CN109825019A - A kind of multi-functional acryl plates - Google Patents
A kind of multi-functional acryl plates Download PDFInfo
- Publication number
- CN109825019A CN109825019A CN201910136282.0A CN201910136282A CN109825019A CN 109825019 A CN109825019 A CN 109825019A CN 201910136282 A CN201910136282 A CN 201910136282A CN 109825019 A CN109825019 A CN 109825019A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- wear
- acryl plates
- waste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of multi-functional acryl plates, it is made of following raw material: 35-50 parts of waste and old organic glass, 5-7 parts of RE CeO 2, powder 12-15 parts wear-resisting, 3-5 parts of carbon nano-tube fibre, 2-3 parts of ammonium hydrogencarbonate, 2-3 parts of antimony oxide, 5-7 parts of benzophenone, 6-9 parts of benzotriazole, is modified antistatic agent 1-6 parts at 60-70 parts of ethyl methacrylate.The present invention is blended by the processing again to waste and old organic glass with wear-resistant material, electrostatic dissipation material, and the wearability of acrylic board can be effectively improved, and increases anti-static function, avoids the subtle thing absorption such as dust, impurity.
Description
Technical field
The present invention relates to a kind of multi-functional acryl plates, belong to acryl plates production technical field.
Background technique
Acrylic is called PMMA or organic glass, is originated from English acrylic (acrylic plastics), and chemical name is poly- first
Base methyl acrylate.Acrylic is a kind of exploitation high molecular thermoplast earlier, and machine-shaping is more convenient, acrylic
The molding mode of material mainly has cast molding and extrusion forming, can also be soft by its by reheating after acrylic material molding
The mode of change is made the various shape of needs, and acrylic has the preferable transparency and a light transmittance, light transmittance up to 92%,
Chemical stability and weatherability are preferable, very strong to natural environment adaptability.Therefore acrylic material is applied to decoration etc. extensively
In field, but there is the defects of wearing no resistance, easily inhaling dust in existing acrylic board.
Summary of the invention
Technical problem to be solved by the present invention lies in a kind of multi-functional acryl plates are provided, by waste and old organic glass
The processing again of glass is blended with wear-resistant material, electrostatic dissipation material, can effectively improve the wearability of acrylic board, increases
Add anti-static function, avoids the subtle thing absorption such as dust, impurity.
The technical problems to be solved by the invention take following technical scheme to realize:
A kind of multi-functional acryl plates, it is made of following raw material: 50 parts of waste and old organic glass 35-, metering system
60-70 parts of acetoacetic ester, 5-7 parts of RE CeO 2, powder 12-15 parts wear-resisting, 3-5 parts of carbon nano-tube fibre, ammonium hydrogencarbonate 2-3
Part, is modified antistatic agent 1-6 parts at 2-3 parts of antimony oxide, 5-7 parts of benzophenone, 6-9 parts of benzotriazole.
It according to mass ratio is that 1:0.5-1:7-9 is mixed that the wear-resisting powder, which is Si, Ti, Ni powder, Si, Ti, Ni powder
Last granularity is 55-70um.
Each group distribution ratio in the modified antistatic agent are as follows: ethyoxyl laurel is amine 35-50 parts cruel, 8-12 parts of magnesium stearate,
12-18 parts of silane coupling agent, 45-60 parts of water.
The beneficial effects of the present invention are: the present invention is that raw material prepares acryl plates, operation letter using waste and old organic glass
Just, preparation flow is short, raw material is easy to get, production cost is low, while also having and improving waste utilization rate and reduce environmental pollution
Advantage.The present invention is also added into RE CeO 2 and antimony oxide in the feed, and the two can reduce coefficient of friction, be promoted
Hardness enhances the wearability of acrylic board；Benzophenone, benzotriazole can significantly increase plate to the resistance of ultraviolet light, with
Prevent acryl plates premature aging under ultraviolet irradiation.
Specific embodiment
In order to be easy to understand to technical means, creative features, achievable purpose and effectiveness of the invention, below with reference to tool
Body embodiment, the present invention is further explained.
Embodiment one
A kind of multi-functional acryl plates, it is made of following raw material: 35 parts of waste and old organic glass, methacrylic acid second
70 parts of ester, 6 parts of RE CeO 2,12 parts of wear-resisting powder, 4 parts of carbon nano-tube fibre, 2 parts of ammonium hydrogencarbonate, antimony oxide 2
Part, 5 parts of benzophenone, 6 parts of benzotriazole, modified 1 part of antistatic agent.
It according to mass ratio is that 1:0.5:9 is mixed that the wear-resisting powder, which is Si, Ti, Ni powder, Si, Ti, Ni powder
Granularity is 55-70um.
Each group distribution ratio in the modified antistatic agent are as follows: 45 parts of the cruel amine of ethyoxyl laurel, 8 parts of magnesium stearate, silane are even
Join 12 parts of agent, 45 parts of water.
Embodiment two
A kind of multi-functional acryl plates, it is made of following raw material: 35 parts of waste and old organic glass, methacrylic acid second
70 parts of ester, 7 parts of RE CeO 2,15 parts of wear-resisting powder, 5 parts of carbon nano-tube fibre, 2.5 parts of ammonium hydrogencarbonate, antimony oxide 2
Part, 5 parts of benzophenone, 6 parts of benzotriazole, modified 1 part of antistatic agent.
It according to mass ratio is that 1:1:7 is mixed that the wear-resisting powder, which is Si, Ti, Ni powder, Si, Ti, Ni powder grain
Degree is 55-70um.
Each group distribution ratio in the modified antistatic agent are as follows: 35 parts of the cruel amine of ethyoxyl laurel, 12 parts of magnesium stearate, silane are even
Join 12 parts of agent, 60 parts of water.
Embodiment three
A kind of multi-functional acryl plates, it is made of following raw material: 50 parts of waste and old organic glass, methacrylic acid second
65 parts of ester, 5 parts of RE CeO 2,15 parts of wear-resisting powder, 3 parts of carbon nano-tube fibre, 3 parts of ammonium hydrogencarbonate, antimony oxide 3
Part, 7 parts of benzophenone, 9 parts of benzotriazole, modified 6 parts of antistatic agent.
It according to mass ratio is that 1:1:9 is mixed that the wear-resisting powder, which is Si, Ti, Ni powder, Si, Ti, Ni powder grain
Degree is 55-70um.
Each group distribution ratio in the modified antistatic agent are as follows: 50 parts of the cruel amine of ethyoxyl laurel, 12 parts of magnesium stearate, silane are even
Join 18 parts of agent, 55 parts of water.
Show that acryl plates wearability of the present invention is strong through test result, while increasing anti-static function, keeps away
Exempt from the subtle thing absorption such as dust, impurity.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, without departing from the spirit and scope of the present invention, this hair
Bright to will also have various changes and improvements, these changes and improvements all fall within the protetion scope of the claimed invention.The present invention claims
Protection scope is defined by the appending claims and its equivalent thereof.
Claims (3)
1. a kind of multi-functional acryl plates, it is characterised in that: it is made of following raw material: waste and old organic glass 35-
50 parts, 60-70 parts of ethyl methacrylate, 5-7 parts of RE CeO 2, powder 12-15 parts wear-resisting, carbon nano-tube fibre 3-5
Part, 2-3 parts of ammonium hydrogencarbonate, 2-3 parts of antimony oxide, 5-7 parts of benzophenone, 6-9 parts of benzotriazole, modified antistatic agent 1-
6 parts.
2. a kind of multi-functional acryl plates according to claim 1, it is characterised in that: the wear-resisting powder be Si, Ti,
Ni powder is mixed according to mass ratio for 1:0.5-1:7-9, and Si, Ti, Ni powder size are 55-70um.
3. a kind of multi-functional acryl plates according to claim 1, it is characterised in that: each in the modified antistatic agent
Component proportion are as follows: ethyoxyl laurel is amine 35-50 parts cruel, 8-12 parts of magnesium stearate, 12-18 parts of silane coupling agent, 45-60 parts of water.