CN109811208A - A kind of wear resistant alloy material - Google Patents
A kind of wear resistant alloy material Download PDFInfo
- Publication number
- CN109811208A CN109811208A CN201711158615.7A CN201711158615A CN109811208A CN 109811208 A CN109811208 A CN 109811208A CN 201711158615 A CN201711158615 A CN 201711158615A CN 109811208 A CN109811208 A CN 109811208A
- Authority
- CN
- China
- Prior art keywords
- alloy material
- wear resistant
- resistant alloy
- surplus
- ingredient
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wear resistant alloy materials, are made of alloy material, the ingredient of the alloy material are as follows: Si:2~3%, ZR:0.3%, C:0.5%, Mn:0.2%, Cr:0.5%, Mg:21.8%, surplus are Al and inevitable impurity.Wear resistant alloy material antiwear characteristic with higher of the present invention, surface oxidation-resistant is good, and temperature level is high, and has higher intensity at high temperature.
Description
Technical field
The present invention relates to a kind of wear resistant alloy materials.
Background technique
Surface oxidation-resistant, temperature level, intensity at high temperature, processing performance of existing wear resistant alloy material etc. have
Wait improve.
Summary of the invention
The purpose of the present invention is to provide a kind of wear resistant alloy materials, are made of alloy material, wear-resisting spy with higher
Property, surface oxidation-resistant is good, and temperature level is high, and has higher intensity at high temperature, there is good processing performance and solderable
Property, long service life.
To achieve the above object, it the technical scheme is to design a kind of wear resistant alloy material, is made of alloy material,
By weight percentage, the ingredient of the alloy material are as follows: Si:2~3%, ZR:0.3%, C:0.5%, Mn:0.2%, Cr:0.5%, Mg:
21.8%, surplus is Al and inevitable impurity.
Preferably, a kind of wear resistant alloy material, is made of alloy material, by weight percentage, the alloy material at
Be divided into: Si:2%, ZR:0.3%, C:0.5%, Mn:0.2%, Cr:0.5%, Mg:21.8%, surplus are Al and inevitable impurity.
Preferably, a kind of wear resistant alloy material, is made of alloy material, by weight percentage, the alloy material at
Be divided into: Si:3%, ZR:0.3%, C:0.5%, Mn:0.2%, Cr:0.5%, Mg:21.8%, surplus are Al and inevitable impurity.
Advantages and advantages of the present invention are to provide a kind of wear resistant alloy material, is made of alloy material, have compared with
High antiwear characteristic, surface oxidation-resistant is good, and temperature level is high, and has higher intensity at high temperature, there is good processing
Performance and solderability, long service life.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following embodiment is only used for more
Add and clearly demonstrate technical solution of the present invention, and not intended to limit the protection scope of the present invention.
The technical solution that the present invention embodies is:
Embodiment 1
A kind of wear resistant alloy material, is made of alloy material, by weight percentage, the ingredient of the alloy material are as follows:
Si:2~3%, ZR:0.3%, C:0.5%, Mn:0.2%, Cr:0.5%, Mg:21.8%, surplus be Al and inevitably it is miscellaneous
Matter.
Embodiment 2
A kind of wear resistant alloy material, is made of alloy material, by weight percentage, the ingredient of the alloy material are as follows:
Si:2%, ZR:0.3%, C:0.5%, Mn:0.2%, Cr:0.5%, Mg:21.8%,
Surplus is Al and inevitable impurity.
Embodiment 3
A kind of wear resistant alloy material, is made of alloy material, by weight percentage, the ingredient of the alloy material are as follows:
Si:3%, ZR:0.3%, C:0.5%, Mn:0.2%, Cr:0.5%, Mg:21.8%,
Surplus is Al and inevitable impurity.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (3)
1. a kind of wear resistant alloy material, which is characterized in that it is made of alloy material, by weight percentage, the alloy material
Ingredient are as follows: Si:2~3%, ZR:0.3%, C:0.5%, Mn:0.2%, Cr:0.5%, Mg:21.8%, surplus is for Al and inevitably
Impurity.
2. a kind of wear resistant alloy material according to claim 1, which is characterized in that be made of alloy material, by weight hundred
Divide than meter, the ingredient of the alloy material are as follows: Si:2%, ZR:0.3%, C:0.5%, Mn:0.2%, Cr:0.5%, Mg:21.8%, surplus
For Al and inevitable impurity.
3. a kind of wear resistant alloy material according to claim 1, which is characterized in that be made of alloy material, by weight hundred
Divide than meter, the ingredient of the alloy material are as follows: Si:3%, ZR:0.3%, C:0.5%, Mn:0.2%, Cr:0.5%, Mg:21.8%, surplus
For Al and inevitable impurity.