CN1098390A - A kind of artificial granite wall or floor tile and production method thereof - Google Patents
A kind of artificial granite wall or floor tile and production method thereof Download PDFInfo
- Publication number
- CN1098390A CN1098390A CN 94100951 CN94100951A CN1098390A CN 1098390 A CN1098390 A CN 1098390A CN 94100951 CN94100951 CN 94100951 CN 94100951 A CN94100951 A CN 94100951A CN 1098390 A CN1098390 A CN 1098390A
- Authority
- CN
- China
- Prior art keywords
- resin
- floor tile
- wall
- granite
- whiteruss
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of decorative imitated granite wall and floor tile and manufacturing process thereof.It is a major ingredient with the natural granite tankage mainly, is equipped with unsaturated polyester resin, solidifying agent, promotor, photostabilizer and whiteruss, forms through surface layer processing, main stor(e)y preparation, demoulding cutting process.Has (8-10kg/m in light weight
2), big, the rub resistance of intensity, high-low temperature resistant, advantage such as indeformable and will never fade.Production technique is simple, and production cost has only 1/10 of natural granite sheet material, can directly paste with cement mortar during use, and can reach the decorative effect of natural granite fully.
Description
The invention belongs to the building and ornament materials articles for use, particularly a kind of decorative imitated granite wall and floor tile and manufacturing process thereof.
Existing artificial granite decorative sheet is mainly synthesized by inorganic or organic raw material.Wherein inorganic artificial granite sheet material is how synthetic with stone, sand, cement etc., its weak point be heavy, folding strength is low, scratch-resistant performance is poor, easily aging, work-ing life is short, and is prone to the phenomenon of fading; Do aggregate and existing organic artificial granite sheet material is many with stone, glass cullet, with unsaturated polyester 191
#Make binding agent, it is formulated to be equipped with oxygenated pigment, its weak point be yielding, be pasted not strongly, easy to change, and solidify temperature required height, need to adopt temperature increasing facility in the production, production cost is higher.
Purpose of the present invention just provide a kind of in light weight, intensity is high, rub resistance, the ultraviolet radiation resisting ability is strong, cost is low, easily make and easy working artificial granite wall or floor tile and production method thereof.
The present invention is a major ingredient with the natural granite tankage mainly, and it is formulated to be equipped with unsaturated polyester resin, solidifying agent, promotor, photostabilizer and whiteruss, and this artificial granite wall or floor tile contains following component:
Components by weight
Natural granite tankage 100
196
#Resin 18-22
Solidifying agent (peroxidation is hexanone also) 0.55-0.63
Promotor (cobalt naphthenate) 0.50-0.53
195
#Resin 1.80-2.00
Photostabilizer (α hydroxyl-4 benzophenone) 0.17-0.25
Whiteruss 0.95-1.10
The production stage of this wall floor tile is as follows:
1, surface layer is handled: with 195
#Resin or 193
#Resin and photostabilizer, whiteruss mix, and on mould, form the layer of transparent film with the brush brushing, and be stand-by.
2, main stor(e)y preparation: with natural granite tankage, 196
#Resin, solidifying agent, promotor are mixed in proportion, and are placed on the above-mentioned mould of having brushed, and is floating with trowel, vibrates 3-5 minute then, made its spontaneous curing 12-24 hour, and solidifying temperature required is 15-25 ℃.
3, above-mentioned 5-8mm after solidification treatment is thick work in-process carry out demoulding, cutting process, promptly make the finished product artificial granite wall or floor tile.
Advantage of the present invention and positively effect are as follows:
(1) has (8-10kg/m in light weight
2), big, the rub resistance of intensity, high-low temperature resistant, advantage such as indeformable and will never fade, can reach the decorative effect of natural granite fully.
(2) production cost is low, has only 1/10 of natural granite sheet material.
(3) production technique is simple, solidifies temperature required lowly, and the time is short, easily makes, and easily construction can directly be pasted with cement mortar, overcome the construction process of pasting natural granite sheet material complexity.
Below in conjunction with embodiment in detail the present invention is described in detail.
Embodiment 1
(1) product embodiments:
Natural granite tankage 100kg
196
#Resin 18kg
Solidifying agent (peroxidation is hexanone also) 0.55kg
Promotor (cobalt naphthenate) 0.50kg
195
#Resin 1.80kg
Photostabilizer (α hydroxyl-4 benzophenone) 0.17kg
Whiteruss 0.95kg
(2) production method embodiment: with 195
#Resin 1.8kg is equipped with photostabilizer 0.17kg, whiteruss 0.95kg, after fully stirring,, is 25 ℃ in temperature and solidifies 24 hours down on mould with the brush brushing, forms the thin facial mask of layer of transparent, then with natural granite tankage 100kg, 196
#Resin 18kg, solidifying agent 0.55kg, promotor 0.50kg thorough mixing are placed on the facial mask that makes together, and be floating with trowel, vibrates 3 minutes then, makes its spontaneous curing 24 hours, and temperature is controlled at 25 ℃, promptly gets the thick artificial granite wall or floor tile 10m of 6mm
2, carry out demoulding, cutting process at last, promptly make the finished product artificial granite wall or floor tile.
Embodiment 2:
(1) product embodiments:
Natural granite tankage 100kg
196
#Resin 22kg
Solidifying agent (peroxidation is hexanone also) 0.63kg
Promotor (cobalt naphthenate) 0.55kg
195
#Resin 2.00kg
Photostabilizer (α hydroxyl-4 benzophenone) 0.25kg
Whiteruss 1.10kg
(2) production method embodiment: by above-mentioned formula ratio, solidified 12 hours, temperature is controlled at 15 ℃, and time of vibration is 5 minutes, and other is with embodiment 1.
Embodiment 3:
(1) product embodiments:
Natural granite tankage 100kg
196
#Resin 19.5kg
Solidifying agent (peroxidation is hexanone also) 0.58kg
Promotor (cobalt naphthenate) 0.53kg
195
#Resin 1.90kg
Photostabilizer (α hydroxyl-4 benzophenone) 0.23kg
Whiteruss 1.00kg
(2) production method embodiment: by above-mentioned formula ratio, solidified 18 hours, temperature is controlled at 18 ℃, and time of vibration is 4 minutes, and other is with embodiment 1.
Claims (8)
1, a kind of artificial granite wall or floor tile is characterized in that it contains following component:
Components by weight
Natural granite tankage 100
196
#Resin 18-22
Solidifying agent (peroxidation is hexanone also) 0.55-0.63
Promotor (cobalt naphthenate) 0.50-0.55
195
#Resin 1.80-2.00
Photostabilizer (α hydroxyl-4 benzophenone) 0.17-0.25
Whiteruss 0.95-1.10
2, artificial granite wall or floor tile according to claim 1 is characterized in that containing following component:
Natural granite tankage 100kg
196
#Resin 18kg
Solidifying agent (peroxidation is hexanone also) 0.55kg
Promotor (cobalt naphthenate) 0.50kg
195
#Resin 1.80kg
Photostabilizer (α hydroxyl-4 benzophenone) 0.17kg
Whiteruss 0.95kg
3, artificial granite wall or floor tile according to claim 1 is characterized in that containing following component:
Natural granite tankage 100kg
196
#Resin 22kg
Solidifying agent (peroxidation is hexanone also) 0.63kg
Promotor (cobalt naphthenate) 0.55kg
195
#Resin 2.00kg
Photostabilizer (α hydroxyl-4 benzophenone) 0.25kg
Whiteruss 1.00kg
4, artificial granite wall or floor tile according to claim 1 is characterized in that containing following component:
Natural granite tankage 100kg
196
#Resin 19.5kg
Solidifying agent (peroxidation is hexanone also) 0.58kg
Promotor (cobalt naphthenate) 0.53kg
195
#Resin 1.90kg
Photostabilizer (α hydroxyl-4 benzophenone) 0.23kg
Whiteruss 1.00kg
5, a kind of production method of artificial granite wall or floor tile is characterized in that the production stage of this wall floor tile is as follows:
(1) surface layer is handled: with 195
#Resin and photostabilizer, whiteruss mix, and on mould, form the layer of transparent film with the brush brushing, and be stand-by.
(2) main stor(e)y preparation: with natural granite tankage, 196
#Resin, solidifying agent, promotor mix by formula rate, are placed on the above-mentioned mould of having brushed, and is floating with trowel, vibrates 3-5 minute then, made its spontaneous curing 12-24 hour, and solidifying temperature required is 15-25 ℃.
(3) above-mentioned 5-8mm after solidification treatment is thick work in-process carry out demoulding, cutting process, promptly make the finished product artificial granite wall or floor tile.
6, the production method of artificial granite wall or floor tile according to claim 5 is characterized in that adopting 195 in surface layer is handled
#Resin or 193
#Resin.
7, the production method of artificial granite wall or floor tile according to claim 5 is characterized in that adding whiteruss in surface layer is handled.
8, the production method of artificial granite wall or floor tile according to claim 5 is characterized in that adopting 196 in main stor(e)y preparation technology
#Resin.