CN109774202A - A kind of preparation method of nano-negative ion PVC board - Google Patents
A kind of preparation method of nano-negative ion PVC board Download PDFInfo
- Publication number
- CN109774202A CN109774202A CN201811540880.6A CN201811540880A CN109774202A CN 109774202 A CN109774202 A CN 109774202A CN 201811540880 A CN201811540880 A CN 201811540880A CN 109774202 A CN109774202 A CN 109774202A
- Authority
- CN
- China
- Prior art keywords
- pvc board
- nano
- negative ion
- preparation
- subjected
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of nano-negative ion PVC board of dalle technical field, method includes the following steps: step 1: mixing；Step 2: it squeezes；Step 3: cutting；Step 4: coating；Step 5: printing；Step 6: mopping；Step 7: aperture, this programme making sheet is simple, and PVC board long service life, anion layer is not easily to fall off, and anion release is uniform.
Description
Technical field
The invention discloses a kind of preparation methods of nano-negative ion PVC board, specially dalle technical field.
Background technique
Currently, the material with function and for indoor wall decoration is mainly coating for wall surface, it is applied in manufacture
Additive added with such effect when material need to only be added in proportion and is stirred, entire production technology and manufacturing process
It is fairly simple.However, the coating only has monotone to match, pattern effect cannot be produced, can not produce 3D anaglyph and
The marble having a sense of hierarchy and other floral designs, therefore it is generally only applicable to wall body decoration, though some commercial coating products are containing negative
Ion, but anion cannot be discharged for a long time, it is easy to concentrate release and be damaged to fall off on most surface layer the reason is that anion is contained, it is existing
Wallpaper product, which is not possible to realize, includes anion, and surface is not wear-resisting scratch-resistant, can not shampoo.
Summary of the invention
The purpose of the present invention is to provide a kind of preparation methods of nano-negative ion PVC board, to solve above-mentioned background skill
The existing wallpaper product proposed in art, which is not possible to realize, includes anion, and surface is not wear-resisting scratch-resistant, the problem of can not shampooing.
To achieve the above object, the invention provides the following technical scheme: a kind of preparation side of nano-negative ion PVC board
Method, method includes the following steps:
Step 1: mixing: cooling after PVC board material, toner and nanometer anion powder are stirred and evenly mixed at a temperature of 110 DEG C
It is spare；
Step 2: it squeezes: the spare mixing in step 1 being put into and carries out being squeezed into big plate in group machine；
Step 3: plate big in step 2 cutting: is cut into required specification PVC board；
Step 4: the PVC board in step 3 coating: is subjected to the coating of single side nano-negative ion solution, drying by rubber roller；
Step 5: the PVC board in step 4 printing: is being subjected to one side print containing nano-negative ion level by silk-screen
Brush, drying；
Step 6: mopping: the PVC board in step 5 is subjected to varnish application in the single side with printing surface and UV solidifies；
Step 7: the PVC board in step 6 aperture: is subjected to uniform pore openings, polishing in the single side with varnish face.
Preferably, the mesh number of the nanometer anion powder in the step 1 is greater than 500 mesh.
Preferably, the cooling temperature in the step 1 is room temperature.
Preferably, the aperture depth in the step 7 gos deep into PVC board and not through PVC board.
Preferably, oven drying is used in the step 4 and step 5.
Compared with prior art, the beneficial effects of the present invention are:
1) this programme is stirred mixing making sheet using PVC board material, toner and nanometer anion powder, so that PVC board table
Face itself is capable of releasing negative ion；
2) this programme uses one side glue roll coating nano-negative ion solution layer, and coating uniformly, improves anion burst size；
3) this programme is printed using single side silk-screen, improves PVC board aesthetics；
4) this programme uses single side varnish application, improves the wear-resisting scratch-proofness of PVC board；
5) this programme uses single side uniform pore openings, and anion is avoided to concentrate release, improves PVC board anion release time,
This programme making sheet is simple, and PVC board long service life, anion layer is not easily to fall off, and anion release is uniform.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The present invention provides a kind of technical solution: a kind of preparation method of nano-negative ion PVC board, this method includes following
Step:
Step 1: mixing: cooling after PVC board material, toner and nanometer anion powder are stirred and evenly mixed at a temperature of 110 DEG C
It is spare；
Step 2: it squeezes: the spare mixing in step 1 being put into and carries out being squeezed into big plate in group machine；
Step 3: plate big in step 2 cutting: is cut into required specification PVC board；
Step 4: the PVC board in step 3 coating: is subjected to the coating of single side nano-negative ion solution, drying by rubber roller；
Step 5: the PVC board in step 4 printing: is being subjected to one side print containing nano-negative ion level by silk-screen
Brush, drying；
Step 6: mopping: the PVC board in step 5 is subjected to varnish application in the single side with printing surface and UV solidifies；
Step 7: the PVC board in step 6 aperture: is subjected to uniform pore openings, polishing in the single side with varnish face.
Wherein, the mesh number of the nanometer anion powder in step 1 be greater than 500 mesh, particle is small, improve nanometer anion powder with
The mixed effect of PVC board material and toner, plate surface is uneven when avoiding making sheet, and the cooling temperature in step 1 is room
Temperature avoids the excessively high extruding after-contraction deformation of temperature, and the aperture depth in step 7 gos deep into PVC board and not through PVC board, convenient for negative
The release of ion avoids timber intensity from reducing excessively high, oven drying is used in step 4 and step 5, do not use air-dried and hot wind
Drying, avoids the nano-negative ion layer of plate surface and silk-screen layer in uneven thickness.
Embodiment
Step 1: mixing: after PVC board material, red toner and nanometer anion powder are stirred and evenly mixed at a temperature of 110 DEG C
Cooling is spare, and nano-negative ion powder content is the 20% of PVC board material and red toner total content；
Step 2: it squeezes: the spare mixing in step 1 being put into group machine and is squeezed into a thickness of the big plate of 10cm；
Step 3: plate big in step 2 cutting: is cut into the PVC board of 0.5*0.6m specification；
Step 4: the PVC board in step 3 coating: is subjected to the coating of single side nano-negative ion solution, coating by rubber roller
With a thickness of 0.5mm, the baking oven that PVC board is put into 80 DEG C is dried；
Step 5: the PVC board in step 4 printing: is being subjected to bloth printing containing nano-negative ion level by silk-screen
Printing, print thickness 0.2mm dry the baking oven that PVC board is put into 80 DEG C；
Step 6: mopping: carrying out varnish application in the single side with printing surface for the PVC board in step 5 and UV solidify,
Varnish application is with a thickness of 0.5mm；
Step 7: the PVC board in step 6 aperture: is subjected to uniform pore openings, aperture depth in the single side with varnish face
Go deep into PVC board, opening diameter 0.1mm polishes to tapping.
| PVC board perforated area (%) | Anion burst size (a/cm2Second) |
| 0.5% | >300 |
| 1% | >600 |
| 1.5% | >900 |
| 2% | >1200 |
(perforated area percentage and anion burst size compare)
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (5)
1. a kind of preparation method of nano-negative ion PVC board, it is characterised in that: method includes the following steps:
Step 1: mixing: cooling is standby after PVC board material, toner and nanometer anion powder are stirred and evenly mixed at a temperature of 110 DEG C
With；
Step 2: it squeezes: the spare mixing in step 1 being put into and carries out being squeezed into big plate in group machine；
Step 3: plate big in step 2 cutting: is cut into required specification PVC board；
Step 4: the PVC board in step 3 coating: is subjected to the coating of single side nano-negative ion solution, drying by rubber roller；
Step 5: printing: the PVC board in step 4 is printed on one side by silk-screen containing nano-negative ion level, is dried
It is dry；
Step 6: mopping: the PVC board in step 5 is subjected to varnish application in the single side with printing surface and UV solidifies；
Step 7: the PVC board in step 6 aperture: is subjected to uniform pore openings, polishing in the single side with varnish face.
2. a kind of preparation method of nano-negative ion PVC board according to claim 1, it is characterised in that: the step
The mesh number of nanometer anion powder in one is greater than 500 mesh.
3. a kind of preparation method of nano-negative ion PVC board according to claim 1, it is characterised in that: the step
Cooling temperature in one is room temperature.
4. a kind of preparation method of nano-negative ion PVC board according to claim 1, it is characterised in that: the step
Aperture depth in seven gos deep into PVC board and not through PVC board.
5. a kind of preparation method of nano-negative ion PVC board according to claim 1, it is characterised in that: the step
Four and step 5 in use oven drying.