CN109836536A - A kind of fire proofing - Google Patents
A kind of fire proofing Download PDFInfo
- Publication number
- CN109836536A CN109836536A CN201711191341.1A CN201711191341A CN109836536A CN 109836536 A CN109836536 A CN 109836536A CN 201711191341 A CN201711191341 A CN 201711191341A CN 109836536 A CN109836536 A CN 109836536A
- Authority
- CN
- China
- Prior art keywords
- fire proofing
- fire
- melamine
- antioxidant
- vinyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of fire proofing, the fire proofing is grouped as by each group that quality is following percentage: 12%~24% antioxidant, 11%~15% titanate coupling agent, 1%~3% ammonium polyphosphate, 1%~3% melamine, 1%~3% graphite powder, 3%~12% polyurethane adhesive, 1%~5% stearic acid, 5%~8% calcium zinc stabilizer, surplus are vinyl acetate.The invention has the beneficial effects that: the utility model material technology is simple, and material source is extensive, low in cost, and good flame retardation effect is easy to large-scale production, has a vast market foreground.
Description
One, technical field
The present invention relates to a kind of new materials, more particularly to a kind of fire proofing.
Two, background technique
Fire proofing be able to suppress or retardation burning and oneself be not easy to burning material, be widely used in taking
The fields such as dress, petroleum, chemical industry, metallurgy, shipbuilding, fire-fighting, national defence.
Due in addition to some nontoxic inorganic fire retardantss, magnesium hydroxide, aluminium hydroxide etc. for now.Halogen system
The application of (bromine system and chlorine system) fire retardant is also very extensive, and main cause is comparatively the additive amount of halogenated flame retardant compares
Few, the flame retarding efficiency of halogen system especially bromide fire retardant is especially high.From the point of view of present situation, halogen and with synergistic effect
Halogen-antimony system has occupied dominant contribution in world's amount of flame-retardant agent, and it is bromide fire retardant that wherein dosage is maximum, mainly has
Tetrabromobisphenol A, decabromodiphenyl oxide, tetrabromo-phthalic xylenol acid anhydride, dibromoneopentyl glycol, 1986 according to Switzerland scientist, it is more
When dibromodiphenyl ether burns, toxic carcinogenic more bromo dibenzo dioxanes and dibenzofurans are generated, the same year, also there was class in Germany
Like report.Oppose halide as the scientist (including ecologist, environmentalist, greenization scholar) of fire retardant and appears in west
Square developed country (the especially Germany and Sweden in Northern Europe), the fire retardant bring environmental security in relation to halide is a little
Place causes extensive concern.
The key of fire proofing greenization is the selection of fire retardant.The Green Sustainable direction of fire retardant should right and wrong
PBT, non-CMR substance, rather than without bromine or Halogen.Aggretion type or macromolecular fire retardant are inherent due to having in its structure
Hypotoxicity, abiotic cumulative bad and make environment-friendly flame retardant agent hot spot developing direction.
A kind of simple process is studied at this stage, and material source is extensive, and low in cost, good flame retardation effect is easy to scale metaplasia
It produces, the fire proofing having a vast market foreground is very important.
Three, summary of the invention
In order to overcome the shortcoming of existing new material, the present invention provides a kind of fire proofings.
The technical proposal of the invention is realized in this way.
A kind of fire proofing of this programme, the fire proofing are grouped as by each group that quality is following percentage: 12%
~24% antioxidant, 11%~15% titanate coupling agent, 1%~3% ammonium polyphosphate, 1%~3% melamine, 1%~
3% graphite powder, 3%~12% polyurethane adhesive, 1%~5% stearic acid, 5%~8% calcium zinc stabilizer, surplus are vinyl acetate
Rouge.
The fire proofing is grouped as by each group that quality is following percentage: 15% antioxidant, 12% titanate esters are coupled
Agent, 2% ammonium polyphosphate, 1% melamine, 3% graphite powder, 7% polyurethane adhesive, 4% stearic acid, 6% calcium zinc stabilizer, surplus
For vinyl acetate.
The fire proofing is grouped as by each group that quality is following percentage: 21% antioxidant, 14% titanate esters are coupled
Agent, 2% ammonium polyphosphate, 2% melamine, 2% graphite powder, 5% polyurethane adhesive, 2% stearic acid, 7% calcium zinc stabilizer, surplus
For vinyl acetate.
The fire proofing is grouped as by each group that quality is following percentage: 19% antioxidant, 12% titanate esters are coupled
Agent, 3% ammonium polyphosphate, 3% melamine, 3% graphite powder, 5% polyurethane adhesive, 1% stearic acid, 8% calcium zinc stabilizer, surplus
For vinyl acetate.
The invention has the beneficial effects that: the utility model material technology is simple, and material source is extensive, low in cost, fire-retardant effect
Fruit is good, is easy to large-scale production, has a vast market foreground.
Four, specific embodiment
Embodiment 1
A kind of fire proofing, by 15kg antioxidant, 12kg titanate coupling agent, 2kg ammonium polyphosphate, 1kg melamine,
3kg graphite powder, 7kg polyurethane adhesive, 4kg stearic acid, 6kg calcium zinc stabilizer, it is fire-retardant that 50kg vinyl acetate is mixed and made into 100kg
Material, the utility model material technology is simple, and material source is extensive, low in cost, and good flame retardation effect is easy to large-scale production, has
Vast market prospect.
Embodiment 2
A kind of fire proofing, by 21kg antioxidant, 14kg titanate coupling agent, 2kg ammonium polyphosphate, 2kg melamine,
2kg graphite powder, 5kg polyurethane adhesive, 2kg stearic acid, 7kg calcium zinc stabilizer, it is fire-retardant that 45kg vinyl acetate is mixed and made into 100kg
Material, the utility model material technology is simple, and material source is extensive, low in cost, and good flame retardation effect is easy to large-scale production, has
Vast market prospect.
Embodiment 3
A kind of fire proofing, by 19kg antioxidant, 12kg titanate coupling agent, 3kg ammonium polyphosphate, 3kg melamine,
3kg graphite powder, 5kg polyurethane adhesive, 1kg stearic acid, 8kg calcium zinc stabilizer, it is fire-retardant that 46kg vinyl acetate is mixed and made into 100kg
Material, the utility model material technology is simple, and material source is extensive, low in cost, and good flame retardation effect is easy to large-scale production, has
Vast market prospect.
One embodiment of the present invention has been described in detail above, but the content is only preferable implementation of the invention
Example, should not be considered as limiting the scope of the invention.It is all according to all the changes and improvements made by the present patent application range
Deng should still be within the scope of the patent of the present invention.
Claims (4)
1. a kind of fire proofing, it is characterised in that: the fire proofing is grouped as by each group that quality is following percentage: 12%
~24% antioxidant, 11%~15% titanate coupling agent, 1%~3% ammonium polyphosphate, 1%~3% melamine, 1%~
3% graphite powder, 3%~12% polyurethane adhesive, 1%~5% stearic acid, 5%~8% calcium zinc stabilizer, surplus are vinyl acetate
Rouge.
2. a kind of fire proofing according to claim 1, it is characterised in that: the fire proofing is following percentage by quality
The each group of ratio is grouped as: 15% antioxidant, 12% titanate coupling agent, 2% ammonium polyphosphate, 1% melamine, 3% graphite powder,
7% polyurethane adhesive, 4% stearic acid, 6% calcium zinc stabilizer, surplus are vinyl acetate.
3. a kind of fire proofing according to claim 1, it is characterised in that: the fire proofing is following percentage by quality
The each group of ratio is grouped as: 21% antioxidant, 14% titanate coupling agent, 2% ammonium polyphosphate, 2% melamine, 2% graphite powder,
5% polyurethane adhesive, 2% stearic acid, 7% calcium zinc stabilizer, surplus are vinyl acetate.
4. a kind of fire proofing according to claim 1, it is characterised in that: the fire proofing is following percentage by quality
The each group of ratio is grouped as: 19% antioxidant, 12% titanate coupling agent, 3% ammonium polyphosphate, 3% melamine, 3% graphite powder,
5% polyurethane adhesive, 1% stearic acid, 8% calcium zinc stabilizer, surplus are vinyl acetate.