CN105199259A - Stone-wood floor and production technology and laying method thereof - Google Patents

Stone-wood floor and production technology and laying method thereof Download PDF

Info

Publication number
CN105199259A
CN105199259A CN201510552216.3A CN201510552216A CN105199259A CN 105199259 A CN105199259 A CN 105199259A CN 201510552216 A CN201510552216 A CN 201510552216A CN 105199259 A CN105199259 A CN 105199259A
Authority
CN
China
Prior art keywords
parts
stone
wood floor
floor
wood
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510552216.3A
Other languages
Chinese (zh)
Inventor
王东
王天义
张举
王森
张金果
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanzhao Leixin Calcium Industry New Material Technology Co Ltd
Original Assignee
Nanzhao Leixin Calcium Industry New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanzhao Leixin Calcium Industry New Material Technology Co Ltd filed Critical Nanzhao Leixin Calcium Industry New Material Technology Co Ltd
Priority to CN201510552216.3A priority Critical patent/CN105199259A/en
Publication of CN105199259A publication Critical patent/CN105199259A/en
Pending legal-status Critical Current

Abstract

The invention belongs to the technical field of indoor and outdoor building decorative materials and production technologies thereof, and provides a stone-wood floor and a production technology and laying method thereof. The stone-wood floor is prepared from, by weight, 90-100 parts of ground limestone, 30-35 parts of PVC, 0.3-0.6 part of stearic acid, 2-2.5 parts of chlorinated polyethylene, 0.5-1.0 part of a foaming agent, 6-7 parts of a foaming control agent and 2-3 parts of a stabilizer. The raw materials are highly mixed and stirred, extruded, molded, ground, slotted and coated to obtain a finished product. The processing procedures are simplified, the cost is lowered, the product quality is improved, the hardness, abrasion resistance and flexibility of the produced product are improved, PVC is foamed to generate pores through the foaming technology, and the pores are filled with microstructures such as the ground limestone, so that the product density reaches 1.2 g/cm<3> which is close to that of a pure wood floor, and the cheap and fine stone-wood floor can be truly obtained.

Description

A kind of stone-wood floor and production technique thereof and laying method
Technical field
The invention belongs to architectural decoration material and technical field of producing thereof, particularly relate to a kind of stone-wood floor and production technique thereof and laying method.
Background technology
In recent years, along with the raising of people's living standard, stone-wood floor is with environmental protection, ultralight ultra-thin, superpower wear-resistant, snappiness and superpower shock resistance, fire protection flame retarding, waterproof and dampproof, sound-absorbing noise control, anti-microbial property, little and the seamless welding of seam, cutting splicing is easily simple, installation is quick, assortment are various, acid-alkali-corrosive-resisting, heat conduction is warming, easy maintenance, environmental protection is renewable, the advantages such as international popular, certain application is obtained in the field such as fitting-up and garden landscape, stone-wood floor overcomes flax floor, rubber floor covering, carpet, ceramic tile, marble, timber floor, numerous deficiencies on the floors such as plastic floor leather, have again the advantage on various floor concurrently simultaneously, receive the favor of consumers in general.But because the proportioning raw materials cost of existing stone-wood floor is higher, manufacturing procedure is complicated, causes the market price of stone-wood floor higher, is unfavorable for applying, and current stone-wood floor product can also improve further in degree of deformation, wear resistance and erosion resistance etc.
Applying date 2009.05.27, application number 200910145550.1 discloses a kind of stone-wood floor and production method thereof, be raw material with 60 ~ 80% water-ground limestones, 12 ~ 18% Plant Powders, 15-30%PVC resin and 1 ~ 3% composite calcium zinc properties-correcting agent, through high temperature polymerization, after changing high molecular chemical characters, form stone-wood floor particulate substrates, particulate substrates is used and is joined the extrusion moulding of particular manufacturing craft equipment, forms stone-wood floor shape base material.Go out the sheet material of various exquisite wood texture again through surface heat-transferring explained hereafter, then through Environment-friendlywear-resistant wear-resistant process, form a kind of stone-wood floor product being better than wood like wood.Although the standby stone-wood floor of this patent system also has good fire prevention, corrosion-resistant and be out of shape little advantage, its density is comparatively large, super solid wood material far away, increase transportation cost, in addition, its hardness higher elasticity is little, differ comparatively large with solid wooden floor board, the effect of trampling after laying is far away from solid wooden floor board.
Therefore develop that a kind of production cost is lower, production process is comparatively simple, product performance are more superior stone-wood floor and production technique thereof be desirability.
Summary of the invention
The object of this invention is to provide a kind of production cost lower, product density, intensity reach the characteristic of solid wooden floor board, do not affect by water soaking, stone-wood floor more superior in degree of deformation, wear resistance and erosion resistance.
Another object of the present invention is to provide a kind of production technique of this stone-wood floor.
Another object of the present invention is to provide a kind of laying method of this stone-wood floor.
For achieving the above object, the technical solution used in the present invention is:
A kind of stone-wood floor, wherein, the material of preparing of this stone-wood floor comprises following raw material and weight part:
Water-ground limestone is 90 ~ 100 parts, PVC is 30 ~ 35 parts, stearic acid is 0.3 ~ 0.6 part, chlorinatedpolyethylene is 2 ~ 2.5 parts, whipping agent is 0.5 ~ 1.0 part, foaming control agent is 6 ~ 7 parts, stablizer is 2 ~ 3 parts.
Preferably, the material of preparing of this stone-wood floor comprises following raw material and weight part: water-ground limestone is 95 parts, PVC is 33 parts, stearic acid is 0.5 part, chlorinatedpolyethylene is 2.3 parts, whipping agent is 0.7 part, foaming control agent is 6.5 parts, stablizer is 2.5 parts.
A production technique for above-mentioned stone-wood floor, it comprises the following steps:
Step (1), there is provided the mixture comprising following raw material: water-ground limestone is 90 ~ 100 parts, PVC is 30 ~ 35 parts, stearic acid is 0.3 ~ 0.6 part, chlorinatedpolyethylene is 2 ~ 2.5 parts, whipping agent is 0.5 ~ 1.0 part, foaming control agent is 6 ~ 7 parts, stablizer is 2 ~ 3 parts, described mixture is added in homogenizer, and the temperature of setting high-speed stirrer is 110-120 DEG C, churning time is 30-40 minute, and then the temperature of homogenizer is set as 30-40 DEG C after mix and blend, carry out again obtaining batch mixing after 15-20 minute high-speed mixing stirs,
Step (2), utilized by above-mentioned batch mixing automatic infrared to detect vacuum intake equipment accurately to join in forcing machine, when waiting for that mixture temperature is down to 160-175 DEG C, direct extrusion molding obtains floor blank, control in extrusion extruder screw temperature 160-180 DEG C, mold heated temperature 165-175 DEG C, mold heated soaking time is at 40-50 minute;
Step (3), by above-mentioned floor blank after the cutting of infrared rays cutting facility, obtain the uniform floor base material of length thickness, again by this base material after high-accuracy abrasive finishing machine abrasive finishing, obtain base material that is surperficial very smooth, fixed thickness, the surface layer of floor base material bond one deck solid wood veneer or decoration wearing layer, and then through four side moulder, two-ends milling machine equipment to its four sides open mounting groove;
Step (4), floor base material four sides being held successfully to mounting groove has the surface heat-transferring of natural wood grain texture and application process to obtain floor to be checked, and application process comprises: single roller coat cloth, UV drying, priming paint sanding, the cleaning of plate flour dirt, flow coating machine coating and heating levelling;
Step (5), finally detects floor to be checked, detects qualified rear packaging and dispatches from the factory.
Present invention also offers a kind of laying method of stone-wood floor, the operation in the steps below of its feature:
(1) first ground is repaired smooth;
(2) one deck perlite carpet veneer is laid on the ground;
(3) on perlite carpet veneer, lay stone-wood floor, be fastened and connected by the tongue and groove of its side between adjacent stone-wood floor, and knock and make it smooth;
(4) cutting process is carried out to the stone-wood floor spread to body of wall edge, make stone-wood floor edge and body of wall retain certain interval; Arrange spring clip at gap location interval, spring clip compresses the stone-wood floor at most edge, ensures that the stone-wood floor that edge matches closely fastens;
(5) bond panel strip on the body of wall that stone-wood floor edge is corresponding, and the edge of stone-wood floor is close in the bottom of panel strip, in order to block the gap of stone-wood floor edge.
The each raw material preparing above-mentioned stone-wood floor has following functions and advantage:
Wherein, water-ground limestone: by natural carbonate mineral as calcite, marble, Wingdale grind and form, raw material sources are extensive, and cost is low, stable performance.As PVC filling modifying agent, its chemical purity is high, inertia greatly, not easily chemical reaction, possess Heat stability is good, can not decompose below 400 DEG C, whiteness is high, oil absorbency is low, refractive index is low, matter is soft, the advantage such as dry, little, nontoxic, tasteless containing crystal water, the low wear(ing)value of hardness, odorless, good dispersity.
PVC: be the thermoplastic resin be polymerized under initiator effect by vinylchlorid.As base-material, there is difficult combustion, acid-alkali-corrosive-resisting, resistance to microorganism, wear-resistant and good heat retention and elastic advantage.
Stearic acid: stearicacid is PVC heat stabilizer, oilness, prevents in processing " coking " as uv-resistant agent, to uvioresistant, reduce the oxidation rate of PVC under UV environment.
Chlorinatedpolyethylene: CPE softening agent can absorb a part of external lubricant aborning, adds in PVC as excellent toughening agent modified dose of PVC plastic, improves the shock strength of material, flexural strength.
Whipping agent: use AC and NaHC0 3composite foamable agent, foams to PVC, increases the resistance to chemical attack, weathering resistance, flame retardant resistance etc. of product.
Foaming control agent: (1) stablizer impels material plasticizing; (2) improve melt body, the intensity of material, prevent bubble from merging to make evenly; (3) ensure that melt body has good fluidity.
Stablizer: prevent the thermal destruction in the mixing and molding process of material, therefore needs stablizer with cooling.
In sum, owing to containing whipping agent, foaming control agent in raw materials of the present invention, these two kinds of components foam to PVC, water-ground limestone can be made after foaming to disperse fully, the loading level of effective raising water-ground limestone, foam process makes PVC foam produce pore, fills the microtextures such as water-ground limestone and cause product density to reach 1.2g/cm in pore 3close with pure wood floors, there is certain elasticity and snappiness.Calcium carbonate reserves are large, and price is low, because this reducing production cost; The add-on of calcium carbonate can increase resistance to deformation degree, the erosion resistance of product after improving simultaneously, secondly the stearic acid after proportion optimizing, chlorinatedpolyethylene, stablizer also a nearly step enhance resistance to deformation degree, fastness to rubbing, the erosion resistance of PVC, based on above-mentioned principle, each component in raw materials acts synergistically mutually, makes the performance of the finished product more superior.
The production technique of this stone-wood floor has the following advantages:
Unique raw material hybrid mode: each raw material is in step (1) after excessive temperature and low temperature high-speed stirring, pulverous raw material chemical property is stablized preferably, extremely be beneficial to the shaping link of twin-screw extruder in step (2) to produce, the finished product processing performance is increased substantially;
Simplify operation: because calcium carbonate density is comparatively large, make the raw material after stirring can deliver to extrusion link uniformly and stably under vacuum intake equipment in step (2), so this link does not need granulation and empty shutoff operation.This improves products production efficiency, reduce production energy consumption, save production cost;
In step (2), this extrusion link, extruder temperature is at 160-180 DEG C, mold heated temperature is at 165-175 DEG C, wherein mold heated soaking time is at 40-50 minute, the parameter more than arranged can the chemical property of steady extruding link material effectively, very scientifically carries out even extrusion.
In sum, the present invention, through simplifying manufacturing procedure, reduces costs and improves the quality of products.Specifically eliminate traditional granulating working procedure and holes blocking operation, improve products production efficiency, reduce production energy consumption, save production cost, its hardness of the product produced, wear resistance, snappiness are obtained for increase, foam process is adopted to make PVC foam produce pore, fill in pore the microtextures such as water-ground limestone cause product density to reach 1.2g/cm3 and pure wood floors close, really achieve inexpensive stone-wood floor.
In the laying method of this solid wooden floor board, adopt perlite felt as the bed course of bottom, perlite belongs to inorganic heat insulation material, has flame retardant properties good, can reach A level fire-protection standard, ageing-resistant, can with the building same life-span.Perlite felt has good elasticity, and stone-wood floor also has certain elasticity and snappiness in addition, has certain buffering effect when people tramples, and strengthens the comfort of trampling.Compared with prior art, this laying method is simple to operate, convenient and swift, and efficiency is high, tramples comfortable.
Accompanying drawing explanation
Fig. 1 is a kind of stone-wood floor production technological process of the present invention.
Embodiment
Embodiment 1:
A kind of stone-wood floor, wherein, the material of preparing of this stone-wood floor comprises following raw material and weight part:
Water-ground limestone is 90 parts, PVC is 30 parts, stearic acid is 0.3 part, chlorinatedpolyethylene is 2 parts, whipping agent is 0.5 part, foaming control agent is 6 parts, stablizer is 2 parts.
As shown in Figure 1, the production technique of this stone-wood floor, it comprises the following steps:
Step (1), there is provided the mixture comprising following raw material: water-ground limestone is 90 parts, PVC is 30 parts, stearic acid is 0.3 part, chlorinatedpolyethylene is 2 parts, whipping agent is 0.5 part, foaming control agent is 6 parts, stablizer is 2 parts, described mixture is added in homogenizer, and the temperature of setting high-speed stirrer be 110 DEG C, churning time is 30 minutes, and then the temperature of homogenizer is set as 30 DEG C after mix and blend, then carries out obtaining batch mixing after 15 minutes high-speed mixing stir;
Step (2), utilized by above-mentioned batch mixing automatic infrared to detect vacuum intake equipment accurately to join in forcing machine, when waiting for that mixture temperature is down to 160 DEG C, direct extrusion molding obtains floor blank, control in extrusion extruder screw temperature 160 DEG C, mold heated temperature 165 DEG C, mold heated soaking time is at 40 minutes;
Step (3), by above-mentioned floor blank after the cutting of infrared rays cutting facility, obtain the uniform floor base material of length thickness, again by this base material after high-accuracy abrasive finishing machine abrasive finishing, obtain base material that is surperficial very smooth, fixed thickness, the surface layer of floor base material bond one deck solid wood veneer or decoration wearing layer, and then through four side moulder, two-ends milling machine equipment to its four sides open mounting groove;
Step (4), floor base material four sides being held successfully to mounting groove has the surface heat-transferring of natural wood grain texture and application process to obtain floor to be checked, and application process comprises: single roller coat cloth, UV drying, priming paint sanding, the cleaning of plate flour dirt, flow coating machine coating and heating levelling;
Step (5), finally detects floor to be checked, detects qualified rear packaging and dispatches from the factory.
Embodiment 2:
A kind of stone-wood floor, wherein, the material of preparing of this stone-wood floor comprises following raw material and weight part:
Water-ground limestone is 95 parts, PVC is 33 parts, stearic acid is 0.5 part, chlorinatedpolyethylene is 2.3 parts, whipping agent is 0.7 part, foaming control agent is 6.5 parts, stablizer is 2.5 parts.
A production technique for above-mentioned stone-wood floor, it comprises the following steps:
Step (1), there is provided the mixture comprising following raw material: water-ground limestone is 95 parts, PVC is 33 parts, stearic acid is 0.5 part, chlorinatedpolyethylene is 2.3 parts, whipping agent is 0.7 part, foaming control agent is 6.5 parts, stablizer is 2.5 parts, described mixture is added in homogenizer, and the temperature of setting high-speed stirrer be 115 DEG C, churning time is 35 minutes, and then the temperature of homogenizer is set as 35 DEG C after mix and blend, then carries out obtaining batch mixing after 18 minutes high-speed mixing stir;
Step (2), utilized by above-mentioned batch mixing automatic infrared to detect vacuum intake equipment accurately to join in forcing machine, when waiting for that mixture temperature is down to 170 DEG C, direct extrusion molding obtains floor blank, control in extrusion extruder screw temperature 170 DEG C, mold heated temperature 170 DEG C, mold heated soaking time is at 45 minutes;
Step (3), by above-mentioned floor blank after the cutting of infrared rays cutting facility, obtain the uniform floor base material of length thickness, again by this base material after high-accuracy abrasive finishing machine abrasive finishing, obtain base material that is surperficial very smooth, fixed thickness, the surface layer of floor base material bond one deck solid wood veneer or decoration wearing layer, and then through four side moulder, two-ends milling machine equipment to its four sides open mounting groove;
Step (4), floor base material four sides being held successfully to mounting groove has the surface heat-transferring of natural wood grain texture and application process to obtain floor to be checked, and application process comprises: single roller coat cloth, UV drying, priming paint sanding, the cleaning of plate flour dirt, flow coating machine coating and heating levelling;
Step (5), finally detects floor to be checked, detects qualified rear packaging and dispatches from the factory.
Embodiment 3:
A kind of stone-wood floor, wherein, the material of preparing of this stone-wood floor comprises following raw material and weight part:
Water-ground limestone is 100 parts, PVC is 35 parts, stearic acid is 0.6 part, chlorinatedpolyethylene is 2.5 parts, whipping agent is 1.0 parts, foaming control agent is 7 parts, stablizer is 3 parts.
A production technique for above-mentioned stone-wood floor, it comprises the following steps:
Step (1), there is provided the mixture comprising following raw material: water-ground limestone is 100 parts, PVC is 35 parts, stearic acid is 0.6 part, chlorinatedpolyethylene is 2.5 parts, whipping agent is 1.0 parts, foaming control agent is 7 parts, stablizer is 3 parts, described mixture is added in homogenizer, and the temperature of setting high-speed stirrer be 120 DEG C, churning time is 40 minutes, and then the temperature of homogenizer is set as 40 DEG C after mix and blend, then carries out obtaining batch mixing after 20 minutes high-speed mixing stir;
Step (2), utilized by above-mentioned batch mixing automatic infrared to detect vacuum intake equipment accurately to join in forcing machine, when waiting for that mixture temperature is down to 175 DEG C, direct extrusion molding obtains floor blank, control in extrusion extruder screw temperature 180 DEG C, mold heated temperature 175 DEG C, mold heated soaking time is at 50 minutes;
Step (3), by above-mentioned floor blank after the cutting of infrared rays cutting facility, obtain the uniform floor base material of length thickness, again by this base material after high-accuracy abrasive finishing machine abrasive finishing, obtain base material that is surperficial very smooth, fixed thickness, the surface layer of floor base material bond one deck solid wood veneer or decoration wearing layer, and then through four side moulder, two-ends milling machine equipment to its four sides open mounting groove;
Step (4), floor base material four sides being held successfully to mounting groove has the surface heat-transferring of natural wood grain texture and application process to obtain floor to be checked, and application process comprises: single roller coat cloth, UV drying, priming paint sanding, the cleaning of plate flour dirt, flow coating machine coating and heating levelling;
Step (5), finally detects floor to be checked, detects qualified rear packaging and dispatches from the factory.
Embodiment 4:
A kind of stone-wood floor, wherein, the material of preparing of this stone-wood floor comprises following raw material and weight part:
Water-ground limestone is 91 parts, PVC is 31 parts, stearic acid is 0.4 part, chlorinatedpolyethylene is 2.1 parts, whipping agent is 0.6 part, foaming control agent is 6.3 parts, stablizer is 2.3 parts.
A production technique for above-mentioned stone-wood floor, it comprises the following steps:
Step (1), there is provided the mixture comprising following raw material: water-ground limestone is 91 parts, PVC is 31 parts, stearic acid is 0.4 part, chlorinatedpolyethylene is 2.1 parts, whipping agent is 0.6 part, foaming control agent is 6.3 parts, stablizer is 2.3 parts, described mixture is added in homogenizer, and the temperature of setting high-speed stirrer be 113 DEG C, churning time is 33 minutes, and then the temperature of homogenizer is set as 33 DEG C after mix and blend, then carries out obtaining batch mixing after 16 minutes high-speed mixing stir;
Step (2), utilized by above-mentioned batch mixing automatic infrared to detect vacuum intake equipment accurately to join in forcing machine, when waiting for that mixture temperature is down to 168 DEG C, direct extrusion molding obtains floor blank, control in extrusion extruder screw temperature 168 DEG C, mold heated temperature 168 DEG C, mold heated soaking time is at 48 minutes;
Step (3), by above-mentioned floor blank after the cutting of infrared rays cutting facility, obtain the uniform floor base material of length thickness, again by this base material after high-accuracy abrasive finishing machine abrasive finishing, obtain base material that is surperficial very smooth, fixed thickness, the surface layer of floor base material bond one deck solid wood veneer or decoration wearing layer, and then through four side moulder, two-ends milling machine equipment to its four sides open mounting groove;
Step (4), floor base material four sides being held successfully to mounting groove has the surface heat-transferring of natural wood grain texture and application process to obtain floor to be checked, and application process comprises: single roller coat cloth, UV drying, priming paint sanding, the cleaning of plate flour dirt, flow coating machine coating and heating levelling;
Step (5), finally detects floor to be checked, detects qualified rear packaging and dispatches from the factory.
The laying method of stone-wood floor prepared by above-described embodiment 1-4, operation in the steps below:
(1) first ground is repaired smooth;
(2) one deck perlite carpet veneer is laid on the ground;
(3) on perlite carpet veneer, lay stone-wood floor, be fastened and connected by the tongue and groove of its side between adjacent stone-wood floor, and knock and make it smooth;
(4) cutting process is carried out to the stone-wood floor spread to body of wall edge, make stone-wood floor edge and body of wall retain certain interval; Arrange spring clip at gap location interval, spring clip compresses the stone-wood floor at most edge, ensures that the stone-wood floor that edge matches closely fastens;
(5) bond panel strip on the body of wall that stone-wood floor edge is corresponding, and the edge of stone-wood floor is close in the bottom of panel strip, in order to block the gap of stone-wood floor edge.

Claims (7)

1. a stone-wood floor, is characterized in that: the material of preparing of this stone-wood floor comprises following raw material and weight part: water-ground limestone is 90 ~ 100 parts, PVC is 30 ~ 35 parts, stearic acid is 0.3 ~ 0.6 part, chlorinatedpolyethylene is 2 ~ 2.5 parts, whipping agent is 0.5 ~ 1.0 part, foaming control agent is 6 ~ 7 parts, stablizer is 2 ~ 3 parts.
2. a kind of stone-wood floor as claimed in claim 1, is characterized in that: the material of preparing of this stone-wood floor comprises following raw material and weight part: water-ground limestone is 90 parts, PVC is 30 parts, stearic acid is 0.3 part, chlorinatedpolyethylene is 2 parts, whipping agent is 0.5 part, foaming control agent is 6 parts, stablizer is 2 parts.
3. a kind of stone-wood floor as claimed in claim 1, is characterized in that: the material of preparing of this stone-wood floor comprises following raw material and weight part: water-ground limestone is 95 parts, PVC is 33 parts, stearic acid is 0.5 part, chlorinatedpolyethylene is 2.3 parts, whipping agent is 0.7 part, foaming control agent is 6.5 parts, stablizer is 2.5 parts.
4. a kind of stone-wood floor as claimed in claim 1, is characterized in that: the material of preparing of stone-wood floor comprises following raw material and weight part: water-ground limestone is 100 parts, PVC is 35 parts, stearic acid is 0.6 part, chlorinatedpolyethylene is 2.5 parts, whipping agent is 1.0 parts, foaming control agent is 7 parts, stablizer is 3 parts.
5. a kind of stone-wood floor as claimed in claim 1, is characterized in that: the material of preparing of stone-wood floor comprises following raw material and weight part: water-ground limestone is 91 parts, PVC is 31 parts, stearic acid is 0.4 part, chlorinatedpolyethylene is 2.1 parts, whipping agent is 0.6 part, foaming control agent is 6.3 parts, stablizer is 2.3 parts.
6. the production technique of a kind of stone-wood floor as claimed in claim 1, is characterized in that comprising the following steps:
Step (1), there is provided the mixture comprising following raw material: water-ground limestone is 90 ~ 100 parts, PVC is 30 ~ 35 parts, stearic acid is 0.3 ~ 0.6 part, chlorinatedpolyethylene is 2 ~ 2.5 parts, whipping agent is 0.5 ~ 1.0 part, foaming control agent is 6 ~ 7 parts, stablizer is 2 ~ 3 parts, described mixture is added in homogenizer, and the temperature of setting high-speed stirrer is 110-120 DEG C, churning time is 30-40 minute, and then the temperature of homogenizer is set as 30-40 DEG C after mix and blend, carry out again obtaining batch mixing after 15-20 minute high-speed mixing stirs,
Step (2), utilized by above-mentioned batch mixing automatic infrared to detect vacuum intake equipment accurately to join in forcing machine, when waiting for that mixture temperature is down to 160-175 DEG C, direct extrusion molding obtains floor blank, control in extrusion extruder screw temperature 160-180 DEG C, mold heated temperature 165-175 DEG C, mold heated soaking time is at 40-50 minute;
Step (3), by above-mentioned floor blank after the cutting of infrared rays cutting facility, obtain the uniform floor base material of length thickness, again by this base material after high-accuracy abrasive finishing machine abrasive finishing, obtain base material that is surperficial very smooth, fixed thickness, the surface layer of floor base material bond one deck solid wood veneer or decoration wearing layer, and then through four side moulder, two-ends milling machine equipment to its four sides open mounting groove;
Step (4), floor base material four sides being held successfully to mounting groove has the surface heat-transferring of natural wood grain texture and application process to obtain floor to be checked, and application process comprises: single roller coat cloth, UV drying, priming paint sanding, the cleaning of plate flour dirt, flow coating machine coating and heating levelling;
Step (5), finally detects floor to be checked, detects qualified rear packaging and dispatches from the factory.
7. a laying method for stone-wood floor, the operation in the steps below of its feature:
(1) first ground is repaired smooth;
(2) one deck perlite carpet veneer is laid on the ground;
(3) on perlite carpet veneer, lay stone-wood floor, be fastened and connected by the tongue and groove of its side between adjacent stone-wood floor, and knock and make it smooth;
(4) cutting process is carried out to the stone-wood floor spread to body of wall edge, make stone-wood floor edge and body of wall retain certain interval; Arrange spring clip at gap location interval, spring clip compresses the stone-wood floor at most edge, ensures that the stone-wood floor that edge matches closely fastens;
(5) bond panel strip on the body of wall that stone-wood floor edge is corresponding, and the edge of stone-wood floor is close in the bottom of panel strip, in order to block the gap of stone-wood floor edge.
CN201510552216.3A 2015-09-02 2015-09-02 Stone-wood floor and production technology and laying method thereof Pending CN105199259A (en)