CN109834788A - A kind of woodwork anti-corrosion method - Google Patents
A kind of woodwork anti-corrosion method Download PDFInfo
- Publication number
- CN109834788A CN109834788A CN201711202458.5A CN201711202458A CN109834788A CN 109834788 A CN109834788 A CN 109834788A CN 201711202458 A CN201711202458 A CN 201711202458A CN 109834788 A CN109834788 A CN 109834788A
- Authority
- CN
- China
- Prior art keywords
- woodwork
- parts
- preservative
- corrosion method
- temperature process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of anti-corrosion method, in particular to a kind of woodwork anti-corrosion method, comprising the following steps: (1) woodwork is dried, makes its moisture below 15%；(2) preservative is injected into woodwork in vacuum high-pressure；(3) woodwork after addition preservative is then subjected to high-temperature process, the time is 10 ~ 15 hours；(4) woodwork after high-temperature process ventilation is placed on to air-dry.Quaternary ammonium salt, mantoquita, sodium tetraborate and ammonium hydroxide in the present invention be all it is nontoxic, it is environmentally protective；And be conducive to absorption of the woodwork to preservative under conditions of high pressure vacuum.
Description
Technical field
The present invention relates to a kind of anti-corrosion method, in particular to a kind of woodwork anti-corrosion method.
Background technique
Woodwork is a kind of organic material, has apparent biological nature, is easily invaded by biologies such as bacterium, worm, the raw drilling worms in sea
It attacks, so the long-time service of woodwork especially long-term outdoor use is very restricted.Spoilage organisms can cause woodwork
Rot, destroy it.Before use, select suitable preservative according to different application environments, appropriate place is carried out
Reason, then can effectively delay woodwork rotten.As the improvement of people's living standards, the demand to timber also increasingly increases
Add.It is extremely limited that China can fell the forest reserves used, therefore, carry out preservative treatment to woodwork, extend making for woodwork
It is to save one of timber, the important channel to protect forest resources with the time limit.Nowadays timber that China uses after preservative treatment is very
It is few, and the traditional anti-corrosion method big to the mankind and environmental hazard is used mostly.
Summary of the invention
The present invention overcomes deficiencies in the prior art, provide a kind of woodwork anti-corrosion method, solve the above problem
Defect.
In order to solve the above-mentioned technical problem, the present invention is achieved by the following technical solutions: a kind of woodwork anti-corrosion side
Method, comprising the following steps:
Woodwork is dried, makes its moisture below 15%；
Preservative is injected into woodwork in vacuum high-pressure；
Then the woodwork after addition preservative is subjected to high-temperature process, the time is 10 ~ 15 hours；
Woodwork after high-temperature process is placed on ventilation to air-dry.
According to parts by weight, the preservative includes following component: 8 ~ 10 parts of quaternary ammonium salt, 30 ~ 40 parts of mantoquita, sodium tetraborate
2 ~ 4 parts, 3 ~ 5 parts of ammonium hydroxide.
Preferably, according to parts by weight, the preservative includes following component: 9 parts of quaternary ammonium salt, 35 parts of mantoquita,
3 parts of sodium tetraborate, 4 parts of ammonium hydroxide.
Advantageous effect of the invention is: quaternary ammonium salt, mantoquita, sodium tetraborate and ammonium hydroxide in the present invention are all nontoxic, greens
Environmental protection；And be conducive to absorption of the woodwork to preservative under conditions of high pressure vacuum.
Specific embodiment
Present invention is further described in detail With reference to embodiment:
A kind of woodwork anti-corrosion method, comprising the following steps:
Woodwork is dried, makes its moisture below 15%；
9 parts of quaternary ammonium salt, 35 parts of mantoquita, 3 parts of sodium tetraborate, 4 parts of ammonium hydroxide preparations are injected into woodwork in vacuum high-pressure
At preservative；
Then the woodwork after addition preservative is subjected to high-temperature process, the time is 10 ~ 15 hours；
Woodwork after high-temperature process is placed on ventilation to air-dry.
Technical characteristic of the present invention without description can realize that details are not described herein by or using the prior art, certainly,
Above-mentioned specific embodiment is not limitation of the present invention, and the present invention is also not limited to above-mentioned specific embodiment, this skill
The variations, modifications, additions or substitutions that the those of ordinary skill in art field is made within the essential scope of the present invention should also be fallen into
In protection scope of the present invention.
Claims (3)
1. a kind of woodwork anti-corrosion method, which comprises the following steps:
(1) woodwork is dried, makes its moisture below 15%；
(2) preservative is injected into woodwork in vacuum high-pressure；
(3) woodwork after addition preservative is then subjected to high-temperature process, the time is 10 ~ 15 hours；
(4) woodwork after high-temperature process ventilation is placed on to air-dry.
2. woodwork anti-corrosion method as described in claim 1, which is characterized in that according to parts by weight, the preservative includes
Following component: 8 ~ 10 parts of quaternary ammonium salt, 30 ~ 40 parts of mantoquita, 2 ~ 4 parts of sodium tetraborate, 3 ~ 5 parts of ammonium hydroxide.
3. woodwork anti-corrosion method according to claim 2, which is characterized in that according to parts by weight, the preservative packet
Include following component: 9 parts of quaternary ammonium salt, 35 parts of mantoquita, 3 parts of sodium tetraborate, 4 parts of ammonium hydroxide.