The fire retardant can be liquid or solid fire retardant；
Then it is uniformly added into mixture and is modified production into mono-/bis-screw apparatus, in the case where manually or automatically controlling, mono-/bis-
Screw apparatus is by mixture pelletizing at the fire-retardant raw material of hot melt adhesive with fire retardation；
Then under 20 °C ~ 300 °C processing temperature environment, the fire-retardant raw material of hot melt adhesive is shaped to by way of being cast or rolling
Hot-melt adhesive membrane；
Then according to production needs, step B, step C, step D, step E or step F are respectively enterd；
Step B, it is one that the flame-retardant foam layer, hot-melt adhesive membrane and the fire retardant that set gradually from the bottom to top, which are passed through calendering formation,
Body is made fire-retardant sound-absorbing hot melt adhesive decoration material, enters step G；
Then step C is integrated with fire retardant hot synthetic type again first by flame-retardant foam layer and hot-melt adhesive membrane calendering formation；Or
Then person is integrated with flame-retardant foam layer hot synthetic type again first by hot-melt adhesive membrane and fire retardant calendering formation；Wherein fire-retardant bubble
Foam layer, hot-melt adhesive membrane and fire retardant are successively arranged from the bottom to top, and fire-retardant sound-absorbing hot melt adhesive decoration material is so made, enters step
G；
Step D, it is one that the flame-retardant foam layer, hot-melt adhesive membrane and the fire retardant that set gradually from the bottom to top, which are passed through tape casting,
Body is made fire-retardant sound-absorbing hot melt adhesive decoration material, enters step G；
Then step E is integrated with fire retardant hot synthetic type again first by flame-retardant foam layer and hot-melt adhesive membrane tape casting；Or
Then person is integrated with flame-retardant foam layer hot synthetic type again first by hot-melt adhesive membrane and fire retardant tape casting；Wherein fire-retardant bubble
Foam layer, hot-melt adhesive membrane and fire retardant are successively arranged from the bottom to top, and fire-retardant sound-absorbing hot melt adhesive decoration material is so made, enters step
G；
Then step F is integrated with fire retardant hot synthetic type again first by flame-retardant foam layer and hot-melt adhesive membrane hot synthetic type；Or
Then person is integrated with flame-retardant foam layer hot synthetic type again first by hot-melt adhesive membrane and fire retardant hot synthetic type；Wherein fire-retardant bubble
Foam layer, hot-melt adhesive membrane and fire retardant are successively arranged from the bottom to top, and fire-retardant sound-absorbing hot melt adhesive decoration material is so made, enters step
G；
Step G, by fire-retardant sound-absorbing hot melt adhesive decorate material be sent into cooling device in carry out cooling treatment, batched after cooling treatment at
Product.
The flame-retardant foam layer is foaming melamine；The hot-melt adhesive membrane is that TPU flame-retardant hot-melt adhesive film or EVA hinder
Fire hot-melt adhesive membrane；The fire retardant is polyacrylonitrile fire retardant.
The flame-retardant foam layer with a thickness of 0.1mm ~ 10mm；The hot-melt adhesive membrane with a thickness of 0.01mm ~ 100mm.
The invention has the following beneficial effects: a kind of fire-retardant sound-absorbing hot melt adhesive decoration material of the present invention and its production technology, have more
The fire-retardant and sound absorption of layer, flame retardant effect, sound insulating and absorbing significant effect, will not generate during fire-retardant has human body and environment
Harmful toxic gas is one of the optimal selection of novel environment friendly fire-fighting.
Fig. 1 is the structural schematic diagram of the embodiment of the present invention one.
Fig. 2 is the structural schematic diagram of the embodiment of the present invention two.
Fig. 3 is the production schematic diagram of the embodiment of the present invention three.
Fig. 4 is the production schematic diagram one of the embodiment of the present invention four.
Fig. 5 is the production schematic diagram two of the embodiment of the present invention four.
Fig. 6 is the production schematic diagram of the embodiment of the present invention five.
Fig. 7 is the production schematic diagram one of the embodiment of the present invention six.
Fig. 8 is the production schematic diagram two of the embodiment of the present invention six.
Fig. 9 is the production schematic diagram one of the embodiment of the present invention seven.
Figure 10 is the production schematic diagram two of the embodiment of the present invention seven.
The present invention will be further described below with reference to the drawings.
Embodiment one, a kind of fire-retardant sound-absorbing hot melt adhesive decoration material, as shown in Figure 1, it include set gradually from the bottom to top it is fire-retardant
Froth bed 30, hot-melt adhesive membrane 20 and fire retardant 10, the flame-retardant foam layer 30, hot-melt adhesive membrane 20 and fire retardant 10 pass through pressure
Prolong or is cast or hot synthetic type is integrated.Preferably, the flame-retardant foam layer 30 is foaming melamine, and foaming melamine exists
Pernicious gas will not be generated during fire-retardant, and there is preferable sound-absorbing soundproof effect, and the flame-retardant foam layer 30 can also be
Other flame-retardant foams and material.Preferably, the hot-melt adhesive membrane 20 is TPU flame-retardant hot-melt adhesive film 20 or EVA flame-retardant hot-melt
Glue film 20, TPU flame-retardant hot-melt adhesive film 20 or EVA flame-retardant hot-melt adhesive film 20 will not generate harmful gas during fire-retardant
Body, and there are preferable sound-absorbing soundproof effect, the hot-melt adhesive membrane 20 or other films with hot melt adhesive property
Or the glue with fire retardation.Preferably, the fire retardant 10 is polyacrylonitrile fire retardant 10, and polyacrylonitrile fire retardant 10 exists
Pernicious gas will not be generated during fire-retardant, and there is preferable sound-absorbing soundproof effect, and the fire retardant 10 can also be other
Fire proofing, further, the fire retardant 10 may be provided with embossing or printing layer, according to actual decoration or can fit up needs,
Different embossing or printing layer are printed, it is flexible in application, it is applied widely.A kind of fire-retardant sound-absorbing hot melt mucilage binding described in the present embodiment one
Decorations material has multi-layer fire-retarded and sound absorption, and flame retardant effect, sound insulating and absorbing significant effect will not generate during fire-retardant to people
Body and the harmful toxic gas of environment are one of the optimal selections of novel environment friendly fire-fighting.It can be widely applied to furniture, automobile, build
In the industries such as material, building, it is applied especially to cinema, music hall, museum, exhibition center, library, hearing room, gallery, auction
The Room, gymnasium, Conference Hall, multifunctional hall, hotel lobby, hospital, market, school, qin room, meeting room, studio, recording studio,
KTV private room, bar, industrial premises, computer room, family's noise reduction etc. be more demanding to acoustic enviroment and place of top grade decoration.
Embodiment two, a kind of fire-retardant sound-absorbing hot melt adhesive decoration material, as shown in Fig. 2, its with embodiment one the difference is that,
There is flame-retardant layer 40 in the upper layer heat seal of the fire retardant 10, it is preferred that the flame-retardant layer 40 is fire-retardant TPU film, the flame-retardant layer
40 will not generate pernicious gas during fire-retardant, and have preferable sound-absorbing soundproof effect.Further, the flame-retardant layer 40
It may be provided with embossing or printing layer, different embossing or printing layer can be printed, using spirit according to actual decoration or finishing needs
It is living, it is applied widely.
Embodiment three, as shown in figure 3, a kind of production technology of fire-retardant sound-absorbing hot melt adhesive decoration material, comprising the following steps:
Step A makes hot-melt adhesive membrane 20:
Then under 20 °C ~ 300 °C processing temperature environment, the fire-retardant raw material of hot melt adhesive is shaped to by way of being cast or rolling
Hot-melt adhesive membrane 20；
According to production needs, B is entered step；
The flame-retardant foam layer 30 set gradually from the bottom to top, hot-melt adhesive membrane 20 and fire retardant 10 are passed through calendering formation by step B
It is integrated, fire-retardant sound-absorbing hot melt adhesive decoration material is made, enters step G；
Fire-retardant sound-absorbing hot melt adhesive is decorated in material feeding cooling device 2 and carries out cooling treatment, passes through volume after cooling treatment by step G
Roller 9 batches as finished product.The cooling device 2 is air cooling or water-cooling apparatus, or cooling guide wheel, jelly water dispenser etc..
Further, the flame-retardant foam layer is foaming melamine；The hot-melt adhesive membrane is that TPU flame-retardant hot-melt adhesive is thin
Film or EVA flame-retardant hot-melt adhesive film；The fire retardant is polyacrylonitrile fire retardant.The flame-retardant foam layer with a thickness of 0.1mm ~
10mm；The hot-melt adhesive membrane with a thickness of 0.01mm ~ 100mm.
A kind of production technology of fire-retardant sound-absorbing hot melt adhesive decoration material, the fire-retardant sound-absorbing hot melt produced described in the present embodiment three
Mucilage binding decorations material has multi-layer fire-retarded and sound absorption, and flame retardant effect, sound insulating and absorbing significant effect will not generate during fire-retardant
It is one of the optimal selection of novel environment friendly fire-fighting to human body and the harmful toxic gas of environment.
Example IV, as shown in Figure 4 and Figure 5, the difference with embodiment three are, make hot-melt adhesive membrane 20 by step A
Afterwards, C is entered step；Step C is then warm with fire retardant 10 again first by 20 calendering formation of flame-retardant foam layer 30 and hot-melt adhesive membrane
Synthesis type is integrated；Or first by 10 calendering formation of hot-melt adhesive membrane 20 and fire retardant, then again with 30 heat seal of flame-retardant foam layer
It is molded as one；Wherein flame-retardant foam layer 30, hot-melt adhesive membrane 20 and fire retardant 10 are successively arranged from the bottom to top, and resistance is so made
Sound hot melt adhesive decoration material is burnt and sucked, G is entered step；Fire-retardant sound-absorbing hot melt adhesive is decorated in material feeding cooling device 2 and is carried out by step G
Cooling treatment is batched as finished product by winding up roller 9 after cooling treatment.A kind of fire-retardant sound-absorbing hot melt adhesive decoration material described in the present embodiment four
Production technology, produced fire-retardant sound-absorbing hot melt adhesive decoration material have multi-layer fire-retarded and sound absorption, flame retardant effect,
Sound insulating and absorbing significant effect will not generate to human body and the harmful toxic gas of environment during fire-retardant, be novel environment friendly fire-fighting
One of optimal selection.
Embodiment five, as shown in fig. 6, the difference of itself and embodiment three is, after step A makes hot-melt adhesive membrane 20, into
Enter step D；The flame-retardant foam layer 30 set gradually from the bottom to top, hot-melt adhesive membrane 20 and fire retardant 10 are passed through curtain coating by step D
It is molded as one, fire-retardant sound-absorbing hot melt adhesive decoration material is made, enters step G, wherein hot-melt adhesive membrane 20 passes through extrusion die 5
Middle extrusion molding；Fire-retardant sound-absorbing hot melt adhesive is decorated in material feeding cooling device 2 and carries out cooling treatment by step G, after cooling treatment
It is batched by winding up roller 9 as finished product.A kind of production technology of fire-retardant sound-absorbing hot melt adhesive decoration material, is produced described in the present embodiment five
The fire-retardant sound-absorbing hot melt adhesive decoration material come has multi-layer fire-retarded and sound absorption, flame retardant effect, sound insulating and absorbing significant effect, resistance
Will not be generated during combustion be to human body and the harmful toxic gas of environment novel environment friendly fire-fighting one of optimal selection.
Embodiment six, as shown in Figure 7 and Figure 8, the difference with embodiment three are, make hot-melt adhesive membrane 20 by step A
Afterwards, E is entered step；Step E is then warm with fire retardant 10 again first by 20 tape casting of flame-retardant foam layer 30 and hot-melt adhesive membrane
Synthesis type is integrated；Or first by 10 tape casting of hot-melt adhesive membrane 20 and fire retardant, then again with 30 heat seal of flame-retardant foam layer
It is molded as one；Wherein flame-retardant foam layer 30, hot-melt adhesive membrane 20 and fire retardant 10 are successively arranged from the bottom to top, and resistance is so made
Sound hot melt adhesive decoration material is burnt and sucked, enters step G, wherein hot-melt adhesive membrane 20 passes through extrusion molding in extrusion die 5；Step G,
Fire-retardant sound-absorbing hot melt adhesive decorated into material be sent into cooling device 2 and carry out cooling treatment, after cooling treatment by winding up roller 9 batch at
Product.A kind of production technology of fire-retardant sound-absorbing hot melt adhesive decoration material, the fire-retardant sound-absorbing hot melt produced described in the present embodiment six
Mucilage binding decorations material has multi-layer fire-retarded and sound absorption, and flame retardant effect, sound insulating and absorbing significant effect will not generate during fire-retardant
It is one of the optimal selection of novel environment friendly fire-fighting to human body and the harmful toxic gas of environment.
Embodiment seven, as shown in Figure 9 and Figure 10, the difference with embodiment three are, make hot-melt adhesive membrane 20 by step A
Afterwards, F is entered step；Step F, first by flame-retardant foam layer 30 and hot-melt adhesive membrane 20 by 1 hot synthetic type of heating device, then again
It is integrated with fire retardant 10 by 1 hot synthetic type of heating device；Or hot-melt adhesive membrane 20 and fire retardant 10 are first passed through into heating
Then 1 hot synthetic type of device is integrated with flame-retardant foam layer 30 by 1 hot synthetic type of heating device again；Wherein flame-retardant foam layer
30, hot-melt adhesive membrane 20 and fire retardant 10 are successively arranged from the bottom to top, fire-retardant sound-absorbing hot melt adhesive decoration material are so made, into step
Rapid G；Fire-retardant sound-absorbing hot melt adhesive is decorated in material feeding cooling device 2 and carries out cooling treatment, passes through volume after cooling treatment by step G
Roller 9 batches as finished product.The heating device 1 is electric heating, oil heating, gas heating or roller heating device, with specific reference to reality
Depending on the process requirement of border.A kind of production technology of fire-retardant sound-absorbing hot melt adhesive decoration material, is produced described in the present embodiment seven
Fire-retardant sound-absorbing hot melt adhesive decoration material has multi-layer fire-retarded and sound absorption, flame retardant effect, sound insulating and absorbing significant effect, fire-retardant mistake
Will not be generated in journey be to human body and the harmful toxic gas of environment novel environment friendly fire-fighting one of optimal selection.
The above description is only a preferred embodiment of the present invention, thus it is all according to the configuration described in the scope of the patent application of the present invention, feature
And the equivalent change or modification that principle is done, it is included in the scope of the patent application of the present invention.
Claims (10)
1. a kind of fire-retardant sound-absorbing hot melt adhesive decoration material, it is characterised in that: it include the flame-retardant foam layer set gradually from the bottom to top,
Hot-melt adhesive membrane and fire retardant, the flame-retardant foam layer, hot-melt adhesive membrane and fire retardant pass through calendering or curtain coating or hot synthetic type
It is integrated.
2. a kind of fire-retardant sound-absorbing hot melt adhesive decoration material according to claim 1, it is characterised in that: the flame-retardant foam layer is
Foam melamine.
3. a kind of fire-retardant sound-absorbing hot melt adhesive decoration material according to claim 1, it is characterised in that: the hot-melt adhesive membrane is
TPU flame-retardant hot-melt adhesive film or EVA flame-retardant hot-melt adhesive film.
4. a kind of fire-retardant sound-absorbing hot melt adhesive decoration material according to claim 1, it is characterised in that: the fire retardant is poly- third
Alkene nitrile fire retardant.
5. a kind of fire-retardant sound-absorbing hot melt adhesive decoration material according to claim 1, it is characterised in that: the upper layer of the fire retardant
Heat seal has flame-retardant layer.
6. a kind of fire-retardant sound-absorbing hot melt adhesive decoration material according to claim 5, it is characterised in that: the flame-retardant layer is fire-retardant
TPU film.
7. a kind of fire-retardant sound-absorbing hot melt adhesive decoration material according to claim 6, it is characterised in that: the fire retardant is fire-retardant
Layer may be provided with embossing or printing layer.
8. a kind of production technology of fire-retardant sound-absorbing hot melt adhesive decoration material, which is characterized in that it the following steps are included:
Step A makes hot-melt adhesive membrane:
Hot melt adhesive and fire retardant are first pressed (30% ~ 99.9%): the weight ratio of (0.1% ~ 70%) mixes, and will mix at normal temperature
Object is closed to stir to being mixed thoroughly；The fire retardant can be liquid or solid fire retardant；
Then it is uniformly added into mixture and is modified production into mono-/bis-screw apparatus, in the case where manually or automatically controlling, mono-/bis-
Screw apparatus is by mixture pelletizing at the fire-retardant raw material of hot melt adhesive with fire retardation；
Then under 20 °C ~ 300 °C processing temperature environment, the fire-retardant raw material of hot melt adhesive is shaped to by way of being cast or rolling
Hot-melt adhesive membrane；
Then according to production needs, step B, step C, step D, step E or step F are respectively enterd；
Step B, it is one that the flame-retardant foam layer, hot-melt adhesive membrane and the fire retardant that set gradually from the bottom to top, which are passed through calendering formation,
Body is made fire-retardant sound-absorbing hot melt adhesive decoration material, enters step G；
Then step C is integrated with fire retardant hot synthetic type again first by flame-retardant foam layer and hot-melt adhesive membrane calendering formation；Or
Then person is integrated with flame-retardant foam layer hot synthetic type again first by hot-melt adhesive membrane and fire retardant calendering formation；Wherein fire-retardant bubble
Foam layer, hot-melt adhesive membrane and fire retardant are successively arranged from the bottom to top, and fire-retardant sound-absorbing hot melt adhesive decoration material is so made, enters step
G；
Step D, it is one that the flame-retardant foam layer, hot-melt adhesive membrane and the fire retardant that set gradually from the bottom to top, which are passed through tape casting,
Body is made fire-retardant sound-absorbing hot melt adhesive decoration material, enters step G；
Then step E is integrated with fire retardant hot synthetic type again first by flame-retardant foam layer and hot-melt adhesive membrane tape casting；Or
Then person is integrated with flame-retardant foam layer hot synthetic type again first by hot-melt adhesive membrane and fire retardant tape casting；Wherein fire-retardant bubble
Foam layer, hot-melt adhesive membrane and fire retardant are successively arranged from the bottom to top, and fire-retardant sound-absorbing hot melt adhesive decoration material is so made, enters step
G；
Then step F is integrated with fire retardant hot synthetic type again first by flame-retardant foam layer and hot-melt adhesive membrane hot synthetic type；Or
Then person is integrated with flame-retardant foam layer hot synthetic type again first by hot-melt adhesive membrane and fire retardant hot synthetic type；Wherein fire-retardant bubble
Foam layer, hot-melt adhesive membrane and fire retardant are successively arranged from the bottom to top, and fire-retardant sound-absorbing hot melt adhesive decoration material is so made, enters step
G；
Step G, by fire-retardant sound-absorbing hot melt adhesive decorate material be sent into cooling device in carry out cooling treatment, batched after cooling treatment at
Product.
9. a kind of production technology of fire-retardant sound-absorbing hot melt adhesive decoration material according to claim 8, it is characterised in that: the resistance
Firing froth bed is foaming melamine；The hot-melt adhesive membrane is TPU flame-retardant hot-melt adhesive film or EVA flame-retardant hot-melt adhesive film；
The fire retardant is polyacrylonitrile fire retardant.
10. a kind of production technology of fire-retardant sound-absorbing hot melt adhesive decoration material according to claim 9, it is characterised in that: described
Flame-retardant foam layer with a thickness of 0.1mm ~ 10mm；The hot-melt adhesive membrane with a thickness of 0.01mm ~ 100mm.