CN109749138A - A kind of antibacterial rubber material - Google Patents
A kind of antibacterial rubber material Download PDFInfo
- Publication number
- CN109749138A CN109749138A CN201711063040.0A CN201711063040A CN109749138A CN 109749138 A CN109749138 A CN 109749138A CN 201711063040 A CN201711063040 A CN 201711063040A CN 109749138 A CN109749138 A CN 109749138A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- antibacterial
- rubber material
- plasticizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of antibacterial rubber materials, are mainly made of the following component counted with mass fraction: 18-40 parts of natural rubber, 18-20 parts of acrylic rubber, 5-12 parts of tetrapropanate fluorine rubber, 3-5 parts of butadiene-styrene rubber, 0.5-2.5 parts of galic essential oil, 2-4 parts of vulcanizing agent, 18-25 parts of calcium carbonate, 8-18 parts of PVC modifier, 0.5-1.2 parts of plasticizer, 1.1-1.5 parts of epoxy aliphatic acid methyl ester, 0.1-0.8 parts of cobalt oxide.By adding a variety of antimicrobial components the anti-microbial property of material itself greatly enhanced in rubber material of the invention, be suitable for various gnotobasis.
Description
Technical field
The present invention relates to high molecular material production technical field more particularly to a kind of antibacterial rubber materials.
Background technique
As rubber is more and more applied to a variety of occasions, the requirement for rubber performance is also more diversified, wherein
Anti-microbial property is exactly one of which to the higher performance of material requirements, and in some medical aseptic occasions, the requirement of sterile rubber is outstanding
It is high.
Summary of the invention
In order to solve the above-mentioned technical problem, a kind of rubber material that anti-microbial property is good is provided, the present invention provides following technology
Scheme:
A kind of antibacterial rubber material, is made of the following component counted with mass fraction: 18-40 parts of natural rubber, acrylic acid
18-20 parts of ester rubber, 5-12 parts of tetrapropanate fluorine rubber, 3-5 parts of butadiene-styrene rubber, 0.5-2.5 parts of galic essential oil, 2-4 parts of vulcanizing agent, carbon
Sour calcium 18-25 parts, 8-18 parts of PVC modifier, 0.5-1.2 parts of plasticizer, 1.1-1.5 parts of epoxy aliphatic acid methyl ester, cobalt oxide
0.1-0.8 parts.
It further, further include 0.3-0.5 parts of activating agent.
It further, further include 2-5 parts of glass fibre.
Further, be made of the following component counted with mass fraction: 25 parts of natural rubber, 17 parts of acrylic rubber,
8.5 parts of tetrapropanate fluorine rubber, 4 parts of butadiene-styrene rubber, 1.5 parts of galic essential oil, 3 parts of vulcanizing agent, 20 parts of calcium carbonate, 12 parts of PVC modifier,
0.8 part of plasticizer, 1.3 parts of epoxy aliphatic acid methyl ester, 0.2 part of cobalt oxide.
By adding a variety of antimicrobial components the anti-microbial property of material itself greatly enhanced, be suitable for various asepsis rings
Border.
Specific embodiment
Embodiment 1,
A kind of antibacterial rubber material, is made of the following component counted with mass fraction: 25 parts of natural rubber, acrylate rubber
17 parts of glue, 8.5 parts of tetrapropanate fluorine rubber, 4 parts of butadiene-styrene rubber, 1.5 parts of galic essential oil, 3 parts of vulcanizing agent, 20 parts of calcium carbonate, PVC are modified
12 parts of agent, 0.8 part of plasticizer, 1.3 parts of epoxy aliphatic acid methyl ester, 0.2 part of cobalt oxide.
Embodiment 2,
A kind of antibacterial rubber material, is made of the following component counted with mass fraction: 20 parts of natural rubber, acrylate rubber
18 parts of glue, 5 parts of tetrapropanate fluorine rubber, 3 parts of butadiene-styrene rubber, 0.5 part of galic essential oil, 2 parts of vulcanizing agent, 18 parts of calcium carbonate, PVC modifier
8 parts, 0.5 part of plasticizer, 1.1 parts of epoxy aliphatic acid methyl ester, 0.1 part of cobalt oxide.
Embodiment 3,
A kind of antibacterial rubber material, is made of the following component counted with mass fraction: 30 parts of natural rubber, acrylate rubber
20 parts of glue, 12 parts of tetrapropanate fluorine rubber, 5 parts of butadiene-styrene rubber, 2.5 parts of galic essential oil, 4 parts of vulcanizing agent, 25 parts of calcium carbonate, PVC are modified
18 parts of agent, 1.2 parts of plasticizer, 1.5 parts of epoxy aliphatic acid methyl ester, 0.3 part of cobalt oxide.
It is enlightenment with above-mentioned desirable embodiment according to the present invention, through the above description, relevant staff is complete
Various changes and amendments can be carried out without departing from the scope of the technological thought of the present invention'.This invention it is technical
Range is not limited to the contents of the specification, it is necessary to which the technical scope thereof is determined according to the scope of the claim.
Claims (4)
1. a kind of antibacterial rubber material, it is characterised in that: be made of the following component counted with mass fraction: natural rubber 18-40
Part, 18-20 parts of acrylic rubber, 5-12 parts of tetrapropanate fluorine rubber, 3-5 parts of butadiene-styrene rubber, 0.5-2.5 parts of galic essential oil, vulcanization
2-4 parts of agent, 18-25 parts of calcium carbonate, 8-18 parts of PVC modifier, 0.5-1.2 parts of plasticizer, epoxy aliphatic acid methyl ester 1.1-1.5
Part, 0.1-0.8 parts of cobalt oxide.
2. a kind of antibacterial rubber material as described in claim 1, it is characterised in that: further include 0.3-0.5 parts of activating agent.
3. a kind of antibacterial rubber material as described in claim 1, it is characterised in that: further include 2-5 parts of glass fibre.
4. a kind of antibacterial rubber material as described in claim 1, it is characterised in that: by the following component group in terms of mass fraction
At: 25 parts of natural rubber, 17 parts of acrylic rubber, 8.5 parts of tetrapropanate fluorine rubber, 4 parts of butadiene-styrene rubber, 1.5 parts of galic essential oil, sulphur
3 parts of agent, 20 parts of calcium carbonate, 12 parts of PVC modifier, 0.8 part of plasticizer, 1.3 parts of epoxy aliphatic acid methyl ester, 0.2 part of cobalt oxide.