CN105039849A - Alloy used for gear mould - Google Patents
Alloy used for gear mould Download PDFInfo
- Publication number
- CN105039849A CN105039849A CN201510406753.7A CN201510406753A CN105039849A CN 105039849 A CN105039849 A CN 105039849A CN 201510406753 A CN201510406753 A CN 201510406753A CN 105039849 A CN105039849 A CN 105039849A
- Authority
- CN
- China
- Prior art keywords
- alloy
- alloy used
- weight percent
- gear mould
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of alloy materials, and particularly relates to alloy used for a gear mould. The alloy comprises, by weight, 4%-6% of carbon, 2%-4% of tungsten, 1%-1.5% of aluminum, 0.25%-0.45% of tin, 0.3%-0.45% of titanium, 0.4%-1% of zinc, 2%-3% of cobalt and the balance iron. The alloy used for the gear mould has the beneficial effects of being low in cost, high in structural strength, good in chemical stability and long in service life.
Description
Technical field
The invention belongs to technical field of alloy material, be specifically related to a kind of alloy for gear die.
Background technology
Mould is used to the instrument of formed article, belong to precision tool, complex-shaped, bear the expansive force of blank, all have higher requirements to structural strength, rigidity, surface hardness, surfaceness and working accuracy, being used for the quality of the material making mould then determines the quality of mould, usually the punching block die manufacturing cost adopted in prior art is high, cycle is long, the advantage of lower cost of alloy material, and more easily realizes the requirement of mould in plasticity, hardness, intensity etc.
Summary of the invention
Goal of the invention of the present invention is, provide a kind of structural strength high, chemical stability is good, the alloy for gear die of long service life.
In order to realize above goal of the invention, the invention provides a kind of alloy for gear die, comprising the component of following weight percent: carbon 4-6%; Tungsten 2-4%; Aluminium 1-1.5%; Tin 0.25-0.45%; Titanium 0.3-0.45%; Zinc 0.4-1%; Cobalt 2-3%; Surplus is iron.
Further, the rare earth that weight percent is 0.2-0.3% can also be added.
Further, the molybdenum that weight percent is 0.5-0.8% can also be added.
The invention has the beneficial effects as follows: the cost of this mould alloy is low, and structural strength is high, chemical stability is good, and long service life.
Embodiment
The preferred embodiments of the invention 1 are: a kind of alloy for gear die, comprises the component of following weight percent: carbon 4.5%; Tungsten 2%; Aluminium 1%; Tin 0.45%; Titanium 0.45%; Zinc 0.5%; Cobalt 3%; Surplus is iron.
Preferred embodiment 2 is: a kind of alloy for gear die, comprises the component of following weight percent: carbon 5%; Tungsten 2%; Aluminium 1.2%; Tin 0.25%; Titanium 0.4%; Zinc 0.7%; Cobalt 2.5%; The rare earth of 0.2%; Surplus is iron.
Preferred embodiment 3 is: a kind of alloy for gear die, comprises the component of following weight percent: carbon 6%; Tungsten 4%; Aluminium 1.2%; Tin 0.3%; Titanium 0.35%; Zinc 0.8%; Cobalt 2.5%; The molybdenum of 0.8%; Surplus is iron.
The above, be only the preferred embodiments of the present invention, is not restriction the present invention being made to any other form, and any amendment done according to technical spirit of the present invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (3)
1. for an alloy for gear die, it is characterized in that: the component comprising following weight percent: carbon 4-6%; Tungsten 2-4%; Aluminium 1-1.5%; Tin 0.25-0.45%; Titanium 0.3-0.45%; Zinc 0.4-1%; Cobalt 2-3%; Surplus is iron.
2. a kind of alloy for gear die according to claim 1, is characterized in that: can also add the rare earth that weight percent is 0.2-0.3%.
3. a kind of alloy for gear die according to claim 1 and 2, is characterized in that: can also add the molybdenum that weight percent is 0.5-0.8%.