CN109774291A - A kind of production technology of outer reinforcement polyester base cloth - Google Patents
A kind of production technology of outer reinforcement polyester base cloth Download PDFInfo
- Publication number
- CN109774291A CN109774291A CN201711119091.0A CN201711119091A CN109774291A CN 109774291 A CN109774291 A CN 109774291A CN 201711119091 A CN201711119091 A CN 201711119091A CN 109774291 A CN109774291 A CN 109774291A
- Authority
- CN
- China
- Prior art keywords
- polyester
- cloth
- glass fiber
- outer reinforcement
- base fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of production technologies of outer reinforcement polyester base cloth, the outer reinforcement polyester base cloth is polymerized by glass fiber grid cloth and polyester blank base fabric, glass fiber grid cloth and polyester base cloth are placed on depositing on cloth holder before special equipment, after the special equipment is adjusted, the glass fiber grid cloth and the polyester blank base fabric are introduced into composite roll through deflector roll, the coated mode of the glass fiber grid cloth one side is uniformly applied and spreads special high temperature-proof glue, then after compound under the composite roll certain pressure, it is sent into compound heat drying area, through cutting after compound evenly drying, outer reinforcement polyester base cloth finished product is made in curling.The present invention is polymerized by glass fiber grid cloth and polyester blank base fabric, the coated mode of glass fiber grid cloth one side is uniformly applied and spreads special high temperature-proof glue, to increase, polyester blank base fabric is longitudinal or vertical and horizontal pulling force, improve the production efficiency of product, it avoids in the case where speed is too fast, shrink and other issues.
Description
Technical field
The present invention relates to tire base fabric manufacturing technology field more particularly to a kind of production technologies of outer reinforcement polyester base cloth.
Background technique
Existing tire base fabric is made of being formed by polyester fiber net impregnation, and adhesive used in impregnation sizing determines
The ultimate strength of tire base fabric, knee value, thermal stability, the performances such as fracture elongation, all tire base fabric post-production coiled materials
The performance that must have in process and coiled material later period use process, however existing tire base fabric glue film performance is poor, stretching resistance effect
Fruit is often not ideal enough.
Summary of the invention
The purpose of the invention is to overcome the deficiencies of the prior art and provide a kind of production of outer reinforcement polyester base cloth
Technique.
The present invention is achieved through the following technical solutions:
A kind of production technology of outer reinforcement polyester base cloth, the outer reinforcement polyester base cloth by glass fiber grid cloth and
Polyester blank base fabric is polymerized, and the glass fiber grid cloth and the polyester base cloth are placed on before special equipment and deposit cloth holder
On, after the special equipment is adjusted, the glass fiber grid cloth and the polyester blank base fabric are introduced into composite roll through deflector roll
In, the coated mode of the glass fiber grid cloth one side is uniformly applied and spreads special high temperature-proof glue, then by described multiple
Close it is compound under roller certain pressure after, be sent into compound heat drying area, cut after compound evenly drying, crimp that outer reinforcement is made is poly-
Ester tire base fabric finished product.
Further, temperature is 150 degrees Celsius in the dry section.
Further, the polyester blank base fabric is long polyester tire base fabric or short polyester tire base fabric.
Compared with prior art, the beneficial effects of the present invention are: the present invention passes through glass fiber grid cloth and polyester base
Cloth is polymerized, and the coated mode of glass fiber grid cloth one side is uniformly applied and spreads special high temperature-proof glue, to increase poly-
Ester tire base fabric is longitudinal or vertical and horizontal pulling force, improves the production efficiency of product, avoids shrinking in the case where speed is too fast
And other issues.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
A kind of production technology of outer reinforcement polyester base cloth, the outer reinforcement polyester base cloth by glass fiber grid cloth and
Polyester blank base fabric is polymerized, and the polyester blank base fabric is long polyester tire base fabric or short polyester tire base fabric, by the glass
Screen grid cloth and the polyester base cloth are placed on depositing on cloth holder before special equipment, after the special equipment is adjusted, by institute
It states glass fiber grid cloth and the polyester blank base fabric is introduced into composite roll through deflector roll, the glass fiber grid cloth one side is coated
Mode, which uniformly applies, spreads special high temperature-proof glue, then after compound under the composite roll certain pressure, is sent into compound add
Warm dry section, temperature is 150 degrees Celsius in the dry section, is cut after compound evenly drying, crimps outer reinforcement polyester is made
Tire base fabric finished product.
In conclusion the present invention is polymerized by glass fiber grid cloth and polyester blank base fabric, by glass fiber grid cloth one
The coated mode in face, which uniformly applies, spreads special high temperature-proof glue, to increase, polyester blank base fabric is longitudinal or vertical and horizontal pulling force,
The production efficiency for improving product, avoids in the case where speed is too fast, shrink and other issues.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modifications, equivalent replacements, and improvements etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (3)
1. a kind of production technology of outer reinforcement polyester base cloth, it is characterised in that: the outer reinforcement polyester base cloth passes through glass
Screen grid cloth and polyester blank base fabric are polymerized, before the glass fiber grid cloth and the polyester base cloth are placed on special equipment
Deposit on cloth holder, after the special equipment is adjusted, the glass fiber grid cloth and the polyester blank base fabric are drawn through deflector roll
Enter in composite roll, the coated mode of the glass fiber grid cloth one side is uniformly applied and spreads special high temperature-proof glue, is then passed through
Cross it is compound under the composite roll certain pressure after, be sent into compound heat drying area, cut after compound evenly drying, crimp and be made
Outer reinforcement polyester base cloth finished product.
2. a kind of production technology of outer reinforcement polyester base cloth according to claim 1, it is characterised in that: the dry section
Interior temperature is 150 degrees Celsius.
3. a kind of production technology of outer reinforcement polyester base cloth according to claim 1, it is characterised in that: the polyester blank
Base fabric is long polyester tire base fabric or short polyester tire base fabric.