CN109848646A - A kind of anti-curing process of machining - Google Patents
A kind of anti-curing process of machining Download PDFInfo
- Publication number
- CN109848646A CN109848646A CN201811620180.8A CN201811620180A CN109848646A CN 109848646 A CN109848646 A CN 109848646A CN 201811620180 A CN201811620180 A CN 201811620180A CN 109848646 A CN109848646 A CN 109848646A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- processing
- connecting column
- curing process
- machining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-curing process of machining to form the first connecting column, the second connecting column and lug boss by one pre-treated workpiece of die cast；Pre-treated workpiece is put into a ball blast machine and is handled, pre-treated workpiece numerically-controlled machine tool is subjected to time processing after the completion of processing, forms workpiece to be formed, processes the first processing hole and the second processing hole；Workpiece to be formed is cleaned, the first processing hole and the second processing hole are nearby posted into the anti-roasting note of high temperature, workpiece to be formed is subjected to paint baking；By work pieces process threaded hole to be formed；Workpiece to be formed is subjected to infiltration processing and forms workpiece to be detected.Reduce it is subsequent scrape paint, do and prevent roasting process costs, improve production efficiency.
Description
Technical field
The present invention relates to machining field more particularly to a kind of anti-curing process of machining.
Background technique
Due to the porosity of casting, metallic sintered products, product can lead to the problem of leakage or surface treatment quality, cause to cast
It makes or the product quality disqualification rate of powder metallurgy is 10% or more, some is even up to 90% or more.Impregnation is exactly using double
The liquid substance for closing energy property, makes aforesaid liquid enter micropore by means such as vacuum, pressurizations, and then heating 85 degree becomes liquid
Solid solid, this addresses the problem the above problems.
With the rapid development of processing industry, client is higher and higher for the quality requirement of workpiece, but existing product exists
In machining process, impregnation after the completion of all hole processings leads to the residual for having containing immersion liquid in thread, complete dental inlay in this way
It is obstructed to cover rear thread go-no go gauge drift.It generally requires in existing production and processing and is done over again with screw thread screw tap, production efficiency is very low, manually
Loss is too big, and production cost is larger；And in original processing technology, product baking vanish after processing is completed, all machined surfaces are all
Need to paste the anti-roasting patch of high temperature resistant, drawback: the anti-roasting patch of high temperature resistant is at high cost, and artificial demand is big.
Summary of the invention
For overcome the deficiencies in the prior art, anti-curing process is machined one of the objects of the present invention is to provide a kind of,
It can solve the big problem of loss at high cost.
An object of the present invention adopts the following technical scheme that realization:
A kind of motor accessory, the motor accessory include the first connecting column, the second connecting column and lug boss, the lug boss
Between first connecting column and second connecting column, the motor accessory is additionally provided with the first processing hole and the second processing
Hole.
A kind of anti-curing process of machining of motor accessory, including following below scheme: a motor accessory, the motor accessory are provided
Including the first connecting column, the second connecting column and lug boss, boss between the first connecting column and the second connecting column, match by motor
Part is additionally provided with the first processing hole and the second processing hole.Die casting step: pass through one pre-treated workpiece of die cast, the first connection of molding
Column, the second connecting column and lug boss；One-pass molding step: pre-treated workpiece being put into a ball blast machine and is handled, and processing is completed
Pre-treated workpiece numerically-controlled machine tool is subjected to time processing afterwards, forms workpiece to be formed, processes the first processing hole and the second processing
Hole；Paint baking step: cleaning workpiece to be formed, and the first processing hole and the second processing hole are nearby posted the anti-roasting note of high temperature, will
Workpiece to be formed carries out paint baking；Post forming step: by work pieces process threaded hole to be formed；Infiltrate processing step: will be to
Shaping workpiece carries out infiltration processing and forms workpiece to be detected.
It further, further include going pre-treated workpiece burr and deburring to handle in the one-pass molding step.
It further, further include carrying out the workpiece after paint baking to scrape paint processing in the paint baking step.
Further, the anti-curing process of machining further includes inlaying spiral tooth socket for workpiece to be detected.
Further, the anti-curing process of the machining further includes step of leaking hunting: to workpiece to be detected leak hunting detection with
It checks air-tightness, chooses unqualified workpiece.
Further, the anti-curing process of machining further includes quality inspection step: whether the size for detecting workpiece to be detected accords with
It closes and requires.
Further, if the size of workpiece to be detected is met the requirements, workpiece to be detected is packed.
Further, if the size of workpiece to be detected is unsatisfactory for requiring, workpiece to be detected is put into and scraps area.
Further, in the infiltration processing step, infiltrate processing containing immersion liquid be waterglass or it is organic containing immersion liquid.
Compared with prior art, the beneficial effects of the present invention are:
By one pre-treated workpiece of die cast, the first connecting column, the second connecting column and lug boss are formed；Work will be pre-processed
Part is put into a ball blast machine and handles, and pre-treated workpiece numerically-controlled machine tool is carried out time processing after the completion of processing, is formed to be formed
Workpiece processes the first processing hole and the second processing hole；Workpiece to be formed is cleaned, near the first processing hole and the second processing hole
The anti-roasting note of high temperature is posted, workpiece to be formed is subjected to paint baking；By work pieces process threaded hole to be formed；By workpiece to be formed into
Row infiltration processing forms workpiece to be detected.Reduce it is subsequent scrape paint, do and prevent roasting process costs, improve production efficiency.
The above description is only an overview of the technical scheme of the present invention, in order to better understand the technical means of the present invention,
And it can be implemented in accordance with the contents of the specification, and in order to allow above and other objects, features and advantages of the invention can
It is clearer and more comprehensible, it is special below to lift preferred embodiment, and cooperate attached drawing, detailed description are as follows.
Detailed description of the invention
Fig. 1 is the perspective view of motor accessory of the present invention；
Fig. 2 is another perspective view of motor accessory shown in Fig. 1；
Fig. 3 is the another perspective view of motor accessory shown in Fig. 1；
Fig. 4 is the cross-sectional view of motor accessory shown in Fig. 1；
Fig. 5 present invention machines the flow chart of anti-curing process.
In figure: 100, motor accessory；11, the first processing hole；12, the second processing hole；13, inner cavity；14, the first connecting column；
15, the second connecting column；16, lug boss.
Specific embodiment
In the following, being described further in conjunction with attached drawing and specific embodiment to the present invention, it should be noted that not
Under the premise of conflicting, new implementation can be formed between various embodiments described below or between each technical characteristic in any combination
Example.
It should be noted that it can be directly on another component when component is referred to as " being fixed on " another component
Or there may also be components placed in the middle.When a component is considered as " connection " another component, it, which can be, is directly connected to
To another component or it may be simultaneously present component placed in the middle.When a component is considered as " being set to " another component, it
It can be and be set up directly on another component or may be simultaneously present component placed in the middle.Term as used herein is " vertical
", " horizontal ", "left", "right" and similar statement for illustrative purposes only.
Unless otherwise defined, all technical and scientific terms used herein and belong to technical field of the invention
The normally understood meaning of technical staff is identical.Term as used herein in the specification of the present invention is intended merely to description tool
The purpose of the embodiment of body, it is not intended that in the limitation present invention.Term " and or " used herein includes one or more phases
Any and all combinations of the listed item of pass.
Please refer to Fig. 1-4, a kind of motor accessory 100 includes the first connecting column 14, the second connecting column 15 and lug boss 16, institute
Lug boss 16 is stated between first connecting column 14 and second connecting column 15, the motor accessory 100 is additionally provided with
First processing hole and the second processing hole are nearby posted the anti-roasting note of high temperature, by the electricity by one processing hole 11 and the second processing hole 12
Machine accessory carries out paint baking.The motor accessory 100 as production motor accessory, it is described first processing hole 11 and second plus
Work hole 12 is used for the assembling of motor, reduces the error rate in the processing first processing hole 11 and the second processing hole 12, production efficiency
It is high.
Referring to Fig. 5, a kind of anti-curing process of machining of motor accessory, including following below scheme:
A motor accessory is provided, the motor accessory includes the first connecting column, the second connecting column and lug boss, boss
Between the first connecting column and the second connecting column, motor accessory is additionally provided with the first processing hole and the second processing hole.
Die casting step: by one pre-treated workpiece of die cast, the first connecting column, the second connecting column and lug boss are formed；
One-pass molding step: pre-treated workpiece is put into a ball blast machine and is handled, by pre-treated workpiece after the completion of processing
Numerically-controlled machine tool carries out time processing, forms workpiece to be formed, processes the first processing hole and the second processing hole；
It further include going pre-treated workpiece burr and deburring to handle in the one-pass molding step.Pass through ball blast
Processing is cleared up using High-velocity Projectiles or strengthens cast(ing) surface specifically, carrying out Luo Sha ﹑ decoring and cleaning to casting simultaneously.Compared to it
For his process for treating surface, it faster, more effectively, and can to part retain or punching press after casting process.Preferably, in institute
It states in one-pass molding step, further includes going pre-treated workpiece burr and deburring to handle.
Paint baking step: cleaning workpiece to be formed, and it is anti-roasting that the first processing hole and the second processing hole are nearby posted high temperature
Workpiece to be formed is carried out paint baking by note；Reduce it is subsequent scrape paint, do and prevent roasting process costs, improve production efficiency.
It further include carrying out the workpiece after paint baking to scrape paint processing in the paint baking step.
Post forming step: by work pieces process threaded hole to be formed；
In the post forming step, further include by numerically-controlled machine tool be work pieces process plane to be formed.
Infiltration processing step: workpiece to be formed is subjected to infiltration processing and forms workpiece to be detected.
In the infiltration processing step, after workpiece to be formed is carried out infiltration processing, workpiece to be formed is subjected to baking vanish
Processing.Due to the porosity of casting, metallic sintered products, product can lead to the problem of leakage or surface treatment quality, cause to cast
Or the product quality disqualification rate of powder metallurgy, 10% or more, some is even up to 90% or more.Impregnation is exactly using having a double meaning
The liquid substance of energy property, makes aforesaid liquid enter micropore by means such as vacuum, pressurizations, and then heating 85 degree makes liquid become hard
Real solid, this addresses the problem the above problems.Infiltration processing is not being changed into please being optimized for down for using effect, threaded hole adds
Before work, the fraction defective after set of having a denture made in this way is reduced to 5%, improves the qualification rate of product, saves manually, reduces and do over again
Rate.
In the infiltration processing step, infiltrate processing containing immersion liquid be waterglass or it is organic containing immersion liquid, further increase
The quality of surface treatment.
Specifically, the anti-curing process of machining further includes inlaying spiral tooth socket for workpiece to be detected.
It leaks hunting step: leak hunting detection to workpiece to be detected to check air-tightness, choose unqualified workpiece.Preferably,
The anti-curing process of machining further includes quality inspection step: whether the size for detecting workpiece to be detected meets the requirements.If work to be detected
The size of part is met the requirements, and workpiece to be detected is packed.If the size of workpiece to be detected is unsatisfactory for requiring, workpiece to be detected is put
Enter to scrap area.Improve the detection efficiency of workpiece.
The above embodiment is only the preferred embodiment of the present invention, and the scope of protection of the present invention is not limited thereto,
The variation and replacement for any unsubstantiality that those skilled in the art is done on the basis of the present invention belong to institute of the present invention
Claimed range.
Claims (10)
1. a kind of motor accessory, it is characterised in that: the motor accessory includes the first connecting column, the second connecting column and lug boss,
For the boss between first connecting column and second connecting column, the motor accessory is additionally provided with the first processing hole
And second processing hole.
2. a kind of anti-curing process of machining of motor accessory described in claim 1, which is characterized in that including following below scheme:
There is provided a motor accessory, the motor accessory includes the first connecting column, the second connecting column and lug boss, and boss is in the
Between one connecting column and the second connecting column, motor accessory is additionally provided with the first processing hole and the second processing hole.
Die casting step: by one pre-treated workpiece of die cast, the first connecting column, the second connecting column and lug boss are formed；
One-pass molding step: pre-treated workpiece being put into a ball blast machine and is handled, by pre-treated workpiece numerical control after the completion of processing
Lathe carries out time processing, forms workpiece to be formed, processes the first processing hole and the second processing hole；
Paint baking step: cleaning workpiece to be formed, and the first processing hole and the second processing hole are nearby posted the anti-roasting note of high temperature, will
Workpiece to be formed carries out paint baking；
Post forming step: by work pieces process threaded hole to be formed；
Infiltration processing step: workpiece to be formed is subjected to infiltration processing and forms workpiece to be detected.
3. machining anti-curing process as described in claim 1, it is characterised in that: in the one-pass molding step, further include
Burr and deburring is gone to handle pre-treated workpiece.
4. machining anti-curing process as described in claim 1, it is characterised in that: in the paint baking step, further include
Workpiece after paint baking is carried out to scrape paint processing.
5. machining anti-curing process as described in claim 1, it is characterised in that: the anti-curing process of the machining further include for
Detection workpiece inlays spiral tooth socket.
6. machining anti-curing process as described in claim 1, it is characterised in that: the anti-curing process of machining further includes leaking hunting
Step: leak hunting detection to workpiece to be detected to check air-tightness, choose unqualified workpiece.
7. machining anti-curing process as claimed in claim 6, it is characterised in that: the anti-curing process of machining further includes quality inspection
Step: whether the size for detecting workpiece to be detected meets the requirements.
8. machining anti-curing process as claimed in claim 7, it is characterised in that: if the size of workpiece to be detected is met the requirements,
Workpiece to be detected is packed.
9. machining anti-curing process as claimed in claim 7, it is characterised in that: if the size of workpiece to be detected is unsatisfactory for wanting
It asks, workpiece to be detected is put into and scraps area.
10. machining anti-curing process as described in claim 1, it is characterised in that: in the infiltration processing step, at infiltration
Reason containing immersion liquid be waterglass or it is organic contain immersion liquid.