CN109777650A - A kind of highly concentrated miniature glass scavenger specially - Google Patents
A kind of highly concentrated miniature glass scavenger specially Download PDFInfo
- Publication number
- CN109777650A CN109777650A CN201711117414.2A CN201711117414A CN109777650A CN 109777650 A CN109777650 A CN 109777650A CN 201711117414 A CN201711117414 A CN 201711117414A CN 109777650 A CN109777650 A CN 109777650A
- Authority
- CN
- China
- Prior art keywords
- quality
- glass
- acid
- glass cleaner
- surfactant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of highly concentrated miniature glass scavenger speciallies, including acid, chelating agent, organic solvent, surfactant and water;The acid is one of acetic acid, nitric acid and citric acid or a variety of;The quality of the acid is the 0.5%~2.5% of glass cleaner quality;The quality of the chelating agent is the 1.0%~2.0% of glass cleaner quality;The quality of the organic solvent is the 0.5%~2.5% of glass cleaner quality;The quality of the surfactant is the 1.5%~5% of glass cleaner quality.Compared with prior art, cleaning agent preparation method provided by the invention is simple, and cost is relatively low, mild condition, Environmental Safety, and is cooperated by various components, keeps it high to the detersive efficiency of optical glass, solves the problems, such as the cleaning of milling and polishing fluid.
Description
Technical field
The invention belongs to glass cleaner technical field more particularly to a kind of highly concentrated miniature glass scavenger speciallies.
Background technique
For white glass after plain grinding or polishing, surface has the dirts such as a large amount of milling or polishing fluid to be firmly attached to glass
Glass surface will produce bigger effect subsequent handling if not removing.
The prior art is generally handled using following three kinds:
(1) it is directly scrubbed with clear water.The method is time-consuming and laborious, and brush does not wash clean;
(2) using porcelain on the market must net or monarch nourish after the highly acids liquid medicine such as beauty are diluted with water and scrub.The method is to milling
And the dirts such as polishing fluid have preferable removal effect, but have biggish corrosivity to skin, workpiece, metal equipment, are not suitable for
It uses;
(3) it is not processed after glass plain grinding or polishing, it is big tentatively to remove surface for addition soaking technology directly before ultrasonic wave
Partial dirt, but the method cost is higher, and glass surface dirt it is dry and hard after be more difficult to clean.
Summary of the invention
In consideration of it, the technical problem to be solved in the present invention is that providing a kind of highly concentrated miniature glass scavenger specially.
The present invention provides a kind of highly concentrated miniature glass scavenger speciallies, including acid, chelating agent, organic solvent, surface work
Property agent and water;The acid is one of acetic acid, nitric acid and citric acid or a variety of;The quality of the acid is glass cleaner quality
0.5%~2.5%;The quality of the chelating agent is the 1.0%~2.0% of glass cleaner quality;The organic solvent
Quality is the 0.5%~2.5% of glass cleaner quality;The quality of the surfactant is glass cleaner quality
1.5%~5%.
Preferably, the chelating agent is ethylenediamine tetra-acetic acid.
Preferably, the organic solvent is butyl.
Preferably, the surfactant is alkyl phenol polyoxyethylene ether and/or alkyl sulfonates surfactant.
Preferably, the alkyl sulfonates surfactant is dodecyl sodium sulfate.
Preferably, the alkyl phenol polyoxyethylene ether is octyl phenol polyoxyethylene ether and/or nonylphenol polyoxyethylene ether.
Preferably, the surfactant is alkyl phenol polyoxyethylene ether and alkyl sulfonates surfactant;It is described
The mass ratio of alkyl phenol polyoxyethylene ether and alkyl sulfonates surfactant is (1~2): (2~1).
The present invention also provides a kind of application methods of highly concentrated miniature glass scavenger specially, comprising:
Above-mentioned glass cleaner is diluted with water, then optical glass is cleaned.
Preferably, the volume ratio of the glass cleaner and water is 1: (1~50).
Preferably, the time of the cleaning is 5~15s.
The present invention provides a kind of highly concentrated miniature glass scavenger speciallies, including acid, chelating agent, organic solvent, surface work
Property agent and water;The acid is one of acetic acid, nitric acid and citric acid or a variety of;The quality of the acid is glass cleaner quality
0.5%~2.5%;The quality of the chelating agent is the 1.0%~2.0% of glass cleaner quality;The organic solvent
Quality is the 0.5%~2.5% of glass cleaner quality;The quality of the surfactant is glass cleaner quality
1.5%~5%.Compared with prior art, cleaning agent preparation method provided by the invention is simple, and cost is relatively low, mild condition, ring
It ensures safety, and is cooperated by various components, keep it high to the detersive efficiency of optical glass, solve milling and polishing fluid
Cleaning problem.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
The present invention provides a kind of highly concentrated miniature glass scavenger speciallies, including acid, chelating agent, organic solvent, surface work
Property agent and water;The acid is one of acetic acid, nitric acid and citric acid or a variety of;The quality of the acid is glass cleaner quality
0.5%~2.5%;The quality of the chelating agent is the 1.0%~2.0% of glass cleaner quality;The organic solvent
Quality is the 0.5%~2.5% of glass cleaner quality;The quality of the surfactant is glass cleaner quality
1.5%~5%.
Cleaning agent preparation method provided by the invention is simple, and cost is relatively low, mild condition, Environmental Safety, and by various
Component cooperates, and keeps it high to the detersive efficiency of optical glass, solves the problems, such as the cleaning of milling and polishing fluid.
The present invention is not particularly limited the source of all raw materials, is commercially available.
The acid is one of acetic acid, nitric acid and citric acid or a variety of, is the main component of cleaning agent, milling and polishing
Liquid can be removed quickly under acid environment.Since the acidity of acetic acid is stronger compared with citric acid acidity, scuffing is caused in order to reduce
Risk, more preferably citric acid;The quality of the acid is preferably the 1.0%~2.5% of glass cleaner quality, more preferably
1.0%~2.0%, it is further preferably 1.5%~2.0%.
The quality of the chelating agent is preferably the 1.0%~1.5% of glass cleaner quality;The type of the chelating agent is
Chelating agent well known to those skilled in the art has no special limitation, is preferably ethylenediamine tetra-acetic acid in the present invention
(EDTA).Chelating agent is used to enhance the resistance to hard water ability of cleaning agent, and can reinforce the cleaning ability to milling, polishing fluid.
The quality of the organic solvent is preferably the 1.0%~2.5% of glass cleaner quality, more preferably 1.0%~
2.0%, it is further preferably 1.5%~2.0%, most preferably 1.5%;The type of the organic solvent is that those skilled in the art are ripe
The organic solvent known, has no special limitation, preferably alcohol ethers solvent and/or alcohol solvent of ether ester type in the present invention, more
Preferably butyl.Organic solvent primarily serves auxiliary cleaning action in the present invention, dirty to a small number of organics to play
Better effect, while can be reduced the dosage of surfactant.
The quality of the surfactant is preferably the 2.0%~5.0% of glass cleaner quality, more preferably 2.0%
~4.0%, it is further preferably 2.5%~4.0%, is further preferably 2.5%~3.5%;The surfactant is art technology
Surfactant known to personnel has no special limitation, is preferably alkyl phenol polyoxyethylene ether and/or alkane in the present invention
Base sulfonate surfactant;Wherein, the alkyl phenol polyoxyethylene ether is poly- for alkyl phenol well known to those skilled in the art
Ethylene oxide ether has no special limitation, is preferably octyl phenol polyoxyethylene ether and/or Nonyl pheno in the present invention
Ether;The alkyl sulfonates surfactant is alkyl sulfonates surfactant well known to those skilled in the art, more
Preferably dodecyl sodium sulfate;In the present invention, more preferably using the surfactant of compounding, i.e. alkyl phenol polyoxyethylene ether
With alkyl sulfonates surfactant;The mass ratio of the alkyl phenol polyoxyethylene ether and alkyl sulfonates surfactant
Preferably (1~2): (2~1), more preferably (1~1.5): (2~1.5);In some embodiments provided by the invention, described
The mass ratio of alkyl phenol polyoxyethylene ether and alkyl sulfonates surfactant is preferably 1.5: 2;Provided by the invention another
In some embodiments, the mass ratio of the alkyl phenol polyoxyethylene ether and alkyl sulfonates surfactant is preferably 1: 1.5.
The main landing low surface tension of surfactant increases infiltrative effect, and increases the cleaning ability of cleaning agent.
Glass cleaner provided by the invention in addition to the above components, may also include other mild decontamination ingredients, will not
Influence the using effect for the cleaning agent that the present invention obtains;Other described mild decontamination ingredients can be sodium gluconate can also for except
Other surfaces activating agent such as neopelex except above-mentioned surfactant;But it is most preferred, it is provided by the invention
Glass cleaner only includes said components.
Glass cleaner preparation method provided by the invention is simple, detersive efficiency is high, at low cost, Environmental Safety;1~50 times
Room temperature, which scrubs 5~15s, after dilution can remove the stains such as the milling of glass surface, polishing fluid, after cleaning, learn through using
The cleaning agent does not hurt glass, skin friendly, and has carried out reliability test to glass, does not influence to produce after cleaning agent cleaning glass
The quality of product (glass);And the glass cleaner has no irritating odor without substances such as benzene, chlorine, heavy metals, meets green ring
Guaranteed request.
The present invention also provides a kind of application methods of above-mentioned glass cleaner, comprising: above-mentioned acid optical glass is clear
Lotion is diluted with water, and then cleans to optical glass.
The volume ratio of the glass cleaner and water is preferably 1: (1~50), more preferably 1: (10~50), further preferably for
1: (20~50) are further preferably 1: (30~50) are further preferably 1: (40~50), most preferably 1: 40;It is normal after being diluted with water
The lower pH value of temperature is preferably 2~4.
After dilution, optical glass is cleaned;The optical glass is optical glass well known to those skilled in the art
, special limitation is had no, is preferably mobile phone faceplate glass in the present invention;The time of the cleaning is preferably 5~15s, more
Preferably 8~12s is further preferably 10s.
In order to further illustrate the present invention, detailed to a kind of glass cleaner progress provided by the invention with reference to embodiments
Thin description.
Reagent used in following embodiment is commercially available;
Acetic acid: Tianjin Ke Miou chemical reagent, content > 99%;
EDTA: enlightening chemical reagent, content > 99% are won in Tianjin;
Butyl: Tianjin Ke Miou chemical reagent, content > 99%;
Alkyl phenol polyoxyethylene ether: Hai'an petrochemical industry, content > 80%;
Dodecyl sodium sulfate: Corning, content > 80%.
Embodiment 1
A kind of highly concentrated miniature glass scavenger specially, is grouped as: acetic acid 2%, second by following groups by mass percentage
Ethylenediamine tetraacetic acid (EDTA) 1%, butyl 1.5%, alkyl phenol polyoxyethylene ether (OP-10) 1%, dodecyl sodium sulfate
1.5%, surplus is water.
10s is scrubbed to the glass room temperature after plain grinding after 40 times of the glass cleaner provided using embodiment 1 dilutions, it can be fast
Other stains such as the milling of speed removal glass surface.After glass scrub, learn that the cleaning agent does not hurt glass through examining.And it is right
Glass has carried out reliability test, has no effect on glass quality after the glass after cleaning agent cleaning plain grinding.
Embodiment 2
A kind of highly concentrated miniature glass scavenger specially, is grouped as: acetic acid 1%, nitre by following groups by mass percentage
Acid 0.5%, ethylenediamine tetra-acetic acid 1%, ethylene glycol ether acetate 1.5%, alkyl phenol polyoxyethylene ether (OP-10) 1%, 12
Sodium alkyl sulfonate 1.5%, surplus are water.
10s is scrubbed to the glass room temperature after plain grinding after 40 times of the glass cleaner provided using embodiment 2 dilutions, it can be fast
Other stains such as the milling of speed removal glass surface.After glass scrub, learn that the cleaning agent does not hurt glass and silk through examining
The ink layer of print.And reliability test has been carried out to glass, the nature of glass is had no effect on after the glass after cleaning agent cleaning plain grinding
Amount.
Claims (3)
1. a kind of highly concentrated miniature glass scavenger specially, which is characterized in that including acid, chelating agent, organic solvent, surfactant
With water;The acid is one of acetic acid, nitric acid and citric acid or a variety of;The quality of the acid is glass cleaner quality
0.5%~2.5%;The quality of the chelating agent is the 1.0%~2.0% of glass cleaner quality;The matter of the organic solvent
Amount is the 0.5%~2.5% of glass cleaner quality;The quality of the surfactant is acid cleaning agent for optical glass quality
1.5%~5%.
2. glass cleaner according to claim 1, which is characterized in that the chelating agent is ethylenediamine tetra-acetic acid.
3. glass cleaner according to claim 1, which is characterized in that the organic solvent is butyl.