CN109777244A - A kind of woodenware surface heat-transferring quick drying paint and its application method - Google Patents
A kind of woodenware surface heat-transferring quick drying paint and its application method Download PDFInfo
- Publication number
- CN109777244A CN109777244A CN201910065022.9A CN201910065022A CN109777244A CN 109777244 A CN109777244 A CN 109777244A CN 201910065022 A CN201910065022 A CN 201910065022A CN 109777244 A CN109777244 A CN 109777244A
- Authority
- CN
- China
- Prior art keywords
- quick drying
- surface heat
- drying paint
- ethyl alcohol
- woodenware
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of woodenware surface heat-transferring quick drying paint of the present invention and its application method belong to technical field of coatings, to solve the problems, such as the thermally transferred pattern on woodenware, solvent resistant and adhesive force is not bad, the component and weight percent of the coating are as follows: butyl acetate cellulose 6-8%, aldehyde resin 25--35%, polyvinyl butyral resin 2-5%, levelling agent 0.1-0.3%, isobutanol 20-35%, ethyl alcohol 15-30%, propylene glycol methyl ether acetate 10-15%.The present invention also provides a kind of application methods of woodenware surface heat-transferring quick drying paint, and when in use, the volume ratio of the coating and diluent is 1:1.Filming performance of the present invention is excellent, is very suitable for the treatment process of thermally transferred pattern, can meet to protection thermally transferred pattern complete display well and provide the requirement of good adhesive force, and have quick-drying and good mechanical performance.
Description
Technical field
The invention belongs to technical field of coatings, more particularly to a kind of woodenware surface heat-transferring quick drying paint.
Background technique
Currently, as people are to growing, many factories in wood furniture field of furniture appearance diversification decoration demand
Family wants the processing that thermally transferred pattern is carried out on its product, so that the relatively dull appearance of antique traditional furniture itself is added new
Decorative element more has artistic appreciation.
But often adhesive force and solvent resistance are not very well, so that common woodcare paint exists to ink used in thermally transferred pattern
Thermally transferred pattern can be made to be partly solubilized destruction when constructing thereon, and requirement is not achieved in adhesive force, therefore thermal transfer exists
Application on woodenware has been more limited.
Summary of the invention
The purpose of invention is to provide a kind of woodenware surface heat-transferring quick drying paint and its application method, to solve on woodenware
Thermally transferred pattern not solvent resistant and the bad problem of adhesive force.
A kind of woodenware surface heat-transferring quick drying paint of the present invention, its component and weight percent are:
Butyl acetate cellulose 6-8%；
Aldehyde resin 25--35%；
Polyvinyl butyral resin 2-5%；
Levelling agent 0.1-0.3%；
Isobutanol 20-35%；
Ethyl alcohol 15-30%；
Propylene glycol methyl ether acetate 10-15%.
The butyl acetate cellulose selects the CAB553-0.4 of Yi Shiman, and the aldehyde resin selects the CT- of BASF
A81 resin, the polyvinyl butyral resin select Japanese ponding S-LEC BL-S resin, and the levelling agent selects Bi Kegong
The BYK-333 auxiliary agent of department, the different butanol select Shanghai City Sen Fei Chemical Company product, and the ethyl alcohol selects Shandong Province
Zibo Xin Rong Chemical Industry Science Co., Ltd product, the propylene glycol methyl ether acetate select the limited public affairs of the high luxuriant Chemical trade of Dongguan City
Take charge of product.
A kind of application method of woodenware surface heat-transferring quick drying paint of the present invention, when in use, the coating and diluent
Volume ratio be 1:1.
The component and weight percent of the coating are as follows:
Butyl acetate cellulose 6-8%；
Aldehyde resin 25--35%；
Polyvinyl butyral resin 2-5%；
Levelling agent 0.1-0.3%；
Isobutanol 20-35%；
Ethyl alcohol 15-30%；
Propylene glycol methyl ether acetate 10-15%.
The component and weight percent of the diluent are as follows:
Isobutanol 65-75%；
Ethyl alcohol 10-15%；
Propylene glycol methyl ether acetate 10-20%.
The butyl acetate cellulose selects the CAB553-0.4 of Yi Shiman, and the aldehyde resin selects the CT- of BASF
A81 resin, the polyvinyl butyral resin select Japanese ponding S-LEC BL-S resin, and the levelling agent selects Bi Kegong
The BYK-333 auxiliary agent of department, the different butanol select Shanghai City Sen Fei Chemical Company product, and the ethyl alcohol selects Shandong Province
Zibo Xin Rong Chemical Industry Science Co., Ltd product, the propylene glycol methyl ether acetate select the limited public affairs of the high luxuriant Chemical trade of Dongguan City
Take charge of product.
The film forming performance of paint of the invention is excellent, is very suitable for the treatment process of thermally transferred pattern.Wherein, butyl acetate
Cellulose is alcohol-soluble, and solvent release is good after construction, while obtained hardness of paint film is high, effectively improves the glass of paint film
Change temperature, it helps improve working efficiency；Aldehyde resin is then widely used in solvent-based ink, can be with the pattern of thermal transfer
Good adhesive force is generated, also has many advantages, such as good compatibility, quick-drying, glossiness, yellowing resistance；Polyvinyl alcohol contracting fourth
Urea formaldehyde plays the role of improving toughness in paint film, itself has excellent flexibility and flexibility.
The present invention can meet to protection thermally transferred pattern complete display well and provide the requirement of good adhesive force,
And there is quick-drying and good mechanical performance.
Specific embodiment
Embodiment 1:
Formulation for coating material: (weight percent)
Butyl acetate cellulose solution (butyl acetate cellulose and ethyl alcohol 1: 7/3 dissolve) 20%, aldehyde resin solution (polyacetals tree
Rouge and propylene glycol methyl ether acetate 1: 3/7 dissolve) 40%, polyvinyl butyral resin solution (polyvinyl butyral resin and
Ethyl alcohol 1: 4 dissolves) 15%, BYK-333 auxiliary agent 0.2%, isobutanol 24.8%, total 100%.
Diluent:
Isobutanol 70%, ethyl alcohol 15%, propylene glycol methyl ether acetate 15% add up to 100%.
Use ratio: host agent: diluent=1: 1；
Form of construction work: manual spray, one ' cross '.
Actually detected data are as follows: using alkyd varnish HG/T2453-1993 standard
1, former paint appearance colorless clear viscous liquids, no mechanical admixture
2, mian paint solid content 37%
3, surface drying time (25 DEG C) 15min
4, (25 DEG C) 3h is done solid work the time
5, paint film appearance is transparent, smooth no morbid state
6,1 grade of adhesive force (cross-hatching)
7, limits of harmful substances (dissoluble lead, cadmium, chromium, mercury) is not detected
8, pencil hardness (scratch) HB
9, thermally transferred pattern integrality complete display
10, the paint film transparency is good
Embodiment 2:
Formulation for coating material: (weight percent)
Butyl acetate cellulose solution (butyl acetate cellulose and ethyl alcohol 1: 7/3 dissolve) 20%, aldehyde resin solution (polyacetals tree
Rouge and propylene glycol methyl ether acetate 1: 3/7 dissolve) 45%, polyvinyl butyral resin solution (polyvinyl butyral resin and
Ethyl alcohol 1: 4 dissolves) 12%, BYK-333 auxiliary agent 0.2%, isobutanol 22.8%, total 100%.
Diluent:
Isobutanol 70%, ethyl alcohol 15%, propylene glycol methyl ether acetate 15% add up to 100%.
Use ratio: host agent: diluent=1: 1；
Form of construction work: manual spray, one ' cross '.
Actually detected data are as follows: using alkyd varnish HG/T2453-1993 standard
1, former paint appearance colorless clear viscous liquids, no mechanical admixture
2, mian paint solid content 39.9%
3, surface drying time (25 DEG C) 14min
4, (25 DEG C) 3h is done solid work the time
5, paint film appearance is transparent, smooth no morbid state
6,1 grade of adhesive force (cross-hatching)
7, limits of harmful substances (dissoluble lead, cadmium, chromium, mercury) is not detected
8, pencil hardness (scratch) HB
9, thermally transferred pattern integrality complete display
10, the paint film transparency is good
Embodiment 3:
Formulation for coating material: (weight percent)
Butyl acetate cellulose solution (butyl acetate cellulose and ethyl alcohol 1: 7/3 dissolve) 25%, aldehyde resin solution (polyacetals tree
Rouge and propylene glycol methyl ether acetate 1: 3/7 dissolve) 40%, polyvinyl butyral resin solution (polyvinyl butyral resin and
Ethyl alcohol 1: 4 dissolves) 15%, BYK-333 auxiliary agent 0.15%, isobutanol 17.85%, total 100%.
Diluent:
Isobutanol 70%, ethyl alcohol 15%, propylene glycol methyl ether acetate 15% add up to 100%.
Use ratio: host agent: diluent=1: 1；
Form of construction work: manual spray, one ' cross '.
Actually detected data are as follows: using alkyd varnish HG/T2453-1993 standard
1, former paint appearance colorless clear viscous liquids, no mechanical admixture
2, mian paint solid content 41.4%
3, surface drying time (25 DEG C) 10min
4, (25 DEG C) 3h is done solid work the time
5, paint film appearance is transparent, smooth no morbid state
6,1 grade of adhesive force (cross-hatching)
7, limits of harmful substances (dissoluble lead, cadmium, chromium, mercury) is not detected
8, pencil hardness (scratch) HB
9, thermally transferred pattern integrality complete display
10, the paint film transparency is good
Embodiment 4:
Formulation for coating material: (weight percent)
Butyl acetate cellulose solution (butyl acetate cellulose and ethyl alcohol 1: 7/3 dissolve) 22%, aldehyde resin solution (polyacetals tree
Rouge and propylene glycol methyl ether acetate 1: 3/7 dissolve) 45%, polyvinyl butyral resin solution (polyvinyl butyral resin and
Ethyl alcohol 1: 4 dissolves) 15%, BYK-333 auxiliary agent 0.2%, isobutanol 15.8%, total 100%.
Diluent:
Isobutanol 70%, ethyl alcohol 15%, propylene glycol methyl ether acetate 15% add up to 100%.
Use ratio: host agent: diluent=1: 1；
Form of construction work: manual spray, one ' cross '.
Actually detected data are as follows: using alkyd varnish HG/T2453-1993 standard
1, former paint appearance colorless clear viscous liquids, no mechanical admixture
2, mian paint solid content 44%
3, surface drying time (25 DEG C) 13min
4, (25 DEG C) 3h is done solid work the time
5, paint film appearance is transparent, smooth no morbid state
6,1 grade of adhesive force (cross-hatching)
7, limits of harmful substances (dissoluble lead, cadmium, chromium, mercury) is not detected
8, pencil hardness (scratch) B
9, thermally transferred pattern integrality complete display
10, the paint film transparency is good.
Claims (4)
1. a kind of woodenware surface heat-transferring quick drying paint, which is characterized in that its component and weight percent are:
Butyl acetate cellulose 6-8%；
Aldehyde resin 25--35%；
Polyvinyl butyral resin 2-5%；
Levelling agent 0.1-0.3%；
Isobutanol 20-35%；
Ethyl alcohol 15-30%；
Propylene glycol methyl ether acetate 10-15%.
2. quick drying paint as described in claim 1, the levelling agent is BYK-333 auxiliary agent.
3. a kind of application method of woodenware surface heat-transferring quick drying paint, which is characterized in that when in use, the coating and dilution
The volume ratio of agent is 1:1；
The component and weight percent of the coating are as follows:
Butyl acetate cellulose 6-8%；
Aldehyde resin 25--35%；
Polyvinyl butyral resin 2-5%；
Levelling agent 0.1-0.3%；
Isobutanol 20-35%；
Ethyl alcohol 15-30%；
Propylene glycol methyl ether acetate 10-15%；
The component and weight percent of the diluent are as follows:
Isobutanol 65-75%；
Ethyl alcohol 10-15%；
Propylene glycol methyl ether acetate 10-20%.
4. the application method of quick drying paint as claimed in claim 3, the levelling agent is BYK-333 auxiliary agent.