CN109852168A - A kind of aqueous luminous paint - Google Patents
A kind of aqueous luminous paint Download PDFInfo
- Publication number
- CN109852168A CN109852168A CN201711233841.7A CN201711233841A CN109852168A CN 109852168 A CN109852168 A CN 109852168A CN 201711233841 A CN201711233841 A CN 201711233841A CN 109852168 A CN109852168 A CN 109852168A
- Authority
- CN
- China
- Prior art keywords
- parts
- modified nano
- luminous paint
- zno
- preservative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of coatings, it include following components according to mass fraction meter more particularly, to a kind of aqueous luminous paint: 6-10 parts of Modified Nano-ZnO, 10-12 parts of titanium dioxide, 10-13 parts of glycerol, 20-30 parts of luminescent powder, 30-50 parts of acrylate and vinyl acetate emulsion, 1-2 parts of butyl glycol ether, 0.5-0.7 parts of preservative DR-7010,50-60 parts of water.Coating of the invention has brightness height, long action time, wear-resisting durable feature.
Description
Technical field
The present invention relates to technical field of coatings, more particularly, to a kind of aqueous luminous paint.
Background technique
Coating, which refers to, to be coated on body surface under certain conditions and can be formed film and play protection, decoration or other are special
A kind of liquid or solid material of function (insulation, antirust, mould proof, heat-resisting etc.), our usually described paint are only therein
It is a kind of.And due to different use demands in coating, need to assign coating different functions, luminous paint is exactly that one kind has
The new coating of specific function, by that object can be made to have luminous power at night in body surface coating luminescent coating, from
And make it with special application.For example it can be carried out in vehicle of the night to traveling in expressway two sides coating luminous paint
Guiding role, to reduce the generation of night traffic accident.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of aqueous luminous paints.
To solve the above problems, a kind of aqueous luminous paint of the invention, includes following components according to mass fraction meter: table
Modified nano zinc oxide 6-10 parts of face, 10-12 parts of titanium dioxide, 10-13 parts of glycerol, 20-30 parts of luminescent powder, acrylate and vinyl acetate emulsion 30-50
Part, 1-2 parts of butyl glycol ether, 0.5-0.7 parts of preservative DR-7010,50-60 parts of water.
Further, include following components according to mass fraction meter: 7 parts of Modified Nano-ZnO, 10 parts of titanium dioxide,
10 parts of glycerol, 25 parts of luminescent powder, 30 parts of acrylate and vinyl acetate emulsion, 1 part of butyl glycol ether, 0.5 part of preservative DR-7010,55 parts of water.
Further, include following components according to mass fraction meter: 8 parts of Modified Nano-ZnO, 10 parts of titanium dioxide,
12 parts of glycerol, 20 parts of luminescent powder, 40 parts of acrylate and vinyl acetate emulsion, 1 part of butyl glycol ether, 0.6 part of preservative DR-7010,55 parts of water.
Further, the luminous Powder Particle Size is 200-300 mesh, and the Modified Nano-ZnO granularity is 10-
16nm。
Further, a kind of above-mentioned Modified Nano-ZnO the preparation method is as follows:
It is made into certain density titanate coupling agent solution with dispersing agent, is being stirring evenly and then adding into a certain amount of nano zine oxide
Powder, coupling agent dosage be 40%, continue stirring after a certain period of time, washing filtering and at a certain temperature after dries pulverizing to obtain the final product
Above-mentioned Modified Nano-ZnO.
Further, the preparation method of above-mentioned aqueous luminous paint comprising the steps of:
(1) in stirred tank, luminescent powder, Modified Nano-ZnO, zinc oxide, titanium dioxide are sequentially added, starts stirring,
15min is stirred under 300 revs/min of revolving speed, stirring material is placed in mortar grinds 30min later；
(2) acrylate and vinyl acetate emulsion, water and step (1) are sequentially added in container and finally obtains object, and ethylene glycol fourth is added after stirring 15min
Ether, glycerol and preservative DR-7010, continuing stirring 10min can be prepared by above-mentioned aqueous luminous paint.
The beneficial effects of the present invention are: coating of the invention has brightness height, long action time, wear-resisting durable spy
Point.
Specific embodiment
Below with reference to embodiment, the present invention will be further described.These embodiments are retouched to typical case of the invention
It states, however, the present invention is not limited thereto, test method as used in the following examples unless otherwise specified, is conventional method, is made
Raw material, reagent etc. are unless otherwise specified the raw materials and reagents that can be obtained from commercial sources such as conventional markets.
A kind of aqueous luminous paint of the invention, includes following components according to mass fraction meter: surface-modified nano oxidation
6-10 parts of zinc, 10-12 parts of titanium dioxide, 10-13 parts of glycerol, 20-30 parts of luminescent powder, 30-50 parts of acrylate and vinyl acetate emulsion, butyl glycol ether 1-
2 parts, 0.5-0.7 parts of preservative DR-7010,50-60 parts of water.
Embodiment 1:
Include following components according to mass fraction meter: 7 parts of Modified Nano-ZnO, 10 parts of glycerol, shines at 10 parts of titanium dioxide
25 parts of powder, 30 parts of acrylate and vinyl acetate emulsion, 1 part of butyl glycol ether, 0.5 part of preservative DR-7010,55 parts of water；
Preparation method:
(1) in stirred tank, luminescent powder, Modified Nano-ZnO, zinc oxide, titanium dioxide are sequentially added, starts stirring,
15min is stirred under 300 revs/min of revolving speed, stirring material is placed in mortar grinds 30min later；
(2) acrylate and vinyl acetate emulsion, water and step (1) are sequentially added in container and finally obtains object, and ethylene glycol fourth is added after stirring 15min
Ether, glycerol and preservative DR-7010, continuing stirring 10min can be prepared by above-mentioned aqueous luminous paint.
Embodiment 2:
Include following components according to mass fraction meter: 8 parts of Modified Nano-ZnO, 12 parts of glycerol, shines at 10 parts of titanium dioxide
20 parts of powder, 40 parts of acrylate and vinyl acetate emulsion, 1 part of butyl glycol ether, 0.6 part of preservative DR-7010,55 parts of water；
Preparation method:
(1) in stirred tank, luminescent powder, Modified Nano-ZnO, zinc oxide, titanium dioxide are sequentially added, starts stirring,
15min is stirred under 300 revs/min of revolving speed, stirring material is placed in mortar grinds 30min later；
(2) acrylate and vinyl acetate emulsion, water and step (1) are sequentially added in container and finally obtains object, and ethylene glycol fourth is added after stirring 15min
Ether, glycerol and preservative DR-7010, continuing stirring 10min can be prepared by above-mentioned aqueous luminous paint.
Embodiment 3:
Include following components according to mass fraction meter: 6 parts of Modified Nano-ZnO, 10 parts of glycerol, shines at 10 parts of titanium dioxide
20 parts of powder, 31 parts of acrylate and vinyl acetate emulsion, 1 part of butyl glycol ether, 0.6 part of preservative DR-7010,50 parts of water；
Preparation method:
(1) in stirred tank, luminescent powder, Modified Nano-ZnO, zinc oxide, titanium dioxide are sequentially added, starts stirring,
15min is stirred under 300 revs/min of revolving speed, stirring material is placed in mortar grinds 30min later；
(2) acrylate and vinyl acetate emulsion, water and step (1) are sequentially added in container and finally obtains object, and ethylene glycol fourth is added after stirring 15min
Ether, glycerol and preservative DR-7010, continuing stirring 10min can be prepared by above-mentioned aqueous luminous paint.
Performance detection is carried out to the coating that above-described embodiment 1 and 2 prepares, the results are shown in Table 1:
The coating that 1 Examples 1 and 2 of table prepare carries out performance test results
Certainly, the above is merely preferred embodiments of the present invention, it is not intended to restrict the invention, therefore, it is all of the invention
Made any modifications, equivalent replacements, and improvements etc., should be included in protection scope of the present invention within spirit and principle.
Claims (4)
1. a kind of aqueous luminous paint, which is characterized in that according to mass fraction meter include following components: surface-modified nano oxidation
6-10 parts of zinc, 10-12 parts of titanium dioxide, 10-13 parts of glycerol, 20-30 parts of luminescent powder, 30-50 parts of acrylate and vinyl acetate emulsion, butyl glycol ether 1-
2 parts, 0.5-0.7 parts of preservative DR-7010,50-60 parts of water.
2. a kind of aqueous luminous paint according to claim 1, which is characterized in that according to mass fraction meter include with the following group
Point: 7 parts of Modified Nano-ZnO, 10 parts of titanium dioxide, 10 parts of glycerol, 25 parts of luminescent powder, 30 parts of acrylate and vinyl acetate emulsion, ethylene glycol fourth
1 part of ether, 0.5 part of preservative DR-7010,55 parts of water.
3. a kind of aqueous luminous paint according to claim 1, which is characterized in that according to mass fraction meter include with the following group
Point: 8 parts of Modified Nano-ZnO, 10 parts of titanium dioxide, 12 parts of glycerol, 20 parts of luminescent powder, 40 parts of acrylate and vinyl acetate emulsion, ethylene glycol fourth
1 part of ether, 0.6 part of preservative DR-7010,55 parts of water.
4. a kind of aqueous luminous paint according to claim 1-3, it is characterised in that: the luminous Powder Particle Size is
200-300 mesh, the Modified Nano-ZnO granularity are 10-16nm.