CN109814192A - Colored filter Blue pigment dispersion composition - Google Patents
Colored filter Blue pigment dispersion composition Download PDFInfo
- Publication number
- CN109814192A CN109814192A CN201811377783.XA CN201811377783A CN109814192A CN 109814192 A CN109814192 A CN 109814192A CN 201811377783 A CN201811377783 A CN 201811377783A CN 109814192 A CN109814192 A CN 109814192A
- Authority
- CN
- China
- Prior art keywords
- colored filter
- pigment
- pigment dispersion
- blue
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention reside in provide a kind of colored filter Blue pigment dispersion composition with high coloring power and high brightness of colored filter that can be used for meeting new spec display device.As solution, it is to provide the colored filter Blue pigment dispersion composition of following display device, it is the colored filter Blue pigment dispersion composition being mainly made of coloring pigment, pigment dispersion aids, resin and organic solvent, and the coloring pigment includes C.I. pigment blue 15: 6 and Phthalocyanine Zinc class viridine green.
Description
Technical field
The present invention relates to the colored filter blue pigments point that the colored filter that can be used for colour display device is formed
Powder composition.
Background technique
In recent years, the display device of almost all of television set, computer, mobile phone etc. is all gradually by liquid crystal colour disply
It is occupied.Colored filter for liquid crystal colour disply usually have transparent substrate, formed on the transparent substrate by
Red pixel area, green pixel area, the coloring layer that is constituted of trichromatic colored pattern in blue pixel area and each in order to distinguish
Colored pattern and form light shielding part (black matix) on the transparent substrate.These red pixel areas, green pixel area, blue picture
Plain area is the structure that the film of the good synthetic resin for having dispersed organic pigment of heat resistance, light resistance is provided on substrate, is made
Organic pigment red, that green and blue is assorted can be used for organic pigment.
As the backlight in the liquid crystal colour disply, have using cold-cathode tube (cold-cathode tube)
Type, the type using LCD, type using white organic EL unit etc..It in addition to this, can in the normal structure of various countries
Using the specification (BT.2020) of the RGBW color in such display device, in the display device using LCD, expecting to have can
It copes with 4K8K television set and the widened colored filter of new spec bring colour gamut can be coped with.Moreover, also being deposited in blue (B)
A possibility that previous colored filter is unable to fully reply with blue composition.
Moreover, even if using the colored filter group described in Patent Document 1 for having shared blue pigment and violet pigment
Object is closed, sufficient tinting strength, tinting power, high brightness are also unable to get, thus the reply to display device in new spec and insufficient.
Existing technical literature
Patent document
Patent document 1: Japanese Unexamined Patent Publication 2013-148872 bulletin
Summary of the invention
There is height the issue of the present invention is to provide a kind of colored filter that can be used for meeting new spec display device
The colored filter of tinting strength, tinting power and high brightness Blue pigment dispersion composition.
Present inventor has made intensive studies in order to solve the above problems, as a result, it has been found that by using as coloring pigment
C.I. pigment blue 15: 6 with Phthalocyanine Zinc class viridine green, and pigment dispersion aids and resin are applied in combination, can obtain can be used for having
Having high coloring power and high brightness and having for the colored filter of the display device of standby LCD light source or the organic EL light source of white is fitted
The colored filter Blue pigment dispersion composition of the form and aspect of the color that turns blue closed, so as to complete the present invention.
I.e. the present invention is as follows:
(1) a kind of colored filter of display device Blue pigment dispersion composition, for mainly by coloring pigment, pigment point
Dissipate the colored filter Blue pigment dispersion composition that auxiliary agent, resin and organic solvent are constituted, which is characterized in that the coloring
Pigment includes C.I. pigment blue 15: 6 and Phthalocyanine Zinc class viridine green.
(2) the colored filter Blue pigment dispersion composition of the display device according to (1), which is characterized in that as
The resin includes alkali soluble resin and photopolymerizable compound.
(3) the colored filter Blue pigment dispersion composition of the display device according to (1) or (2), which is characterized in that
The C.I. pigment blue 15: 6 with the quality ratio of the Phthalocyanine Zinc class viridine green be 99.9:0.1~90.0:10.0.
(4) the colored filter Blue pigment dispersion composition of the display device according to any one of (1)~(3),
It is characterized in that, Phthalocyanine Zinc class viridine green is one or more of C.I. naphthol green 59 and C.I. naphthol green 58.
(5) a kind of colored filter of display device Blue pigment dispersion anti-corrosion agent composition, for mainly by coloring pigment,
The blue face of the colored filter for the display device that pigment dispersion aids, resin, photopolymerizable compound and organic solvent are constituted
Material dispersion anti-corrosion agent composition, which is characterized in that the coloring pigment includes C.I. pigment blue 15: 6 and Phthalocyanine Zinc class green face
Material.
(6) the colored filter Blue pigment dispersion anti-corrosion agent composition of the display device according to (5), feature exist
In as the resin, comprising alkali soluble resin and photopolymerizable compound.
(7) the colored filter Blue pigment dispersion anti-corrosion agent composition of the display device according to (5) or (6), it is special
Sign is, the C.I. pigment blue 15: 6 and the quality ratio of the Phthalocyanine Zinc class viridine green are 99.9:0.1~90.0:
10.0。
(8) colored filter of the display device according to any one of (5)~(7) is combined with Blue pigment dispersion resist
Object, which is characterized in that Phthalocyanine Zinc class viridine green is one or more of C.I. naphthol green 59 and C.I. naphthol green 58.
It is can be obtained according to the present invention in dispersion stabilization with high coloring power and while high brightness also excellent colored filter
Mating plate Blue pigment dispersion composition.
Hereinafter, for the colored filter Blue pigment dispersion composition of the display device of that present invention, illustrate its it is each at
Point.
Specific embodiment
The present invention is to be related to the colored filter Blue pigment dispersion composition and colored filter indigo plant of display device
Color pigment disperses the invention of anti-corrosion agent composition, can also be not to be as colored filter Blue pigment dispersion composition
The composition of resist.
No matter which kind of composition, the colored filter Blue pigment dispersion composition of the display device of that present invention is that can be used for showing
The composition of the colored filter of device, as the effect of the invention by its bring, it is possible to provide there is high coloring power and highlight
Degree, therefore the colored filter of display device Blue pigment dispersion composition and colored filter Blue pigment dispersion are against corrosion
Agent composition.
The present invention is colored filter Blue pigment dispersion composition and divides relative to the colored filter blue pigment
Powder composition has cooperated colored filter Blue pigment dispersion made of alkali soluble resin, photopolymerizable compound etc. against corrosion
Agent composition.
And colored filter Blue pigment dispersion composition includes light-cured type and non-light-cured type.
[composition of A. colored filter Blue pigment dispersion composition]
Colored filter of the invention with Blue pigment dispersion composition mainly by coloring pigment, pigment dispersion aids, resin and
Organic solvent is constituted, and can cooperate pigment dispersing agent.
(pigment)
The colored filter of the display device of that present invention uses Blue pigment dispersion composition to contain C.I. pigment blue 15 as pigment: 6
(C.I.PB15:6) with Phthalocyanine Zinc class viridine green.
Phthalocyanine Zinc class viridine green refers to containing the pigment with the compound of the phthalocyanine structure of metal centered on zinc.In addition,
Can be with C.I. pigment blue 15: 6 cooperate in the range of play effect of the present invention, can also be for by with the metal centered on zinc
The pigment that the compound of phthalocyanine structure and the complex of other pigment are constituted.
As Phthalocyanine Zinc class viridine green, C.I. naphthol green 59 (C.I.PG59) and C.I. naphthol green 58 (C.I.PG58) can be used
One or more of.When adding the pigment with the compound of the Phthalocyanine Zinc structure, colored filter Blue pigment dispersion is made
When composition and the colored filter of display device Blue pigment dispersion anti-corrosion agent composition, it can be improved as the bright of composition
Brightness, transmissivity when degree or formation film.
Have the colored filter of display device of the organic EL light source of white etc. in Blue pigment dispersion composition in the present invention,
Total solid content of the total usage amount of coloring pigment relative to composition, it is preferably 5~80 mass % in terms of quality ratio, more excellent
Select 20~50 mass %.
In order to assign high brightness, comparison to the colored filter of the display device of that present invention Blue pigment dispersion composition
Degree, as above-mentioned each coloring pigment, it is preferable to use the pigment of micronized processing.By carrying out micronized processing, can make to colour
The primary particle size of pigment is finer and uniform.
As the processing of above-mentioned micronized, such as be preferably carried out the micronized processing: will comprising untreated coloring pigment,
Water-soluble inorganic salts are (for sodium chloride, barium chloride, potassium chloride etc., preferably sodium chloride, as used water-soluble inorganic salt
Preferably 50 μm or less of average grain diameter) and do not dissolve the water soluble disperse medium (alkoxyl alcohol of above-mentioned water-soluble inorganic salt substantially
Class, di-alcohols, ethers etc.) mixture by kneader, roller mill, ball mill, grater (attritor), sand mill,
Institute is made on the well as planetary stirring machine (planetary mixer) that Japanese Unexamined Patent Publication 2006-192385 bulletin is recorded
The TRI-MIX (trade (brand) name) of Co. Ltd. system, as continuous single-shaft kneading machine Asada Iron Works Co., Ltd. miracle
After the kneading device of KCK etc. is kneaded, the salt mill for removing above-mentioned water-soluble inorganic salt and above-mentioned water soluble disperse medium is carried out
Processing.
In turn, the viewpoint equably being miniaturize according to the crystal growth that can inhibit coloring pigment, preferably in aftermentioned pigment point
Micronized processing is carried out in the presence of scattered auxiliary agent.The usage amount of pigment dispersion aids at this time is relative to 100 mass of coloring pigment
Part is 0.5~30 mass parts, preferably 3~10 mass parts.
And except C.I. pigment blue 15: in addition to 6, within the scope of the effect of the invention, such as C.I. pigment can be shared
Blue pigment well known to blue 15:3 (C.I.PB15:3), C.I. pigment blue 16 (C.I.PB16) etc..In addition, as viridine green,
In the range of reducing brightness, contrast within the scope of the effect of the invention and not, such as C.I. pigment Green 7 can be used
(C.I.PG7), C.I. pigment green 36 (C.I.PG36) etc..
But the pigment of inadequacy violet is preferred.
(pigment dispersion aids)
As the pigment dispersion aids of Blue pigment dispersion composition of the colored filter for the display device of that present invention, preferably
With C.I. pigment blue 15: importing on the basic framework that 6 (epsilon copper phthalocyanine pigment) have same or similar molecular structure can be improved
With the acidic-group of the compatibility of organic solvent, so that the pigment dispersion aids of the pigment dispersing agent with acidic-group be made.
Such pigment dispersion aids are in the micronized of pigment, the process of dispersion, since the partial adsorbates of basic framework are in pigment table
Face, and the affinity with organic solvent, pigment dispersing agent can be improved in acidic-group, so have fine when dispersing pigment
Change, after dispersion through when the raisings such as dispersion stabilization effect.In addition, pigment dispersion aids itself are dissolution in organic solvent
Or the state dispersed with particle, due to being adsorbed in larger scope in surface of pigments, so further preferably.
Wherein, whens using as acidic-group with sulfonic pigment dispersion aids etc., good result can be obtained.
In the colored filter pigment dispersion in Blue pigment dispersion composition, with acidic-group of the display device of that present invention
The usage amount of auxiliary agent is 0.5~30 mass parts relative to 100 mass parts of coloring pigment.When the above-mentioned pigment with acidic-group point
When dissipating the content of auxiliary agent less than 0.5 mass parts, pigment dispersion effect is reduced, on the other hand, when more than 30 mass parts, pigment point
Scattered effect does not further increase.
The above-mentioned pigment dispersion aids with acidic-group are as follows:
(1) using the coloring pigment for carrying out micronized processing there is no the pigment dispersion aids with acidic-group
When, in the coloring pigment dispersion handled through micronized, relative to 100 mass parts of coloring pigment, using with acidic-group
0.5~30 mass parts of pigment dispersion aids, preferably 3~15 mass parts.
(2) using the coloring pigment for carrying out micronized processing in the presence of the pigment dispersion aids with acidic-group when,
Color pigment uses 0.5~30 mass parts of pigment dispersion aids in micronized processing, relative to 100 mass parts of coloring pigment, excellent
3~15 mass parts are selected, the coloring pigment handled through micronized has in dispersion relative to 100 mass parts use of coloring pigment
0~29.5 mass parts of pigment dispersion aids of acidic-group, preferably 0~12 mass parts.
And the usage amount of the used pigment dispersion aids with acidic-group is handled with through micronized in micronized processing
Coloring pigment usage amount of used pigment dispersion aids with acidic-group when pigment disperses summation relative to
100 mass parts of coloring pigment, the pigment dispersion aids with acidic-group are 0.5~30 mass parts, preferably 3~15 mass parts.
More specifically, as the pigment dispersion aids with acidic-group, the pigment used with sulphur acidic-group is dispersed
The case where auxiliary agent, is illustrated.
As blue pigment make C.I. pigment blue 15: when 6 dispersion, as described above, by as epsilon copper phthalocyanine pigment and C.I. pigment
Blue 15:6 is the sulfonated bodies of the pigment and/or pigment with anthraquinone skeleton of identical skeleton as pigment dispersion aids.
(polymer pigment dispersant)
Polymer pigment dispersant can be cooperated in the colored filter Blue pigment dispersion composition of the display device of that present invention.
As such polymer pigment dispersant, the height with basic group used in colored filter field in the past can be used
Molecule pigment dispersing agent.
The display device of that present invention colored filter in Blue pigment dispersion composition, when using polymer pigment dispersant
Usage amount relative to 100 mass parts of coloring pigment, preferably 1~100 mass parts, more preferable 1~60 mass parts.When above-mentioned high score
When the content of sub- pigment dispersing agent is less than 1 mass parts, pigment dispersion effect can be reduced sometimes, on the other hand, when more than 100 mass
There are a possibility that developability reduction etc. when part.
As the polymer pigment dispersant with basic group, such as following substance can be enumerated.
(1) polyamino compound (such as poly- (rudimentary) alkylene amines of polyallylamine, polyvinylamine, polyethylene polyimides etc. etc.)
Amino and/or imino group react generation at least one kind of in polyester, polyamide and polyesteramide with free carboxy
Object.
(2) it is respectively provided at least one side at least one kind of in polyester side chains, polyether lateral chain and polypropylene side chain in the molecule
The carbodiimides of chain and Basic nitrogen-containing groups.
(3) the low molecule ammoniate of the double propyl amine of poly- (rudimentary) alkylene imine, methyl-imino etc. with there is free carboxylic
The reaction product of the polyester of base.
(4) make the isocyanate group of polyisocyanate compounds successively with the alcohols of methoxy poly (ethylene glycol) etc., caprolactone polyester
Deng the polyesters with 1 hydroxyl, the compound with 2~3 isocyanate group reactive functional groups, there is isocyanates
Reaction product obtained by the reaction of the aliphatic or hetero ring type hydrocarbon compound of base reactive functional groups and tertiary amino.
(5) polymer with the acrylate of alcohol hydroxyl group and polyisocyanate compounds and the hydrocarbonylation with amino are closed
The reaction product of object reaction.
(6) make reaction product obtained by low molecule ammoniate addition polyether chain.
(7) reaction product obtained by reacting the compound with isocyanate group with the compound with amino.
(8) make polyepoxides and the linear polymer with free carboxyl and the organic amine chemical combination with 1 secondary amino group
The reaction product of object reaction.
(9) have the polycarbonate compound for the functional group that can be reacted with amino and reacting for polyamino compound raw in one-side ends
At object.
(10) methyl methacrylate, ethyl methyl acrylate, propylacrylate methyl esters, butyl methacrylate, tristearin are selected from
Base methyl acrylate, benzyl acrylic methyl esters, methacrylate, ethyl propylene acid esters, propyl acrylate, butylacrylic acid
At least one kind of and acrylamide in the methyl acrylate or acrylate of ester, sterylacrylic acid ester, benzyl acrylate etc.,
Methacrylamide, N- methylol amide, vinyl imidazole, vinylpyridine, the monomer with amino and polycaprolactone skeleton
Deng the polymerizable monomer containing basic group at least one kind of and styrene, styrene derivative, other polymerizable monomer
In at least one kind of copolymer.
(11) third be made of the block that tertiary amino, quaternary ammonium base etc. have the block of basic group and do not have basic functionality
Olefin(e) acid based block copolymer etc..
(12) polyallylamine and polycarbonate compound is made to carry out pigment dispersing agent obtained by Michael addition reaction.
(13) carbodiimides of at least one polybutadiene chain and Basic nitrogen-containing groups are respectively provided with.
(14) it is respectively provided with the Carbodiimides of side chain and Basic nitrogen-containing groups of at least one with amide groups in the molecule
Close object.
(15) with the Component units containing ethylene oxide chain and propylene oxide chain and with quaternized by quaternizing agent
The polyurethanes compound of amino.
(16) following compound: make intramolecular that there is the isocyanate group and molecule of isocyanate compound of chlorinated isocyanurates ring
The active hydrogen-based reaction of interior active hydrogen-based and the compound with carbazole ring and/or azo benzene skeleton and obtain, relative to this
Isocyanate group of the intramolecular of compound from the isocyanate compound with chlorinated isocyanurates ring and pass through isocyanates
Base reacts the total amount of urethane bond generated and urea bond with active hydrogen-based, and the number of carbazole ring and azo benzene skeleton is
15~85%.
(resin)
As the colored filter Blue pigment dispersion for the display device for having the organic EL light source of white of the invention etc.
The resin of composition, may be used in the all-wave length region of 400~700nm of visible light region transmissivity be 80% or more, it is excellent
Select 95% or more resin.As these resins, heat-curing resin, thermoplastic resin, alkali soluble resin can be used.
Colored filter Blue pigment dispersion of such resin relative to the display device for having the organic EL light source of white etc.
The total solid content of composition, total amount preferably 5~94 mass %, more preferable 20~50 of used resin in terms of mass fraction
The range of quality %.
As heat-curing resin, thermoplastic resin, such as can to enumerate butyral resin, styrene-maleic acid copolymer, chlorination poly-
Ethylene, chlorinated polypropylene, polyvinyl chloride, vinyl chloride vinyl acetate copolymer, polyvinyl acetate, polyurethane based resin, phenol
Urea formaldehyde, polyester resin, acrylic resin, alkyd resin, styrene resin, polyamide, rubber resin, cyclisation rubber
Glue, epoxy resin, cellulose family, polybutadiene, polyimide resin, benzoguanamine resin, melamine resin, urea resin
Deng.
And according to circumstances may be used also in the project in the colored filter of display device with Blue pigment dispersion anti-corrosion agent composition
Cooperate aftermentioned optical polymerism resin.
(alkali soluble resin as resin)
Alkali soluble resin can be cooperated in the colored filter Blue pigment dispersion composition of the display device of that present invention.As
Such resin, plays a role relative to pigment as adhesive and when manufacturing colored filter, in its development treatment work
Developer solution used in sequence is not particularly limited as long as particularly preferably having soluble developer solution relative to alkaline developer,
Previous used developer solution can be used.Wherein, particularly preferably preferably there is 1 or more with the alkali soluble resin of carboxyl
Carboxyl ethylene unsaturated monomer and other copolymerizable ethylene unsaturated monomers copolymer.
Specifically, the ethylene unsaturated monomer with carboxyl such as acrylic acid, methacrylic acid can be enumerated and be selected from and have
The copolymerizable styrene of the ethylene unsaturated monomer of carboxyl, 2- hydroxyethylmethacry,ate, 2- hydroxyethylacrylate methyl esters,
Allyl acrylate, allyl methacrylate, benzyl acrylate, benzyl acrylic methyl esters, cyclohexylacrylic ester, hexamethylene
Base methyl acrylate, glyceryl mono acrylic ester, glyceryl methyl acrylate, N-phenylmaleimide, polystyrene divide greatly
In the monomer of sub- monomer, polymethyl methacrylate macromonomer, phosphinylidyne epoxy group diacrylate etc., oligomeric species extremely
The copolymer of few a kind of ethylene unsaturated monomer.
As the acid value of the alkali soluble resin in the present invention, preferably 50 in terms of developing property~
300mgKOH/g.And above-mentioned acid value is theoretical acid value in the present invention, for based on carboxyl ethylene unsaturated monomer with
The value that its content arithmetic acquires.
In addition, the alkali soluble resin from the point of view of in terms of usually from developing property, in organic solvent deliquescent, in the present invention
Weight average molecular weight preferably 1,000~100,000.And in the present invention, the weight average molecular weight of above-mentioned alkali soluble resin is base
In the weight average molecular weight for the polystyrene conversion that GPC is obtained.In the present invention, (the water generation of Water 2690 is used as device
Corporation), 5 μM of IXED-D of PLgel (Polymer Laboratories corporation) is used as chromatographic column.
The usage amount of alkali soluble resin in the present invention is 1~300 matter relative to used 100 mass parts of coloring pigment
Measure part, preferably 10~200 mass parts.At this point, there is developing property drop when the usage amount of alkali soluble resin is less than 1 mass parts
A possibility that low.On the other hand, when more than 300 mass parts, since colorant concentration can be reduced relatively, so having conduct
Film is difficult to a possibility that reaching target color density.
(barium sulfate)
In order to improve the heat resistance (brightness) of colored filter of the invention Blue pigment dispersion composition, primary grain can be used
Diameter is the barium sulfate of 5~20nm.
The usage amount of barium sulfate uses 0~25 mass parts, the preferably model of 5~20 mass parts relative to 100 mass parts of coloring pigment
It encloses.
Above-mentioned barium sulfate is in the dispersion for the coloring pigment that micronized is handled or dispersion used later.
(organic solvent)
It, can be compatibly as the organic solvent of Blue pigment dispersion composition of the colored filter for the display device of that present invention
Use the organic solvent used in the field of liquid crystal color filter resist in the past.Specifically, in normal pressure
(1.013×102KPa the based organic solvent, ether organic solvent, ether-ether class that the boiling point under) is 100~220 DEG C are organic molten
Agent, organic solvent of ketone, aromatic hydrocarbon organic solvent, nitrogenous class organic solvent etc..When containing boiling point being more than largely 220 DEG C
When organic solvent, made of by coating chromatic optical filter Blue pigment dispersion composition or the composition containing the composition
When film preliminary drying, organic solvent is unable to fully evaporate and remain in dry coating, so that having the heat resistance of dry coating reduces
A possibility that.In addition, when largely organic solvent containing boiling point less than 100 DEG C, it is difficult to it is no mottled and be equably coated with, thus
A possibility that in the presence of surface smoothness excellent film is unable to get.
As the organic solvent for colored filter of the invention with Blue pigment dispersion composition, specifically, can
Illustrate ethylene glycol single methyl ether, ethylene glycol monomethyl ether, ethylene glycol monoisopropyl ether, ethylene glycol monobutyl ether, diethylene glycol list
Methyl ether, diethylene glycol monoethyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl, glycol monobutyl ether, diethylene glycol
The ether organic solvent of Anaesthetie Ether, diethylene glycol dimethyl ether, diethylene glycol methyl ethyl ether etc.;Ethylene glycol single methyl ether second
Acid esters, ethylene glycol monomethyl ether acetate, ethylene glycol monobutyl ether acetic acid esters, propylene glycol monomethyl ether, propylene glycol list
The ether based organic solvent of monoethyl ether acetate etc.;The ketone of methyl iso-butyl ketone (MIBK), cyclohexanone, 2-HEPTANONE, δ-butyrolactone etc. has
Solvent;2 hydroxy propanoic acid methyl esters, 2 hydroxy propanoic acid ethyl ester, 2- hydroxy-2-methyl ethyl propionate, 3- methyl -3- methoxyl group fourth
Base propionic ester, 3- methoxy methyl propionate, 3- methoxypropionate, 3- ethoxypropanoate, 3- ethoxyl ethyl propionate,
The based organic solvent of ethoxy ethyl acetate, hydroxyl ethyl acetate, formic acid n- pentyl ester etc.;Methanol, ethyl alcohol, isopropanol, butanol
Deng alcohols solvent;The nitrogenous class of N-Methyl pyrrolidone, n,N-Dimethylformamide, n,N-dimethylacetamide etc. is organic molten
Agent etc..These can individually or two or more is used in mixed way.
In these organic solvents, dissolubility, dispersibility, in terms of, preferably diethylene glycol dimethyl ether, diethyl two
Alcohol methyl ethyl ether, ethylene glycol single methyl ether acetic acid esters, propylene glycol monomethyl ether, propylene glycol monoethyl acetic acid esters,
Cyclohexanone, 2-HEPTANONE, 2 hydroxy propanoic acid ethyl ester, 3- methyl -3- methoxybutyl propionic ester, 3- methoxypropionate, 3- second
Oxygroup methyl propionate, formic acid n- pentyl ester etc., more preferable propylene glycol monomethyl ether.
The colored filter of the display device of that present invention is mainly dispersed by coloring pigment, pigment with Blue pigment dispersion composition
Auxiliary agent, resin and organic solvent are constituted, these ingredients display device colored filter in Blue pigment dispersion composition
It is total to account for 90~100 mass %.In addition, polymer pigment dispersant can further be added, as such polymeric pigments point
The arbitrary substance in aforementioned can be used in powder.
In addition, can also by the colored filter of the display device of that present invention with Blue pigment dispersion composition with do not have photo-curable
State used as resist with composition.
(additive that can be added as needed)
According to the manufacturing method of the colored filter Blue pigment dispersion composition of display device, photopolymerization can be suitably used and draw
Send out the various additives of agent, hot polymerization inhibitor, ultraviolet absorbing agent, antioxidant etc..As above-mentioned Photoepolymerizationinitiater initiater, such as can
Enumerate aftermentioned substance.
(manufacturing method of the colored filter of the display device of that present invention Blue pigment dispersion composition)
The colored filter that display device is manufactured to the above raw material is used is said with the method for Blue pigment dispersion composition
It is bright.And in the case where not being the colored filter Blue pigment dispersion anti-corrosion agent composition of the display device of photo-curable,
Cooperation photopolymerizable compound is not needed.
Therefore, pigment blue 15 containing C.I.: 6 pigment dispensing composition and Phthalocyanine Zinc class viridine green point is prepared as described below first
Powder composition.
Pigment blue 15 containing C.I.: 6 pigment dispensing composition
It obtains by (preferably there is anthracene for identical skeleton with C.I. pigment blue 15: 6 in the pigment dispersion aids with acidic-group
The pigment of quinone skeleton and/or the sulfonated bodies of pigment) in the presence of or it is non-in the presence of through micronized handle C.I. pigment blue 15: 6,
Resin, polymer pigment dispersant as needed, organic solvent, barium sulfate as needed, further as needed its
The mixture that his additive is constituted.Obtained mixture is used into roller mill, kneader, high-speed stirring apparatus, ball mill, ball
The various dispersion machines of grinding machine, sand mill, ultrasonic dispersing machine, high pressure dispersing machine etc. are kneaded, decentralized processing, are obtained containing C.I.
Pigment blue 15: 6 pigment dispensing composition.
Phthalocyanine Zinc class viridine green dispersive composition
It obtains by (preferably there is the face of identical skeleton with Phthalocyanine Zinc class viridine green in the pigment dispersion aids with acidic-group
The sulfonated bodies etc. of material) in the presence of or it is non-in the presence of through micronized handle Phthalocyanine Zinc class viridine green, pigment dispersion aids it is (excellent
Choosing with Phthalocyanine Zinc class viridine green have identical skeleton pigment sulfonated bodies etc.), resin, polymeric pigments as needed divide
The mixture that powder, organic solvent, barium sulfate, further other additives as needed are constituted.By obtained mixing
Object uses roller mill, kneader, high-speed stirring apparatus, ball mill, ball mill, sand mill, ultrasonic dispersing machine, high pressure dispersing machine
Deng various dispersion machines be kneaded, decentralized processing, obtain Phthalocyanine Zinc class viridine green dispersive composition.
The pigment blue 15 containing C.I. obtained as described above: 6 pigment dispensing composition and Phthalocyanine Zinc class green face can be used
Expect dispersive composition, will be provided with the colored filter Blue pigment dispersion composition example of the display device of the organic EL light source of white
Such as obtained by the manufacturing method of following (1), (2).
At this point, the pigment dispensing composition of following pigment containing complementary color can also be shared as needed.The pigment of the pigment containing complementary color point
Powder composition: complementary color pigment as needed can be used in the presence of the pigment dispersion aids with acidic-group or non-presence
The lower complementary color pigment handled through micronized, thus with above-mentioned pigment blue 15 containing C.I.: 6 pigment dispensing composition is got similarly
Pigment dispensing composition.
(1) it first passes through in advance by pigment blue 15 containing C.I.: 6 pigment dispensing composition, Phthalocyanine Zinc class viridine green discrete sets
The process that object is mixed in a manner of becoming regulated proportion with complementary color pigment as needed is closed, tree is added as needed thereafter
Rouge, barium sulfate, organic solvent, other additives, to manufacture the display device for having the organic EL light source of white of the invention
Colored filter Blue pigment dispersion composition.
(2) it first passes through in the pigment blue 15 containing C.I. manufactured as described above: being mixed as needed in 6 pigment dispensing composition in advance
Resin, barium sulfate, organic solvent, others are added thereafter as needed and add for the process that complementary color pigment becomes regulated proportion
Add agent, thus manufacture pigment blue 15 containing C.I.: 6 colored filter Blue pigment dispersion composition, on the other hand, about phthalein
Cyanines zinc class viridine green dispersive composition, similarly by the colored filter blue of manufacture class containing Phthalocyanine Zinc viridine green
Pigment dispensing composition and the process being mixed manufacture colored filter of the invention Blue pigment dispersion composition.
Passing through pigment blue 15 containing C.I. obtained by the above method: 6 pigment dispensing composition and Phthalocyanine Zinc class green face
Resin, barium sulfate, organic solvent, other additives is added in material dispersive composition as needed to use to prepare colored filter
Blue pigment dispersion composition.
Then, the colored filter of preparation in Blue pigment dispersion composition relative to C.I. pigment blue 15: 6 and Phthalocyanine Zinc
Class viridine green mixing complementary color pigment becomes defined ratio, to obtain of the invention having white organic EL light source
The colored filter of display device Blue pigment dispersion composition.
In the manufacturing method of above-mentioned (1), (2), using in the presence of the pigment dispersion aids with acidic-group through micro-
When the micronized pigment of granulated processed, micronized pigment can not also make it contain the pigment dispersion with acidic-group in dispersion
Auxiliary agent manufactures.
In addition, above-mentioned (1), (2) manufacturing method in, resin, barium sulfate can in the production of pigment dispensing composition and/or
It is added after production pigment dispensing composition.
In addition, above-mentioned (1), (2) manufacturing method in, from the viewpoint of can be obtained high coloring power and high brightness, preferably make
The pigment handled in the presence of the pigment dispersion aids with acidic-group through micronized.
Currently, as the side for manufacturing colored filter with Blue pigment dispersion anti-corrosion agent composition using colored filter
Method, predominantly uses the photoresist method of Photocurable composition, uses hereinafter, being divided into the colored filter that photoresist method uses
The colored filter of photo-curable Blue pigment dispersion composition and non-photo-curable unlike those described above blue pigment point
Powder composition, ingredient respectively contained for it etc. is described below.
Colored filter Blue pigment dispersion composition relative to the display device for having the organic EL light source of white etc.
Total solid content, the total amount of the resin used in terms of mass fraction preferably 5~94 mass %, more preferable 20~50 mass %
Range.
The case where [colored filter of B. display device with Blue pigment dispersion anti-corrosion agent composition being photo-curable]
It then, is the feelings of photo-curable with Blue pigment dispersion anti-corrosion agent composition to the colored filter of the display device of that present invention
Condition is illustrated.
When the colored filter of the display device of that present invention with Blue pigment dispersion anti-corrosion agent composition is photo-curable, its composition
Active energy ray-curable and for the anti-corrosion agent composition of alkali development can be carried out, mainly by pigment, pigment dispersion aids, tree
Rouge and organic solvent are constituted, and further may include alkali-soluble comprising barium sulfate, as the photopolymerizable compound of the resin
Resin.
As other than pigment, pigment dispersion aids, polymer pigment dispersant, photopolymerizable compound resin, barium sulfate and
Type, the use level of organic solvent, are used according to above-mentioned colored filter with the explanation of Blue pigment dispersion composition.
And about organic solvent, from the dissolubility, the dispersibility of coloring pigment, coating etc. of above-mentioned alkali soluble resin
Viewpoint is set out, preferably the colored filter of the display device of that present invention in Blue pigment dispersion anti-corrosion agent composition contain 50 matter
Measure % or more, more preferable 70 mass % or more.
(photopolymerizable compound)
Colored filter optical polymerism used in Blue pigment dispersion anti-corrosion agent composition as the display device of that present invention
Compound, can be used intramolecular have monomer, oligomer, optical polymerism resin etc. of 1 or more optical polymerism unsaturated bond with
Above-mentioned colored filter identical photopolymerizable compound documented in Blue pigment dispersion composition.With optical polymerism
Monomer, oligomer of unsaturated bond etc. refer to that aftermentioned Photoepolymerizationinitiater initiater passes through the active-energy of ultraviolet light, electron ray etc.
The effect of line and free radical, cation that while decomposing generates, it is polymerizable and resinification the monomer with unsaturated bond, oligomeric
Object.
As photopolymerizable compound, there is the monomer of 1 optical polymerism unsaturated bond as intramolecular, metering system can be enumerated
Sour methyl esters, butyl methacrylate, 2- ethylhexyl methyl acrylate, methacrylate, butyl propyleneglycol acid esters, 2- ethyl hexyl
The alkyl acrylic methyl esters or acrylate of base acrylate etc.;The aralkyl of benzyl acrylic methyl esters, benzyl acrylate etc.
Methyl acrylate or acrylate;The alkoxyalkyl third of butoxyethyl group methyl acrylate, butoxyethyl group acrylate etc.
E pioic acid methyl ester or acrylate;N, N- dimethylaminoethylacryl acid methyl esters, N, N- dimethyl amino ethyl acrylate etc.
Aminoalkyl methyl acrylate or acrylate;Diethylene glycol ethyl ether, triethylene glycol butyl ether, dipropylene glycol methyl ether etc.
Alkyl ether methyl acrylate or acrylate;The polyalkylene glycol aryl of six ethylene glycol phenyl ethers etc.
The methyl acrylate or acrylate of ether;Isobornyl acid methyl esters or acrylate;Glyceryl methyl acrylate or propylene
Acid esters;2- hydroxyethyl methyl esters or acrylate etc..
There is the monomer of 2 or more optical polymerism unsaturated bonds as the intramolecular of photopolymerizable compound, bisphenol-A two can be enumerated
Methyl acrylate, 1,4-butanediol diacrylate methyl esters, 1,3-BDO diacrylate methyl esters, diethylene glycol diacrylate first
Ester, glyceryl diacrylate methyl esters, neopentyl glycol diacrylate methyl esters, polyethylene glycol diacrylate methyl esters, polypropylene glycol dipropyl
E pioic acid methyl ester, tetraethylene glycol diacrylate methyl esters, trimethylolpropane tris methyl acrylate, three methyl acrylate of pentaerythrite,
Pentaerythrite tetrapropylene acid methyl esters, dipentaerythritol tetrapropylene acid methyl esters, six methyl acrylate of dipentaerythritol, dipentaerythritol
Five methyl acrylates, bisphenol a diacrylate, 1,4-butanediol diacrylate, 1,3-BDO diacrylate, diethyl two
Alcohol diacrylate, glyceryl diacrylate, neopentylglycol diacrylate, polyethyleneglycol diacrylate, polypropylene glycol
Diacrylate, tetraethylene glycol diacrylate, trimethylolpropane trimethacrylate, pentaerythritol triacrylate, season penta
Tetra-acrylate, dipentaerythritol tetraacrylate, dipentaerythritol hexaacrylate, Dipentaerythritol Pentaacrylate
Deng.These monomers can be used singly or two or more kinds in combination.
Photopolymerizable compound is polymerize obtained oligomer in addition, can be used.
As the optical polymerism resin of photopolymerizable compound, it may be used at hydroxyl, carboxyl, amino isoreactivity substituent group
Linear macromolecule on via isocyanate group, aldehyde radical, epoxy group etc. import the light such as (methyl) acyclic compound, cinnamic acid
The resin of crosslinkable groups.It also can be used styrene-maleic anhydride copolymer, alpha-olefin-copolymer-maleic anhydride etc. and include
The linear macromolecule of acid anhydrides is carried out by hydroxy alkyl (methyl) acrylate etc. with (methyl) acyclic compound of hydroxyl
Half-esterification polymer.
The photopolymerizable compound that above-mentioned resin can be formed can be used singly or two or more kinds in combination.In the present invention, optical polymerism
Colored filter total solid in Blue pigment dispersion anti-corrosion agent composition of the usage amount of compound relative to display device
Ingredient, the preferred range of 3~50 mass % in terms of mass fraction.
(Photoepolymerizationinitiater initiater)
Photopolymerization used in colored filter Blue pigment dispersion anti-corrosion agent composition as the display device of that present invention is drawn
Agent is sent out, as long as can produce free radical, cation by the active energy ray of irradiation ultraviolet light, electron ray etc., without special
It limits, such as benzophenone, N can be enumerated, tetraethyl -4 N ' -, 4 '-diaminobenzophenones, 4- methoxyl group -4 '-dimethylamino
Base benzophenone, benzil, 2,2- diethoxy acetophenone, styrax, styrax methyl ether, benzoin isobutyl butyl ether, benzyl
Dimethyl ketal, Alpha-hydroxy isobutyl group benzophenone, thioxanthones, 2-chlorothioxanthone, 1- hydroxycyclohexyl phenyl ketone, tert-butyl anthraquinone, 1-
Chloroanthraquinone, 2,3- dichloroanthraquinone, 3- chloro-2-methyl anthraquinone, 2- ethyl hydrazine, 1,4-naphthoquinone, 1,2- benzo anthraquinone, Isosorbide-5-Nitrae-diformazan
Base anthraquinone, 2- phenyl anthraquinone, 2- methyl-1 [4- (methyl mercapto) phenyl] -2- morpholinopropane -1- ketone, triazines photopolymerization cause
Agent etc..These Photoepolymerizationinitiater initiaters can be used singly or two or more kinds in combination.
In the present invention, colored filter blue pigment of the content of above-mentioned Photoepolymerizationinitiater initiater relative to above-mentioned display device
Disperse the total solid content in anti-corrosion agent composition, the preferred range of 1~20 mass % in terms of mass fraction.
The colored filter of the display device of that present invention is with Blue pigment dispersion anti-corrosion agent composition mainly by coloring pigment, face
Expect dispersing aid, polymer pigment dispersant, alkali soluble resin, photopolymerizable compound, Photoepolymerizationinitiater initiater, barium sulfate and
Organic solvent is constituted, and mentioned component is aggregated in colored filter with accounting for 90~100 matter in Blue pigment dispersion anti-corrosion agent composition
Measure %.
(additive that can be added as needed)
It, can be according to need when the colored filter of the display device of that present invention with Blue pigment dispersion anti-corrosion agent composition is photo-curable
It will be suitably using various additives such as hot polymerization inhibitor, ultraviolet absorbing agent, antioxidants.
[the case where colored filter Blue pigment dispersion anti-corrosion agent composition of C. display device is non-photo-curable]
When the colored filter Blue pigment dispersion anti-corrosion agent composition of display device is non-photo-curable, above-mentioned B. is not contained
The colored filter of display device used optical polymerism when with Blue pigment dispersion anti-corrosion agent composition being photo-curable
Object, Photoepolymerizationinitiater initiater are closed, can further cooperate the colored filter Blue pigment dispersion of above-mentioned display device as needed
Resin other than photopolymerizable compound shown in the composition explanation of composition.
(additive that can be added as needed)
It, can basis when the colored filter Blue pigment dispersion anti-corrosion agent composition of the display device of that present invention is non-photo-curable
It needs suitably to use the various additives such as ultraviolet absorbing agent, antioxidant.
(manufacturing method of the colored filter of the display device of that present invention Blue pigment dispersion anti-corrosion agent composition)
To the method for the colored filter Blue pigment dispersion anti-corrosion agent composition for using above material manufacture display device into
Row explanation.When the colored filter of display device with Blue pigment dispersion anti-corrosion agent composition is optical polymerism, relative to above-mentioned
It is poly- further to add photopolymerizable compound, light for the colored filter of obtained display device Blue pigment dispersion composition
Initiator, alkali soluble resin as needed, barium sulfate, organic solvent, other additives are closed, so that it is aobvious to obtain the present invention
The colored filter of showing device Blue pigment dispersion anti-corrosion agent composition.
In addition, alkali soluble resin, barium sulfate, organic solvent, other additives can further be added when it is non-optical polymerism
Deng it is any, to obtain the colored filter Blue pigment dispersion anti-corrosion agent composition of the display device of that present invention.Under
It is also identical in the manufacturing method stated.
Specifically, can for example be obtained by following manufacturing methods (1), (2).
(1) in advance by above-mentioned pigment blue 15 containing C.I.: 6 pigment dispensing composition, the dispersion of Phthalocyanine Zinc class viridine green
Composition is with C.I. pigment blue 15: 6, Phthalocyanine Zinc class viridine green, complementary color pigment as needed, which mix, becomes rule
The colored filter of the obtained display device such as fixed ratio is further added as needed in Blue pigment dispersion composition
Enter photopolymerizable compound, Photoepolymerizationinitiater initiater, alkali soluble resin, barium sulfate, organic solvent, other additives etc., from
And obtain the colored filter Blue pigment dispersion anti-corrosion agent composition of the display device of that present invention.
(2) above-mentioned pigment blue 15 containing C.I.: 6 pigment dispensing composition and Phthalocyanine Zinc class viridine green dispersive composition
In, respectively as needed be added polymerizable compound, Photoepolymerizationinitiater initiater, alkali soluble resin, barium sulfate, organic solvent, its
His additive, to obtain the colored filter Blue pigment dispersion anti-corrosion agent composition of display device.
Thereafter the process by mixing the colored filter of above-mentioned display device with Blue pigment dispersion anti-corrosion agent composition, from
And to manufacture the colored filter of the display device of that present invention Blue pigment dispersion anti-corrosion agent composition.
In the colored filter Blue pigment dispersion resist of the obtained display device of method by (1) and (2)
In composition, photopolymerizable compound, Photoepolymerizationinitiater initiater, alkali-soluble tree as needed are further added as needed
Rouge, barium sulfate, organic solvent, other additives, to prepare each colored filter pigment dispersion anti-corrosion agent composition.It connects
, each colored filter of preparation pigment is dispersed into anti-corrosion agent composition and C.I. pigment blue 15: 6, Phthalocyanine Zinc class green face
Material, complementary color pigment as needed carry out mixing and become defined ratio, to obtain the colour of the display device of that present invention
Optical filter Blue pigment dispersion anti-corrosion agent composition.
In addition, manufacturing display device as the colored filter of the display device of that present invention is used with Blue pigment dispersion composition
Colored filter method, can be used including to device necessary to it and as the composition other than the pigment dispensing composition
Well known method manufactures.
For the colored filter with specific composition of the invention Blue pigment dispersion composition, wherein being used as its face
Color characteristic (x, y, Y), preferably coloration x are 0.125~0.135.It is preferred that y be 0.040~0.121, particularly preferred 0.044~
0.100。
Embodiment
Embodiment is exemplified below to illustrate the present invention in further detail, but the present invention is not only defined in these embodiments.
And in the case where no special declaration, " % " " mean " quality % ", " part " means " mass parts ".
<pigment dispersion aids>
Phthalocyanine derivates: DISPER BYK-2100 (Bi Ke chemical company system)
<pigment dispersing agent>
LP21116: Bi Ke chemical company's system, acrylic polymer, amine value 29,40 mass % of solid component content
<alkali soluble resin>
ZAH110: Soken Chemical Company system, acid value: 100mgKOH/g, weight average molecular weight: about 15000,35 matter of solid component content
Measure %
<photopolymerizable compound>
DPHA: dipentaerythritol hexaacrylate
<organic solvent>
PGMEA: propylene glycol monomethyl ether
PGME: propylene glycol monomethyl ether
Based on cooperating shown in following table 1, colored filter Blue pigment dispersion composition is obtained.
Table 1
<colored filter Blue pigment dispersion anti-corrosion agent composition>
Each ingredient of above-described embodiment and comparative example is subjected to the composition that mixing becomes table 1, it is used to the oxygen of 0.2mm Φ
Change zirconium pearl to be kneaded 6 hours with paint conditioner, to obtain colored filter Blue pigment dispersion composition.
Table 2
Then, colored filter table 1 recorded Blue pigment dispersion composition and other materials'use high-speed stirrings
It mixes after machine uniformly mixes and become the composition of table 2, is filtered with 3 μm of the membrane filter in aperture, to obtain colored filter
Mating plate Blue pigment dispersion anti-corrosion agent composition.
(evaluation)
<production of sample>
The colored filter of embodiment and comparative example is coated on glass using sol evenning machine with Blue pigment dispersion anti-corrosion agent composition
On glass substrate.Then, it is exposed with high-pressure sodium lamp after preliminary drying 3 minutes in 100 DEG C, further after 230 DEG C carry out 30 minutes
It dries.
<color characteristics contrast>
About embodiment and the said sample of comparative example, by color characteristics (x, y, the Y) spectrophotometer (Shimadzu of each resist
Make society, institute system, UV-2500PC, 2 ° of visuals field of illuminant-C) it is measured.Coloration x=0.1332, y=0.120, x=are acquired respectively
0.1330, y=0.090 and the brightness Y under x=0.1337, y=0.090, contrast.
<film thickness>
About film thickness, film cutter is cut into 5mm or so, with film thickness gauge (KLA-Tencor Corporation system, surface wheel
Wide instrument Alpha-Step IQ) it is measured.
<viscosity>
The viscosity at 25 DEG C is measured using E type viscosimeter (Toki Sangyo Co., Ltd.'s system, R100 type Viscometer Model RE100L).
<dispersion stabilization>
The colored filter Blue pigment dispersion resist group used in the resist method of above-described embodiment and comparative example
Object is closed, is collected in vial and is sealed respectively, it will be after the taking care of 1 month at each temperature of 40 DEG C, 5 DEG C and room temperature (23 DEG C)
State evaluated according to following evaluation criterions.
Zero: the rate of change in viscosity of keeping front and back is 10% or less
×: the rate of change in viscosity of keeping front and back is more than 10%
According to above-described embodiment and comparative example when being made colored filter Blue pigment dispersion anti-corrosion agent composition, point
It dissipates and has good stability.And according to embodiment, brightness more higher than comparative example and contrast can be obtained.
In addition, though the ingredient other than the pigment of embodiment and comparative example is identical as its use level, but example composition is viscous
It spends lower.
Claims (8)
1. a kind of colored filter of display device Blue pigment dispersion composition, for mainly by coloring pigment, pigment point
Dissipate the colored filter Blue pigment dispersion composition that auxiliary agent, resin and organic solvent are constituted, which is characterized in that the coloring
Pigment includes C.I. pigment blue 15: 6 and Phthalocyanine Zinc class viridine green.
2. the colored filter of display device according to claim 1 Blue pigment dispersion composition, which is characterized in that
It include alkali soluble resin and photopolymerizable compound as the resin.
3. the colored filter of display device according to claim 1 or 2 Blue pigment dispersion composition, feature exist
In the C.I. pigment blue 15: 6 with the quality ratio of the Phthalocyanine Zinc class viridine green be 99.9:0.1~90.0:10.0.
4. the colored filter of display device described in any one of claim 1 to 3 Blue pigment dispersion composition,
It is characterized in that, Phthalocyanine Zinc class viridine green is one or more of C.I. naphthol green 59 and C.I. naphthol green 58.
5. a kind of colored filter of display device Blue pigment dispersion anti-corrosion agent composition, for mainly by coloring pigment,
The blue face of the colored filter for the display device that pigment dispersion aids, resin, photopolymerizable compound and organic solvent are constituted
Material dispersion anti-corrosion agent composition, which is characterized in that the coloring pigment includes C.I. pigment blue 15: 6 and Phthalocyanine Zinc class green face
Material.
6. the colored filter of display device according to claim 5 Blue pigment dispersion anti-corrosion agent composition, special
Sign is, includes alkali soluble resin and photopolymerizable compound as the resin.
7. the colored filter of display device according to claim 5 or 6 Blue pigment dispersion anti-corrosion agent composition,
Be characterized in that, the C.I. pigment blue 15: 6 with the quality ratio of the Phthalocyanine Zinc class viridine green be 99.9:0.1~90.0:
10.0。
8. the colored filter of the display device according to any one of claim 5~7 Blue pigment dispersion resist
Composition, which is characterized in that Phthalocyanine Zinc class viridine green is one or more of C.I. naphthol green 59 and C.I. naphthol green 58.