CN109825236A - A kind of bicomponent environment-friendly type adhesive and its preparation process - Google Patents
A kind of bicomponent environment-friendly type adhesive and its preparation process Download PDFInfo
- Publication number
- CN109825236A CN109825236A CN201910079384.3A CN201910079384A CN109825236A CN 109825236 A CN109825236 A CN 109825236A CN 201910079384 A CN201910079384 A CN 201910079384A CN 109825236 A CN109825236 A CN 109825236A
- Authority
- CN
- China
- Prior art keywords
- component
- friendly type
- type adhesive
- promotor
- bicomponent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to technical field of adhesive, are related to a kind of bicomponent environment-friendly type adhesive, are mixed by component A and component B according to mass ratio 1:0.9~1.4, component A: toluene di-isocyanate(TDI);Component B: polyester polyol, polyethylene glycol, promotor, calcium carbonate, catalyst, stabilizer.The invention also discloses the preparation processes of above-mentioned bicomponent environment-friendly type adhesive, comprising: component A is toluene di-isocyanate(TDI);Component B first prepares promotor according to mass ratio, and then the pure and mild polyethylene glycol of polyester polyols is added sequentially in reaction kettle, stirring is warming up to 100 DEG C, sequentially adds promotor, calcium carbonate, catalyst, stabilizer, after mixing evenly, it is cooled to room temperature, obtains component B.Formaldehydeless dual-component polyurethane adhesive disclosed in this invention is free of formaldehyde in component, and glue-joint strength, enduring quality are similar to the adhesive containing formaldehydes;Cost of material is lower, and preparing process is simple, easy to use, can substitute the adhesive containing formaldehyde.
Description
Technical field
The invention belongs to technical field of adhesive, be related to adhesive more particularly to a kind of bicomponent environment-friendly type adhesive and
Its preparation process.
Background technique
Wooden building materials are as the most important components in domestic market of building materials for home decoration, always by the blueness of the majority of consumers
It looks at, such as timber floor, wood furniture, wooden cabinet, wardrobe.In most wooden building materials, adhesive is as such product
Important auxiliary agent in production process, always by outer of interest in the industry.
Since formaldehyde has good stationarity, woodwork group fiber can be made to knit, and contraction is smaller, damages less, saves inherently
Physical capacity is strong;Uniform, penetration power is strong, can enhance tissue elasticity etc. is fixed, important work is played to the stability for improving adhesive
With becoming the important constituent of adhesive.At present on the market used in 70% or more adhesive all can release formaldehyde, thus
Influence environmental quality and consumer health.Woodwork in use, with the extension of time, constantly releasing free first
Aldehyde when building up to a certain amount of, can cause human body potentially to injure, and not environmentally.
Summary of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to a kind of open formaldehydeless pair
Component polyurethane adhesive.
A kind of bicomponent environment-friendly type adhesive is mixed by component A and component B according to mass ratio 1:0.9~1.4, excellent
Mass ratio 1:1.2 is selected,
Component A: toluene di-isocyanate(TDI);Component B: polyester polyol, polyethylene glycol, promotor, calcium carbonate, catalyst, stabilization
Agent;
Wherein, the mass fraction of each ingredient described in component B are as follows:
Polyester polyol 30%~55%, preferably 35%,
Polyethylene glycol 20%~35%, preferably 25%,
Promotor 10%~25%, preferably 15%,
Calcium carbonate 5%~20%, preferably 10%,
Catalyst 5%~15%, preferably 10%,
Stabilizer 5%~10%, preferably 5%.
In the more excellent disclosed example of the present invention, the ingredient of the promotor is organo-silicon compound, and main body is vinyl trimethoxy
Base silane, silica, the composition mass fraction of the two are as follows:
Organo-silicon compound 70%~90%, preferably 80%,
Silica 1 0%~30%, preferably 20%.
The invention also discloses the preparation processes of above-mentioned bicomponent environment-friendly type adhesive, comprising:
Component A is toluene di-isocyanate(TDI);
The preparation step of component B: according to mass ratio, first preparing promotor, then by the pure and mild polyethylene glycol of polyester polyols according to
Secondary to be added in reaction kettle, stirring is warming up to 100 DEG C, sequentially adds promotor, calcium carbonate, catalyst, stabilizer, and stirring is equal
It after even, is cooled to room temperature, obtains component B.
By component A and component B according to mass ratio 1:(0.9~1.4 when use) mixing, after mixing evenly, i.e., usable, institute
Obtain adhesive solid content 70 ± 2%, 3000 ± 500cps of viscosity.
Beneficial effect
The invention discloses a kind of formaldehydeless dual-component polyurethane adhesive, formaldehyde is free of in component, but glue-joint strength, persistently
Performance is similar to the adhesive containing formaldehydes;Cost of material is lower, and preparing process is simple, easy to use, is applied to woodwork
The adhesive containing formaldehyde can be substituted when manufacture.
Specific embodiment
The following describes the present invention in detail with reference to examples, so that those skilled in the art more fully understand this hair
It is bright, but the invention is not limited to following embodiments.
Embodiment 1
The composition (according to mass fraction) of two-component adhesive main component: 100 parts of toluene di-isocyanate(TDI), polyester polyol 45
It is part, 25 parts of polyethylene glycol, 10 parts of stabilizer (8 parts of organic silicon compound, 2 parts of silica), 10 parts of calcium carbonate, 5 parts of catalyst, steady
Determine 5 parts of agent.
Organic silicon compound and silica are mixed and made into promotor according to following mass fraction first, then by polyester polyols
The pure and mild following mass fraction of polyethylene glycol is added to stirring in reaction kettle with this and is warming up to 100 DEG C, sequentially adds promotor, carbon
Sour calcium, catalyst, stabilizer are cooled to room temperature after mixing evenly, and component B is made, by component A and component B according to mass ratio 1:
1 mixing, after mixing evenly, can use.
Embodiment 2
The composition (according to mass fraction) of two-component adhesive main component: 100 parts of toluene di-isocyanate(TDI), polyester polyol 55
It is part, 30 parts of polyethylene glycol, 12 parts of stabilizer (9 parts of organic silicon compound, 3 parts of silica), 12 parts of calcium carbonate, 6 parts of catalyst, steady
Determine 5 parts of agent.
Organic silicon compound and silica are mixed and made into promotor according to following mass fraction first, then by polyester polyols
The pure and mild following mass fraction of polyethylene glycol is added to stirring in reaction kettle with this and is warming up to 100 DEG C, sequentially adds promotor, carbon
Sour calcium, catalyst, stabilizer are cooled to room temperature after mixing evenly, and component B is made, by component A and component B according to mass ratio 1:
1.2 mixing, after mixing evenly, can use.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright specification is applied directly or indirectly in other relevant technical fields,
Similarly it is included within the scope of the present invention.
Claims (10)
1. a kind of bicomponent environment-friendly type adhesive is mixed by component A and component B according to mass ratio 1:0.9~1.4, component
A: toluene di-isocyanate(TDI);Component B: polyester polyol, polyethylene glycol, promotor, calcium carbonate, catalyst, stabilizer;
Wherein, the mass fraction of each ingredient described in component B are as follows:
Polyester polyol 30%~55%,
Polyethylene glycol 20%~35%,
Promotor 10%~25%,
Calcium carbonate 5%~20%,
Catalyst 5%~15%,
Stabilizer 5%~10%.
2. bicomponent environment-friendly type adhesive according to claim 1, it is characterised in that: by component A and component B according to mass ratio
1:1.2 mixing.
3. bicomponent environment-friendly type adhesive according to claim 1, it is characterised in that: the matter of polyester polyol described in component B
Measuring score is 35%.
4. bicomponent environment-friendly type adhesive according to claim 1, it is characterised in that: the quality of polyethylene glycol described in component B
Score is 25%.
5. bicomponent environment-friendly type adhesive according to claim 1, it is characterised in that: the quality of promotor described in component B point
Number is 15%.
6. bicomponent environment-friendly type adhesive according to claim 1, it is characterised in that: the quality of calcium carbonate described in component B point
Number is 10%.
7. bicomponent environment-friendly type adhesive according to claim 1, it is characterised in that: the quality of catalyst described in component B point
Number is 10%.
8. bicomponent environment-friendly type adhesive according to claim 1, it is characterised in that: the quality of stabilizer described in component B point
Number is 5%.
9. bicomponent environment-friendly type adhesive according to claim 1, it is characterised in that: the ingredient of the promotor is organosilicon
Compound, main body are vinyltrimethoxysilane, silica, the composition mass fraction of the two are as follows: organo-silicon compound 70%
~90%, preferably 80%;Silica 1 0%~30%, preferably 20%.
10. preparing the technique of any bicomponent environment-friendly type adhesive of the claims 1-9, it is characterised in that: include:
Component A is toluene di-isocyanate(TDI);
The preparation step of component B: according to mass ratio, first preparing promotor, then by the pure and mild polyethylene glycol of polyester polyols according to
Secondary to be added in reaction kettle, stirring is warming up to 100 DEG C, sequentially adds promotor, calcium carbonate, catalyst, stabilizer, and stirring is equal
It after even, is cooled to room temperature, obtains component B.