CN109837056A - A kind of preparation method of the effective Rapid-Repair glue of automobile exhaust - Google Patents
A kind of preparation method of the effective Rapid-Repair glue of automobile exhaust Download PDFInfo
- Publication number
- CN109837056A CN109837056A CN201711202359.7A CN201711202359A CN109837056A CN 109837056 A CN109837056 A CN 109837056A CN 201711202359 A CN201711202359 A CN 201711202359A CN 109837056 A CN109837056 A CN 109837056A
- Authority
- CN
- China
- Prior art keywords
- repair
- automobile exhaust
- glue
- slurry
- silica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of preparation methods of the effective Rapid-Repair glue of automobile exhaust, this method is mainly using waterborne organic silicon resin as raw material, industrial chemicals, inorganic powder, the glass fibre etc. for adding certain mass, are handled, filling obtained repair sheets after vacuum degassing through ball milling mixing.In use, the glue can directly be applied to the breakages such as automobile exhaust pipe, ternary catalyzing unit shell, repair sheets can be dried by passing through tail gas high temperature after starting automobile, kept its repair part again closed, reached gastight purpose.Repair sheets made of the present invention belong to one pack system colloid, and shrinking percentage is small, and sealing effect is excellent, and special corollary equipment is not necessarily to when use, facilitates construction.
Description
Technical field
The present invention relates to a kind of preparation methods of the effective Rapid-Repair glue of automobile exhaust, belong to composite material manufacture and application
Technical field.
Background technique
Vehicle can encounter in motion scratches chassis, causes automobile exhaust pipe or ternary catalyzing unit outer casing rupture, vehicle more
Year traveling also result in automobile exhaust pipe or ternary catalyzing unit shell knot rust it is thinning and then damaged.The method repaired mostly at present is all
It is closed using the progress of one layer of pipe collar bundled fixed thin steel shell in breakage.This method for repairing and mending construction is relatively complicated, and seals
Ineffective easy gas leakage causes automobile power insufficient, and exhaust emissions is not up to standard etc..For this purpose, market in urgent need one kind can be quick
And sealing effect good product or method solves above-mentioned technical problem.
Summary of the invention
The present invention mainly solves automobile exhaust pipe or ternary catalyzing unit outer casing rupture uses for the purpose of solving the above problems
Cumbersome, the bad problem of sealing effect of method construction of pipe collar bundled fixed repairing.And a kind of easy construction is provided, sealing effect
Good, manufacture craft is simple, and raw material sources are extensive, the Rapid-Repair glue preparation method of easy large-scale production.
To achieve the above object, the present invention adopts the following technical solutions: a kind of system of the effective Rapid-Repair glue of automobile exhaust
Preparation Method, this method add the inorganic raw material etc. of certain mass, at ball milling mixing mainly using waterborne organic silicon resin as raw material
Reason, filling obtained repair sheets after vacuum degassing.I.e. by waterborne organic silicon resin and industrial chemicals, inorganic powder, glass fibre etc.
Then ingredient by mass percentage various raw material components is added in sand mill, slurry crosses 80 meshes after ball-milling treatment 5h.It is made
Slurry be transferred in de-airing mixer, degassing processing is carried out at vacuum degree 0.01-0.03MPa；The colloid handled is filling
Into sealing in silica gel packing tube, the effective Rapid-Repair glue of automobile exhaust is made.
Specific method is realized by following processing steps:
(1) by the ingredient by mass percentage such as waterborne organic silicon resin and industrial chemicals, inorganic powder, glass fibre,
Middle waterborne organic silicon resin, industrial chemicals, inorganic powder, glass fibre are with 40%-70%:10%-20%:20%-50%:
The ratio of 1%-10% weighs various raw material components and is added in sand mill, and slurry crosses 80 meshes after ball-milling treatment 5h；
Above-mentioned industrial chemicals uses one of silica solution or sodium metasilicate；Inorganic powder uses zirconium oxide, aluminium oxide, oxidation
One of silicon is a variety of.
(2) slurry obtained in step (1) is transferred in de-airing mixer, is carried out at vacuum degree 0.01-0.03MPa
Degassing processing；
(3) colloid that step (2) has been handled is filling into sealing in silica gel packing tube, it is made that automobile exhaust is effective quickly to repair
Glue.
Beneficial effects of the present invention: compared with prior art, having easy construction and easily closed, provided by it is dedicated fast
Fast repair sheets, lower cost for material, manufacture craft is simple, easy mass production.Repair sheets made of the present invention belong to one pack system
Colloid, shrinking percentage is small, and sealing effect is excellent, and special corollary equipment is not necessarily to when use, facilitates construction.
Specific embodiment:
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is described in further detail.
Embodiment 1
Weigh waterborne organic silicon resin 1kg, silica solution 0.4kg, zirconium oxide 0.3kg, silica 0.7kg, glass fibre
The above material is fitted into ball milling 5h in sand mill, slurry was taken out 80 meshes later, is transferred in vacuum degassing machine and stir by 0.1kg
Degasification is mixed, vacuum degree control is in 0.02MPa.The slurry handled well is filling into sealing in silica gel packing tube, automobile exhaust is made
Effective Rapid-Repair glue.
Embodiment 2
Weigh waterborne organic silicon resin 1.4kg, silica solution 0.5kg, zirconium oxide 0.2kg, aluminium oxide 0.1kg, silica
The above material is fitted into ball milling 5h in sand mill, slurry was taken out 80 meshes later by 0.25kg, glass fibre 0.05kg, is turned
Enter stirring degassing in vacuum degassing machine, vacuum degree control is in 0.03MPa.The slurry handled well is filling into close in silica gel packing tube
The effective Rapid-Repair glue of automobile exhaust is made in envelope.
Embodiment 3
Weigh waterborne organic silicon resin 1.7kg, silica solution 0.25kg, aluminium oxide 0.3kg, silica 0.2kg, glass fibre
The above material is fitted into ball milling 5h in sand mill, slurry was taken out 80 meshes later, is transferred in vacuum degassing machine and stir by 0.05kg
Degasification is mixed, vacuum degree control is in 0.01MPa.The slurry handled well is filling into sealing in silica gel packing tube, automobile exhaust is made
Effective Rapid-Repair glue.
The effective Rapid-Repair glue of automobile exhaust prepared by above-described embodiment 1 to 3, in use, the glue can be directly applied to
The breakages such as automobile exhaust pipe, ternary catalyzing unit shell, repair sheets can be dried by tail gas high temperature after automobile by starting, and repair it
It is again closed to mend part, reaches air tight purpose.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modification within mind and principle, equivalent replacement and improvement etc., should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of preparation method of the effective Rapid-Repair glue of automobile exhaust, this method mainly using waterborne organic silicon resin as raw material,
Industrial chemicals, inorganic powder, the glass fibre for adding certain mass, are handled through ball milling mixing, and filling be made is repaired after vacuum degassing
Glue.
2. the preparation method of the effective Rapid-Repair glue of automobile exhaust as described in claim 1, this method is by following techniques
What step was realized:
(1) by waterborne organic silicon resin and industrial chemicals, inorganic powder, glass fibre ingredient by mass percentage, wherein aqueous
Organic siliconresin, industrial chemicals, inorganic powder, glass fibre are with 40%-70%:10%-20%:20%-50%:1%-10%
Ratio weigh various raw material components and be added in sand mills, slurry crosses 80 meshes after ball-milling treatment 5h；
Above-mentioned industrial chemicals uses one of silica solution or sodium metasilicate；Inorganic powder is using in zirconium oxide, aluminium oxide, silica
It is one or more；
(2) slurry obtained in step (1) is transferred in de-airing mixer, degasification is carried out at vacuum degree 0.01-0.03MPa
Processing；
(3) colloid that step (2) has been handled is filling into sealing in silica gel packing tube, the effective Rapid-Repair of automobile exhaust is made
Glue.
3. the preparation method of the effective Rapid-Repair glue of automobile exhaust as claimed in claim 2, this method is by following specific
What processing step and technical conditions were realized:
Waterborne organic silicon resin 1kg, silica solution 0.4kg, zirconium oxide 0.3kg, silica 0.7kg, glass fibre 0.1kg are weighed,
The above material is fitted into ball milling 5h in sand mill, slurry was taken out into 80 meshes later, is transferred to stirring degassing in vacuum degassing machine,
Vacuum degree control is filling into sealing in silica gel packing tube by the slurry handled well in 0.02MPa, and it is effective quickly that automobile exhaust is made
Repair sheets.
4. the preparation method of the effective Rapid-Repair glue of automobile exhaust as claimed in claim 2, this method is by following specific
What processing step and technical conditions were realized:
Waterborne organic silicon resin 1.4kg, silica solution 0.5kg, zirconium oxide 0.2kg, aluminium oxide 0.1kg, silica 0.25kg are weighed,
The above material is fitted into ball milling 5h in sand mill, slurry was taken out 80 meshes later, is transferred to vacuum and remove by glass fibre 0.05kg
Stirring degassing in mechanism of qi, vacuum degree control is filling into sealing in silica gel packing tube by the slurry handled well in 0.03MPa, is made
The effective Rapid-Repair glue of automobile exhaust.
5. the preparation method of the effective Rapid-Repair glue of automobile exhaust as claimed in claim 2, this method is by following specific
What processing step and technical conditions were realized:
Weigh waterborne organic silicon resin 1.7kg, silica solution 0.25kg, aluminium oxide 0.3kg, silica 0.2kg, glass fibre
The above material is fitted into ball milling 5h in sand mill, slurry was taken out 80 meshes later, is transferred in vacuum degassing machine and stir by 0.05kg
Mix degasification, vacuum degree control is filling into sealing in silica gel packing tube by the slurry handled well in 0.01MPa, and automobile exhaust is made
Effective Rapid-Repair glue.
6. the application method of the effective Rapid-Repair glue of automobile exhaust as described in any one in claim 2-5, this method
It is the breakage that prepared Rapid-Repair glue is directly applied to automobile exhaust pipe, ternary catalyzing unit shell, after starting automobile
Repair sheets can be dried by tail gas high temperature, keep its repair part again closed, reach air tight purpose.