CN109893912A - A kind of aroma type active carbon bacterium resisting is except formaldehyde strainer and preparation method thereof - Google Patents
A kind of aroma type active carbon bacterium resisting is except formaldehyde strainer and preparation method thereof Download PDFInfo
- Publication number
- CN109893912A CN109893912A CN201910136115.6A CN201910136115A CN109893912A CN 109893912 A CN109893912 A CN 109893912A CN 201910136115 A CN201910136115 A CN 201910136115A CN 109893912 A CN109893912 A CN 109893912A
- Authority
- CN
- China
- Prior art keywords
- parts
- active carbon
- type active
- aroma type
- bacterium resisting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of aroma type active carbon bacterium resisting except formaldehyde strainer and preparation method thereof, is related to air conditioner filter screen processing technique field.The aroma type active carbon bacterium resisting is made of raw material from the following weight except formaldehyde strainer: 80-100 parts of acrylic resin, 10-12 parts of sulfonated phenol formaldehyde resin, 6-8 parts of active carbon, 4-6 parts of diatomite, 2-5 parts of manganese dioxide, 4-6 parts of vinyl acetate, 2-4 parts of nano silica, 2-3 parts of monoglyceride, 8-10 parts of composite plant aromatic particulate, 2-4 parts of sodium tripolyphosphate, 06-0.8 parts of dispersing agent, 0.2-0.6 parts of plasticizer.Preparation method specifically include that the preparation of manganese dioxide load diatomite, stirring centrifugation, high temperature and pressure stand, high-speed stirred.The present invention overcomes the deficiencies in the prior art, fragrance ingredient is added while guaranteeing that air conditioner filter screen has certain antibacterial mite-removing effect, so that room air is continued faint scent, and combine using Multiple components and have the function that absorb formaldehyde, further fresh air promotes the using effect of air-conditioning.
Description
Technical field
The present invention relates to air conditioner filter screen processing technique fields, and in particular to a kind of aroma type active carbon bacterium resisting removes formaldehyde strainer
And preparation method thereof.
Background technique
With the increasingly raising of people's living standard, the air-conditioning of a home from home, especially public place can be brought for people
The central air-conditioning generally used has been widely used in daily life and work.But due to the main function of air-conditioning
Making refrigeration or heating, it is desirable that people make need to keep space is relatively closed to can be only achieved higher constant temperature effect using air-conditioning, but
It is closed for a long time to make indoor generation peculiar smell, people are influenced using sense organ, and due to fitting up most furniture and coating now
Contain formaldehyde, the content that long-time confined space can increase formaldehyde in air to a certain extent influences health.
The main function of traditional air-conditioning filter net was the dust and impurities in air filtering, reduced the damage of air-conditioning body
Consumption, the further enhanced feature of air-conditioning filter net is essentially antibacterial and other effects, all from the filter effect of air-conditioning filter net and to make
Considered on the service life, thus study at this stage it is a be able to maintain it is with fresh air, reduce the air conditioner filter screen that gathers of indoor formaldehyde and be
One direction important and with practical value.
Summary of the invention
In view of the shortcomings of the prior art, the present invention provides a kind of aroma type active carbon bacterium resisting except formaldehyde strainer and its preparation side
Method adds fragrance ingredient while guaranteeing that air conditioner filter screen has certain antibacterial mite-removing effect, room air is made to continue faint scent, and
And combined using Multiple components and have the function that absorb formaldehyde, further fresh air promotes the using effect of air-conditioning.
In order to achieve the above object, technical solution of the present invention is achieved by the following technical programs:
A kind of aroma type active carbon bacterium resisting removes formaldehyde strainer, and the aroma type active carbon bacterium resisting is except formaldehyde strainer is by following heavy
The raw material of amount part is made: 80-100 parts of acrylic resin, 10-12 parts of sulfonated phenol formaldehyde resin, 6-8 parts of active carbon, diatomite 4-6
Part, 2-5 parts of manganese dioxide, 4-6 parts of vinyl acetate, 2-4 parts of nano silica, 2-3 parts of monoglyceride, composite plant aromatic particulate
8-10 parts, 2-4 parts of sodium tripolyphosphate, 06-0.8 parts of dispersing agent, 0.2-0.6 parts of plasticizer.
Preferably, the aroma type active carbon bacterium resisting removes formaldehyde strainer and is made of raw material from the following weight: polypropylene tree
90 parts of rouge, 11 parts of sulfonated phenol formaldehyde resin, 7 parts of active carbon, 5 parts of diatomite, 3.5 parts of manganese dioxide, 5 part, nanometer two of vinyl acetate
3 parts of silica, 2.5 parts of monoglyceride, 9 parts of composite plant aromatic particulate, 3 parts of sodium tripolyphosphate, 0.7 part of dispersing agent, plasticizer
0.4 part.
Preferably, the composite plant aromatic particulate is honeysuckle, peppermint, lemonlike citrus leaf, Radix Glycyrrhizae, spiceleaf, lavender, cloves
In any several be mixed with.
Preferably, the dispersing agent is ethylene-acrylic acid copolymer, copper stearate, oxidized polyethylene wax mass ratio 2: 1: 2
Mixture.
Preferably, the plasticizer is phthalic acid, di-n-octyl phthalate, BBP(Butyl Benzyl Phthalate, neighbour
Any one in dicyclo-hexyl phthlate.
The aroma type active carbon bacterium resisting except formaldehyde strainer preparation method the following steps are included:
(1) it after deionized water concussion dispersion being added in manganese dioxide powder, adds after diatomite after high-speed stirred mixing
Air-dry, be sintered under high temperature, crush afterwards manganese dioxide load diatomite is spare；
(2) active carbon and composite plant aromatic particulate are mixed and is added in deionized water, after mixing evenly in centrifuge
High speed centrifugation is carried out, it is spare to obtain sediment；
(3) it is stirred evenly after mixing acrylic resin, sulfonated phenol formaldehyde resin, vinyl acetate high temperature, under high temperature and pressure
Cooling is taken out after standing a period of time to be ground up, sieved, and it is spare to obtain mixture；
(4) by said mixture, manganese dioxide load diatomite, sediment, nano silica, monoglyceride, trimerization phosphorus
Sour sodium, dispersing agent, plasticizer mixed with deionized water after at a temperature of 80-100 DEG C high-speed stirred, it is rear to stand, must handle expect it is standby
With；
(5) above-mentioned processing material is subjected to spinning, obtains base-material fiber, then base-material fiber is obtained fragrant according to specification weaving networking
Odor type active carbon bacterium resisting removes formaldehyde strainer.
Preferably, the revolving speed that step (1) high speed is stirred is 1200-1400r/min, mixing time 15-
20min。
Preferably, the revolving speed of step (2) the high speed centrifugation is 4000-4200r/min, centrifugation time 5-8min.
Preferably, the temperature of step (3) the high temperature stirring is 120-140 DEG C, and the temperature that high temperature and pressure is stood is
100-110 DEG C, pressure 15-18MPa, time of repose 40-60min.
The present invention provides a kind of aroma type active carbon bacterium resisting except formaldehyde strainer and preparation method thereof, excellent compared with prior art
Point is:
(1) present invention is carried out manganese dioxide and diatomite using sintering process compound, makes resulting manganese dioxide load silicon
Diatomaceous earth can be effective and long-term absorption formaldehyde, achieve the effect that purify air, promoted product the effect of.
(2) present invention prepares fragrance ingredient using natural plants, and keeps plant fragrance particle and active carbon compound, extends
The action time of fragrance ingredient makes product achieve the purpose that permanent faint scent, enhances the function and effect of product, promotes the practicality.
(3) present invention effectively promotes the anti-microbial property of product added with substances such as vinyl acetate, nano silicas, and
And cooperate the stability of addition enhancing product in other materials, improve the comprehensive performance of product.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below with reference to the embodiment of the present invention pair
Technical solution in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is a part of the invention
Embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making wound
Every other embodiment obtained under the premise of the property made labour, shall fall within the protection scope of the present invention.
Embodiment 1:
A kind of aroma type active carbon bacterium resisting removes formaldehyde strainer, and the aroma type active carbon bacterium resisting is except formaldehyde strainer is by following heavy
The raw material of amount part is made: 80 parts of acrylic resin, 10 parts of sulfonated phenol formaldehyde resin, 6 parts of active carbon, 4 parts of diatomite, manganese dioxide 2
Part, 4 parts of vinyl acetate, 2 parts of nano silica, 2 parts of monoglyceride, 8 parts of composite plant aromatic particulate, sodium tripolyphosphate 2 part, point
06 part of powder, 0.2 part of plasticizer.
The composite plant aromatic particulate is honeysuckle, peppermint, lemonlike citrus leaf, Radix Glycyrrhizae, spiceleaf, lavender, any in cloves
It is several to be mixed with；The dispersing agent is ethylene-acrylic acid copolymer, copper stearate, oxidized polyethylene wax mass ratio 2: 1: 2
Mixture；The plasticizer is phthalic acid, di-n-octyl phthalate, BBP(Butyl Benzyl Phthalate, phthalic acid
Any one in dicyclohexyl maleate.
The aroma type active carbon bacterium resisting except formaldehyde strainer preparation method the following steps are included:
(1) it after deionized water concussion dispersion being added in manganese dioxide powder, adds after diatomite after high-speed stirred mixing
Air-dry, be sintered under high temperature, crush afterwards manganese dioxide load diatomite is spare；
(2) active carbon and composite plant aromatic particulate are mixed and is added in deionized water, after mixing evenly in centrifuge
High speed centrifugation is carried out, it is spare to obtain sediment；
(3) it is stirred evenly after mixing acrylic resin, sulfonated phenol formaldehyde resin, vinyl acetate high temperature, under high temperature and pressure
Cooling is taken out after standing a period of time to be ground up, sieved, and it is spare to obtain mixture；
(4) by said mixture, manganese dioxide load diatomite, sediment, nano silica, monoglyceride, trimerization phosphorus
Sour sodium, dispersing agent, plasticizer mixed with deionized water after at a temperature of 80-100 DEG C high-speed stirred, it is rear to stand, must handle expect it is standby
With；
(5) above-mentioned processing material is subjected to spinning, obtains base-material fiber, then base-material fiber is obtained fragrant according to specification weaving networking
Odor type active carbon bacterium resisting removes formaldehyde strainer.
Wherein, the revolving speed that step (1) high speed is stirred is 1200-1400r/min, mixing time 15-
20min；The revolving speed of step (2) the high speed centrifugation is 4000-4200r/min, centrifugation time 5-8mi；The step
(3) temperature of high temperature stirring is 120-140 DEG C, and the temperature that high temperature and pressure is stood is 100-110 DEG C, pressure 15-18MPa,
Time of repose is 40-60min.
Embodiment 2:
A kind of aroma type active carbon bacterium resisting removes formaldehyde strainer, and the aroma type active carbon bacterium resisting is except formaldehyde strainer is by following heavy
The raw material of amount part is made: 100 parts of acrylic resin, 12 parts of sulfonated phenol formaldehyde resin, 8 parts of active carbon, 6 parts of diatomite, manganese dioxide
5 parts, 6 parts of vinyl acetate, 4 parts of nano silica, 3 parts of monoglyceride, 10 parts of composite plant aromatic particulate, 4 parts of sodium tripolyphosphate,
0.8 part of dispersing agent, 0.6 part of plasticizer.
The composite plant aromatic particulate is honeysuckle, peppermint, lemonlike citrus leaf, Radix Glycyrrhizae, spiceleaf, lavender, any in cloves
It is several to be mixed with；The dispersing agent is ethylene-acrylic acid copolymer, copper stearate, oxidized polyethylene wax mass ratio 2: 1: 2
Mixture；The plasticizer is phthalic acid, di-n-octyl phthalate, BBP(Butyl Benzyl Phthalate, phthalic acid
Any one in dicyclohexyl maleate.
The aroma type active carbon bacterium resisting except formaldehyde strainer preparation method the following steps are included:
(1) it after deionized water concussion dispersion being added in manganese dioxide powder, adds after diatomite after high-speed stirred mixing
Air-dry, be sintered under high temperature, crush afterwards manganese dioxide load diatomite is spare；
(2) active carbon and composite plant aromatic particulate are mixed and is added in deionized water, after mixing evenly in centrifuge
High speed centrifugation is carried out, it is spare to obtain sediment；
(3) it is stirred evenly after mixing acrylic resin, sulfonated phenol formaldehyde resin, vinyl acetate high temperature, under high temperature and pressure
Cooling is taken out after standing a period of time to be ground up, sieved, and it is spare to obtain mixture；
(4) by said mixture, manganese dioxide load diatomite, sediment, nano silica, monoglyceride, trimerization phosphorus
Sour sodium, dispersing agent, plasticizer mixed with deionized water after at a temperature of 80-100 DEG C high-speed stirred, it is rear to stand, must handle expect it is standby
With；
(5) above-mentioned processing material is subjected to spinning, obtains base-material fiber, then base-material fiber is obtained fragrant according to specification weaving networking
Odor type active carbon bacterium resisting removes formaldehyde strainer.
Wherein, the revolving speed that step (1) high speed is stirred is 1200-1400r/min, mixing time 15-
20min；The revolving speed of step (2) the high speed centrifugation is 4000-4200r/min, centrifugation time 5-8mi；The step
(3) temperature of high temperature stirring is 120-140 DEG C, and the temperature that high temperature and pressure is stood is 100-110 DEG C, pressure 15-18MPa,
Time of repose is 40-60min.
Embodiment 3:
A kind of aroma type active carbon bacterium resisting removes formaldehyde strainer, and the aroma type active carbon bacterium resisting is except formaldehyde strainer is by following heavy
The raw material of amount part is made: 90 parts of acrylic resin, 11 parts of sulfonated phenol formaldehyde resin, 7 parts of active carbon, 5 parts of diatomite, manganese dioxide
3.5 parts, 5 parts of vinyl acetate, 3 parts of nano silica, 2.5 parts of monoglyceride, 9 parts of composite plant aromatic particulate, sodium tripolyphosphate 3
Part, 0.7 part of dispersing agent, 0.4 part of plasticizer.
The composite plant aromatic particulate is honeysuckle, peppermint, lemonlike citrus leaf, Radix Glycyrrhizae, spiceleaf, lavender, any in cloves
It is several to be mixed with；The dispersing agent is ethylene-acrylic acid copolymer, copper stearate, oxidized polyethylene wax mass ratio 2: 1: 2
Mixture；The plasticizer is phthalic acid, di-n-octyl phthalate, BBP(Butyl Benzyl Phthalate, phthalic acid
Any one in dicyclohexyl maleate.
The aroma type active carbon bacterium resisting except formaldehyde strainer preparation method the following steps are included:
(1) it after deionized water concussion dispersion being added in manganese dioxide powder, adds after diatomite after high-speed stirred mixing
Air-dry, be sintered under high temperature, crush afterwards manganese dioxide load diatomite is spare；
(2) active carbon and composite plant aromatic particulate are mixed and is added in deionized water, after mixing evenly in centrifuge
High speed centrifugation is carried out, it is spare to obtain sediment；
(3) it is stirred evenly after mixing acrylic resin, sulfonated phenol formaldehyde resin, vinyl acetate high temperature, under high temperature and pressure
Cooling is taken out after standing a period of time to be ground up, sieved, and it is spare to obtain mixture；
(4) by said mixture, manganese dioxide load diatomite, sediment, nano silica, monoglyceride, trimerization phosphorus
Sour sodium, dispersing agent, plasticizer mixed with deionized water after at a temperature of 80-100 DEG C high-speed stirred, it is rear to stand, must handle expect it is standby
With；
(5) above-mentioned processing material is subjected to spinning, obtains base-material fiber, then base-material fiber is obtained fragrant according to specification weaving networking
Odor type active carbon bacterium resisting removes formaldehyde strainer.
Wherein, the revolving speed that step (1) high speed is stirred is 1200-1400r/min, mixing time 15-
20min；The revolving speed of step (2) the high speed centrifugation is 4000-4200r/min, centrifugation time 5-8mi；The step
(3) temperature of high temperature stirring is 120-140 DEG C, and the temperature that high temperature and pressure is stood is 100-110 DEG C, pressure 15-18MPa,
Time of repose is 40-60min.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that
There is also other identical elements in process, method, article or equipment including the element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features；And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (9)
1. a kind of aroma type active carbon bacterium resisting removes formaldehyde strainer, which is characterized in that the aroma type active carbon bacterium resisting is filtered except formaldehyde
Net is made of raw material from the following weight: 80-100 parts of acrylic resin, 10-12 parts of sulfonated phenol formaldehyde resin, 6-8 parts of active carbon,
4-6 parts of diatomite, 2-5 parts of manganese dioxide, 4-6 parts of vinyl acetate, 2-4 parts of nano silica, 2-3 parts of monoglyceride, compound plant
8-10 parts of object aromatic particulate, 2-4 parts of sodium tripolyphosphate, 06-0.8 parts of dispersing agent, 0.2-0.6 parts of plasticizer.
2. a kind of aroma type active carbon bacterium resisting according to claim 1 removes formaldehyde strainer, which is characterized in that the aroma type
Active carbon bacterium resisting is made of raw material from the following weight except formaldehyde strainer: 90 parts of acrylic resin, is lived at 11 parts of sulfonated phenol formaldehyde resin
It is 7 parts of charcoal of property, 5 parts of diatomite, 3.5 parts of manganese dioxide, 5 parts of vinyl acetate, 3 parts of nano silica, 2.5 parts of monoglyceride, compound
9 parts of plant fragrance particle, 3 parts of sodium tripolyphosphate, 0.7 part of dispersing agent, 0.4 part of plasticizer.
3. a kind of aroma type active carbon bacterium resisting according to claim 1 removes formaldehyde strainer, it is characterised in that: the compound plant
Object aromatic particulate is honeysuckle, peppermint, lemonlike citrus leaf, Radix Glycyrrhizae, spiceleaf, lavender, any in cloves several is mixed with.
4. a kind of aroma type active carbon bacterium resisting according to claim 1 removes formaldehyde strainer, it is characterised in that: the dispersing agent
For ethylene-acrylic acid copolymer, copper stearate, oxidized polyethylene wax mass ratio 2: 1: 2 mixture.
5. a kind of aroma type active carbon bacterium resisting according to claim 1 removes formaldehyde strainer, it is characterised in that: the plasticizer
It is any one in phthalic acid, di-n-octyl phthalate, BBP(Butyl Benzyl Phthalate, dicyclohexyl phthalate
Kind.
6. the preparation method that a kind of aroma type active carbon bacterium resisting removes formaldehyde strainer, which is characterized in that the aroma type active carbon is anti-
Bacterium except formaldehyde strainer preparation method the following steps are included:
(1) it after deionized water concussion dispersion being added in manganese dioxide powder, adds after diatomite and is air-dried after high-speed stirred mixing,
Be sintered under high temperature, crush afterwards manganese dioxide load diatomite is spare；
(2) active carbon and composite plant aromatic particulate are mixed and is added in deionized water, carried out in centrifuge after mixing evenly
It is spare to obtain sediment for high speed centrifugation；
(3) it stirs evenly after mixing acrylic resin, sulfonated phenol formaldehyde resin, vinyl acetate high temperature, is stood under high temperature and pressure
Cooling is taken out after a period of time to be ground up, sieved, and it is spare to obtain mixture；
(4) by said mixture, manganese dioxide load diatomite, sediment, nano silica, monoglyceride, sodium tripolyphosphate,
Dispersing agent, plasticizer mixed with deionized water after at a temperature of 80-100 DEG C high-speed stirred, it is rear to stand, must handle expect it is spare；
(5) above-mentioned processing material is subjected to spinning, obtains base-material fiber, then base-material fiber is obtained into aroma type according to specification weaving networking
Active carbon bacterium resisting removes formaldehyde strainer.
7. the preparation method that a kind of aroma type active carbon bacterium resisting according to claim 6 removes formaldehyde strainer, it is characterised in that:
The revolving speed that step (1) high speed is stirred is 1200-1400r/min, mixing time 15-20min.
8. the preparation method that a kind of aroma type active carbon bacterium resisting according to claim 6 removes formaldehyde strainer, it is characterised in that:
The revolving speed of step (2) the high speed centrifugation is 4000-4200r/min, centrifugation time 5-8min.
9. the preparation method that a kind of aroma type active carbon bacterium resisting according to claim 6 removes formaldehyde strainer, it is characterised in that:
The temperature of step (3) the high temperature stirring is 120-140 DEG C, and the temperature that high temperature and pressure is stood is 100-110 DEG C, and pressure is
15-18MPa, time of repose 40-60min.