CN109776948A - For making the modified polypropene of optical fiber loose tube - Google Patents
For making the modified polypropene of optical fiber loose tube Download PDFInfo
- Publication number
- CN109776948A CN109776948A CN201711124962.8A CN201711124962A CN109776948A CN 109776948 A CN109776948 A CN 109776948A CN 201711124962 A CN201711124962 A CN 201711124962A CN 109776948 A CN109776948 A CN 109776948A
- Authority
- CN
- China
- Prior art keywords
- content
- antioxidant
- base
- agent
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of for making the modified polypropene of optical fiber loose tube.Including base-material, nucleating agent, coupling agent, antioxidant and fluoropolymer modifier, the base-material is polypropylene, polyethylene and ethylene copolymers;On the basis of 100 parts of base-material, the content of the nucleating agent is 0.5-1 parts, and the content of the coupling agent is to be nucleated 0.008-0.02 part of agent content, and the content of the antioxidant is 0.8-1.2 parts, and the base-material is polyethylene-polypropylene copolymer;The nucleating agent is the mixture of kaolin, silica, talcum powder.Modified copolymer of the present invention has many advantages, such as that cheap, extruded velocity is fast, cleanliness is high, compound with regular structure, thus there is good mechanical property, good heat resistance and chemical stability, it is aided with the addition of nucleating agent, coupling agent, antioxidant and fluoropolymer modifier simultaneously, so that the Loose tube produced has comprehensive service performance well, sufficiently satisfy the use demand.
Description
Technical field
The present invention relates to a kind of for making the modified polypropene of optical fiber loose tube, belongs to Loose tube material technical field.
Background technique
Loose tube is widely used in FIBER OPTIC FIBERS & CABLE, and main component is PBT, and PBT material is high because having
The advantages that Young's modulus and low-expansion coefficient and be widely used;But PBT price is high, and has the defects of hydrolytic resistance is poor, therefore
It needs to be modified, improves its comprehensive performance.
Summary of the invention
The present invention is in view of the foregoing drawbacks, it is therefore intended that improve it is a kind of can improve Loose tube performance for making optical fiber pine set
The modified polypropene of pipe.
Thus the technical solution adopted by the present invention is that: the present invention includes base-material, nucleating agent, coupling agent, antioxidant and contains
Fluorine rheological agent, the base-material are polypropylene, polyethylene and ethylene copolymers;
On the basis of 100 parts of base-material, the content of the nucleating agent is 0.5-1 parts, and the content of the coupling agent contains for nucleating agent
0.008-0.02 part of amount, the content of the antioxidant are 0.8-1.2 parts, and the base-material is polyethylene-polypropylene copolymer;
The nucleating agent is the mixture of kaolin, silica, talcum powder.
The coupling agent is epoxy silane coupling agent.
The antioxidant is made of phenolic antioxidant and phosphite ester antioxidant.
The content of the phenolic antioxidant is 8-12 times of phosphite ester antioxidant content.
The invention has the advantages that modified copolymer of the present invention has, cheap, extruded velocity is fast, cleanliness
The advantages that height, compound with regular structure, thus there is good mechanical property, good heat resistance and chemical stability, while auxiliary
With the addition of nucleating agent, coupling agent, antioxidant and fluoropolymer modifier, so that the Loose tube produced has synthesis well and makes
With performance, sufficiently satisfy the use demand.
Specific embodiment
Embodiment 1:
The present invention includes base-material, nucleating agent, coupling agent, antioxidant and fluoropolymer modifier, and the base-material is polypropylene, polyethylene
Copolymer;
On the basis of 100 parts of base-material, the content of the nucleating agent is 0.8 part, and the content of the coupling agent is nucleation agent content
0.01 part, the content of the antioxidant is 1.2 parts, and the base-material is polyethylene-polypropylene copolymer;
The nucleating agent is the mixture of kaolin, silica, talcum powder.
The coupling agent is epoxy silane coupling agent.
The antioxidant is made of phenolic antioxidant and phosphite ester antioxidant.
The content of the phenolic antioxidant is 10 times of phosphite ester antioxidant content.
Embodiment 2:
The present invention includes base-material, nucleating agent, coupling agent, antioxidant and fluoropolymer modifier, and the base-material is polypropylene, polyethylene
Copolymer;
On the basis of 100 parts of base-material, the content of the nucleating agent is 0.6 part, and the content of the coupling agent is nucleation agent content
0.015 part, the content of the antioxidant is 0.8 part, and the base-material is polyethylene-polypropylene copolymer;
The nucleating agent is the mixture of kaolin, silica, talcum powder.
The coupling agent is epoxy silane coupling agent.
The antioxidant is made of phenolic antioxidant and phosphite ester antioxidant.
The content of the phenolic antioxidant is 9 times of phosphite ester antioxidant content.
Embodiment 3:
The present invention includes base-material, nucleating agent, coupling agent, antioxidant and fluoropolymer modifier, and the base-material is polypropylene, polyethylene
Copolymer;
On the basis of 100 parts of base-material, the content of the nucleating agent is 1 part, and the content of the coupling agent is nucleation agent content
0.009 part, the content of the antioxidant is 1.1 parts, and the base-material is polyethylene-polypropylene copolymer;
The nucleating agent is the mixture of kaolin, silica, talcum powder.
The coupling agent is epoxy silane coupling agent.
The antioxidant is made of phenolic antioxidant and phosphite ester antioxidant.
The content of the phenolic antioxidant is 12 times of phosphite ester antioxidant content.
Claims (4)
1. the modified polypropene for making optical fiber loose tube, which is characterized in that including base-material, nucleating agent, coupling agent, antioxidant
And fluoropolymer modifier, the base-material are polypropylene, polyethylene and ethylene copolymers;
On the basis of 100 parts of base-material, the content of the nucleating agent is 0.5-1 parts, and the content of the coupling agent contains for nucleating agent
0.008-0.02 part of amount, the content of the antioxidant are 0.8-1.2 parts, and the base-material is polyethylene-polypropylene copolymer;
The nucleating agent is the mixture of kaolin, silica, talcum powder.
2. according to claim 1 for making the modified polypropene of optical fiber loose tube, which is characterized in that the coupling agent
For epoxy silane coupling agent.
3. according to claim 1 for making the modified polypropene of ferrule, which is characterized in that the antioxidant by
Phenolic antioxidant and phosphite ester antioxidant composition.
4. according to claim 3 for making the modified polypropene of ferrule, which is characterized in that the phenols antioxygen
The content of agent is 8-12 times of phosphite ester antioxidant content.