CN109849471A - Military anti-infrared camouflage painting tarpaulin - Google Patents
Military anti-infrared camouflage painting tarpaulin Download PDFInfo
- Publication number
- CN109849471A CN109849471A CN201811421215.5A CN201811421215A CN109849471A CN 109849471 A CN109849471 A CN 109849471A CN 201811421215 A CN201811421215 A CN 201811421215A CN 109849471 A CN109849471 A CN 109849471A
- Authority
- CN
- China
- Prior art keywords
- tarpaulin
- parts
- screen cloth
- infrared camouflage
- military anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of tarpaulins, especially military anti-infrared camouflage painting tarpaulin, it includes high-strength polyester fibers screen cloth, counterdie and facial mask, the facial mask and counterdie are fitted in the upper surface and lower end surface of high-strength polyester fibers screen cloth respectively, the counterdie and facial mask are PVC glue film, printing pigment of the invention uses inorganic cobalt element pigment, environmentally friendly, pollution-free；Printed patterns heat resisting temperature is up to 800 DEG C, and open air is exposed to the sun up to 20 years colors without significant change, and has fine weatherability, gloss retention, resistance to acid and alkali, long service life；The combination for passing through different color pigment according to specific needs, designs the military anti-infrared camouflage color tarpaulin with different infrared ray reflection wavelengths.
Description
Technical field
The present invention relates to a kind of tarpaulin, especially military anti-infrared camouflage painting tarpaulin.
Background technique
Tarpaulin material have very extensive military context, as base camp tent, a group of planes, big gun group, military vehicle, missile truck,
The shield of the targets of military importance such as interim command post, launching site, rear area warehouse, is directed to answering for various functional tarpaulins
With existing camouflage color paulin canopy is had the disadvantage that 1, printed using ink, not environmentally；2, weatherability, gloss retention, resistance to
Soda acid performance is poor, can be faded using time length；3, anti-infrared most by coating anti-infrared coating, it cannot be according to practical need
To use different outside line reflection wavelengths.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of using inorganic cobalt element pigment, passes through according to specific needs
The military anti-infrared camouflage painting paulin with the printing of different infrared ray reflection wavelengths is designed in the combination of different color pigment
Cloth.
The technical solution of the present invention is as follows: military anti-infrared camouflage painting tarpaulin, it includes high-strength polyester fibers screen cloth, bottom
Film and facial mask, the facial mask and counterdie are fitted in the upper surface and lower end surface of high-strength polyester fibers screen cloth respectively, the counterdie and
Facial mask is PVC glue film.
Further, the PVC glue film includes the raw material of following mass fraction: suspension method-polyvinyl chloride resin powder 25-30
Part, 18-24 parts of ditridecyl phthalate, 0.5-1.0 parts of epoxidized soybean oil, 5.0-8.0 parts of antimony oxide, magnesium hydroxide 3.9-
5.0 parts, 0.08-0.15 parts of ultraviolet absorbing agent, 0.03-0.09 parts of antioxidant, 1.0-1.5 parts of barium-zinc liquid stabilization agent, lightweight
5.0-13 parts of activated Calcium carbonate, different oxygen acid esters 0.40-1.0 parts.
Further, the PVC glue film production method specifically includes the following steps:
A1: mixing
By raw material by formula investment high speed blender, stirs 10-15 minutes, melted at a temperature of 100-140 DEG C
Melt state mixture；
A2: filtering
It is the filter screen filtration of 150 mesh by mixture mesh number obtained in A1, obtains filtrate；
A3: high temperature roll milling
Filtrate obtained in A2 is injected in high-temperature roller furnace and carries out pressurization roll milling, wherein reaction temperature 160-180
DEG C, pressure 60MPa, sustained response 3h；
A4: prolong and be pressed into glue film
Filtrate after high temperature roll milling obtained in A3 is produced through calender calendering formation with a thickness of 1mm-3mm's
PVC glue film, it is desirable that extruder temperature is 220 DEG C -240 DEG C, and conveying section temperature is 230 DEG C -250 DEG C, extrusion pressure 50MPa-
60MPa, drying temperature are 80 DEG C -100 DEG C, a length of 4h-6h, speed of production 5m/min-30m/min when dry；
A5: printing
By PVC glue film obtained in A4, being printed out on PVC glue film using glue film printing machine and cobalt element pigment is had not
With the military anti-infrared camouflage color tarpaulin of infrared reflection wavelength, wherein the printing precision of glue film printing machine is 1440dpi, is beaten
Print-out rate is 6pass 20m2/ h, operation temperature are 18 DEG C -28 DEG C, relative humidity 50%-75%.
Further, the high-strength polyester fibers screen cloth production method specifically includes the following steps:
B1: pretreatment is pasted on screen cloth
The processing of PVC paste dip coated, coating weight 50-350g/m are carried out to high-strength polyester fibers screen cloth using coating machine2；
Wherein, the raw material of PVC paste includes the raw material of following mass fraction: suspension method -25-30 parts of polyvinyl chloride resin powder, O-phthalic
18-24 parts of acid diesters, 0.5-1.0 parts of epoxidized soybean oil, 5.0-8.0 parts of antimony oxide, 3.9-5.0 parts of magnesium hydroxide, barium zinc
1.0-1.5 parts of liquid stability agent；PVC paste the preparation method comprises the following steps: by the 3-5 days time of immersion of raw material container, be allowed to sufficiently inhale
It receives, is stirred with high-speed mixer, using the effect of the frictional force and shearing force generated between material and bucket wall and material, into
The sufficient blended absorbent of row, reuses the filter screen filtration of 150 mesh；
B2: screen cloth is sent
By B1 obtain pad after high-strength polyester fibers screen cloth using automatic tension control transmission frame carry out screen cloth hair
It send, it is wrinkle resistant for principle when the control of tension is sent with screen cloth, tension is controlled in 100-300N；
B3: screen cloth preheating
By high-strength polyester fibers screen cloth obtained in B2 by preheating roller, pre- heat roller temperature is 80-120 DEG C.
Further, the military anti-infrared camouflage painting tarpaulin production method the following steps are included:
C1: high temperature fitting
After facial mask, counterdie and high-strength polyester fibers screen cloth are sufficiently heated or preheated, three layers at fitting embossing device
It fits together, laminate pressure 3-5Mpa, binding temperature is 160-180 DEG C, obtains military anti-infrared camouflage painting tarpaulin
Semi-finished product；
C2: embossing
Military anti-infrared camouflage painting tarpaulin semi-finished product obtained in C1 are subjected to facial mask embossed surface using embossing machine
Processing, the military anti-infrared camouflage painting tarpaulin after obtaining stamp, then by the military anti-infrared camouflage painting after stamp
Tarpaulin is fully cooled sizing by chill roll, obtains military anti-infrared camouflage painting tarpaulin finished product；
C3: test package
Military anti-infrared camouflage painting tarpaulin finished product obtained in C2 is tested, winds packaging.
The invention has the benefit that 1, printing pigment of the invention uses inorganic cobalt element pigment, it is environmentally friendly, pollution-free；
2, printed patterns heat resisting temperature is up to 800 DEG C, and open air is exposed to the sun up to 20 years colors without significant change, and have fine weatherability,
Gloss retention, resistance to acid and alkali, long service life；3, pass through the combination of different color pigment according to specific needs, designing has
The military anti-infrared camouflage color tarpaulin of different infrared ray reflection wavelengths.
Specific embodiment
Embodiment 1
Military anti-infrared camouflage painting tarpaulin, it includes high-strength polyester fibers screen cloth, counterdie and facial mask, the facial mask and
Counterdie is fitted in the upper surface and lower end surface of high-strength polyester fibers screen cloth respectively, and the counterdie and facial mask are PVC glue film.
The PVC glue film includes the raw material of following mass fraction: 25 parts of suspension method-polyvinyl chloride resin powder, O-phthalic
18 parts of acid diesters, 0.5 part of epoxidized soybean oil, 5.0 parts of antimony oxide, 3.9 parts of magnesium hydroxide, 0.08 part of ultraviolet absorbing agent,
0.03 part of antioxidant, 1 part of barium-zinc liquid stabilization agent, 5 parts of light active calcium carbonate, 0.4 part of different oxygen acid esters.
The production method of the PVC glue film specifically includes the following steps:
A1: mixing
By raw material by formula investment high speed blender, is stirred 10 minutes at a temperature of 100 DEG C, it is mixed to obtain molten condition
Close material；
A2: filtering
It is the filter screen filtration of 150 mesh by mixture mesh number obtained in A1, obtains filtrate；
A3: high temperature roll milling
Filtrate obtained in A2 is injected in high-temperature roller furnace and carries out pressurization roll milling, wherein reaction temperature is 160 DEG C, pressure
It is by force 60MPa, sustained response 3h；
A4: prolong and be pressed into glue film
By the filtrate after high temperature roll milling obtained in A3, through calender calendering formation, the PVC glue with a thickness of 1mm is produced
Film, it is desirable that extruder temperature is 220 DEG C, and conveying section temperature is 230 DEG C, extrusion pressure 50MPa, and drying temperature is 80 DEG C, dry
Shi Changwei 4h, speed of production 5m/min；
A5: printing
By PVC glue film obtained in A4, being printed out on PVC glue film using glue film printing machine and cobalt element pigment is had not
With the military anti-infrared camouflage color tarpaulin of infrared reflection wavelength, wherein the printing precision of glue film printing machine is 1440dpi, is beaten
Print-out rate is 6pass 20m2/ h, operation temperature are 18 DEG C, relative humidity 50%.
The production method of the high-strength polyester fibers screen cloth specifically includes the following steps:
B1: pretreatment is pasted on screen cloth
The processing of PVC paste dip coated, coating weight 50g/m are carried out to high-strength polyester fibers screen cloth using coating machine2；Its
In, the raw material of PVC paste includes the raw material of following mass fraction: 25 parts of suspension method-polyvinyl chloride resin powder, ditridecyl phthalate
18 parts, 0.5 part of epoxidized soybean oil, 5.0 parts of antimony oxide, 3.9 parts of magnesium hydroxide, 1.0 parts of barium-zinc liquid stabilization agent；PVC paste
The preparation method comprises the following steps: the 3 day time of immersion of raw material container to be allowed to fully absorb, is stirred with high-speed mixer, utilize
The effect of the frictional force and shearing force that generate between material and bucket wall and material carries out sufficient blended absorbent, reuses 150 mesh
Filter screen filtration；
B2: screen cloth is sent
By B1 obtain pad after high-strength polyester fibers screen cloth using automatic tension control transmission frame carry out screen cloth hair
It send, it is wrinkle resistant for principle when the control of tension is sent with screen cloth, tension is controlled in 100N；
B3: screen cloth preheating
By high-strength polyester fibers screen cloth obtained in B2 by preheating roller, pre- heat roller temperature is 80.
The production method of the military anti-infrared camouflage painting tarpaulin the following steps are included:
C1: high temperature fitting
After facial mask, counterdie and high-strength polyester fibers screen cloth are sufficiently heated or preheated, three layers at fitting embossing device
It fits together, laminate pressure 3Mpa, binding temperature is 160 DEG C, obtains military anti-infrared camouflage painting tarpaulin semi-finished product；
C2: embossing
Military anti-infrared camouflage painting tarpaulin semi-finished product obtained in C1 are subjected to facial mask embossed surface using embossing machine
Processing, the military anti-infrared camouflage painting tarpaulin after obtaining stamp, then by the military anti-infrared camouflage painting after stamp
Tarpaulin is fully cooled sizing by chill roll, obtains military anti-infrared camouflage painting tarpaulin finished product；
C3: test package
Military anti-infrared camouflage painting tarpaulin finished product obtained in C2 is tested, winds packaging.
Embodiment 2
Military anti-infrared camouflage painting tarpaulin, it includes high-strength polyester fibers screen cloth, counterdie and facial mask, the facial mask and
Counterdie is fitted in the upper surface and lower end surface of high-strength polyester fibers screen cloth respectively, and the counterdie and facial mask are PVC glue film.
The PVC glue film includes the raw material of following mass fraction: 27 parts of suspension method-polyvinyl chloride resin powder, O-phthalic
21 parts of acid diesters, 0.7 part of epoxidized soybean oil, 6 parts of antimony oxide, 4.2 parts of magnesium hydroxide, 0.11 part of ultraviolet absorbing agent, resist
0.05 part of oxygen agent, 0.2 part of barium-zinc liquid stabilization agent, 8 parts of light active calcium carbonate, 0.7 part of different oxygen acid esters.
The production method of the PVC glue film specifically includes the following steps:
A1: mixing
By raw material by formula investment high speed blender, is stirred 12 minutes at a temperature of 120 DEG C, it is mixed to obtain molten condition
Close material；
A2: filtering
It is the filter screen filtration of 150 mesh by mixture mesh number obtained in A1, obtains filtrate；
A3: high temperature roll milling
Filtrate obtained in A2 is injected in high-temperature roller furnace and carries out pressurization roll milling, wherein reaction temperature is 170 DEG C, pressure
It is by force 60MPa, sustained response 3h；
A4: prolong and be pressed into glue film
By the filtrate after high temperature roll milling obtained in A3, through calender calendering formation, the PVC glue with a thickness of 2mm is produced
Film, it is desirable that extruder temperature is 230 DEG C, and conveying section temperature is 240 DEG C, extrusion pressure 55MPa, and drying temperature is 90 DEG C, dry
Shi Changwei 5h, speed of production 20m/min；
A5: printing
By PVC glue film obtained in A4, being printed out on PVC glue film using glue film printing machine and cobalt element pigment is had not
With the military anti-infrared camouflage color tarpaulin of infrared reflection wavelength, wherein the printing precision of glue film printing machine is 1440dpi, is beaten
Print-out rate is 6pass 20m2/ h, operation temperature are 18 DEG C -2822 DEG C, relative humidity 60%.
The production method of the high-strength polyester fibers screen cloth specifically includes the following steps:
B1: pretreatment is pasted on screen cloth
The processing of PVC paste dip coated, coating weight 200g/m are carried out to high-strength polyester fibers screen cloth using coating machine2；Its
In, the raw material of PVC paste includes the raw material of following mass fraction: 27 parts of suspension method-polyvinyl chloride resin powder, ditridecyl phthalate
20 parts, 0.7 part of epoxidized soybean oil, 7 parts of antimony oxide, 4.2 parts of magnesium hydroxide, 1.2 parts of barium-zinc liquid stabilization agent；PVC paste
The preparation method comprises the following steps: the 4 day time of immersion of raw material container to be allowed to fully absorb, be stirred with high-speed mixer, utilize object
The effect of the frictional force and shearing force that generate between material and bucket wall and material, carries out sufficient blended absorbent, reuses 150 purposes
Filter screen filtration；
B2: screen cloth is sent
By B1 obtain pad after high-strength polyester fibers screen cloth using automatic tension control transmission frame carry out screen cloth hair
It send, it is wrinkle resistant for principle when the control of tension is sent with screen cloth, tension is controlled in 200N；
B3: screen cloth preheating
By high-strength polyester fibers screen cloth obtained in B2 by preheating roller, pre- heat roller temperature is 100 DEG C.
The production method of the military anti-infrared camouflage painting tarpaulin the following steps are included:
C1: high temperature fitting
After facial mask, counterdie and high-strength polyester fibers screen cloth are sufficiently heated or preheated, three layers at fitting embossing device
It fits together, laminate pressure 4Mpa, binding temperature is 170 DEG C, obtains military anti-infrared camouflage painting tarpaulin semi-finished product；
C2: embossing
Military anti-infrared camouflage painting tarpaulin semi-finished product obtained in C1 are subjected to facial mask embossed surface using embossing machine
Processing, the military anti-infrared camouflage painting tarpaulin after obtaining stamp, then by the military anti-infrared camouflage painting after stamp
Tarpaulin is fully cooled sizing by chill roll, obtains military anti-infrared camouflage painting tarpaulin finished product；
C3: test package
Military anti-infrared camouflage painting tarpaulin finished product obtained in C2 is tested, winds packaging.
Embodiment 3
Military anti-infrared camouflage painting tarpaulin, it includes high-strength polyester fibers screen cloth, counterdie and facial mask, the facial mask and
Counterdie is fitted in the upper surface and lower end surface of high-strength polyester fibers screen cloth respectively, and the counterdie and facial mask are PVC glue film.
The PVC glue film includes the raw material of following mass fraction: 30 parts of suspension method-polyvinyl chloride resin powder, O-phthalic
24 parts of acid diesters, 1.0 parts of epoxidized soybean oil, 8.0 parts of antimony oxide, 5.0 parts of magnesium hydroxide, 0.15 part of ultraviolet absorbing agent,
0.09 part of antioxidant, 1.5 parts of barium-zinc liquid stabilization agent, 13 parts of light active calcium carbonate, 1.0 parts of different oxygen acid esters.
The production method of the PVC glue film specifically includes the following steps:
A1: mixing
By raw material by formula investment high speed blender, is stirred 15 minutes at a temperature of 140 DEG C, it is mixed to obtain molten condition
Close material；
A2: filtering
It is the filter screen filtration of 150 mesh by mixture mesh number obtained in A1, obtains filtrate；
A3: high temperature roll milling
Filtrate obtained in A2 is injected in high-temperature roller furnace and carries out pressurization roll milling, wherein reaction temperature is 180 DEG C, pressure
It is by force 60MPa, sustained response 3h；
A4: prolong and be pressed into glue film
By the filtrate after high temperature roll milling obtained in A3, through calender calendering formation, the PVC glue with a thickness of 3mm is produced
Film, it is desirable that extruder temperature is 240 DEG C, and conveying section temperature is 250 DEG C, extrusion pressure 60MPa, and drying temperature is 100 DEG C, dry
Shi Changwei 6h, speed of production 30m/min；
A5: printing
By PVC glue film obtained in A4, being printed out on PVC glue film using glue film printing machine and cobalt element pigment is had not
With the military anti-infrared camouflage color tarpaulin of infrared reflection wavelength, wherein the printing precision of glue film printing machine is 1440dpi, is beaten
Print-out rate is 6pass 20m2/ h, operation temperature are 28 DEG C, relative humidity 75%.
The production method of the high-strength polyester fibers screen cloth specifically includes the following steps:
B1: pretreatment is pasted on screen cloth
The processing of PVC paste dip coated, coating weight 350g/m are carried out to high-strength polyester fibers screen cloth using coating machine2；Its
In, the raw material of PVC paste includes the raw material of following mass fraction: 30 parts of suspension method-polyvinyl chloride resin powder, ditridecyl phthalate
24 parts, 1.0 parts of epoxidized soybean oil, 8.0 parts of antimony oxide, 5.0 parts of magnesium hydroxide, 1.5 parts of barium-zinc liquid stabilization agent；PVC paste
The preparation method comprises the following steps: the 5 day time of immersion of raw material container to be allowed to fully absorb, is stirred with high-speed mixer, utilize
The effect of the frictional force and shearing force that generate between material and bucket wall and material carries out sufficient blended absorbent, reuses 150 mesh
Filter screen filtration；
B2: screen cloth is sent
By B1 obtain pad after high-strength polyester fibers screen cloth using automatic tension control transmission frame carry out screen cloth hair
It send, it is wrinkle resistant for principle when the control of tension is sent with screen cloth, tension is controlled in 300N；
B3: screen cloth preheating
By high-strength polyester fibers screen cloth obtained in B2 by preheating roller, pre- heat roller temperature is 120 DEG C.
The production method of the military anti-infrared camouflage painting tarpaulin the following steps are included:
C1: high temperature fitting
After facial mask, counterdie and high-strength polyester fibers screen cloth are sufficiently heated or preheated, three layers at fitting embossing device
It fits together, laminate pressure 5Mpa, binding temperature is 180 DEG C, obtains military anti-infrared camouflage painting tarpaulin semi-finished product；
C2: embossing
Military anti-infrared camouflage painting tarpaulin semi-finished product obtained in C1 are subjected to facial mask embossed surface using embossing machine
Processing, the military anti-infrared camouflage painting tarpaulin after obtaining stamp, then by the military anti-infrared camouflage painting after stamp
Tarpaulin is fully cooled sizing by chill roll, obtains military anti-infrared camouflage painting tarpaulin finished product；
C3: test package
Military anti-infrared camouflage painting tarpaulin finished product obtained in C2 is tested, winds packaging.
Embodiment 4: the military anti-infrared camouflage painting tarpaulin specific performance index of the present invention
As a comparison case with the common camouflage painting tarpaulin sold on the market, testing example 1-3 and comparative example respectively
Mechanical property and stability, the results are shown in Table 1:
The 1 military anti-infrared camouflage painting tarpaulin performance indicator of the present invention of table
As shown in Table 1, the tension load of military anti-infrared camouflage painting tarpaulin made from the embodiment of the present invention 1 reaches
1800 (N/cm), trap tear strength reach 200 (N), and peel strength reaches 150 (N/mm), army made from the embodiment of the present invention 2
Reach 2000 (N/cm) with the tension load of anti-infrared camouflage painting tarpaulin, trap tear strength reaches 220 (N), and removing is strong
Degree reaches 170 (N/mm), and the tension load of military anti-infrared camouflage painting tarpaulin made from the embodiment of the present invention 3 reaches 1900
(N/cm), trap tear strength reaches 210 (N), and peel strength reaches 160 (N/mm), it is seen that made from embodiment 2 it is military prevent it is red
The tension load of outside line camouflage painting tarpaulin, trap tear strength and peel strength effect are preferable, in addition,
Military anti-infrared camouflage painting tarpaulin made from embodiment 1-3 have preferable resistance to infrared linear, anti-perforation type,
Low temperature becomes folding endurance and anti-flammability, and in construction and use process, environment and human body not will cause with any harm；And market
On the tension load of common camouflage painting tarpaulin sold be 1500 (N/cm), trap tear strength is 1800 (N), peel strength
For 140 (N/mm), it is clear that, the tension load for the common camouflage painting tarpaulin sold on the market, trap tear strength, stripping
All military anti-infrared camouflage painting tarpaulin well below made from 1-3 of the embodiment of the present invention from intensity, and it is permeability resistance, low
Temperature becomes folding endurance and anti-flammability is all poor.
The above embodiments and description only illustrate the principle of the present invention and most preferred embodiment, is not departing from this
Under the premise of spirit and range, various changes and improvements may be made to the invention, these changes and improvements both fall within requirement and protect
In the scope of the invention of shield.
Claims (5)
1. military anti-infrared camouflage painting tarpaulin, it is characterised in that: it includes high-strength polyester fibers screen cloth, counterdie and facial mask,
The facial mask and counterdie are fitted in the upper surface and lower end surface of high-strength polyester fibers screen cloth respectively, and the counterdie and facial mask are
PVC glue film.
2. military anti-infrared camouflage painting tarpaulin according to claim 1, it is characterised in that: the PVC glue film includes
The raw material of following mass fraction: suspension method -25-30 parts of polyvinyl chloride resin powder, 18-24 parts of ditridecyl phthalate, epoxy is big
0.5-1.0 parts of soya-bean oil, 5.0-8.0 parts of antimony oxide, 3.9-5.0 parts of magnesium hydroxide, 0.08-0.15 parts of ultraviolet absorbing agent,
0.03-0.09 parts of antioxidant, 1.0-1.5 parts of barium-zinc liquid stabilization agent, 5.0-13 parts of light active calcium carbonate, different oxygen acid esters
0.40-1.0 parts.
3. military anti-infrared camouflage painting tarpaulin according to claim 1, it is characterised in that: the system of the PVC glue film
Make method specifically includes the following steps:
A1: mixing
By raw material by formula investment high speed blender, is stirred 10-15 minutes at a temperature of 100-140 DEG C, obtain molten
State mixture；
A2: filtering
It is the filter screen filtration of 150 mesh by mixture mesh number obtained in A1, obtains filtrate；
A3: high temperature roll milling
Filtrate obtained in A2 is injected in high-temperature roller furnace and carries out pressurization roll milling, wherein reaction temperature is 160-180 DEG C, pressure
It is by force 60MPa, sustained response 3h；
A4: prolong and be pressed into glue film
By the filtrate after high temperature roll milling obtained in A3, through calender calendering formation, the PVC glue with a thickness of 1mm-3mm is produced
Film, it is desirable that extruder temperature is 220 DEG C -240 DEG C, and conveying section temperature is 230 DEG C -250 DEG C, extrusion pressure 50MPa-60MPa, is done
Dry temperature is 80 DEG C -100 DEG C, a length of 4h-6h, speed of production 5m/min-30m/min when dry；
A5: printing
By PVC glue film obtained in A4, printed out on PVC glue film with Different Red using glue film printing machine and cobalt element pigment
The military anti-infrared camouflage color tarpaulin of outside line reflection wavelength, wherein the printing precision of glue film printing machine is 1440dpi, printing speed
Degree is 6pass 20m2/ h, operation temperature are 18 DEG C -28 DEG C, relative humidity 50%-75%.
4. military anti-infrared camouflage painting tarpaulin according to claim 1, it is characterised in that: the high-strength polyester fibers
The production method of screen cloth specifically includes the following steps:
B1: pretreatment is pasted on screen cloth
The processing of PVC paste dip coated, coating weight 50-350g/m are carried out to high-strength polyester fibers screen cloth using coating machine2；Wherein,
The raw material of PVC paste includes the raw material of following mass fraction: suspension method -25-30 parts of polyvinyl chloride resin powder, ditridecyl phthalate
18-24 parts, 0.5-1.0 parts of epoxidized soybean oil, 5.0-8.0 parts of antimony oxide, 3.9-5.0 parts of magnesium hydroxide, barium-zinc liquid peace
Determine 1.0-1.5 parts of agent；PVC paste the preparation method comprises the following steps: by the 3-5 days time of immersion of raw material container, be allowed to fully absorb, with height
Fast blender is stirred, and using the effect of the frictional force and shearing force generated between material and bucket wall and material, is carried out abundant
Blended absorbent, reuse the filter screen filtration of 150 mesh；
B2: screen cloth is sent
By B1 obtain pad after high-strength polyester fibers screen cloth using automatic tension control transmission frame carry out screen cloth transmission,
It is wrinkle resistant for principle when the control of power is sent with screen cloth, tension is controlled in 100-300N；
B3: screen cloth preheating
By high-strength polyester fibers screen cloth obtained in B2 by preheating roller, pre- heat roller temperature is 80-120 DEG C.
5. military anti-infrared camouflage painting tarpaulin described in -4 according to claim 1, it is characterised in that: the military anti-infrared
The production method of line camouflage painting tarpaulin the following steps are included:
C1: high temperature fitting
After facial mask, counterdie and high-strength polyester fibers screen cloth are sufficiently heated or preheated, three layers are bonded at fitting embossing device
Together, laminate pressure 3-5Mpa, binding temperature are 160-180 DEG C, obtain military anti-infrared camouflage painting tarpaulin half at
Product；
C2: embossing
Military anti-infrared camouflage painting tarpaulin semi-finished product obtained in C1 are subjected to the processing of facial mask embossed surface using embossing machine,
Then military anti-infrared camouflage painting tarpaulin after obtaining stamp passes through the military anti-infrared camouflage painting tarpaulin after stamp
Supercooling roller is fully cooled sizing, obtains military anti-infrared camouflage painting tarpaulin finished product；
C3: test package
Military anti-infrared camouflage painting tarpaulin finished product obtained in C2 is tested, winds packaging.