CN109796721A - A kind of ABS alloy material easy to clean and preparation method thereof - Google Patents

A kind of ABS alloy material easy to clean and preparation method thereof Download PDF

Info

Publication number
CN109796721A
CN109796721A CN201811624991.5A CN201811624991A CN109796721A CN 109796721 A CN109796721 A CN 109796721A CN 201811624991 A CN201811624991 A CN 201811624991A CN 109796721 A CN109796721 A CN 109796721A
Authority
CN
China
Prior art keywords
alloy material
abs alloy
abs
clean
easy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811624991.5A
Other languages
Chinese (zh)
Inventor
杨亚娣
文听雷
任东方
吴摞
李荣群
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Orinko Advanced Plastics Co Ltd
Original Assignee
Orinko Advanced Plastics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Orinko Advanced Plastics Co Ltd filed Critical Orinko Advanced Plastics Co Ltd
Priority to CN201811624991.5A priority Critical patent/CN109796721A/en
Publication of CN109796721A publication Critical patent/CN109796721A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of ABS alloy materials easy to clean and preparation method thereof, it is characterised in that: the alloy material is prepared in parts by weight by following components: 50-90 parts of ABS resin;10-60 parts of polycarbonate;1-10 parts of filler;2-10 parts of surface modifier;1-5 parts of compatilizer;0.3-1 parts of antioxidant;0.5-2.5 parts of lubricant;0.2-1 parts of organic solvent;Strong base-weak acid salt 0.2-1;ABS alloy material prepared by the present invention is not easy to accumulate dust, and easy wiped clean.

Description

A kind of ABS alloy material easy to clean and preparation method thereof
Technical field
The present invention relates to technical field of polymer materials, specially a kind of ABS alloy material easy to clean and preparation method thereof.
Background technique
Currently, the development of countries in the world household electric appliances is increasingly increasingly becoming production from human nature, customer experience and safety The core focus of product, in the living conditions, the cleaning of dust, greasy dirt remove the first major issue for having become people's headache;Dust It is extremely harmful for each organ of human body, especially it is attached to that the pollutants such as metal ion, benzene, formaldehyde are generated in finishing Grain object can destroy the mucous membrane tissue of human body by organs such as nasal cavity, the upper respiratory tracts, lead to headache dizziness, visual impairment, breathing A series of diseases such as difficulty, neu obstacle, are in peril of one's life when serious.
Simultaneously in industrial aspect, dust is accumulated for a long time at the functors such as engine or wind wheel component position, influences air quantity, The refrigeration effect of complete machine is seriously affected, in addition dust influences the dynamic balancing of flabellum rotation, seriously affects flabellum and impeller place goes out Air quantity and electrical machinery life.
So providing a kind of ABS alloy material and its system easy to clean being able to solve convenient for ABS alloy material cleaning problems Preparation Method, which becomes us, to be solved the problems, such as.
Summary of the invention
The purpose of the present invention is to provide a kind of ABS alloy materials easy to clean and preparation method thereof, to solve above-mentioned background It proposes to be convenient for ABS alloy material cleaning problems in technology.
To achieve the above object, the invention provides the following technical scheme:
A kind of ABS alloy material easy to clean and preparation method thereof, it is characterised in that: the alloy material be by following components by Parts by weight are prepared:
Preferably, the partial size of the ABS resin is 3-4 μm, mass percent 30%.
Preferably, the filler be white carbon black, poly- methyl carbamide resin, metallic soap, diatomite, in wollastonite at least It is a kind of.
Preferably, the partial size of the filler is 100-200nm.
Preferably, the surface modifier is perfluorocarboxylic acid chromium complex, acrylic acid fluorohydrocarbon esters resin, acrylic acid fluorine At least one of hydrocarbon sulfonamido ethyl ester, chlorotrifluoroethylene-vinylidene fluoride copolymers.
Preferably, the compatilizer is maleic anhydride grafted propylene nitrile butadiene-styrene copolymer, styrene-the third Alkene nitrile-copolymer-maleic anhydride, Styrene-Maleic Anhydride Copolymer and acrylonitrile-styrene-methacrylic acid copolymer At least one of;
The antioxidant is 2,2- methylene-bis- (4- methyl-6-tert butyl phenol), N, N- [3- (3,5- di-t-butyl -4- Hydroxy phenyl) propionyl] hexamethylene diamine, 4,4'- thiobis (6- tert-butyl -3- methylphenol), bis- [1, the 1- dimethyl-of 3,9- 2- [(3- tertiary butyl-4-hydroxy -5- aminomethyl phenyl) propionyloxy] ethyl] four oxaspiro of -2,4,8,10-, N, the bis- [3- of N ' - At least one of (3 ', 5 '-di-t-butyls -4 '-hydroxy phenyl) propionyl hexamethylene diamine.
Preferably, the lubricant is pentaerythritol stearate, N, N- has supportted bis-stearamides, lignite wax, glycerol At least one of monoesters acid value, amide waxe, o-phthalic acid dibutyl ester and butyl stearate;
The organic solvent is ethanol solution.
Preferably, ethyl alcohol mass percent is 80%-90% in the ethanol solution.
Preferably, the strong base-weak acid salt is at least one of hydrogen phosphite sodium, calcium bicarbonate, saleratus.
A kind of preparation method of ABS alloy material easy to clean, it is characterised in that: method includes the following steps:
(1) polycarbonate and strong base-weak acid salt are mixed to get mixture, it is 15- that mixture, which is then placed on pressure, CF4 RF plasma processing 20-50min is used in reactor under the conditions of 120Pa.
(2) by step (1) treated polycarbonate and strong base weak acid salt mixture investment screw extruder, while one And ABS resin, filler, surface modifier, compatilizer, antioxidant and lubricant are put into screw extruder, it is squeezed through melting Out, pelletizing obtains primary ABS alloy material;
(3) primary ABS alloy material will be obtained in (2) and place 36-48H in organic solvent, then air-dried to obtain ABS alloy material product.
Compared with prior art, the beneficial effects of the present invention are: ABS alloy material prepared by the present invention is not easy heap dust stratification Dirt, and easy wiped clean, therefore in the living conditions, dust, greasy dirt are carried out to product made of ABS alloy material convenient for user Cleaning;In industrial aspect, dust long-term accumulation in equipment is prevented, the indirect performance for improving equipment.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described, Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all Belong to the scope of protection of the invention.
In the description of the present invention, it is to be understood that, term " on ", "lower", "front", "rear", "left", "right", "top", The orientation or positional relationship of the instructions such as "bottom", "inner", "outside" is the orientation or positional relationship based on shown in, is merely for convenience of retouching It states the present invention and simplifies description, rather than the device or element of indication or suggestion meaning must have a particular orientation, with specific Orientation construction and operation, therefore be not considered as limiting the invention.
Embodiment 1:
A kind of ABS alloy material easy to clean and preparation method thereof, it is characterised in that: the alloy material be by following components by Parts by weight are prepared:
A kind of ABS alloy material easy to clean the preparation method is as follows:
(1) polycarbonate and strong base-weak acid salt are mixed to get mixture, mixture is then placed on low pressure (30Pa) Under the conditions of reactor (reactor outer wall be stainless steel bulge, reaction chamber center install about two parallel diameters be Disk electrode of the 25cm at a distance of 10cm, top crown and chamber wall ground connection, bottom crown connects radio-frequency power supply) in use CF4 radio frequency plasma Body handles 20min;
(2) by step (1) treated polycarbonate and strong base weak acid salt mixture investment screw extruder, while one And ABS resin, filler, surface modifier, compatilizer, antioxidant and lubricant are put into screw extruder, it is squeezed through melting Out, pelletizing obtains primary ABS alloy material;
(3) primary ABS alloy material will be obtained in (2) and place 36H in organic solvent, then air-dried to obtain ABS Alloy material product.
Embodiment 2:
A kind of ABS alloy material easy to clean the preparation method is as follows:
(1) polycarbonate and strong base-weak acid salt are mixed to get mixture, mixture is then placed on low pressure (30Pa) Under the conditions of reactor (reactor outer wall be stainless steel bulge, reaction chamber center install about two parallel diameters be Disk electrode of the 25cm at a distance of 10cm, top crown and chamber wall ground connection, bottom crown connects radio-frequency power supply) in use CF4 radio frequency plasma Body handles 20min;
(2) by step (1) treated polycarbonate and strong base weak acid salt mixture investment screw extruder, while one And ABS resin, filler, surface modifier, compatilizer, antioxidant and lubricant are put into screw extruder, it is squeezed through melting Out, pelletizing obtains primary ABS alloy material;
(3) primary ABS alloy material will be obtained in (2) and place 36H in organic solvent, then air-dried to obtain ABS Alloy material product.
Embodiment 3:
A kind of ABS alloy material easy to clean the preparation method is as follows:
(1) polycarbonate and strong base-weak acid salt are mixed to get mixture, mixture is then placed on low pressure (30Pa) Under the conditions of reactor (reactor outer wall be stainless steel bulge, reaction chamber center install about two parallel diameters be Disk electrode of the 25cm at a distance of 10cm, top crown and chamber wall ground connection, bottom crown connects radio-frequency power supply) in use CF4 radio frequency plasma Body handles 20min;
(2) by step (1) treated polycarbonate and strong base weak acid salt mixture investment screw extruder, while one And ABS resin, filler, surface modifier, compatilizer, antioxidant and lubricant are put into screw extruder, it is squeezed through melting Out, pelletizing obtains primary ABS alloy material;
(3) primary ABS alloy material will be obtained in (2) and place 36H in organic solvent, then air-dried to obtain ABS Alloy material product.
Embodiment 4:
A kind of ABS alloy material easy to clean the preparation method is as follows:
(1) polycarbonate and strong base-weak acid salt are mixed to get mixture, mixture is then placed on low pressure (30Pa) Under the conditions of reactor (reactor outer wall be stainless steel bulge, reaction chamber center install about two parallel diameters be At a distance of the disk electrode of 10cm, top crown and chamber wall ground connection, bottom crown connect in radio-frequency power supply) with CF4 radio frequency plasma 25cm Body handles 20min;
(2) by step (1) treated polycarbonate and strong base weak acid salt mixture investment screw extruder, while one And ABS resin, filler, surface modifier, compatilizer, antioxidant and lubricant are put into screw extruder, it is squeezed through melting Out, pelletizing obtains primary ABS alloy material;
(3) primary ABS alloy material will be obtained in (2) and place 36H in organic solvent, then air-dried to obtain ABS Alloy material product.
Embodiment 5:
A kind of ABS alloy material easy to clean the preparation method is as follows:
(1) polycarbonate and strong base-weak acid salt are mixed to get mixture, mixture is then placed on low pressure (30Pa) Under the conditions of reactor (reactor outer wall be stainless steel bulge, reaction chamber center install about two parallel diameters be Disk electrode of the 25cm at a distance of 10cm, top crown and chamber wall ground connection, bottom crown connects radio-frequency power supply) in use CF4 radio frequency plasma Body handles 20min;
(2) by step (1) treated polycarbonate and strong base weak acid salt mixture investment screw extruder, while one And ABS resin, filler, surface modifier, compatilizer, antioxidant and lubricant are put into screw extruder, it is squeezed through melting Out, pelletizing obtains primary ABS alloy material;
(3) primary ABS alloy material will be obtained in (2) and place 36H in organic solvent, then air-dried to obtain ABS Alloy material product
Comparative example 1:
A kind of ABS alloy material easy to clean the preparation method is as follows:
(1) polycarbonate and strong base-weak acid salt are mixed to get mixture, mixture is then placed on low pressure (30Pa) Under the conditions of reactor (reactor outer wall be stainless steel bulge, reaction chamber center install about two parallel diameters be Disk electrode of the 25cm at a distance of 10cm, top crown and chamber wall ground connection, bottom crown connects radio-frequency power supply) in use CF4 radio frequency plasma Body handles 20min;
(2) by step (1) treated polycarbonate and strong base weak acid salt mixture investment screw extruder, while one And ABS resin, filler, surface modifier, compatilizer, antioxidant and lubricant are put into screw extruder, it is squeezed through melting Out, pelletizing obtains primary ABS alloy material;
(3) primary ABS alloy material will be obtained in (2) and place 36H in organic solvent, then air-dried to obtain ABS Alloy material product.
Comparative example 2:
A kind of ABS alloy material easy to clean the preparation method is as follows:
(1) polycarbonate and strong base-weak acid salt are mixed to get mixture, mixture is then placed on low pressure (30Pa) Under the conditions of reactor (reactor outer wall be stainless steel bulge, reaction chamber center install about two parallel diameters be Disk electrode of the 25cm at a distance of 10cm, top crown and chamber wall ground connection, bottom crown connects radio-frequency power supply) in use CF4 radio frequency plasma Body handles 20min;
(2) by step (1) treated polycarbonate and strong base weak acid salt mixture investment screw extruder, while one And ABS resin, filler, surface modifier, compatilizer, antioxidant and lubricant are put into screw extruder, it is squeezed through melting Out, pelletizing obtains primary ABS alloy material;
(3) primary ABS alloy material will be obtained in (2) and place 36H in organic solvent, then air-dried to obtain ABS Alloy material product.
Comparative example 3:
A kind of ABS alloy material easy to clean the preparation method is as follows:
(1) in polycarbonate and strong base weak acid salt mixture investment screw extruder, while together in screw extruder Investment ABS resin, filler, surface modifier, compatilizer, antioxidant and lubricant obtain primary through melting extrusion, pelletizing ABS alloy material;
(2) primary ABS alloy material will be obtained in step (1) and places 36H in organic solvent, then air-dried to obtain ABS alloy material product.
ABS alloy material after embodiment 1-5 and comparative example 1-3 preparation is tested for the property, and specific test result is such as Shown in table 1:
Table 1
Remarks: floating ash state 1-10 points, 10 points of surface dirt depositions are most, and 1 point indicates entirely without any dust;Oil dripping The complexity 1-10 of wiped clean points afterwards, 1 point of expression is easily cleaned, and 10 points indicate super difficult cleaning.
Sub-fraction dust is only had accumulated from the ABS alloy material prepared in embodiment 1-5, and in comparative example 1-2 then More dust is had accumulated, therefore as can be seen that ABS alloy material prepared by the present invention from embodiment 1-5 and comparative example 1-2 It is not easy to accumulate dust, and easy wiped clean;Simultaneously by embodiment 1 and comparative example 3 as can be seen that being prepared in ABS alloy material CF4 RF plasma processing is used in step process, from table 1 it follows that after using CF4 RF plasma processing The ABS alloy material of preparation is not easy to accumulate dust, and easy wiped clean.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding And modification, the scope of the present invention is defined by the appended.

Claims (10)

1. a kind of ABS alloy material easy to clean, it is characterised in that: the alloy material be prepared in parts by weight by following components and At:
2. a kind of ABS alloy material easy to clean according to claim 1, it is characterised in that: the partial size of the ABS resin is 3-4 μm, mass percent 30%.
3. a kind of ABS alloy material easy to clean according to claim 1, it is characterised in that: the filler be white carbon black, At least one of poly- methyl carbamide resin, metallic soap, diatomite, wollastonite.
4. a kind of ABS alloy material easy to clean according to claim 3, it is characterised in that: the partial size of the filler 100-200nm。
5. a kind of ABS alloy material easy to clean according to claim 1, it is characterised in that: the surface modifier is complete Carboxylic acid fluoride chromium complex, acrylic acid fluorohydrocarbon esters resin, acrylic acid fluorohydrocarbon sulfonamido ethyl ester, chlorotrifluoroethylene-vinylidene At least one of copolymer.
6. a kind of ABS alloy material easy to clean according to claim 1, it is characterised in that: the compatilizer is maleic acid Acid anhydride grafted propylene nitrile butadiene-styrene copolymer, styrene-acrylonitrile-copolymer-maleic anhydride, phenylethylene-maleic two At least one of acid anhydride copolymer and acrylonitrile-styrene-methacrylic acid copolymer;
The antioxidant is 2,2- methylene-bis- (4- methyl-6-tert butyl phenol), N, N- [3- (3,5- di-t-butyl -4- hydroxyl Phenyl) propionyl] hexamethylene diamine, 4,4'- thiobis (6- tert-butyl -3- methylphenol), bis- [1, the 1- dimethyl -2- of 3,9- [(3- tertiary butyl-4-hydroxy -5- aminomethyl phenyl) propionyloxy] ethyl] four oxaspiro of -2,4,8,10-, N, N '-it is bis- [3- (3 ', At least one of 5 '-di-t-butyls -4 '-hydroxy phenyl) propionyl hexamethylene diamine.
7. a kind of ABS alloy material easy to clean according to claim 1, it is characterised in that: the lubricant is Ji Wusi Alcohol stearate, N, N- have supportted bis-stearamides, lignite wax, monoglyceride acid value, amide waxe, o-phthalic acid dibutyl ester and fourth At least one of base stearate;
The organic solvent is ethanol solution.
8. a kind of ABS alloy material easy to clean according to claim 7, it is characterised in that: ethyl alcohol in the ethanol solution Mass percent 80%-90%.
9. a kind of ABS alloy material easy to clean according to claim 1, it is characterised in that: the strong base-weak acid salt is Asia At least one of dibastic sodium phosphate, calcium bicarbonate, saleratus.
10. a kind of preparation method of such as described in any item ABS alloy materials easy to clean of claim 1-9, it is characterised in that: should Method the following steps are included:
(1) polycarbonate and strong base-weak acid salt are mixed to get mixture, it is 15-120Pa that mixture, which is then placed on pressure, Under the conditions of reactor in use CF4 RF plasma processing 20-50min;
(2) by step (1) treated polycarbonate and strong base weak acid salt mixture investment screw extruder, while existing together ABS resin, filler, surface modifier, compatilizer, antioxidant and lubricant are put into screw extruder, through melting extrusion, are cut Grain, obtains primary ABS alloy material;
(3) primary ABS alloy material will be obtained in (2) and place 36-48H in organic solvent, then air-dried to obtain ABS conjunction Golden material product.
CN201811624991.5A 2018-12-28 2018-12-28 A kind of ABS alloy material easy to clean and preparation method thereof Pending CN109796721A (en)