CN109841294A - 环保型硅太阳能电池用铝浆以及制备方法 - Google Patents
环保型硅太阳能电池用铝浆以及制备方法 Download PDFInfo
- Publication number
- CN109841294A CN109841294A CN201910174852.5A CN201910174852A CN109841294A CN 109841294 A CN109841294 A CN 109841294A CN 201910174852 A CN201910174852 A CN 201910174852A CN 109841294 A CN109841294 A CN 109841294A
- Authority
- CN
- China
- Prior art keywords
- solar cell
- silicon solar
- environment friendly
- aluminium paste
- friendly silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及太阳能电池的技术领域,尤其是一种环保型硅太阳能电池用铝浆,成分主要由以下重量百分比的原料组成:玻璃粉1‑4%,无机粘结相10‑20%,金属导电铝粉65‑85%,改性剂0‑3%,其余为溶剂。本发明的制作的环保型硅太阳能电池用铝浆,导电性能好,制作的电池片翘曲度降低,光电转化率高。且工艺简单,制作方便。
Description
技术领域
本发明涉及太阳能电池的技术领域,尤其是一种环保型硅太阳能电池用铝浆以及制备方法。
背景技术
能源紧缺和环境污染等问题变得日益突出,晶硅太阳能电池已经成为当前最为成熟的光伏发电技术,铝浆性能对晶硅太阳能电池的工艺,稳定性以及提升太阳能电池的光电转化效率作用重大,目前制作的铝浆使用在太阳能电池中,导电性能差,电池片易翘曲,广电转化率低。
发明内容
为了克服现有的技术的不足,本发明提供了一种环保型硅太阳能电池用铝浆以及制备方法。
本发明解决其技术问题所采用的技术方案是:一种环保型硅太阳能电池用铝浆,成分主要由以下重量百分比的原料组成:玻璃粉1-4%,无机粘结相10-20%,金属导电铝粉65-85%,改性剂0-3%,其余为溶剂。
根据本发明的另一个实施例,进一步包括所述铝粉的平均粒度为2-10um。
根据本发明的另一个实施例,进一步包括以下步骤:
步骤一:将无机粘结相和溶剂按比例混合,在100°C的条件下,恒温搅拌1-3小时作为有机载体备用。
步骤二:将有机载体、玻璃粉以及金属导电铝粉按照重量比20:4:76混合,并持续搅拌2-4小时后成浆料。
步骤三:将搅拌后的浆料经由研磨机研磨5-8次形成分散均匀的铝浆。
根据本发明的另一个实施例,进一步包括所述研磨机为三辊研磨机。
本发明的有益效果是,制作的环保型硅太阳能电池用铝浆,导电性能好,制作的电池片翘曲度降低,光电转化率高。且工艺简单,制作方便。
具体实施方式
一种环保型硅太阳能电池用铝浆,成分主要由以下重量百分比的原料组成:玻璃粉1-4%,无机粘结相10-20%,金属导电铝粉65-85%,改性剂0-3%,其余为溶剂。所述铝粉的平均粒度为2-10um。
包括以下步骤:
步骤一:将无机粘结相和溶剂按比例混合,在100°C的条件下,恒温搅拌1-3小时作为有机载体备用。
步骤二:将有机载体、玻璃粉以及金属导电铝粉按照重量比20:4:76混合,并持续搅拌2-4小时后成浆料。
步骤三:将搅拌后的浆料经由研磨机研磨5-8次形成分散均匀的铝浆。较优的,研磨机为三辊研磨机。
实施例1:
本实施例中,一种环保型硅太阳能电池用铝浆成分主要由以下重量百分比的原料组成:玻璃粉1%,无机粘结相10%,金属导电铝粉65%,其余为溶剂。铝粉的平均粒度为2um。制备浆料时,先将10%的无机粘结相和溶剂混合,在100°C的条件下,恒温搅拌1个小时作为有机载体备用。再将20%的有机载体、1%玻璃粉以及65%金属导电铝粉混合,并持续搅拌2小时后成浆料。然后将搅拌后的浆料经由三辊研磨机研磨5次形成分散均匀的铝浆。由于铝粉的平均粒度为2um,小粒径的铝粉颗粒则可以起到填充的效果,使制作的铝浆密度更大,铝浆烧结后能形成更为平整的铝层,其次,在高温烧结的过程中,收缩过程中产生压应力与铝粉的粒径成反比,小粒径铝粉颗粒的比表面积大,烧结压应力高,则导电性能高。平均电阻率为27.4μΩ·cm 。同时,玻璃粉含量越低,可以使电池中的铝硅合金层的厚度减少到2μmz左右,有利于降低电池片的翘曲度。翘曲为1.1mm。
实施例2:
一种环保型硅太阳能电池用铝浆成分主要由以下重量百分比的原料组成:玻璃粉2%,无机粘结相15%,金属导电铝粉75%,改性剂1%,其余为溶剂。铝粉的平均粒度为5um。制备浆料时,先将15%的无机粘结相、1%的改性剂和溶剂混合,在100°C的条件下,恒温搅拌2个小时作为有机载体备用。再将20%的有机载体、2%玻璃粉以及75%金属导电铝粉混合,并持续搅拌3小时后成浆料。然后将搅拌后的浆料经由三辊研磨机研磨6次形成分散均匀的铝浆。此实施例中,平均电阻率为30.8μΩ·cm 。翘曲为1.4mm。
实施例3:
一种环保型硅太阳能电池用铝浆成分主要由以下重量百分比的原料组成:玻璃粉4%,无机粘结相20%,金属导电铝粉85%,改性剂3%,其余为溶剂。铝粉的平均粒度为10um。制备浆料时,先将20%的无机粘结相、3%的改性剂和溶剂混合,在100°C的条件下,恒温搅拌3个小时作为有机载体备用。再将20%的有机载体、4%玻璃粉以及85%金属导电铝粉混合,并持续搅拌4小时后成浆料。然后将搅拌后的浆料经由三辊研磨机研磨8次形成分散均匀的铝浆。此实施例中,平均电阻率为35.7μΩ·cm 。翘曲为1.6mm。
通过本发明可得,制作的环保型硅太阳能电池用铝浆,小粒径铝粉颗粒的比表面积大,烧结压应力高,则导电性能高。玻璃粉的含量越少,制作的电池片翘曲度降低,光电转化率高。且工艺简单,制作方便。
Claims (6)
1.一种环保型硅太阳能电池用铝浆,其特征是,成分主要由以下重量百分比的原料组成:玻璃粉1-4%,无机粘结相10-20%,金属导电铝粉65-85%,改性剂0-3%,其余为溶剂。
2.根据权利要求1所述的环保型硅太阳能电池用铝浆,其特征是,所述铝粉的平均粒度为2-10um。
3.根据权利要求1-2中任一所述的环保型硅太阳能电池用铝浆的制备方法,其特征是,包括以下步骤:
步骤一:将无机粘结相和溶剂按比例混合,在100°C的条件下,恒温搅拌1-3小时作为有机载体备用。
4.步骤二:将有机载体、玻璃粉以及金属导电铝粉按照重量比20:4:76混合,并持续搅拌2-4小时后成浆料。
5.步骤三:将搅拌后的浆料经由研磨机研磨5-8次形成分散均匀的铝浆。
6.根据权利要求3所述的环保型硅太阳能电池用铝浆的制备方法,其特征是,所述研磨机为三辊研磨机。