CN104589680A - Manufacturing method of silicone rubber tire - Google Patents
Manufacturing method of silicone rubber tire Download PDFInfo
- Publication number
- CN104589680A CN104589680A CN201310520819.6A CN201310520819A CN104589680A CN 104589680 A CN104589680 A CN 104589680A CN 201310520819 A CN201310520819 A CN 201310520819A CN 104589680 A CN104589680 A CN 104589680A
- Authority
- CN
- China
- Prior art keywords
- silicone rubber
- silicon rubber
- rubber tire
- manufacturing
- tire model
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of a silicone rubber tire. The manufacturing method comprises following steps: 1) a silicone rubber tire model is uniformly smeared with a releasing agent, and is dried via blowing, the processed silicone rubber tire model is surrounded with steel plates, and the steel plates are processed using the releasing agent; 2) silicone rubber is uniformly mixed with a curing agent at a ratio of 50:1; 3) after uniform mixing of silicone rubber with the curing agent, vacuumizing bubble-removing is carried out, wherein the time of vacuumizing is 10min or less; 4) an obtained silicone rubber mixture is slowly injected into the silicone rubber tire model through a certain injection point, air is removed via vibration at intervals, and curing is carried out for 120min; 5) after 120min of curing, gypsum powder is mixed with water, and is injected into a batten frame until full filling, wherein the weight of gypsum powder is 10 times of that of the silicone rubber; and 6) 20min later, a batten frame is dismounted, and manufacturing of the silicone rubber tire is finished. The manufacturing method is simple, and is convenient for operation; production efficiency is high; worker labor intensity is low; and the obtained silicone rubber tire is excellent in stability, elasticity, wear resistance, and aging resistance.
Description
Technical field
The invention belongs to tire production technical field, be specifically related to a kind of preparation method of silicon rubber tire.
Background technology
Silicon rubber tire belongs to a product classification in silastic product, be adopt condensed type room temperature vulcanized silicone rubber based on raw material, add other packing materials of fixed proportion, the tire made, because of features such as the ageing-resistant chemical resistances of tire silicon rubber, be applicable to requiring that higher place uses to tire.Silicon rubber tire chemistry good stability, material is harmless, and fire resistance is good, environmentally safe, good springiness, rub resistance, and has the features such as pollution-free, simultaneously silicon rubber tire drainage, and earth-grasping force resistance to rolling is stronger.
Summary of the invention
The object of the invention is to, provide a kind of preparation method of silicon rubber tire, preparation method is simple to operation, and production efficiency is high, and labor strength is low, the silicon rubber tire chemistry good stability produced, good springiness, and rub resistance is ageing-resistant.
The preparation method of silicon rubber tire provided by the invention, it comprises the following steps:
1), by silicon rubber tire model releasing agent smear evenly and dry up, surrounded by the silicon rubber tire model surrounding steel plate handled well, releasing agent process also used by steel plate;
2), silicon rubber and curing agent stir with the ratio of 50:1;
3), after silicon rubber and curing agent stir, carry out vacuumizing and exhausting bubble link, the time vacuumized is no more than 10min;
4), by the silicon rubber prepared slowly pour into a mould to silicon rubber tire model along a fixing perfusion point, and frequently shake the air getting rid of the inside, solidification 120min;
5), after 120min completion of cure, the land plaster getting silicon rubber weight 10 times is watered in rear injection batten frame, till filling;
6), remove batten after 20min, silicon rubber tire has been manufactured.
The preparation method of silicon rubber tire provided by the invention, its beneficial effect is: preparation method is simple to operation, and production efficiency is high, and labor strength is low, the silicon rubber tire chemistry good stability produced, good springiness, and rub resistance is ageing-resistant.
Detailed description of the invention
Below in conjunction with an embodiment, the preparation method of silicon rubber tire provided by the invention is described in detail.
Embodiment
The preparation method of the silicon rubber tire of the present embodiment, it comprises the following steps:
1), by silicon rubber tire model releasing agent smear evenly and dry up, surrounded by the silicon rubber tire model surrounding steel plate handled well, releasing agent process also used by steel plate;
2), silicon rubber and curing agent stir with the ratio of 50:1;
3), after silicon rubber and curing agent stir, carry out vacuumizing and exhausting bubble link, the time vacuumized is no more than 10min;
4), by the silicon rubber prepared slowly pour into a mould to silicon rubber tire model along a fixing perfusion point, and frequently shake the air getting rid of the inside, solidification 120min;
5), after 120min completion of cure, the land plaster getting silicon rubber weight 10 times is watered in rear injection batten frame, till filling;
6), remove batten after 20min, silicon rubber tire has been manufactured.
Claims (1)
1. a preparation method for silicon rubber tire, is characterized in that, it comprises the following steps:
1), by silicon rubber tire model releasing agent smear evenly and dry up, surrounded by the silicon rubber tire model surrounding steel plate handled well, releasing agent process also used by steel plate;
2), silicon rubber and curing agent stir with the ratio of 50:1;
3), after silicon rubber and curing agent stir, carry out vacuumizing and exhausting bubble link, the time vacuumized is no more than 10min;
4), by the silicon rubber prepared slowly pour into a mould to silicon rubber tire model along a fixing perfusion point, and frequently shake the air getting rid of the inside, solidification 120min;
5), after 120min completion of cure, the land plaster getting silicon rubber weight 10 times is watered in rear injection batten frame, till filling;
6), remove batten after 20min, silicon rubber tire has been manufactured.