CN109817745A - A kind of back veneer material of photovoltaic cell component - Google Patents
A kind of back veneer material of photovoltaic cell component Download PDFInfo
- Publication number
- CN109817745A CN109817745A CN201711153432.6A CN201711153432A CN109817745A CN 109817745 A CN109817745 A CN 109817745A CN 201711153432 A CN201711153432 A CN 201711153432A CN 109817745 A CN109817745 A CN 109817745A
- Authority
- CN
- China
- Prior art keywords
- parts
- back veneer
- photovoltaic cell
- veneer material
- cell component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to technical field of photovoltaic power generation, feature is related to a kind of back veneer material of photovoltaic cell component.It includes following ingredient according to the mass fraction: 1~10 part of manganese, 5~25 parts of tin, 5~25 parts of vanadium, 70~95 parts of iron, 15~25 parts of zinc.Preferably, a kind of back veneer material of photovoltaic cell component, including following ingredient according to the mass fraction: 3~8 parts of manganese, 10~20 parts of tin, 10~20 parts of vanadium, 80~90 parts of iron, 18~23 parts of zinc.Most preferably, a kind of back veneer material of photovoltaic cell component, including following ingredient according to the mass fraction: 5 parts of manganese, 15 parts of tin, 15 parts of vanadium, 85 parts of iron, 20 parts of zinc.Preferably, the back veneer material of the photovoltaic cell component is with a thickness of 15~25um.The present invention can reduce the appearance of pin hole, can be effectively reduced cost while improving photovoltaic cell component back veneer material metal ductility;And the generation of photoelectric conversion unit electrochemical reaction can be prevented according to the back veneer material that the proportion of technical scheme is made.
Description
Technical field
The invention belongs to technical field of photovoltaic power generation, feature is related to a kind of back veneer material of photovoltaic cell component.
Background technique
The primary structure of photovoltaic cell includes photoelectric conversion unit, protects the encapsulating material of circuit, shell and other match
Nested structure.In order to guarantee the luminous efficiency and service life of photoelectric conversion unit, prevent photoelectric conversion unit from circuit leakage occur
The reasons such as electricity, corrosion lead to luminous efficiency decline and the lost of life, it is desirable that the backboard of photoelectric conversion unit is keeping some strength
While, also require have high barrier property, i.e. barrier steam is contacted with photoelectric conversion unit, prevented in photoelectric conversion unit
There is the generation of electrochemical reaction in portion.Backboard in present photovoltaic cell component uses pure aluminum metal piece, and pure aluminum metal
For piece when thickness is lower than 25um, there are pin hole problems, and this case can seriously damage photoelectric conversion unit.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides one kind can be improved metal ductility, reduces what pin hole occurred
The back veneer material of photovoltaic cell component.
The technical solution adopted in the present invention is as follows: a kind of back veneer material of photovoltaic cell component, including presses mass fraction
The following ingredient of meter: 1~10 part of manganese, 5~25 parts of tin, 5~25 parts of vanadium, 70~95 parts of iron, 15~25 parts of zinc.
Preferably, a kind of back veneer material of photovoltaic cell component, including following ingredient according to the mass fraction: manganese 3~8
Part, 10~20 parts of tin, 10~20 parts of vanadium, 80~90 parts of iron, 18~23 parts of zinc.
Most preferably, a kind of back veneer material of photovoltaic cell component, including following ingredient according to the mass fraction: manganese 5
Part, 15 parts of tin, 15 parts of vanadium, 85 parts of iron, 20 parts of zinc.
Preferably, the back veneer material of the photovoltaic cell component is with a thickness of 15~25um.
The technical effect that above-mentioned technical proposal can be realized is as follows: the present invention can improve photovoltaic cell component backboard
While material metal ductility, the appearance of pin hole is reduced, can be effectively reduced cost;And according to technical scheme
The generation of photoelectric conversion unit electrochemical reaction can be prevented by matching the back veneer material made.
Specific embodiment
Carry out the technical solution that the present invention will be described in detail below by way of specific embodiment, it should be appreciated that below specific
Embodiment be only capable of for explain the present invention and be not to be construed as limitation of the present invention.
Embodiment 1: a kind of back veneer material of photovoltaic cell component, including following ingredient according to the mass fraction: 1 part of manganese,
5 parts of tin, 5 parts of vanadium, 70 parts of iron, 15 parts of zinc.The back veneer material of the photovoltaic cell component is with a thickness of 15~25um.
Obtained back veneer material through the above scheme is seen when being processed as 15 microns of thin slice by electron microscope
It examines, discovery pin hole is seldom, is fully able to reach the requirement of photovoltaic element.
Embodiment 2: a kind of back veneer material of photovoltaic cell component, including following ingredient according to the mass fraction: manganese 10
Part, 25 parts of tin, 25 parts of vanadium, 95 parts of iron, 25 parts of zinc.The back veneer material of the photovoltaic cell component is with a thickness of 15~25um.
Obtained back veneer material through the above scheme is seen when being processed as 15 microns of thin slice by electron microscope
It examines, discovery pin hole is seldom, is fully able to reach the requirement of photovoltaic element.
Embodiment 3: a kind of back veneer material of photovoltaic cell component, including following ingredient according to the mass fraction: 3 parts of manganese,
10 parts of tin, 10 parts of vanadium, 80 parts of iron, 18 parts of zinc.The back veneer material of the photovoltaic cell component is with a thickness of 15~25um.
Obtained back veneer material through the above scheme is seen when being processed as 15 microns of thin slice by electron microscope
It examines, discovery pin hole is seldom, is fully able to reach the requirement of photovoltaic element.
Embodiment 4: a kind of back veneer material of photovoltaic cell component, including following ingredient according to the mass fraction: 8 parts of manganese,
20 parts of tin, 20 parts of vanadium, 90 parts of iron, 23 parts of zinc.The back veneer material of the photovoltaic cell component is with a thickness of 15~25um.
Obtained back veneer material through the above scheme is seen when being processed as 15 microns of thin slice by electron microscope
It examines, discovery pin hole is seldom, is fully able to reach the requirement of photovoltaic element.
Embodiment 5: a kind of back veneer material of photovoltaic cell component, including following ingredient according to the mass fraction: 5 parts of manganese,
15 parts of tin, 15 parts of vanadium, 85 parts of iron, 20 parts of zinc.The back veneer material of the photovoltaic cell component is with a thickness of 15~25um.
Obtained back veneer material through the above scheme is seen when being processed as 15 microns of thin slice by electron microscope
It examines, discovery pin hole is seldom, is fully able to reach the requirement of photovoltaic element.
The present invention can reduce going out for pin hole while improving photovoltaic cell component back veneer material metal ductility
It is existing, it can be effectively reduced cost;And light can be prevented according to the back veneer material that the proportion of technical scheme is made
The generation of electric converting unit electrochemical reaction.
The above description is merely a specific embodiment, but scope of protection of the present invention is not limited thereto, any
Those skilled in the art within the technical scope disclosed by the invention, can without the variation that creative work is expected or
Replacement, should be covered by the protection scope of the present invention.Therefore, protection scope of the present invention should be limited with claims
Subject to fixed protection scope.
Claims (4)
1. a kind of back veneer material of photovoltaic cell component, characterized in that including following ingredient according to the mass fraction: manganese 1~10
Part, 5~25 parts of tin, 5~25 parts of vanadium, 70~95 parts of iron, 15~25 parts of zinc.
2. a kind of back veneer material of photovoltaic cell component according to claim 1, characterized in that including according to the mass fraction
Following ingredient: 3~8 parts of manganese, 10~20 parts of tin, 10~20 parts of vanadium, 80~90 parts of iron, 18~23 parts of zinc.
3. a kind of back veneer material of photovoltaic cell component according to claim 1, characterized in that including according to the mass fraction
Following ingredient: 5 parts of manganese, 15 parts of tin, 15 parts of vanadium, 85 parts of iron, 20 parts of zinc.
4. a kind of back veneer material of photovoltaic cell component according to claim 1, characterized in that the photovoltaic cell component
Back veneer material with a thickness of 15~25um.