CN109826381A - Production process of wallboard outer surface film - Google Patents
Production process of wallboard outer surface film Download PDFInfo
- Publication number
- CN109826381A CN109826381A CN201910105460.3A CN201910105460A CN109826381A CN 109826381 A CN109826381 A CN 109826381A CN 201910105460 A CN201910105460 A CN 201910105460A CN 109826381 A CN109826381 A CN 109826381A
- Authority
- CN
- China
- Prior art keywords
- parts
- film layer
- pvc
- pvc film
- pad pasting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of a wallboard outer surface film, which comprises the following steps: s1, preparing a pvc film layer; step S2 preparing a base fabric layer; step S3 fitting; step S4 computer graphics; step S5 printing; step S6 surface treatment; step S7, trimming and rolling; the PVC film in the step S1 of preparing the PVC film comprises 45-65 parts of PVC resin, 6-8 parts of polypropylene fiber, 0.5-1 part of diphenyl-isooctyl phosphite, 2-4 parts of stabilizer, 3-6 parts of polypropylene fiber, 1 part of glass fiber, 2-6 parts of light calcium carbonate and 1-3 parts of flame-retardant filling material.
Description
[technical field]
The present invention relates to the technical fields of wallboard appearance mask production, especially the production work of wallboard appearance mask
The technical field of skill.
[background technique]
Wallboard is that modern house fits up a kind of very universal finishing material, and Modern Public Building pursues human nature fashion, warp
It is durable and easy to repair long, and the achievement board wall system as Modern Interior Decoration science and technology becomes best selection.Existing wall
Plate surface will use pad pasting covering to enhance dicoration more, and the relationship between quality of surfaces of wall pad pasting shows to the aesthetics of wallboard
There is pad pasting second-rate, pad pasting is easy to damage, and pad pasting fire protecting performance is poor.
[summary of the invention]
The object of the invention is to solve the problems of the prior art, a kind of production work of wallboard appearance mask is proposed
Skill can be improved pad pasting quality, improve pad pasting fire protecting performance.
To achieve the above object, the invention proposes a kind of production technologies of wallboard appearance mask, including following step
It is rapid:
The preparation of step S1pvc film layer: by PVC film layer particle using calendering formation in calender pressure, PVC film layer is formed；
The preparation of step S2 base cloth layer: taking non-woven fabrics, and non-woven fabrics is cut into suitable width, is wound spare；
Step S3 fitting: by PVC film layer obtained in step S1 by addition glue, heating pressurized adhesion is together cold
But, it is wound after cooling spare；
Step S4 computer graphics: go out on wallpaper to need to print the figure of decorative pattern by computer drawing；
Step S5 stamp: wallpaper being placed on digital decorating machine and carries out quick stamp, presses pattern on PVC facial mask surface
It is required that carry out two to six chromaticity printings, using a kind of mill base material of color of every set, intaglio plate revolving speed is 80~120 meters/
Point, after one chromatography of every printing, next chromaticity printing is entered back into after 120~140 DEG C of drying, colored PVC facial mask is made, finally
The colored PVC facial mask being completed for printing is wound into big volume；
Step S6 treatment: in wallpaper surface sprayed protection coating, and it is heated to 120-140 DEG C, heating time are as follows:
80-120s；
Step S7 trimming winding: pad pasting obtained in step S6 is placed in pad pasting cutting machine, is carried out through pad pasting cutting machine
It is spare to carry out packing encapsulation for splitting winding after winding.
Preferably, the raw material of the pvc film layer in the step S1pvc film layer preparation is polyvinyl chloride resin 45-65 parts, gathers
6-8 parts of tacryl, phosphorous acid hexichol -0.5-1 parts of different monooctyl ester, 2-4 parts of stabilizer, 3-6 parts of polypropylene fibre, glass fibre 1
Part, 2-6 parts of precipitated calcium carbonate, 1-3 parts of flame resistant filler material.
Preferably, the raw material of the pvc film layer is put into blender, and 60-70 revs/min of revolving speed, whipping temp
100-120 degree stirs 60-80 minutes, forms PVC film layer slurry, is then plasticized again through entering in mixer, smelting temperature
160-170 degree；Into extruding pelletization in extruder, extruder temperature 160-175 degree, 50-60 revs/min of extruder screw revolving speed
Clock obtains PVC film layer particle.
Preferably, the PVC film after being bonded in the step S3 fitting passes through infrared baking oven for drying adhesive, dry
Dry temperature is 80-110 DEG C.
A kind of production technology of wallboard appearance mask of the present invention the utility model has the advantages that the present invention by setting pad pasting to
Base cloth layer and pvc film layer bilayer bonding structure, make pad pasting better quality, are hardly damaged, by adding in pvc film layer raw material
Flame resistant filler material enhances the fire protecting performance of pad pasting, improves safety, is worth promoting.
Feature and advantage of the invention will be described in detail by embodiment.
[specific embodiment]
A kind of production technology of wallboard appearance mask of the invention, comprising the following steps:
The preparation of step S1pvc film layer: by PVC film layer particle using calendering formation in calender pressure, PVC film layer is formed；
The preparation of step S2 base cloth layer: taking non-woven fabrics, and non-woven fabrics is cut into suitable width, is wound spare；
Step S3 fitting: by PVC film layer obtained in step S1 by addition glue, heating pressurized adhesion is together cold
But, it is wound after cooling spare；
Step S4 computer graphics: go out on wallpaper to need to print the figure of decorative pattern by computer drawing；
Step S5 stamp: wallpaper being placed on digital decorating machine and carries out quick stamp, presses pattern on PVC facial mask surface
It is required that carry out two to six chromaticity printings, using a kind of mill base material of color of every set, intaglio plate revolving speed is 80~120 meters/
Point, after one chromatography of every printing, next chromaticity printing is entered back into after 120~140 DEG C of drying, colored PVC facial mask is made, finally
The colored PVC facial mask being completed for printing is wound into big volume；
Step S6 treatment: in wallpaper surface sprayed protection coating, and it is heated to 120-140 DEG C, heating time are as follows:
80-120s；
Step S7 trimming winding: pad pasting obtained in step S6 is placed in pad pasting cutting machine, is carried out through pad pasting cutting machine
It is spare to carry out packing encapsulation for splitting winding after winding.
Preferably, the raw material of the pvc film layer in the step S1pvc film layer preparation is polyvinyl chloride resin 45-65 parts, gathers
6-8 parts of tacryl, phosphorous acid hexichol -0.5-1 parts of different monooctyl ester, 2-4 parts of stabilizer, 3-6 parts of polypropylene fibre, glass fibre 1
Part, 2-6 parts of precipitated calcium carbonate, 1-3 parts of flame resistant filler material, the raw material of the pvc film layer are put into blender, revolving speed
60-70 revs/min, whipping temp 100-120 degree stirs 60-80 minutes, PVC film layer slurry is formed, then again through entering mixing
It is plasticized in machine, smelting temperature 160-170 degree；Into extruding pelletization in extruder, extruder temperature 160-175 degree is squeezed out
50-60 revs/min of machine screw speed, obtains PVC film layer particle, and the PVC film after being bonded in the step S3 fitting is logical
Infrared baking oven is crossed by drying adhesive, drying temperature is 80-110 DEG C.
Above-described embodiment is the description of the invention, is not limitation of the invention, after any pair of simple transformation of the present invention
Scheme all belong to the scope of protection of the present invention.
Claims (4)
1. a kind of production technology of wallboard appearance mask, it is characterised in that: the following steps are included:
The preparation of step S1pvc film layer: by PVC film layer particle using calendering formation in calender pressure, PVC film layer is formed；
The preparation of step S2 base cloth layer: taking non-woven fabrics, and non-woven fabrics is cut into suitable width, is wound spare；
Step S3 fitting: by PVC film layer obtained in step S1 by addition glue, heating pressurized adhesion cools down together, cold
But it is wound after spare；
Step S4 computer graphics: go out on wallpaper to need to print the figure of decorative pattern by computer drawing；
Step S5 stamp: wallpaper being placed on digital decorating machine and carries out quick stamp, PVC facial mask surface by pattern requirement into
Two to six chromaticity printing of row, using a kind of mill base material of color of every set, intaglio plate revolving speed is 80~120 ms/min, every printing
After one chromatography, next chromaticity printing is entered back into after 120~140 DEG C of drying, colored PVC facial mask is made, will finally be completed for printing
Colored PVC facial mask be wound into big volume；
Step S6 treatment: in wallpaper surface sprayed protection coating, and it is heated to 120-140 DEG C, heating time are as follows: 80-
120s；
Step S7 trimming winding: pad pasting obtained in step S6 is placed in pad pasting cutting machine, is cut through pad pasting cutting machine
It is spare to carry out packing encapsulation for winding after winding.
2. a kind of production technology of wallboard appearance mask as described in claim 1, it is characterised in that: the step
The raw material of pvc film layer in the preparation of S1pvc film layer is polyvinyl chloride resin 45-65 parts, 6-8 parts of polypropylene fibre, phosphorous acid hexichol-different
0.5-1 parts of monooctyl ester, 2-4 parts of stabilizer, 3-6 parts of polypropylene fibre, 1 part of glass fibre, 2-6 parts of precipitated calcium carbonate, flame resistant filler
1-3 parts of material.
3. a kind of production technology of wallboard appearance mask as claimed in claim 2, it is characterised in that: the pvc film layer
Raw material put into blender, 60-70 revs/min of revolving speed, whipping temp 100-120 degree, stir 60-80 minute, formation PVC
Then membrane layer pulp is plasticized through entering in mixer again, smelting temperature 160-170 degree；Into extruding pelletization in extruder, squeeze
Out-of-machine temperature 160-175 degree, 50-60 revs/min of extruder screw revolving speed obtain PVC film layer particle.
4. a kind of production technology of wallboard appearance mask as described in claim 1, it is characterised in that: the step S3 patch
For PVC film after being bonded in conjunction by infrared baking oven by drying adhesive, drying temperature is 80-110 DEG C.