CN109837608A - A kind of manufacturing method of high-strength abrasion-proof chinampa grass silk - Google Patents
A kind of manufacturing method of high-strength abrasion-proof chinampa grass silk Download PDFInfo
- Publication number
- CN109837608A CN109837608A CN201711219316.XA CN201711219316A CN109837608A CN 109837608 A CN109837608 A CN 109837608A CN 201711219316 A CN201711219316 A CN 201711219316A CN 109837608 A CN109837608 A CN 109837608A
- Authority
- CN
- China
- Prior art keywords
- chinampa
- manufacturing
- proof
- grass silk
- extrusion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of manufacturing methods of high-strength abrasion-proof chinampa grass silk.The following steps are included: the first step, wear-resistant masterbatch, macromolecule matrix resin and processing aid are added in kneader and are combined；Material after kneading by extruder plasticizing, extrusion and is granulated by second step；Third step, by wear-resistant masterbatch obtained above, macromolecule matrix resin, Masterbatch, age resister and processing aid, hopper is added in mixing in proportion, and through screw extruder melting extrusion；4th step, the material after extrusion become chinampa grass fiber after supercooling, traction, heat treatment.Method of manufacturing technology of the invention is simple, and manufacturing cost is low, by using the wear-resistant strength height for the chinampa grass silk that this technique manufactures, to substantially increase the service life of chinampa grass silk.
Description
Technical field
The present invention relates to a kind of chinampa more particularly to a kind of manufacturing methods of high-strength abrasion-proof chinampa grass silk.
Background technique
Chinampa is divided into injection molding chinampa and braiding chinampa by production technology.Chinampa is molded using injection molding
Lawn by a plastic grain extrusion forming in a mold, and is bent by technique with the technology of bending, make blade of grass it is equidistant, etc. gauges
Rule arrangement, blade of grass height complete unity.Suitable for kindergarten, sports ground, balcony, greening, alluvial gold etc..
Lawn is woven to imitate the synthetic fibers of blade of grass shape, is implanted in woven base fabric, the painting of fixed function has been coated at the back side
Layer is to make chinampa on place of making on sports ground, lie fallow, golf court, flower garden terrace and Green space.
Existing chinampa grass silk is affected under rainwater weather condition, and chinampa grass silk is easy to fall off, wear-resisting strong
It spends low.
Summary of the invention
In view of the foregoing drawbacks, the purpose of the present invention is to provide a kind of structure fabrication process is simple, manufacturing cost is low, passes through
Using the wear-resistant strength height for the chinampa grass silk that this technique manufactures, a kind of high-strength abrasion-proof pedaline with long service life
The manufacturing method of level ground grass silk.
Thus the technical scheme adopted by the invention is that:
The following steps are included:
Wear-resistant masterbatch, macromolecule matrix resin and processing aid are added in kneader and are combined by the first step；
Material after kneading by extruder plasticizing, extrusion and is granulated by second step；
Third step, by wear-resistant masterbatch obtained above, macromolecule matrix resin, Masterbatch, age resister and processing aid, by than
Hopper is added in example mixing, and through screw extruder melting extrusion；
4th step, the material after extrusion become chinampa grass fiber after supercooling, traction, heat treatment.
As a further improvement of the above technical scheme, kneading temperature is 180 DEG C in the first step, kneading time 45
Minute.
As a further improvement of the above technical scheme, extruder screw draw ratio is 40 in the third step, and screw rod turns
Speed is 75 r/min, and melting extrusion temperature is 260 DEG C.
As a further improvement of the above technical scheme, cooling temperature is 45 DEG C in the 4th step, and traction temperature is 120
DEG C, heat treatment temperature is 140 DEG C.
The invention has the advantages that
Method of manufacturing technology of the invention is simple, and manufacturing cost is low, the chinampa grass silk manufactured by using this technique
Wear-resistant strength it is high, to substantially increase the service life of chinampa grass silk.
Specific embodiment
A kind of manufacturing method of high-strength abrasion-proof chinampa grass silk, comprising the following steps:
Wear-resistant masterbatch, macromolecule matrix resin and processing aid are added in kneader and are combined by the first step；
Material after kneading by extruder plasticizing, extrusion and is granulated by second step；
Third step, by wear-resistant masterbatch obtained above, macromolecule matrix resin, Masterbatch, age resister and processing aid, by than
Hopper is added in example mixing, and through screw extruder melting extrusion；
4th step, the material after extrusion become chinampa grass fiber after supercooling, traction, heat treatment.
As a further improvement of the above technical scheme, kneading temperature is 180 DEG C in the first step, kneading time 45
Minute.
As a further improvement of the above technical scheme, extruder screw draw ratio is 40 in the third step, and screw rod turns
Speed is 75 r/min, and melting extrusion temperature is 260 DEG C.
As a further improvement of the above technical scheme, cooling temperature is 45 DEG C in the 4th step, and traction temperature is 120
DEG C, heat treatment temperature is 140 DEG C.
Above-mentioned specific embodiment cannot function as limiting the scope of the invention, for the technology people of the art
For member, any alternate modification to made by embodiment of the present invention or transformation are fallen within the scope of protection of the present invention.
Claims (4)
1. a kind of manufacturing method of high-strength abrasion-proof chinampa grass silk, which comprises the following steps:
Wear-resistant masterbatch, macromolecule matrix resin and processing aid are added in kneader and are combined by the first step；
Material after kneading by extruder plasticizing, extrusion and is granulated by second step；
Third step, by wear-resistant masterbatch obtained above, macromolecule matrix resin, Masterbatch, age resister and processing aid, by than
Hopper is added in example mixing, and through screw extruder melting extrusion；
4th step, the material after extrusion become chinampa grass fiber after supercooling, traction, heat treatment.
2. a kind of manufacturing method of high-strength abrasion-proof chinampa grass silk according to claim 1, which is characterized in that described
Kneading temperature is 180 DEG C in the first step, and kneading time is 45 minutes.
3. a kind of manufacturing method of high-strength abrasion-proof chinampa grass silk according to claim 1, which is characterized in that described
Extruder screw draw ratio is 40 in third step, and screw speed is 75 r/min, and melting extrusion temperature is 260 DEG C.
4. a kind of manufacturing method of high-strength abrasion-proof chinampa grass silk according to claim 1, which is characterized in that described
Cooling temperature is 45 DEG C in 4th step, and traction temperature is 120 DEG C, and heat treatment temperature is 140 DEG C.