CN109868422A - 一种粉末冶金刚轮及其制备方法 - Google Patents

一种粉末冶金刚轮及其制备方法 Download PDF

Info

Publication number
CN109868422A
CN109868422A CN201910192662.6A CN201910192662A CN109868422A CN 109868422 A CN109868422 A CN 109868422A CN 201910192662 A CN201910192662 A CN 201910192662A CN 109868422 A CN109868422 A CN 109868422A
Authority
CN
China
Prior art keywords
firm gear
preparation
powder metallurgy
powder
sintering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910192662.6A
Other languages
English (en)
Other versions
CN109868422B (zh
Inventor
张少明
王林山
石韬
汪礼敏
胡强
付东兴
王永慧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Youyan Powder New Materials Co ltd
Original Assignee
GRIPM ADVANCED MATERIALS (BEIJING) CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GRIPM ADVANCED MATERIALS (BEIJING) CO Ltd filed Critical GRIPM ADVANCED MATERIALS (BEIJING) CO Ltd
Priority to CN201910192662.6A priority Critical patent/CN109868422B/zh
Publication of CN109868422A publication Critical patent/CN109868422A/zh
Application granted granted Critical
Publication of CN109868422B publication Critical patent/CN109868422B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种少/无加工、工作过程中可自润滑的谐波减速器用粉末冶金刚轮及其制备方法。本发明的制备方法采用粉末冶金方法，包括高成分均匀性的粘结粉末制备、压制、烧结、后处理等工序。本发明制备的粉末冶金刚轮具有成分均匀、耐磨减摩性好、噪音低、寿命长、少/无加工、成本低等优点，可替代目前采用钢材、铸铁等材料加工制备的刚轮。

Description

一种粉末冶金刚轮及其制备方法
技术领域
本发明属于粉末冶金技术领域，特别涉及用于谐波减速器的一种粉末冶金刚轮及其制备方法。
背景技术
谐波齿轮减速器是一种由固定的内齿刚轮、柔轮、和使柔轮发生径向变形的波发生器组成。与普通减速器相比，具有结构简单、体积小、重量轻、传动比范围大、定位和重复定位精度高、同轴性好、可实现向密闭空间传递运动及动力等优点，广泛应用于电子、航天航空、机器人、化工等行业。由于刚轮与柔轮、柔轮与波发生器发生长时间的变形接触摩擦，导致零件发生磨损，从而引起定位和重复定位精度变差，影响其使用寿命。目前以日本为主的国际谐波减速器生产厂家，采用球墨铸铁材质制造刚轮，利用球墨铸铁的减摩性能，配合刚轮与柔轮之间的脂润滑，实现谐波减速器工作过程的耐磨减摩效果；国内厂家目前仍以合金钢材质制造刚轮，减摩效果较国际厂家不足。同时，刚轮主要制造方案仍为机加工，存在工序长、成本高等不足。
粉末冶金零件具有近净成形、自润滑等优势，已广泛应用于含油轴承、齿轮等零件中，但是并未在谐波减速器方面取得应用。刚轮零件为小模数齿轮零件，对材料成分的均匀性提出了更高的要求。目前已公开的专利CN201711059299，仅仅提出利用粉末冶金技术及材料进行刚轮坯件的制备，无具体的生产工艺数据指标，不具备可操作性。
同时常规混粉技术不足以保证混合后粉体成分的均匀性，对于小模数齿轮零件，压制烧结后变形及性能会有较大波动，使得粉末冶金材料制备的刚轮较常规合金钢或铸铁材质，优势不再明显。
发明内容
本发明的目的是针对现有技术的不足，提出一种粉末冶金刚轮及其制备方法。具体技术方案如下。
一种粉末冶金刚轮，由铁基粉末冶金材料制成，密度≥6.9g/cm3，硬度HRC30-40。
所述粉末冶金刚轮，以铁为主，添加0-2.0％Cu、0-5.0％Ni、0-1.0％Mo、0-1.0％Cr、0-1.0％Mn、0-0.5％Si和0.5-3.0％石墨诸元素中的两种或两种以上。
所述粉末冶金刚轮，其制备方法是根据成分设计，将原料粉末进行配料、混合粘结、压制成形、烧结和后处理等工序制备完成。
所述原料粉末，包括雾化、扩散等工艺制备的粉末。
所述混合粘结工序，是将原料粉末按设定比例配好后，进行混合、粘结，使原料粉体具有更好的成分均匀性、流动性、产品一致性。
所述压制工序，是将混合或粘结粉末进行压制成形，压制压强为500～800MPa，压制温度为室温～140℃，生坯密度≥6.9g/cm3。
所述烧结工序，是将刚轮生坯进行烧结，烧结温度为1000～1300℃，烧结时间为10～120分钟，气氛可以是真空、氢气、分解氨等中的一种。
所述后处理工序，包括整形、热处理、精加工、表面处理和浸润滑介质中一项或一项以上步骤。所述整形步骤工序，是根据产品的尺寸精度要求，采用全整形或齿形整形提高烧结刚轮的尺寸精度。
所述热处理步骤工序，是根据产品的硬度要求，采用淬火、回火等工艺，对烧结或整形后的刚轮进行热处理，提高刚轮的硬度。
所述精加工步骤工序，是对刚轮进行精加工，满足刚轮的尺寸精度要求。
所述表面处理步骤工序，是根据产品的硬度要求，采用表面渗碳渗氮、蒸汽处理等工艺，对烧结或整形后的刚轮进行表面处理，提高表面硬度和耐磨性。
所述浸润滑介质，是根据产品的应用场合与工况要求，选择向刚轮零件浸润滑油或润滑脂，使得润滑介质填充于刚轮零件的微小孔隙内，装配后工作过程中实现刚轮零件的自润滑特性，提高谐波减速器整体的减摩效果与使用寿命；
本发明的有益效果是粉末冶金刚轮具有成分均匀、成分可控、近净成形、耐磨减摩性好、噪音低、成本低、提高谐波减速器使用寿命等优点，可以满足谐波减速器的使用要求。
附图说明
图1为本发明粉末冶金刚轮的照片。
具体实施方式
下面结合附图，对本发明进一步详细说明。
本发明提出一种粉末冶金刚轮及其制备方法，所述方法包括原料粉末配料、混合粘结、压制成形、烧结和后处理等工序。下面以实施例进一步对本发明予以说明。
实施例1
按FLC4805粉末成分配方，将FeNiMoCu雾化粉末与石墨粉，按98.3:0.7(质量百分比)进行配料，加入1％的粘结剂溶液(粘结剂与丙酮的比例为1:10)进行粘结，粘结30分钟，然后将粉末干燥，再添加0.8％润滑剂进行混料，混料时间15分钟，然后进行压制，生坯密度7.0g/cm3，再进行1120℃、30分钟烧结，气氛为分解氨气氛，出炉后零件真空高温浸入润滑油，之后进行整形，使得尺寸符合图纸要求，然后进行表面蒸汽处理，蒸汽处理温度为560℃，时间为1小时。
实施例2
按FLC2-4808粉末成分中除石墨外的合金元素配比，制备FeNiMoCu雾化粉末，与石墨粉按照97.0:3.0(质量百分比)进行配料，加入3％的粘结剂溶液(粘结剂与丙酮的比例为1:10)进行粘结，粘结30分钟，然后将粉末干燥，再添加0.8％润滑剂进行混料，混料时间15分钟，然后进行压制，生坯密度6.95g/cm3，再进行1120℃、30分钟烧结，气氛为真空。出炉后零件真空高温浸入润滑油，之后进行整形，使得尺寸符合图纸要求，然后进行低温渗氮处理。
实施例3
将Fe粉、Ni粉、Cu粉、石墨粉按照按95.2:2.0:2.0:0.8(质量百分比)进行配料，加入1％的粘结剂溶液(粘结剂与丙酮的比例为1:10)进行粘结，粘结30分钟，然后将粉末干燥，再添加0.8％润滑剂进行混料，混料时间15分钟，然后进行压制，生坯密度7.0g/cm3，再进行1120℃、30分钟烧结，气氛为氢气气氛，出炉后零件真空高温浸入润滑油，之后进行整形，使得尺寸符合图纸要求，然后进行表面蒸汽处理，蒸汽处理温度为560℃，时间为1小时。
实施例4
将Fe粉、Ni粉、石墨粉按照按96.7:2.5:0.8(质量百分比)进行配料，加入1％的粘结剂溶液(粘结剂与丙酮的比例为1:10)进行粘结，粘结30分钟，然后将粉末干燥，再添加0.8％润滑剂进行混料，混料时间15分钟，然后进行压制，生坯密度7.0g/cm3，再进行1120℃、30分钟烧结，气氛为真空气氛，出炉后零件真空高温浸入润滑油，之后进行整形，使得尺寸符合图纸要求，然后低温渗氮处理。
实施例5
按FD0408粉末成分配方，将FeCuNiMo扩散粉末与石墨粉、按98.2:0.8(质量百分比)进行混合15分钟，加入1％的粘结剂溶液(粘结剂与丙酮的比例为1:10)进行粘结，粘结30分钟，然后将粉末干燥，再添加0.8％润滑剂进行混料，混料时间15分钟，然后进行压制，生坯密度7.0g/cm3，再进行1120℃、30分钟烧结，在分解氨气氛中，出炉后零件真空高温浸入润滑脂，然后进行整形，使得尺寸符合图纸要求，然后进行淬火、回火调质处理，零件硬度HRC33。
实施例6
将实施例5中的FD0408粉末更换为FD0205，压制温度120℃，生坯密度7.3g/cm3，渗氮处理后，再进行蒸汽处理，蒸汽处理温度为560℃，0.5小时，其他工艺与实施例1一致。
实施例7
将实施例6中模具改为留有加工余量的圆环模具，烧结坯进行渗碳淬火，硬度HRC30-40，然后按产品图纸进行机加工。
上述实施例对本发明的技术方案进行了详细说明。显然，本发明并不局限于所描述的实施例。基于本发明中的实施例，熟悉本技术领域的人员还可据此做出多种变化，但任何与本发明等同或相类似的变化都属于本发明保护的范围。

Claims (8)

1.一种粉末冶金刚轮，其特征在于，所述刚轮是铁基粉末冶金材料，密度≥6.9g/cm3，硬度HRC30-40。
2.根据权利要求1所述粉末冶金刚轮，其特征在于，以铁为主，添加0-2.0％Cu、0-5.0％Ni、0-1.0％Mo、0-1.0％Cr、0-1.0％Mn、0-0.5％Si和0.5-3.0％石墨诸元素中的两种或两种以上。
3.权利要求1所述粉末冶金刚轮的制备方法，其特征在于，包括以下步骤：
1)将原料粉末配料、混合粘结，制备高成分均匀性的粘结粉末；
2)将步骤1)制备的粘结粉末进行压制成形、烧结；
3)后处理工序。
4.根据权利要求3所述粉末冶金刚轮的制备方法，其特征在于，所述混合粘结是将原料粉末配好后，进行混合、粘结；所述原料粉末，除石墨粉之外，采用雾化或扩散工艺制备。
5.根据权利要求3所述粉末冶金刚轮的制备方法，其特征在于，所述压制，是将粘结粉末压制成形，压制压强为500～800MPa，压制温度为室温～140℃，生坯密度≥6.9g/cm3。
6.根据权利要求3所述粉末冶金刚轮的制备方法，其特征在于，所述烧结是将刚轮生坯进行烧结，烧结温度为1000～1300℃，烧结时间为10～120分钟，烧结气氛是真空、氢气和分解氨中的一种。
7.根据权利要求3所述粉末冶金刚轮的制备方法，其特征在于，所述后处理工序包括整形、热处理、精加工、表面处理和浸润滑介质中一项或一项以上步骤。
8.根据权利要求7所述粉末冶金刚轮的制备方法，其特征在于，所述整形，采用全整形或齿形整形提高烧结刚轮的尺寸精度；所述热处理，采用淬火、回火工艺，对烧结或整形后的刚轮进行热处理；所述精加工，是对刚轮进行精加工，满足刚轮的尺寸精度要求；所述表面处理，采用表面渗碳渗氮、蒸汽处理工艺，对烧结或整形后的刚轮进行表面处理；所述浸润滑介质，可选择向刚轮零件浸润滑油或润滑脂，保证工作过程的自润滑特性。
CN201910192662.6A 2019-03-14 2019-03-14 一种粉末冶金刚轮及其制备方法 Active CN109868422B (zh)