CN109852889B - 经济型460MPa级耐候栓钉用盘条、生产方法及栓钉 - Google Patents

经济型460MPa级耐候栓钉用盘条、生产方法及栓钉 Download PDF

Info

Publication number
CN109852889B
CN109852889B CN201910262137.7A CN201910262137A CN109852889B CN 109852889 B CN109852889 B CN 109852889B CN 201910262137 A CN201910262137 A CN 201910262137A CN 109852889 B CN109852889 B CN 109852889B
Authority
CN
China
Prior art keywords
wire rod
stud
percent
mpa
resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201910262137.7A
Other languages
English (en)
Other versions
CN109852889A (zh
Inventor
高航
韩立涛
郭大勇
王秉喜
王宏亮
马立国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Angang Steel Co Ltd
Original Assignee
Angang Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Angang Steel Co Ltd filed Critical Angang Steel Co Ltd
Priority to CN201910262137.7A priority Critical patent/CN109852889B/zh
Publication of CN109852889A publication Critical patent/CN109852889A/zh
Application granted granted Critical
Publication of CN109852889B publication Critical patent/CN109852889B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种经济型460MPa级耐候栓钉用盘条、生产方法及制备的栓钉,所述盘条的成分按重量百分比计如下:[C]0.02%~0.06%,[Si]0.15%~0.25%,[Mn]1.05%~1.25%,[P]≤0.020%,[S]≤0.015%,[Al]0.02%~0.06%,[Ni]0.25%~0.45%,[Cr]0.30%~0.60%,[Cu]0.20%~0.40%,[V]0.01%~0.04%,[Ti]0.005%~0.030%,[Mo]0.10%~0.25%,其余为铁及不可避免的杂质;生产方法,包括冶炼‑连铸‑钢坯加热‑轧制‑吐丝‑盘条冷却;采用本发明所述盘条生产的栓钉具有显著的耐候性能,屈服强度不低于460MPa,同时保持良好的焊接性能。

Description

经济型460MPa级耐候栓钉用盘条、生产方法及栓钉
技术领域
本发明属于线材产品领域,尤其涉及一种经济型460MPa级耐候栓钉用盘条、生产方法及其制备的栓钉。
背景技术
栓钉是电弧螺柱焊用圆柱头焊钉(英文Cheese head studs for arc studwelding)的简称,属于一种高强度刚度连接的紧固件,用于各种钢结构工程中,在不同连接件中起刚性组合连接作用,适用于高层钢骨结构建筑、工业厂房建筑、公路、铁路、桥梁、塔架、汽车、能源、交通设施建筑、机场、车站、电站、管道支架、起重机械及其它各类钢结构等工程。
栓钉的现行国家标准使用国标GB/T10433-2002,适用于土木建筑工程中各类结构的抗剪件,埋设件及锚固件。GB/T10433-2002非等效采用国际标准ISO13918:1998《焊接电弧螺柱焊用螺柱和磁环》,SD型剪切件(焊钉),和日本工业标准JIS B1198-1995《圆柱头焊钉》。Ф10mm~Ф25mm各种规格型号的电弧螺柱焊用圆柱头焊钉,材质SWRCH15A、ML15Al或ML15。
在钢结构中,由于栓钉可以有效地传递剪切力,在很多场合都是必须设置的。但是随着近年来耐候钢材料使用范围的不断扩大,栓钉的材料面临新的问题。母材更换为耐候钢之后,母材与栓钉的耐腐蚀能力差距增大,随着服役时间的延长,破坏必将从栓钉与母材的结合部发生,若栓钉与母材的连接被破坏,则不同连接件之间的剪切力无法传递,必将导致整个建筑结构的破坏。因此为了适应钢结构母材材质的变化,必须要开发一种耐候栓钉材料,由于栓钉对强度和焊接性能均有明确要求,因此,如何在使栓钉材料获得耐候性能的同时保持足够的强度和良好的可焊性成为开发这种材料必须解决的课题。另外,构成钢结构基础材料强度的提高对于减轻结构重量和部件数量具有显著的积极作用,栓钉目前应用的主流强度级别使400MPa,但460MPa强度级别的栓钉已开始逐步推广使用,应该开发一种460MPa级耐候栓钉用钢,满足市场对高强度栓钉的需求。除满足材料的基本性能要求外,降低材料的生产成本对于提高用户使用积极性,加快材料推广速度有利,因此在材料的化学成分构成、生产工艺等方面应该进行经济性的考虑。
发明内容
本发明的目的在于克服上述问题和不足而提供一种经济型460MPa级耐候栓钉用盘条、生产方法及其制备的栓钉,采用本发明所述盘条生产的栓钉具有显著的耐候性能(I指数≥6.0),屈服强度不低于460MPa,同时保持良好的焊接性能(Ce<0.4)。
本发明目的是这样实现的:
一种低成本耐候栓钉用低碳钢盘条,该盘条的成分按重量百分比计如下:[C]0.02%~0.06%,[Si]0.15%~0.25%,[Mn]1.05%~1.25%,[P]≤0.020%,[S]≤0.015%,[Al]0.02%~0.06%,[Ni]0.25%~0.45%,[Cr]0.30%~0.60%,[Cu]0.20%~0.40%,[V]0.01%~0.04%,[Ti]0.005%~0.030%,[Mo]0.10%~0.25%,其余为铁及不可避免的杂质;同时以上各元素在设定具体含量时应满足式(1)和式(2)的要求;
I=26.01[Cu]+3.88[Ni]+1.2[Cr]+1.49[Si]+17.28[P]-7.29[Cu][Ni]-9.1[Ni][P]-33.39[Cu]2≥6.0 (1)
Ce=[C]+[Mn]/6+([Cr]+[Mo]+[V])/5+([Ni]+[Cu])/15<0.40 (2)。
所述盘条组织由铁素体、贝氏体和马氏体组成,按面积计算贝氏体20%-30%,马氏体不超过2.5%,铁素体晶粒尺寸在15-30um。
本发明成分设计理由如下:
碳是钢中的主要强化元素,为了使栓钉具备足够的强度,必须在钢中保留一定的碳元素。同时,碳元素的提高将影响栓钉的焊接性能,因此碳含量不宜过高,因此本发明专利碳含量控制范围0.02%~0.06%。
硅是高碳钢中主要脱氧元素。钢中硅含量低将导致钢脱氧不足,钢坯表明形成针孔气泡等铸坯缺陷;钢中硅含量过高,钢液脱氧后会出现粗大的硅酸盐及杂物。同时,硅含量过高会恶化栓钉的焊接性能。因此,本发明专利钢中硅含量控制在0.15%~0.25%。
锰也是一种提高盘条强度的元素;但是锰元素过高则不利于碳当量的控制,对焊接性能不利。因此钢中锰含量控制在1.05%~1.25%。
磷、硫是钢中有害杂质元素,在不造成其他影响的情况下,越低越好。本发明专利要求盘条[P]≤0.020%,[S]≤0.015%。
铝是较强脱氧元素,含量过高将会导致钢中夹杂物的变形性恶化;但是钢中含有一定量的铝,可以保证钢液充分脱氧,同时有利于钢的组织细化,因此盘条的铝含量控制在0.02%~0.06%。
镍、铬、铜是典型的耐腐蚀元素,因此必须添加一定的量才能使材料获得足够的耐腐蚀性能,同时,钼元素对提高钢的韧性及强度有利。但是镍、铬、铜含量过高对焊接性能不利,因此要求盘条中相应的元素含量为:[Ni]0.25%~0.45%,[Cr]0.30%~0.60%,[Cu]0.20%~0.40%,[Mo]0.10%~0.25%。
钒、钛在钢中易于形成细小弥散的碳氮化物,可以钉轧晶界、细化晶粒,可以提高钢的强度。对于耐候栓钉用材料来说,为了使材料具有足够的耐腐蚀性,必须降低钢中的碳、锰含量,从而对满足栓钉的强度要求带来了困难,因此加入钒、钛进行强化。另一方面,钒、钛的加入量过多不会带来额外的强度增加,且必将导致成本的增加,因此要求[V]0.01%~0.04%,[Ti]0.005%~0.030%。
所述盘条显微组织铁素体、贝氏体和马氏体组成,其中铁素体晶粒尺寸在15-30um之间,按面积计算贝氏体含量在20-30%,马氏体含量不超过2.5%。
本发明技术方案之二是提供一种经济型460MPa级耐候栓钉用盘条的生产方法,包括冶炼-连铸-钢坯加热-轧制-吐丝-盘条冷却;
1)钢坯加热:钢坯加热的目的是使钢坯充分奥氏体化,减小钢坯的变形抗力,使线材轧制过程顺利进行。本发明中,生产盘条采用的钢坯横截面尺寸规格为:(150mm~160mm)×(150mm~160mm),钢坯加热总在炉时间2.5~3小时,均热段温度在950℃~1040℃;
2)轧制:由于高速线材轧机生产线上的冷却能力有限,对轧制过程温度进行控制可以为后续入双模块温度和吐丝温度的控制创造条件,为了实现耐候栓钉用钢盘条的组织细化,本发明要求轧件出预精轧温度控制在840℃~860℃,入双模块温度850℃~870℃;
3)吐丝:盘条的吐丝温度直接影响后续盘条的冷却速度和相变过程,本发明所述盘条吐丝直径为10.0mm~25.0mm,并要求盘条吐丝温度控制在830℃~850℃;
4)盘条冷却:在吐丝温度一定的情况下,盘条的冷却方式和冷却速度直接影响盘条在各个相区的停留时间及组织构成。与EDC工艺相比,采用传统的斯太尔摩风冷工艺生产的盘条虽然在均匀性上存在一定的劣势,但生产组织调度难度和生产成本显著降低。在斯太尔摩风冷工艺中,初始辊道速度主要影响盘条在风冷辊道上的散布状态,进而影响盘条的冷却过程。本发明要求吐丝后盘条采用风冷,具体为斯太尔摩冷却,初始辊道速度0.15-0.25m/min,风机频率全线1400Hz,平均冷速控制在2.5℃/s~6℃/s;
一种460MPa级耐候栓钉,其以所述的盘条为原料经盘条拉拔、镦粗制得,在拉拔变形过程中盘条减面率为8%-15%。
本发明的有益效果在于:
(1)本发明提供了一种经济型460MPa耐候栓钉用盘条,本发明通过合理的成分设计,结合微合金强化和低温轧制及斯太尔摩冷却工艺,使盘条在满足栓钉对可焊性要求的前提下,兼顾了栓钉对耐候性能的要求,使其可以与国内日益扩大使用范围的耐候钢板配合使用,同时,采用本发明所述盘条生产耐候栓钉时,仅需要经过较小的拉拔变形,即可使栓钉的屈服强度不低于460MPa,在满足栓钉对强度要求的同时减少了用户加工量,提高了栓钉的安全性。
(2)本发明提供了一种经济型460MPa级耐候栓钉用盘条及其生产方法,采用本发明所述盘条生产耐候栓钉时,仅需要经过较小的拉拔变形,即可使栓钉的屈服强度不低于460MPa,减少了用户加工量,提高了栓钉的安全性。同时使采用本发明所述盘条生产的栓钉具有显著的耐候性能(I指数不小于6.0)和良好的焊接性能(Ce≤0.4),同时从化学成分上减少贵合金的使用,从生产上使用更成熟成本更低的风冷工艺,使材料具有更好的经济性。
具体实施方式
下面通过实施例对本发明作进一步的说明。
本发明实施例根据技术方案的组分配比,进行冶炼-连铸-钢坯加热-轧制-吐丝-盘条冷却;
(1)钢坯加热:本发明生产盘条采用的钢坯横截面尺寸规格为:(150mm~160mm)×(150mm~160mm),钢坯加热总在炉时间2.5~3小时,均热段温度在950℃~1040℃;
(2)轧制:本发明轧件出预精轧温度控制在840℃~860℃,入双模块温度850℃~870℃;
3)吐丝:盘条吐丝直径为10.0mm~25.0mm,并要求盘条吐丝温度控制在830℃~850℃;
4)盘条冷却:吐丝后盘条采用风冷,初始辊道速度0.15-0.25m/min,平均冷速控制在2.5℃/s~6℃/s。
一种经济型460MPa级耐候栓钉,其以所述的盘条为原料经盘条拉拔、镦粗制得,在拉拔变形过程中盘条减面率为8%-15%。
本发明实施例盘条的成分见表1。本发明实施例盘条的主要生产工艺见表2。本发明实施例盘条的显微组织和性能见表3。
表1本发明实施例盘条的成分(wt%)
Figure BDA0002015630160000071
表2本发明实施例盘条的主要生产工艺
Figure BDA0002015630160000072
表3本发明实施例盘条的显微组织和性能
Figure BDA0002015630160000081
为了表述本发明,在上述中通过实施例对本发明恰当且充分地进行了说明,以上实施方式仅用于说明本发明,而并非对本发明的限制,有关技术领域的普通技术人员,在不脱离本发明的精神和范围的情况下,还可以做出各种变化和变型,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内,本发明的专利保护范围应由权利要求限定。

Claims (3)

1.一种经济型460MPa级耐候栓钉用盘条,其特征在于,所述盘条的成分按质量百分比计如下:[C] 0.02%~0.03%,[Si] 0.23%~0.25%,[Mn] 1.05%~1.25%,[P]≤0.020%,[S]≤0.015%,[Al] 0.02%~0.06%,[Ni] 0.25%~0.38%,[Cr] 0.30%~0.60%,[Cu] 0.20%~0.40%,[V] 0.01%~0.04%,[Ti] 0.005%~0.030%,[Mo]0.10%~0.25%,其余为铁及不可避免的杂质;同时以上各元素在设定具体含量时应满足式(1)和式(2)的要求;
I=26.01[Cu]+3.88[Ni]+1.2[Cr]+1.49[Si]+17.28[P]-7.29[Cu][Ni]-9.1[Ni][P]-33.39[Cu]2≥6.0 (1)
Ce=[C]+[Mn]/6+([Cr]+[Mo]+[V])/5+([Ni]+[Cu])/15<0.40 (2);
所述经济型460MPa级耐候栓钉用盘条的生产方法,包括冶炼-连铸-钢坯加热-轧制-吐丝-盘条冷却;
(1)钢坯加热:生产盘条采用的钢坯横截面尺寸规格为:(150mm~160mm)×(150mm~160mm),钢坯加热总在炉时间2.5~3小时,均热段温度在950℃~1040℃;
(2)轧制:轧件出预精轧温度控制在840℃~860℃,入双模块温度850℃~870℃;
(3)吐丝:盘条吐丝直径为10.0mm~25.0mm,并要求盘条吐丝温度控制在830℃~850℃;
(4)盘条冷却:吐丝后盘条采用风冷,初始辊道速度0.15-0.25m/min,平均冷速控制在2.5℃/s~6℃/s。
2.根据权利要求1所述的一种经济型460MPa级耐候栓钉用盘条,其特征在于,所述盘条组织由铁素体、贝氏体和马氏体组成,按面积计算贝氏体含量20%-30%,马氏体含量不超过2.5%,铁素体晶粒尺寸在15-30um。
3.一种经济型460MPa级耐候栓钉,其以权利要求1或2所述的盘条为原料经盘条拉拔、镦粗制得,在拉拔变形过程中盘条减面率为8%-15%。
CN201910262137.7A 2019-04-02 2019-04-02 经济型460MPa级耐候栓钉用盘条、生产方法及栓钉 Active CN109852889B (zh)