CN109895302A - A kind of production method of silicon rubber tire - Google Patents
A kind of production method of silicon rubber tire Download PDFInfo
- Publication number
- CN109895302A CN109895302A CN201711313072.1A CN201711313072A CN109895302A CN 109895302 A CN109895302 A CN 109895302A CN 201711313072 A CN201711313072 A CN 201711313072A CN 109895302 A CN109895302 A CN 109895302A
- Authority
- CN
- China
- Prior art keywords
- silicon rubber
- rubber tire
- production method
- steel plate
- tire model
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to tire production technical field, in particular to a kind of production method of silicon rubber tire.The production method of the silicon rubber tire, comprising the following steps: (1) drying after smearing silicon rubber tire model uniformly with release agent surrounds the silicon rubber tire model surrounding handled well with steel plate, steel plate is also handled with release agent；(2) silicon rubber and curing agent are stirred evenly with the ratio of 50:1；(3) silicon rubber and curing agent after mixing evenly, carry out vacuumizing and exhausting bubble；(4) silicon rubber prepared is slowly poured to silicon rubber tire model along a fixed perfusion point；(5) 120min after curing completely is injected in batten frame after taking 10 times of silicon rubber weight of land plaster to be watered；(6) batten is removed after 20min, silicon rubber tire completes.The beneficial effects of the present invention are: production method is simple to operation, high production efficiency, labor intensity of workers is low, and the silicon rubber tire chemistry stability produced is good, and elasticity is good, rub resistance, ageing-resistant.
Description
(1) technical field
The present invention relates to tire production technical field, in particular to a kind of production method of silicon rubber tire.
(2) background technique
Silicon rubber tire belongs to a product in silastic product, based on being the room temperature vulcanized silicone rubber using condensed type
The features such as raw material, adds other packing materials of fixed proportion, manufactured tire, chemical resistance ageing-resistant because of tire silicon rubber,
It is suitble to the place more demanding to tire to use, silicon rubber tire chemistry stability is good, and material is harmless, and fire resistance is good,
No pollution to the environment, elasticity is good, rub resistance, and has the characteristics that pollution-free, while silicon rubber tire drainage, road holding rolling
Dynamic resistance is stronger.
(3) summary of the invention
Silicon rubber tire simple, that chemical stability is good is made in order to compensate for the shortcomings of the prior art, the present invention provides a kind of
Production method.
The present invention is achieved through the following technical solutions:
A kind of production method of silicon rubber tire, comprising the following steps:
(1) drying after smearing silicon rubber tire model uniformly with release agent, the silicon rubber tire model surrounding handled well is used
Steel plate surrounds, and steel plate is also handled with release agent；
(2) silicon rubber and curing agent are stirred evenly with the ratio of 50:1；
(3) silicon rubber and curing agent after mixing evenly, carry out vacuumizing and exhausting and steep link, the time vacuumized is no more than 10min；
(4) silicon rubber prepared is slowly poured to silicon rubber tire model along a fixed perfusion point, and is shaken frequently to exclude
The air of the inside solidifies 120min；
(5) 120min after curing completely is injected in batten frame after taking 10 times of silicon rubber weight of land plaster to be watered, until filling；
(6) batten is removed after 20min, silicon rubber tire completes.
The beneficial effects of the present invention are: production method is simple to operation, high production efficiency, labor intensity of workers is low, production
Silicon rubber tire chemistry stability out is good, and elasticity is good, rub resistance, ageing-resistant.
(4) specific embodiment
The following are a kind of specific embodiments of the invention.The embodiment the following steps are included:
(1) drying after smearing silicon rubber tire model uniformly with release agent, the silicon rubber tire model surrounding handled well is used
Steel plate surrounds, and steel plate is also handled with release agent；
(2) silicon rubber and curing agent are stirred evenly with the ratio of 50:1；
(3) silicon rubber and curing agent after mixing evenly, carry out vacuumizing and exhausting and steep link, the time vacuumized is no more than 10min；
(4) silicon rubber prepared is slowly poured to silicon rubber tire model along a fixed perfusion point, and is shaken frequently to exclude
The air of the inside solidifies 120min；
(5) 120min after curing completely is injected in batten frame after taking 10 times of silicon rubber weight of land plaster to be watered, until filling；
(6) batten is removed after 20min, silicon rubber tire completes.
Claims (1)
1. a kind of production method of silicon rubber tire, comprising the following steps:
(1) drying after smearing silicon rubber tire model uniformly with release agent, the silicon rubber tire model surrounding handled well is used
Steel plate surrounds, and steel plate is also handled with release agent；
(2) silicon rubber and curing agent are stirred evenly with the ratio of 50:1；
(3) silicon rubber and curing agent after mixing evenly, carry out vacuumizing and exhausting and steep link, the time vacuumized is no more than 10min；
(4) silicon rubber prepared is slowly poured to silicon rubber tire model along a fixed perfusion point, and is shaken frequently to exclude
The air of the inside solidifies 120min；
(5) 120min after curing completely is injected in batten frame after taking 10 times of silicon rubber weight of land plaster to be watered, until filling；
(6) batten is removed after 20min, silicon rubber tire completes.