CN109750299A - A kind of processing of rust removing technique of spring steel - Google Patents

A kind of processing of rust removing technique of spring steel Download PDF

Info

Publication number
CN109750299A
CN109750299A CN201711072263.3A CN201711072263A CN109750299A CN 109750299 A CN109750299 A CN 109750299A CN 201711072263 A CN201711072263 A CN 201711072263A CN 109750299 A CN109750299 A CN 109750299A
Authority
CN
China
Prior art keywords
spring steel
rust removing
processing
cleaned
cleaning
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711072263.3A
Other languages
Chinese (zh)
Inventor
吕志敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Sea Through Department Of Science And Technology Consulting Co Ltd
Original Assignee
Qingdao Sea Through Department Of Science And Technology Consulting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Sea Through Department Of Science And Technology Consulting Co Ltd filed Critical Qingdao Sea Through Department Of Science And Technology Consulting Co Ltd
Priority to CN201711072263.3A priority Critical patent/CN109750299A/en
Publication of CN109750299A publication Critical patent/CN109750299A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of processing of rust removing technique of spring steel, and operating procedure is as follows: 1) will need to be infiltrated on the spring steel to derust with glycerol;2) surface grinding process, revolving speed 200-300r/min are carried out with electronic water sand wheel;3) by step 2), treated that spring steel is placed in rust removing solution infiltrates 5-10min;4) spot of spring steel surface is cleaned with cooling boiling water;5) by the spring steel infiltration after cleaning in also 4-6% potassium chloride and sodium carbonate mixed aqueous solutions;6) step 5) spring steel is being cleaned with the hydraulic pressure of 7-9MPa again;7) spring steel after cleaning is prevented from being dried in vacuo in drying box, drying temperature is 50-70 DEG C.Entire technological operation is simple, can effectively remove the rusty stain of spring steel, moreover it is possible to which the surface of effective protection spring steel prevents the reproduction of rusty stain, can further genralrlization application.

Description

A kind of processing of rust removing technique of spring steel
Technical field
The present invention relates to derusting technical fields, and in particular to a kind of processing of rust removing technique of spring steel.
Background technique
Present China is due to manufacturing fast development, so that steel product excess capacity usually occurs during production The case where, according to incompletely statistics, lead to the discarded loss of getting rusty of steel due to annual steel excess capacity in China, occupies every 1/4 or so of year steel production, causes serious wasting phenomenon.
Spring steel refer to due to quench and annealed strip under elasticity, and dedicated for manufacture spring and elastic element Steel, spring use under shock and vibration or long-term friendship stress, it requires that spring steel has high tensile strength, elastic limit, height Fatigue strength, spring steel more demanding intensity and fatigue limit.But spring steel will lead to during long-term storage Surface oxidisation, commonly in traditional derusting method, hand cleaning speed is slow, and brain hole intensity is big, and the low efficiency to derust, and chemical So that the surface mass of spring steel construction easily changes, the serious toughness that also will affect spring steel and structure are strong for processing Degree, and the influence to environment, same high-intensitive mechanical derusting technique are bigger to the surface of spring steel construction.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of processing of rust removing technique of spring steel, so that spring steel Surface derusting better effect, and it is not right.
In order to achieve the above object, the present invention is achieved by the following technical programs:
A kind of processing of rust removing technique of spring steel, operating procedure are as follows:
1) it will need to be infiltrated on the spring steel to derust with glycerol;
2) surface grinding process, revolving speed 200-300r/min are carried out with electronic water sand wheel;
3) by step 2), treated that spring steel is placed in rust removing solution infiltrates 5-10min;
4) spot of spring steel surface is cleaned with cooling boiling water;
5) by the spring steel infiltration after cleaning in also 4-6% potassium chloride and sodium carbonate mixed aqueous solutions;
6) step 5) spring steel is being cleaned with the hydraulic pressure of 7-9MPa again;
7) spring steel after cleaning is prevented from being dried in vacuo in drying box, drying temperature is 50-70 DEG C.
Preferably, controlled at 50-60 DEG C in the step 3).
Preferably, the group of rust removing solution is divided into dilute sulfuric acid 20-30%, ammonium citrate 20-30%, carbonic acid in the step 3) Sodium 25-30%, triethanolamine 10-20%.
Preferably, the time of the step 5) infiltration is 10-15min.
Preferably, the drying time of the step 7) is 2-3h.
The present invention provides a kind of processing of rust removing techniques of spring steel, by first carrying out mechanical grinding in operating procedure The rusty stain of removal spring steel surface, convenient for being contacted with rust removing solution, can carry out deep layer so that the surface of spring steel is more coarse The rusty stain of secondary removal spring steel, and cooling boiling water can remove the composition of air in water removal, avoid composition of air in water with Spring steel is further formed rusty stain, and rust removing solution used, can be with bullet in 4-6% potassium chloride and sodium carbonate mixed aqueous solutions Spring steel forms fine and close protective layer, avoids further contacting with air.Entire technological operation is simple, can further genralrlization application.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with implementation of the invention Example, technical scheme in the embodiment of the invention is clearly and completely described.Based on the embodiments of the present invention, this field Those of ordinary skill's every other embodiment obtained without creative efforts, belongs to protection of the present invention Range.
Embodiment 1:
The present embodiment provides a kind of processing of rust removing technique of spring steel, operating procedure is as follows:
1) it will need to be infiltrated on the spring steel to derust with glycerol;
2) surface grinding process, revolving speed 300r/min are carried out with electronic water sand wheel;
3) by step 2), treated that spring steel is placed in rust removing solution infiltrates 5min, controlled at 60 DEG C;
4) spot of spring steel surface is cleaned with cooling boiling water;
5) by the spring steel infiltration after cleaning in also 4% potassium chloride and sodium carbonate mixed aqueous solutions, the time of infiltration is 15min;
6) step 5) spring steel is being cleaned with the hydraulic pressure of 9MPa again;
7) spring steel after cleaning is prevented from being dried in vacuo in drying box, drying temperature is 59 DEG C.
Embodiment 2:
The present embodiment provides a kind of processing of rust removing technique of spring steel, operating procedure is as follows:
1) it will need to be infiltrated on the spring steel to derust with glycerol;
2) surface grinding process, revolving speed 230r/min are carried out with electronic water sand wheel;
3) by step 2), treated that spring steel is placed in rust removing solution infiltrates 8min, controlled at 50 DEG C, the group of rust removing solution It is divided into dilute sulfuric acid 30%, ammonium citrate 30%, sodium carbonate 30%, triethanolamine 10%;
4) spot of spring steel surface is cleaned with cooling boiling water;
5) by the spring steel infiltration after cleaning in also 5% potassium chloride and sodium carbonate mixed aqueous solutions;
6) step 5) spring steel is being cleaned with the hydraulic pressure of 7MPa again;
7) spring steel after cleaning is prevented from being dried in vacuo in drying box, drying temperature is 57 DEG C, drying time 3h.
Embodiment 3:
The present embodiment provides a kind of processing of rust removing technique of spring steel, operating procedure is as follows:
1) it will need to be infiltrated on the spring steel to derust with glycerol;
2) surface grinding process, revolving speed 200r/min are carried out with electronic water sand wheel;
3) by step 2), treated that spring steel is placed in rust removing solution infiltrates 7min, the group of rust removing solution be divided into dilute sulfuric acid 20%, Ammonium citrate 30%, sodium carbonate 30%, triethanolamine 20%;
4) spot of spring steel surface is cleaned with cooling boiling water;
5) by the spring steel infiltration after cleaning in also 4% potassium chloride and sodium carbonate mixed aqueous solutions, the time of infiltration is 10min;
6) step 5) spring steel is being cleaned with the hydraulic pressure of 8MPa again;
7) spring steel after cleaning is prevented from being dried in vacuo in drying box, drying temperature is 50 DEG C, drying time 2h.
Embodiment 4:
The present embodiment provides a kind of processing of rust removing technique of spring steel, operating procedure is as follows:
1) it will need to be infiltrated on the spring steel to derust with glycerol;
2) surface grinding process, revolving speed 260r/min are carried out with electronic water sand wheel;
3) by step 2), treated that spring steel is placed in rust removing solution infiltrates 10min, the group of rust removing solution be divided into dilute sulfuric acid 30%, Ammonium citrate 20%, sodium carbonate 30%, triethanolamine 20%;
4) spot of spring steel surface is cleaned with cooling boiling water;
5) by the spring steel infiltration after cleaning in also 6% potassium chloride and sodium carbonate mixed aqueous solutions;
6) step 5) spring steel is being cleaned with the hydraulic pressure of 7MPa again;
7) spring steel after cleaning is prevented from being dried in vacuo in drying box, drying temperature is 70 DEG C, drying time 3h.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although with reference to the foregoing embodiments Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation Technical solution documented by example is modified or equivalent replacement of some of the technical features;And these modification or Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.

Claims (5)

1. a kind of processing of rust removing technique of spring steel, which is characterized in that operating procedure is as follows:
1) it will need to be infiltrated on the spring steel to derust with glycerol;
2) surface grinding process, revolving speed 200-300r/min are carried out with electronic water sand wheel;
3) by step 2), treated that spring steel is placed in rust removing solution infiltrates 5-10min;
4) spot of spring steel surface is cleaned with cooling boiling water;
5) by the spring steel infiltration after cleaning in also 4-6% potassium chloride and sodium carbonate mixed aqueous solutions;
6) step 5) spring steel is being cleaned with the hydraulic pressure of 7-9MPa again;
7) spring steel after cleaning is prevented from being dried in vacuo in drying box, drying temperature is 50-70 DEG C.
2. the processing of rust removing technique of spring steel as described in claim 1, which is characterized in that control temperature in the step 3) It is 50-60 DEG C.
3. the processing of rust removing technique of spring steel as described in claim 1, which is characterized in that rust removing solution in the step 3) Group is divided into dilute sulfuric acid 20-30%, ammonium citrate 20-30%, sodium carbonate 25-30%, triethanolamine 10-20%.
4. the processing of rust removing technique of spring steel as described in claim 1, which is characterized in that the time of the step 5) infiltration For 10-15min.
5. the processing of rust removing technique of spring steel as described in claim 1, which is characterized in that the drying time of the step 7) For 2-3h.
CN201711072263.3A 2017-11-04 2017-11-04 A kind of processing of rust removing technique of spring steel Pending CN109750299A (en)