CN109866295A - A kind of production method of phase-changing and temperature-regulating bamboo mat - Google Patents
A kind of production method of phase-changing and temperature-regulating bamboo mat Download PDFInfo
- Publication number
- CN109866295A CN109866295A CN201910220812.XA CN201910220812A CN109866295A CN 109866295 A CN109866295 A CN 109866295A CN 201910220812 A CN201910220812 A CN 201910220812A CN 109866295 A CN109866295 A CN 109866295A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- phase
- temperature
- bamboo silk
- changing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of production method that the present invention discloses phase-changing and temperature-regulating bamboo mat comprising following steps: bamboo thread is dried and obtains dry bamboo silk, dry bamboo fusinization is obtained into carbonized bamboo silk, carbonized bamboo silk is immersed in phase-change material to obtain soaking and expects bamboo silk, leaching material bamboo thread is dried to obtain solid material bamboo thread, finished product bamboo silk is obtained to solid material bamboo silk brushing paint, finished product bamboo silk longitude and latitude is woven into phase-changing and temperature-regulating bamboo mat.Constant temperature of the present invention, comfortable, production is simple.
Description
Technical field
The present invention relates to bamboo mat manufacture technology field more particularly to a kind of production methods of phase-changing and temperature-regulating bamboo mat.
Background technique
Bamboo skin is split into bamboo silk generally using bamboos such as fishscale bamboo, moso bamboo, oily bamboos as raw material by bamboo mat, through works such as boiling, immersions
With craft through made of knitting device after skill.
But existing bamboo mat tends not to keep cooling feeling for a long time, and when micro- cool at night, people is when contacting bamboo mat
It can feel ice-cold, be used for a long time such bamboo mat, the use feeling that cannot have not only had, and the body of people can be allowed to come to harm.
Such as application No. is 201810396707.7 Chinese invention patents to disclose a kind of mixed weaving bamboo mat and its processing
The step of technique, processing technology include selection, separation raw material after wire drawing, boiling, drying, cleaning and dry, selects vegetation original
Material is beaten and semi-finished product rattan is made, semi-finished product rattan is carried out to waterproof and mould proof processing, sheet rattan is cut into and is core with cotton yarn
Line be made rattan, by rattan rotating Vortex complete 360 ° of the press polish processing of full circle week, shufflings at the dishes served at a feast, cut out bound edge.But this
The summer sleeping mat temperature that kind method obtains good cannot be maintained at certain temperature, can not mention under hot environment for user
User can be allowed to feel coolness for permanent cooling feeling, while under micro- cool environment, adverse effect is caused to body.
Summary of the invention
It is an object of the present invention to be directed to the above-mentioned deficiency of the prior art, propose that a kind of constant temperature, comfortable, production is simple
The production method of phase-changing and temperature-regulating bamboo mat.
The present invention solves its technical problem, the technical solution adopted is that, the production method for proposing a kind of phase-changing and temperature-regulating bamboo mat,
It includes the following steps:
(A), bamboo silk is put into hot baking room drying and obtains dry bamboo silk between 3-6% to moisture content；
(B), by dry bamboo silk be placed in 200-300 DEG C of temperature, 0.2MPa or more air pressure high pressure carbonization furnace in be heat-treated 2-5h, obtain
To carbonized bamboo silk；
(C), carbonized bamboo silk is completely infused in 3-6h in phase-change material, temperature is maintained at the above 10-20 of fusing point of phase-change material
DEG C obtain leaching material bamboo silk；
(D), by leaching material bamboo silk, from taking-up in phase-change material and below the fusing point of phase-change material at 10-20 DEG C, dry 1-3h is obtained
Admittedly expecting bamboo silk；
(E), the external coating of solid material bamboo silk is painted and air-dries to obtain finished product bamboo silk；
(F), finished product bamboo silk longitude and latitude is woven into phase-changing and temperature-regulating bamboo mat.
Preferably, the phase-change material is polyalcohol.
Further preferably, the polyalcohol is positive dodecanol.
Preferably, the temperature of the hot baking room is 180-250 DEG C in step (A).
Preferably, first to bamboo silk sprinkling mildew and insect proof liquid, the mildew and insect proof liquid includes following before step (A)
The component of mass parts: 2-5 parts of Boratex, 2-12 parts of rosin milk, 3-8 parts of water, 4-7 parts of montmorillonite powder, 3-8 parts of ethyl alcohol.
Preferably, the montmorillonite powder is nanoscale montmorillonite powder.
Preferably, before step (E) brushing paint, first in the external coating oblongleaf garcinia seed oil of solid material bamboo silk.
The invention has the following beneficial effects:
1. bamboo silk can be further dried in bamboo silk carbonization, bamboo silk can dry out in carbonisation and decomposing organic matter, so that
Bamboo silk is internal to form porous structure, increases the adsorption capacity of bamboo silk, more phase-change materials can be stored, so that bamboo mat is using
In can preferably constant temperature, lasting cooling feeling is provided.
2. phase-change material changes state of matter in the case where temperature-resistant can absorb or discharge latent heat, by carbonized bamboo
Silk is impregnated in phase-change material, and bamboo silk inner porosity can adsorb phase-change material, and low temperature drying later makes the phase of absorption
Become material and become solid, stays in porous structure, bamboo mat is maintained at the melting temperature of phase-change material later.
3. phase-change material selects n-dodecane alcohol, fusing point is 26 DEG C, can make 26 DEG C of bamboo mat constant temperature, micro- cool at night
When, people does not have ice sense contact bamboo mat moment, is suitble to all age group crowd.
4. absorbing and releasing latent heat during solid-liquid becomes with phase-change material, lasting refrigerant sense, and bamboo mat can be provided
Local temperature will not be caused to be difficult to distribute and increase because of human body long-time contact bamboo mat, can provide and comfortably sleep for a long time
Dormancy environment is not necessarily to electric drive, safety and environmental protection.
Specific embodiment
The following is specific embodiments of the present invention, and technical scheme of the present invention will be further described, but the present invention is simultaneously
It is not limited to these embodiments.
Embodiment 1:
A kind of production method of phase-changing and temperature-regulating bamboo mat comprising following steps:
(A), bamboo silk is put into hot baking room, is dried at 180 DEG C to moisture content and obtains dry bamboo silk 6%；
(B), by dry bamboo silk be placed in 300 DEG C of temperature, 0.2MPa or more air pressure high pressure carbonization furnace in be heat-treated 5h, be carbonized
Bamboo silk；
(C), carbonized bamboo silk is completely infused in 3h in n-dodecane alcohol, temperature is maintained at 15 DEG C of the fusing point of n-dodecane alcohol or more
Leaching material bamboo silk is obtained, the fusing point of n-dodecane alcohol is 26 DEG C；
(D), by leaching material bamboo silk, from taking-up in n-dodecane alcohol and below the fusing point of n-dodecane alcohol at 20 DEG C, dry 3h is obtained
Admittedly expecting bamboo silk；
(E), the external coating of solid material bamboo silk is painted and air-dries to obtain finished product bamboo silk；
(F), finished product bamboo silk longitude and latitude is woven into phase-changing and temperature-regulating bamboo mat.Finished product bamboo silk needs to cut out extra rim charge after knitting device
And it carries out bound edge and obtains finished product bamboo mat.
Embodiment 2:
A kind of production method of phase-changing and temperature-regulating bamboo mat comprising following steps:
First to bamboo silk sprinkling mildew and insect proof liquid, the mildew and insect proof liquid includes the component of following mass parts: 5 parts of Boratex, rosin
12 parts of lotion, 5.5 parts of water, 7 parts of montmorillonite powder, 3 parts of ethyl alcohol.
(A), bamboo silk is put into hot baking room, is dried at 250 DEG C to moisture content and obtains dry bamboo silk 3%；
(B), by dry bamboo silk be placed in 200 DEG C of temperature, 0.2MPa or more air pressure high pressure carbonization furnace in be heat-treated 2h, be carbonized
Bamboo silk；
(C), carbonized bamboo silk is completely infused in 6h in n-dodecane alcohol, temperature is maintained at 20 DEG C of the fusing point of n-dodecane alcohol or more
Leaching material bamboo silk is obtained, the fusing point of n-dodecane alcohol is 26 DEG C；
(D), by leaching material bamboo silk, from taking-up in n-dodecane alcohol and below the fusing point of n-dodecane alcohol at 10 DEG C, dry 1h is obtained
Admittedly expecting bamboo silk；
(E), the external coating of solid material bamboo silk is painted and air-dries to obtain finished product bamboo silk；
(F), finished product bamboo silk longitude and latitude is woven into phase-changing and temperature-regulating bamboo mat.Finished product bamboo silk needs to cut out extra rim charge after knitting device
And it carries out bound edge and obtains finished product bamboo mat.
Embodiment 3:
A kind of production method of phase-changing and temperature-regulating bamboo mat comprising following steps:
First to bamboo silk sprinkling mildew and insect proof liquid, the mildew and insect proof liquid includes the component of following mass parts: 2 parts of Boratex, rosin
7 parts of lotion, 3 parts of water, 4 parts of nano montmorillonite powder, 5.5 parts of ethyl alcohol.
(A), bamboo silk is put into hot baking room, is dried at 215 DEG C to moisture content and obtains dry bamboo silk 4%；
(B), by dry bamboo silk be placed in 250 DEG C of temperature, 0.2MPa or more air pressure high pressure carbonization furnace in be heat-treated 3.5h, obtain carbon
Change bamboo silk；
(C), carbonized bamboo silk is completely infused in 4.5h in n-dodecane alcohol, temperature is maintained at the fusing point of n-dodecane alcohol or more 10
Leaching material bamboo silk DEG C is obtained, the fusing point of n-dodecane alcohol is 26 DEG C；
(D), by leaching material bamboo silk, from taking-up in n-dodecane alcohol and below the fusing point of n-dodecane alcohol at 15 DEG C, dry 2h is obtained
Admittedly expecting bamboo silk；
(E), the external coating of solid material bamboo silk is painted and air-dries to obtain finished product bamboo silk；
(F), finished product bamboo silk longitude and latitude is woven into phase-changing and temperature-regulating bamboo mat.Finished product bamboo silk needs to cut out extra rim charge after knitting device
And it carries out bound edge and obtains finished product bamboo mat.
Embodiment 4:
A kind of production method of phase-changing and temperature-regulating bamboo mat comprising following steps:
First to bamboo silk sprinkling mildew and insect proof liquid, the mildew and insect proof liquid includes the component of following mass parts: 3.5 parts of Boratex, pine
2 parts of fragrant lotion, 8 parts of water, 5.5 parts of nano montmorillonite powder, 8 parts of ethyl alcohol.
(A), bamboo silk is put into hot baking room, is dried at 200 DEG C to moisture content and obtains dry bamboo silk 4%；
(B), by dry bamboo silk be placed in 220 DEG C of temperature, 0.2MPa or more air pressure high pressure carbonization furnace in be heat-treated 3h, be carbonized
Bamboo silk；
(C), carbonized bamboo silk is completely infused in 4h in n-dodecane alcohol, temperature is maintained at 18 DEG C of the fusing point of n-dodecane alcohol or more
Leaching material bamboo silk is obtained, the fusing point of n-dodecane alcohol is 26 DEG C；
(D), by leaching material bamboo silk, from taking-up in n-dodecane alcohol and below the fusing point of n-dodecane alcohol at 12 DEG C, dry 2h is obtained
Admittedly expecting bamboo silk；
(E), oblongleaf garcinia seed oil is first brushed on the surface of solid material bamboo silk, after air drying, then brushing paint and air-dries and obtain finished product bamboo silk；
(F), finished product bamboo silk longitude and latitude is woven into phase-changing and temperature-regulating bamboo mat.Finished product bamboo silk needs to cut out extra rim charge after knitting device
And it carries out bound edge and obtains finished product bamboo mat.
Embodiment 5:
A kind of production method of phase-changing and temperature-regulating bamboo mat comprising following steps:
(A), bamboo silk is put into hot baking room, is dried at 230 DEG C to moisture content and obtains dry bamboo silk 4%；
(B), by dry bamboo silk be placed in 280 DEG C of temperature, 0.2MPa or more air pressure high pressure carbonization furnace in be heat-treated 3h, be carbonized
Bamboo silk；
(C), carbonized bamboo silk is completely infused in 4h in n-dodecane alcohol, temperature is maintained at 18 DEG C of the fusing point of n-dodecane alcohol or more
Leaching material bamboo silk is obtained, the fusing point of n-dodecane alcohol is 26 DEG C；
(D), by leaching material bamboo silk, from taking-up in n-dodecane alcohol and below the fusing point of n-dodecane alcohol at 12 DEG C, dry 2h is obtained
Admittedly expecting bamboo silk；
(E), oblongleaf garcinia seed oil is first brushed on the surface of solid material bamboo silk, after air drying, then brushing paint and air-dries and obtain finished product bamboo silk；
(F), finished product bamboo silk longitude and latitude is woven into phase-changing and temperature-regulating bamboo mat.Finished product bamboo silk needs to cut out extra rim charge after knitting device
And it carries out bound edge and obtains finished product bamboo mat.
Specific embodiment described herein is only an example for the spirit of the invention.The neck of technology belonging to the present invention
The technical staff in domain can make various modifications or additions to the described embodiments or replace by a similar method
In generation, however, it does not deviate from the spirit of the invention or beyond the scope of the appended claims.
Claims (7)
1. a kind of production method of phase-changing and temperature-regulating bamboo mat, which comprises the steps of:
(A), bamboo silk is put into hot baking room drying and obtains dry bamboo silk between 3-6% to moisture content；
(B), by dry bamboo silk be placed in 200-300 DEG C of temperature, 0.2MPa or more air pressure high pressure carbonization furnace in be heat-treated 2-5h, obtain
To carbonized bamboo silk；
(C), carbonized bamboo silk is completely infused in 3-6h in phase-change material, temperature is maintained at the above 10-20 of fusing point of phase-change material
DEG C obtain leaching material bamboo silk；
(D), by leaching material bamboo silk, from taking-up in phase-change material and below the fusing point of phase-change material at 10-20 DEG C, dry 1-3h is obtained
Admittedly expecting bamboo silk；
(E), the external coating of solid material bamboo silk is painted and air-dries to obtain finished product bamboo silk；
(F), finished product bamboo silk longitude and latitude is woven into phase-changing and temperature-regulating bamboo mat.
2. a kind of production method of phase-changing and temperature-regulating bamboo mat according to claim 1, it is characterised in that: the phase-change material is
Polyalcohol.
3. a kind of production method of phase-changing and temperature-regulating bamboo mat according to claim 2, it is characterised in that: the polyalcohol is positive
Dodecanol.
4. a kind of production method of phase-changing and temperature-regulating bamboo mat according to claim 1, it is characterised in that: in step (A), institute
The temperature for stating hot baking room is 180-250 DEG C.
5. a kind of production method of phase-changing and temperature-regulating bamboo mat according to claim 1, it is characterised in that: before step (A),
First to bamboo silk sprinkling mildew and insect proof liquid, the mildew and insect proof liquid includes the component of following mass parts: 2-5 parts of Boratex, rosin cream
2-12 parts of liquid, 3-8 parts of water, 4-7 parts of montmorillonite powder, 3-8 parts of ethyl alcohol.
6. a kind of production method of phase-changing and temperature-regulating bamboo mat according to claim 5, it is characterised in that: the montmorillonite powder
For nanoscale montmorillonite powder.
7. a kind of production method of phase-changing and temperature-regulating bamboo mat according to claim 1, it is characterised in that: brushed in step (E)
Before paint, first in the external coating oblongleaf garcinia seed oil of solid material bamboo silk.