CN109825005A - A kind of formula of diatom ooze bottom plate - Google Patents
A kind of formula of diatom ooze bottom plate Download PDFInfo
- Publication number
- CN109825005A CN109825005A CN201910137726.2A CN201910137726A CN109825005A CN 109825005 A CN109825005 A CN 109825005A CN 201910137726 A CN201910137726 A CN 201910137726A CN 109825005 A CN109825005 A CN 109825005A
- Authority
- CN
- China
- Prior art keywords
- bottom plate
- diatom ooze
- foaming
- formula
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of formulas of diatom ooze bottom plate, the bottom plate includes the ingredient of following mass ratio: Corvic 18-21%, diatomite 28-32%, calcium carbonate 19.5-21%, stabilizer 1.30-1.35%, polyethylene wax 0.20-0.29%, stearic acid 0.25-0.30%, foaming control agent 2-3%, foam ADC 0.6-0.7%, haloflex 0.9-1.1%, iron oxide yellow 0.115-0.13%, wood powder 1.5-2.2%, small materials in the tube 21-22.5%, reach and dispels formaldehyde, purify air, moistureproof and mildewproof, breathe damping, good toughness, on-deformable purpose.
Description
Technical field
The present invention relates to diatom ooze fields, and in particular to a kind of formula of diatom ooze bottom plate.
Background technique
Currently, during house decoration, mostly uses greatly and need to use baseboard material and fitted up, and traditional
In bottom plate, have the following problems mostly:
1, leukorrhea, blanking bar, bright band, light gray band etc. is presented in plate surface；
2, plate is easily broken；
3, foaming does not reach requirement, and lays particular stress on；
4, plate face torsional deformation；
5, plate face is presented ripple glaze, band, collapses, vertical line；
6, plate surface has impurity.
In view of above some defects, it is badly in need of a kind of material now to solve existing issue.
Summary of the invention
In order to solve the above technical problems, reaching and dispelling purpose of the present invention is to provide a kind of formula of diatom ooze bottom plate
Formaldehyde, purification air, moistureproof and mildewproof, breathing damping, good toughness, on-deformable purpose.
To achieve the above object, a kind of formula of diatom ooze bottom plate of the present invention, the bottom plate include following mass ratio
Ingredient: Corvic 18-21%, diatomite 28-32%, calcium carbonate 19.5-21%, stabilizer 1.30-1.35%, poly- second
Alkene wax 0.20-0.29%, stearic acid 0.25-0.30%, foaming control agent 2-3%, foaming ADC 0.6-0.7%, chlorinated polyethylene
Alkene 0.9-1.1%, iron oxide yellow 0.115-0.13%, wood powder 1.5-2.2%, small materials in the tube 21-22.5%.
Further, the ingredient of the mass ratio of the bottom plate: Corvic 20%, diatomite 30%, calcium carbonate 20%,
Stabilizer 1.32%, polyethylene wax 0.24%, stearic acid 0.28%, foaming control agent 2.4%, foaming ADC 0.64%, chlorination
Polyethylene 1%, iron oxide yellow 0.12%, wood powder 2%, small materials in the tube 22%.
Further, the diatom ooze bottom plate the preparation method comprises the following steps: each raw material are prepared by recipe ratio after, it is mixed to be put into heat
Machine stirring, temperature reach 125 DEG C or more, and temperature is put into material in cold mixing pot when reaching 125 DEG C or more and stirs, and temperature drops to 45
DEG C or less discharge, to lasting cooling, then machine barrel mold heating to be extruded starts to put into production after reaching certain temperature, produces
Product.
Further, the width of product, thickness, flatness are surveyed and claims its weight.
Compared with prior art, the present invention the beneficial effect is that:
Corvic is a kind of polar high molecular polymer of noncrystalline season.
Calcium carbonate is to improve product hardness, wear resistance and intensity stabilization agent；Effect is to increase product stability, extends booting
Period prevents waste material and increases production finished product.
Polyethylene wax, stearic acid have been mainly lubricating action, adjust material fluidity.
Foaming control agent is adjusting expansion density promotion material plasticizing, increasing product, adjusting foam hole is uniform in fact.
Foaming ADC is to decompose to generate gas regulation extrudate density after being heated.
Haloflex is saturation high molecular material, has good oil resistivity, anti-flammability and tinctorial property, and toughness is good
It is good.
There are three effects for diatomite tool, first is that air is purified, second is that except formaldehyde, third is that breathing damping.
Specific embodiment
The present invention provides a kind of embodiment:
Embodiment one
Feeding: Corvic 2000g, diatomite 3000g, calcium carbonate 2000g, stabilizer 132g, polyethylene wax
24g, stearic acid 28g, foaming control agent 240g, foaming ADC64g, haloflex 100g, iron oxide yellow 12g, wood powder 200g,
Small materials in the tube 2200g；
Ingredient: after each raw material are prepared by recipe ratio, it is put into the mixed machine stirring of heat, temperature reaches 130 DEG C, and temperature reaches
Material is put into cold mixing pot at 130 DEG C and is stirred, temperature drops to 40 DEG C of discharges, to lasting cooling, then machine barrel mould to be extruded
Tool heating starts to put into production after reaching certain temperature, and weighing is taken measurements after product out, surveys width, thickness, flatness.
Embodiment two
Feeding: Corvic 2000g, diatomite 3000g, calcium carbonate 2000g, stabilizer 132g, polyethylene wax
24g, stearic acid 28g, foaming control agent 240g, foaming ADC64g, haloflex 100g, iron oxide yellow 12g, wood powder 200g,
Small materials in the tube 2200g；
Ingredient: after each raw material are prepared by recipe ratio, it is put into the mixed machine stirring of heat, temperature reaches 126 DEG C, and temperature reaches
Material is put into cold mixing pot at 126 DEG C and is stirred, temperature drops to 40 DEG C of discharges, to lasting cooling, then machine barrel mould to be extruded
Tool heating starts to put into production after reaching certain temperature, and weighing is taken measurements after product out, surveys width, thickness, flatness.
Embodiment three
Feeding: Corvic 2000g, diatomite 3000g, calcium carbonate 2000g, stabilizer 132g, polyethylene wax
24g, stearic acid 28g, foaming control agent 240g, foaming ADC64g, haloflex 100g, iron oxide yellow 12g, wood powder 200g,
Small materials in the tube 2200g；
Ingredient: after each raw material are prepared by recipe ratio, it is put into the mixed machine stirring of heat, temperature reaches 127 DEG C, and temperature reaches
Material is put into cold mixing pot at 127 DEG C and is stirred, temperature drops to 40 DEG C of discharges, to lasting cooling, then machine barrel mould to be extruded
Tool heating starts to put into production after reaching certain temperature, and weighing is taken measurements after product out, surveys width, thickness, flatness；
Example IV
Feeding: Corvic 2000g, diatomite 3000g, calcium carbonate 2000g, stabilizer 132g, polyethylene wax
24g, stearic acid 28g, foaming control agent 240g, foaming ADC64g, haloflex 100g, iron oxide yellow 12g, wood powder 200g,
Small materials in the tube 2200g；
Ingredient: after each raw material are prepared by recipe ratio, it is put into the mixed machine stirring of heat, temperature reaches 128 DEG C, and temperature reaches
Material is put into cold mixing pot at 128 DEG C and is stirred, temperature drops to 40 DEG C of discharges, to lasting cooling, then machine barrel mould to be extruded
Tool heating starts to put into production after reaching certain temperature, and weighing is taken measurements after product out, surveys width, thickness, flatness；
Embodiment five
Feeding: Corvic 2000g, diatomite 3000g, calcium carbonate 2000g, stabilizer 132g, polyethylene wax
24g, stearic acid 28g, foaming control agent 240g, foaming ADC64g, haloflex 100g, iron oxide yellow 12g, wood powder 200g,
Small materials in the tube 2200g；
Ingredient: after each raw material are prepared by recipe ratio, it is put into the mixed machine stirring of heat, temperature reaches 129 DEG C, and temperature reaches
Material is put into cold mixing pot at 129 DEG C and is stirred, temperature drops to 40 DEG C of discharges, to lasting cooling, then machine barrel mould to be extruded
Tool heating starts to put into production after reaching certain temperature, and weighing is taken measurements after product out, surveys width, thickness, flatness；
Embodiment six
Feeding: Corvic 2000g, diatomite 3000g, calcium carbonate 2000g, stabilizer 132g, polyethylene wax
24g, stearic acid 28g, foaming control agent 240g, foaming ADC64g, haloflex 100g, iron oxide yellow 12g, wood powder 200g,
Small materials in the tube 2200g；
Ingredient: after each raw material are prepared by recipe ratio, it is put into the mixed machine stirring of heat, temperature reaches 131 DEG C, and temperature reaches
Material is put into cold mixing pot at 131 DEG C and is stirred, temperature drops to 40 DEG C of discharges, to lasting cooling, then machine barrel mould to be extruded
Tool heating starts to put into production after reaching certain temperature, and weighing is taken measurements after product out, surveys width, thickness, flatness；
Embodiment seven
Feeding: Corvic 2000g, diatomite 3000g, calcium carbonate 2000g, stabilizer 132g, polyethylene wax
24g, stearic acid 28g, foaming control agent 240g, foaming ADC64g, haloflex 100g, iron oxide yellow 12g, wood powder 200g,
Small materials in the tube 2200g；
Ingredient: after each raw material are prepared by recipe ratio, it is put into the mixed machine stirring of heat, temperature reaches 132 DEG C, and temperature reaches
Material is put into cold mixing pot at 132 DEG C and is stirred, temperature drops to 40 DEG C of discharges, to lasting cooling, then machine barrel mould to be extruded
Tool heating starts to put into production after reaching certain temperature, and weighing is taken measurements after product out, surveys width, thickness, flatness.
Using the wall covering bring benefit of such formula:
Corvic is a kind of polar high molecular polymer of noncrystalline season.
Calcium carbonate is to improve product hardness, wear resistance and intensity stabilization agent；Effect is to increase product stability, extends booting
Period prevents waste material and increases production finished product.
Polyethylene wax, stearic acid have been mainly lubricating action, adjust material fluidity.
Foaming control agent is adjusting expansion density promotion material plasticizing, increasing product, adjusting foam hole is uniform in fact.Foaming
ADC is to decompose to generate gas regulation extrudate density after being heated.
Haloflex is saturation high molecular material, has good oil resistivity, anti-flammability and tinctorial property, and toughness is good
It is good.
There are three effects for diatomite tool, first is that air is purified, second is that except formaldehyde, third is that breathing damping.
Claims (4)
1. a kind of formula of diatom ooze bottom plate, it is characterised in that: the bottom plate includes the ingredient of following mass ratio: polyvinyl chloride tree
Rouge 18-21%, diatomite 28-32%, calcium carbonate 19.5-21%, stabilizer 1.30-1.35%, polyethylene wax 0.20-
0.29%, stearic acid 0.25-0.30%, foaming control agent 2-3%, foaming ADC 0.6-0.7%, haloflex 0.9-
1.1%, iron oxide yellow 0.115-0.13%, wood powder 1.5-2.2%, small materials in the tube 21-22.5%.
2. a kind of formula of diatom ooze bottom plate according to claim 1, it is characterised in that: the mass ratio of the bottom plate at
Point: Corvic 20%, diatomite 30%, calcium carbonate 20%, stabilizer 1.32%, polyethylene wax 0.24%, stearic acid
0.28%, foaming control agent 2.4%, foaming ADC 0.64%, haloflex 1%, iron oxide yellow 0.12%, wood powder 2%, small
Materials in the tube 22%.
3. a kind of formula of diatom ooze bottom plate according to claim 2, it is characterised in that: the preparation of the diatom ooze bottom plate
Method are as follows: after each raw material are prepared by recipe ratio, be put into the mixed machine stirring of heat, temperature reaches 125 DEG C or more, and temperature reaches
Material is put into cold mixing pot at 125 DEG C or more and is stirred, temperature drops to 45 DEG C or less discharges, then to be extruded to lasting cooling
The heating of machine barrel mold starts to put into production after reaching certain temperature, out product.
4. a kind of formula of diatom ooze bottom plate according to claim 3, it is characterised in that: survey the width of product, thickness, put down
It is whole to spend and claim its weight.