CN109881366A - A kind of manufacturing method of kingfisher melt multifunctional non-woven fabric - Google Patents
A kind of manufacturing method of kingfisher melt multifunctional non-woven fabric Download PDFInfo
- Publication number
- CN109881366A CN109881366A CN201910147898.8A CN201910147898A CN109881366A CN 109881366 A CN109881366 A CN 109881366A CN 201910147898 A CN201910147898 A CN 201910147898A CN 109881366 A CN109881366 A CN 109881366A
- Authority
- CN
- China
- Prior art keywords
- emerald green
- melt
- resulting
- woven fabric
- green melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of manufacturing methods of emerald green melt multifunctional non-woven fabric, comprising the following steps: a, by emerald green melt through high temperature solute at pure blackish green crystal；B, the resulting crystal of step a is purified using super airslide disintegrating mill and is refined by Physical Processing, the functional powder shape material of the 4000--8000 mesh of formation；C, the resulting functional powder shape material of step b is added in terylene particle or terylene chips, is mixed and made into emerald green melt master batch；D, fiber is made in the resulting emerald green melt master batch of step c, and is mixed and made into non-woven fabrics with viscose fiber, advantage is: the multifunctional fibre comprising emerald green melt can be obtained, can improve surrounding negative ion concentration 950 it is per cubic centimeter more than, improve the antibacterial ability of skin；With antibacterial action and peculiar smell effect is eliminated, and has effects that anti-mite, eliminate the unusual smell, skin blood can be promoted to recycle, removes skin surface stain, removes the cuticula of necrosis, increases skin gloss, prevents dry skin, aging.
Description
Technical field
The present invention relates to non-woven fabrics fields, and in particular to a kind of manufacturing method of kingfisher melt multifunctional non-woven fabric.
Background technique
It is widely used in the non-woven fabrics such as hygenic towelette, packaging bag by the textile fabric of raw material of high molecular material, but existing
Such textile fabric only have constitute non-woven fabrics simple function.
Emerald green melt is to mix (having removed impurity) by many kinds of substance, through 800--1200 degree Celsius or more high-temperature fusion Cheng Mo
The novel crystal of green is processed by specific physical after natural cooling, purifies refining using super airslide disintegrating mill and the powder of formation
Last shape material.Matching with other ingredients can produce with permanent electric field and pyroelectric effect, has permanent far infrared and releases
Put the function of anion；Have effects that antibacterial, anti-mite at normal temperature, eliminate the unusual smell, and skin blood can be promoted to recycle, goes to allowance for bark
Skin superficial stain removes the cuticula of necrosis, increases skin gloss, prevents dry skin, aging.
Summary of the invention
Object of the present invention is to: a kind of manufacturing method of emerald green melt multifunctional non-woven fabric is provided, emerald green melt material can be washed
Synthetic fibre textile fabric and viscose fiber carry out the combination of non-woven fabrics, and then non-woven fabrics is made to have emitting far-infrared and generation anion
Ability, produce the multifunctional non-woven fabric comprising emerald green melt material for being conducive to human health.
The technical scheme is that a kind of manufacturing method of kingfisher melt multifunctional non-woven fabric, comprising the following steps:
A, by emerald green melt through high temperature solute at pure blackish green crystal；
B, the resulting crystal of step a is purified using super airslide disintegrating mill and is refined by Physical Processing, the 4000-- of formation
The functional powder shape material of 8000 mesh；
C, the resulting functional powder shape material of step b is added in terylene particle or terylene chips, is mixed emerald green molten
Body master batch；
D, fiber is made in the resulting emerald green melt master batch of step c, and is mixed and made into non-woven fabrics with viscose fiber.
Further: the high temperature solute temperature in the step a is 800--1200 DEG C.
Further: the mass ratio of functional powder shape material and terylene particle or terylene chips is 1 in the step c:
45-1:49。
Further: the mass ratio of emerald green melt master batch and viscose fiber is 1:3-5:6 in the step d.
Compared with prior art, the invention has the advantages that the multifunctional fibre comprising emerald green melt can be obtained, after tested,
The non-woven fabrics that the present invention obtains can improve surrounding negative ion concentration 950, and per cubic centimeter above (testing standard is by GB/T 30128-
2013) antibacterial ability of skin, is improved；The fiber that the present invention obtains also has antibacterial action and eliminates peculiar smell effect, to white
Candida albicans, staphylococcus aureus, Escherichia coli, the bacteriostasis of Klebsiella Pneumoniae can reach (90-99%) (testing standard
By GB/T 20944.3-2008).And have effects that anti-mite, eliminate the unusual smell, skin blood can be promoted to recycle, remove skin surface
Stain removes the cuticula of necrosis, increases skin gloss, prevents dry skin, aging.
Specific embodiment
A kind of embodiment 1: manufacturing method of kingfisher melt multifunctional non-woven fabric, comprising the following steps:
A, by emerald green melt through 1005 DEG C of high temperature solute at pure blackish green crystal；
B, the resulting crystal of step a is purified using super airslide disintegrating mill and is refined by Physical Processing, 6700 mesh of formation
Functional powder shape material；
C, the resulting functional powder shape material of step b is added in terylene particle with the mass ratio of 1:46, is mixed
Emerald green melt master batch；
D, the resulting emerald green melt master batch of step c is made fiber, and and viscose fiber nothing is mixed and made into the mass ratio of 4:9
Woven fabric.
A kind of embodiment 2: manufacturing method of kingfisher melt multifunctional non-woven fabric, comprising the following steps:
A, by emerald green melt through 1010 DEG C of high temperature solutes at pure blackish green crystal；
B, the resulting crystal of step a is purified using super airslide disintegrating mill and is refined by Physical Processing, 7100 mesh of formation
Functional powder shape material；
C, the resulting functional powder shape material of step b is added in terylene chips with the mass ratio of 1:47, is mixed
Emerald green melt master batch；
D, fiber is made in the resulting emerald green melt master batch of step c, and is mixed with viscose fiber with the mass ratio of 5:9
Non-woven fabrics.
Made non-woven fabrics after tested, capable of improving surrounding negative ion concentration 950, per cubic centimeter above (press by testing standard
GB/T 30128-2013), improve the antibacterial ability of skin；The fiber that the present invention obtains also has antibacterial action and eliminates peculiar smell
Effect, can reach (90- to the bacteriostasis of Candida albicans, staphylococcus aureus, Escherichia coli, Klebsiella Pneumoniae
99%) (testing standard presses GB/T 20944.3-2008).And have effects that anti-mite, eliminate the unusual smell, skin blood can be promoted to follow
Ring removes skin surface stain, removes the cuticula of necrosis, increases skin gloss, prevents dry skin, aging.
A kind of embodiment 3: manufacturing method of kingfisher melt multifunctional non-woven fabric, comprising the following steps:
A, by emerald green melt through 1155 DEG C of high temperature solutes at pure blackish green crystal；
B, the resulting crystal of step a is purified using super airslide disintegrating mill and is refined by Physical Processing, 7950 mesh of formation
Functional powder shape material；
C, the resulting functional powder shape material of step b is added in terylene particle with the mass ratio of 1:47, mixing system
At emerald green melt master batch；
D, fiber is made in the resulting emerald green melt master batch of step c, and is mixed with viscose fiber with the mass ratio of 2:3
Non-woven fabrics.
A kind of embodiment 4: manufacturing method of kingfisher melt multifunctional non-woven fabric, comprising the following steps:
A, by emerald green melt through 1135 DEG C of high temperature solutes at pure blackish green crystal；
B, the resulting crystal of step a is purified using super airslide disintegrating mill and is refined by Physical Processing, 7800 mesh of formation
Functional powder shape material；
C, the resulting functional powder shape material of step b is added in terylene particle, mass ratio 1:48, mixing system
At emerald green melt master batch；
D, the resulting emerald green melt master batch of step c is made fiber, and and viscose fiber nothing is mixed and made into the mass ratio of 5:6
Woven fabric, non-woven fabrics obtained is "dead" and heavy metal substance.
Certainly the above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow be familiar with technique
People can understand the content of the present invention and implement it accordingly, it is not intended to limit the scope of the present invention.It is all according to this hair
The modification that the Spirit Essence of bright main technical schemes is done, should be covered by the protection scope of the present invention.
Claims (4)
1. a kind of manufacturing method of kingfisher melt multifunctional non-woven fabric, it is characterised in that: the following steps are included:
A, by emerald green melt through high temperature solute at pure blackish green crystal；
B, the resulting crystal of step a is purified using super airslide disintegrating mill and is refined by Physical Processing, the 4000--8000 of formation
Purpose functional powder shape material；
C, the resulting functional powder shape material of step b is added in terylene particle or terylene chips, it is female is mixed and made into emerald green melt
Grain；
D, fiber is made in the resulting emerald green melt master batch of step c, and is mixed and made into non-woven fabrics with viscose fiber.
2. a kind of manufacturing method of emerald green melt multifunctional non-woven fabric according to claim 1, it is characterised in that: the step
High temperature solute temperature in a is 800--1200 DEG C.
3. a kind of manufacturing method of emerald green melt multifunctional non-woven fabric according to claim 1, it is characterised in that: the step
The mass ratio of functional powder shape material and terylene particle or terylene chips is 1:45-1:49 in c.
4. a kind of manufacturing method of emerald green melt multifunctional non-woven fabric according to claim 1, it is characterised in that: the step
The mass ratio of emerald green melt master batch and viscose fiber is 1:3-5:6 in d.