CN109735253A - A kind of comprehensive performance emphasis article gummed tape and its manufacture craft - Google Patents
A kind of comprehensive performance emphasis article gummed tape and its manufacture craft Download PDFInfo
- Publication number
- CN109735253A CN109735253A CN201910112713.XA CN201910112713A CN109735253A CN 109735253 A CN109735253 A CN 109735253A CN 201910112713 A CN201910112713 A CN 201910112713A CN 109735253 A CN109735253 A CN 109735253A
- Authority
- CN
- China
- Prior art keywords
- layer
- comprehensive performance
- antistatic
- covered
- toughening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of comprehensive performance emphasis article gummed tape and its manufacture crafts, including bracing ring and the narrow tape body being wound on bracing ring, wide tape body, the narrow tape body, wide tape body structure is identical, the narrow tape body includes the substrate layer set gradually, antistatic backing, first barrier layer, adhesive layer, second barrier layer, flame-retardant layer, toughening layer, gluing oxidant layer two sides are additionally provided with polyethylene sheets layer, the present invention passes through setting different function layer, the high combination property adhesive tape being prepared, with air tight, it is moisture-proof, waterproof, antistatic, the protective performances such as high-barrier, it can guarantee that combustible and explosive articles are isolated with extraneous aerobic environment, and Mars is isolated and puts spark.
Description
Technical field
The present invention relates to adhesive tape areas, and in particular to a kind of comprehensive performance emphasis article gummed tape and its manufacture craft.
Background technique
Dangerous material include general name that is inflammable, explosive, having aggressive, toxic and other items.Such as gasoline, explosive, strong acid, strong
Alkali, benzene, naphthalene, celluloid, peroxide etc..When transport and storage, it should be handled according to dangerous material regulations, but due to security protection packet
Fill technological lag, the transports of these articles, carrying occasionally have contingency in storing process, cause largely to lose, due to general
Logical gummed tape can not make dangerous material be isolated from the outside, and be easy to happen danger, there is very big security risk.
Summary of the invention
In order to solve the above technical problems, technical solution provided by the invention are as follows: a kind of comprehensive performance emphasis article packaging glue
Band, including bracing ring and the narrow tape body being wound on bracing ring, wide tape body, the narrow tape body, wide tape body structure phase
Together, the narrow tape body includes the substrate layer set gradually, antistatic backing, the first barrier layer, the first adhesive layer, the second barrier
Layer, flame-retardant layer, toughening layer, the second adhesive layer, gluing oxidant layer two sides are additionally provided with polynorbornene sheet layer.
As an improvement, the substrate layer is composite layer, it is combined by PET and foam material.
The composite base material layer had both had good tear-resistant intensity, but also with good stickiness, prevented in packaging emphasis
Voiding problem when article is bonded.
The antistatic backing be selected from antistatic acrylic film, antistatic polychloroethylene film, antistatic polycarbonate membrane, prevent it is quiet
One of voltolisation diethyl terephthalate film, the antistatic backing had both had the function of preventing electrostatic from generating, and be also equipped with Zhuo
Anti- chemical solvent erosion performance more makes emphasis article gummed tape of the invention meet the resistance of severe pack environment.
As an improvement, the toughening layer includes the pure metal layer set gradually, adsorption layer, except oxygen layer.
The metal layer is arranged on flame-retardant layer by the way of metal spraying or hot dip metal coating, and other each layers are equal
It is prepared using hot pressing technique；The metal layer the selection of material is one of metal coating such as zinc, aluminium；The adsorption layer
Be prepared by nano material, specially active carbon nanoparticles, active carbon nanoparticles large specific surface area, aperture is moderate, be evenly distributed and
Adsorption rate is fast, to improve the absorption property of emphasis article gummed tape of the invention；The deoxygenation layer the selection of material is sea
Continuous iron, sponge iron can generate iron colloid with oxygen, to achieve the purpose that deoxygenation.
Metallic composite technology can play the respective advantage of group element material, realize the allocation optimum of group element material, section
About metal material realizes the unappeasable performance requirement of single metal.By metal layer, adsorption layer, except the compound toughening layer of oxygen layer,
Collective effect generates good effect, so that the feature that emphasis article gummed tape of the invention not only has intensity high, tear-resistant,
And smell, gas that packaging article distributes can be adsorbed, the oxygen in the pack environment of periphery can be also removed, reach isolating oxygen
The effect of gas, can be avoided inner heat, prevent inflammable and explosive danger.
As an improvement, the gluing oxidant layer is modified rubber silicon rubber bonder layer.
Modified silicon rubber bonding agent not only has the advantages that tack is high, it is long to hold viscosity, also has chemical reagent-resistant performance
Well, it can repeatedly remove the characteristics of pasting again, and glue surface will not be damaged.
As an improvement, the adhesive layer with a thickness of 0.1-0.3mm.
As an improvement, the pure metal layer is with a thickness of 0.2-0.4mm.
As an improvement, the bracing ring with a thickness of 0.2-0.5mm.
As an improvement, the toughening layer with a thickness of 0.6-1mm.
As an improvement, its production method, comprising the following steps:
(1) be PET by ingredient, the base of foam material expects that machine-shaping forms substrate layer；
(2) by ingredient be from antistatic acrylic film or antistatic polychloroethylene film or antistatic polycarbonate membrane or
The antistatic material of antistatic polyethylene terephthalate's film is processed into antistatic backing and is covered on substrate layer；
(3) it is covered on the antistatic backing on the first barrier layer；
(4) the first gluing oxidant layer is made in the modified silicon rubber bonding agent of deployed viscosity to be covered on the first barrier layer,
Wherein, the first gluing oxidant layer two sides are also covered with polynorbornene sheet layer respectively；
(5) the second barrier layer is covered in the first gluing oxidant layer；
(6) flame-retardant layer is covered on the second barrier layer；
(7) toughening layer is covered on flame-retardant layer, wherein toughening layer includes metal layer, adsorption layer, except oxygen layer, and metal layer is adopted
It is arranged on flame-retardant layer with the mode of metal spraying or hot dip metal coating, adsorption layer is all made of hot pressing technique except oxygen layer
It is prepared, wherein adsorption layer is prepared by nano material, except oxygen layer is prepared by sponge iron；
(8) the modified silicon rubber bonding agent of deployed viscosity is made on the second gluing oxidant layer covering toughening layer.
After using the above structure, the present invention has the advantage that the present invention is prepared by setting different function layer
High combination property adhesive tape has the protective performances such as air tight, moisture-proof, waterproof, antistatic, high-barrier, it is ensured that inflammable and explosive
Article is isolated with extraneous aerobic environment, and Mars and point spark is isolated；
Wherein barrier layer being capable of blocking oxygen, chemical solvent；Substrate is combined using composite layer, can fully ensure that anti-corrosion is imitated
Fruit；The two sides of adhesive layer are equipped with polyethylene sheets, corrosive deposit can be effectively prevent to be externally entering adhesive layer, further
Enhance anti-corrosion effect；Toughening layer has excellent tensile strength and powerful adhesive property, very effective can resist stress, outer
Power, impact and thermal expansion；Pure metal layer has excellent waterproof antiwear；Adhesive layer have humidity, it is resistance to thermal expansion, it is wear-resisting
The characteristics of damage；The two sides of gluing oxidant layer are arranged in polynorbornene sheet layer, corrosive deposit can be effectively prevent to be externally entering
Gluing oxidant layer；In addition adhesive tape ontology includes narrow adhesive tape and wide adhesive tape, is all disposed on bracing ring, can select different rule as needed
The adhesive tape of lattice.
Detailed description of the invention
Fig. 1 is a kind of structural schematic diagram of comprehensive performance emphasis article gummed tape of the present invention.
Fig. 2 is the structural schematic diagram of narrow adhesive tape in a kind of comprehensive performance emphasis article gummed tape of the present invention.
Fig. 3 is the structural schematic diagram of toughening layer in a kind of comprehensive performance emphasis article gummed tape of the present invention.
It is as shown in the figure: 1, bracing ring, 2, narrow tape body, 3, wide tape body, 4, substrate layer, 5, antistatic backing, the 6, first resistance
Interlayer, the 7, first adhesive layer, the 8, second barrier layer, 9, flame-retardant layer, 10, toughening layer, 10.1, pure metal layer, 10.2, absorption
Layer, 10.3, remove oxygen layer, 11, polynorbornene sheet layer, the 12, second adhesive layer.
Specific embodiment
In the following, being described further in conjunction with attached drawing and specific embodiment to the present invention:
In following specific embodiments, described " first " and " second " is to same or similar structure to show area
Not, not order of representation or subordinate relation.In following specific embodiments, such as non-specified otherwise, used material
It is obtained by conventional technology or commercially available approach.Modified silicon rubber bonding agent is commercially available.
In conjunction with attached drawing 1~3,
Embodiment one
A kind of comprehensive performance emphasis article gummed tape, including bracing ring 1 and be wound on bracing ring 1 narrow tape body 2,
Wide tape body 3, the narrow tape body 2,3 structure of wide tape body are identical, the narrow tape body 2 include set gradually substrate layer 4,
Antistatic backing 5, the first barrier layer 6, the first adhesive layer 7, the second barrier layer 8, flame-retardant layer 9, toughening layer 10, the second adhesive
Layer 12,7 two sides of the first gluing oxidant layer are additionally provided with polynorbornene sheet layer 11.
As the present embodiment preferred embodiment, the substrate layer 4 is composite layer, by PET and foam Material cladding
It forms.
As the present embodiment preferred embodiment, the toughening layer 10 include set gradually pure metal layer 10.1,
Adsorption layer 10.2 removes oxygen layer 10.3.
As the present embodiment preferred embodiment, the gluing oxidant layer 7 is modified silicon rubber adhesive layer.
As the present embodiment preferred embodiment, the adhesive layer 7 with a thickness of 0.1mm.
As the present embodiment preferred embodiment, the pure metal layer 10.1 is with a thickness of 0.2mm.
As the present embodiment preferred embodiment, the bracing ring 1 with a thickness of 0.2mm.
As the present embodiment preferred embodiment, the toughening layer 10 with a thickness of 0.6mm.
Its production method, comprising the following steps:
(1) be PET by ingredient, the base of foam material expects that machine-shaping forms substrate layer；
(2) by ingredient be from antistatic acrylic film or antistatic polychloroethylene film or antistatic polycarbonate membrane or
The antistatic material of antistatic polyethylene terephthalate's film is processed into antistatic backing and is covered on substrate layer；
(3) it is covered on the antistatic backing on the first barrier layer；
(4) the first gluing oxidant layer is made in the modified silicon rubber bonding agent of deployed viscosity to be covered on the first barrier layer,
Wherein, the first gluing oxidant layer two sides are also covered with polynorbornene sheet layer respectively；
(5) the second barrier layer is covered in the first gluing oxidant layer；
(6) flame-retardant layer is covered on the second barrier layer；
(7) toughening layer is covered on flame-retardant layer, wherein toughening layer includes metal layer, adsorption layer, except oxygen layer, and metal layer is adopted
It is arranged on flame-retardant layer with the mode of metal spraying or hot dip metal coating, adsorption layer is all made of hot pressing technique except oxygen layer
It is prepared, wherein adsorption layer is prepared by nano material, except oxygen layer is prepared by sponge iron；
(8) the modified silicon rubber bonding agent of deployed viscosity is made on the second gluing oxidant layer covering toughening layer.
Embodiment two
A kind of comprehensive performance emphasis article gummed tape, including bracing ring 1 and be wound on bracing ring 1 narrow tape body 2,
Wide tape body 3, the narrow tape body 2,3 structure of wide tape body are identical, the narrow tape body 2 include set gradually substrate layer 4,
Antistatic backing 5, the first barrier layer 6, the first adhesive layer 7, the second barrier layer 8, flame-retardant layer 9, toughening layer 10, the second adhesive
Layer 12,7 two sides of the first gluing oxidant layer are additionally provided with polynorbornene sheet layer 11.
As the present embodiment preferred embodiment, the substrate layer 4 is composite layer, by PET and foam Material cladding
It forms.
As the present embodiment preferred embodiment, the toughening layer 10 include set gradually pure metal layer 10.1,
Adsorption layer 10.2 removes oxygen layer 10.3.
As the present embodiment preferred embodiment, the gluing oxidant layer 7 is modified silicon rubber adhesive layer.
As the present embodiment preferred embodiment, the adhesive layer 7 with a thickness of 0.3mm.
As the present embodiment preferred embodiment, the pure metal layer 10.1 is with a thickness of 0.4mm.
As the present embodiment preferred embodiment, the bracing ring 1 with a thickness of 0.5mm.
As the present embodiment preferred embodiment, the toughening layer 10 with a thickness of 1mm.
Its production method, comprising the following steps:
(1) be PET by ingredient, the base of foam material expects that machine-shaping forms substrate layer；
(2) by ingredient be from antistatic acrylic film or antistatic polychloroethylene film or antistatic polycarbonate membrane or
The antistatic material of antistatic polyethylene terephthalate's film is processed into antistatic backing and is covered on substrate layer；
(3) it is covered on the antistatic backing on the first barrier layer；
(4) the first gluing oxidant layer is made in the modified silicon rubber bonding agent of deployed viscosity to be covered on the first barrier layer,
Wherein, the first gluing oxidant layer two sides are also covered with polynorbornene sheet layer respectively；
(5) the second barrier layer is covered in the first gluing oxidant layer；
(6) flame-retardant layer is covered on the second barrier layer；
(7) toughening layer is covered on flame-retardant layer, wherein toughening layer includes metal layer, adsorption layer, except oxygen layer, and metal layer is adopted
It is arranged on flame-retardant layer with the mode of metal spraying or hot dip metal coating, adsorption layer is all made of hot pressing technique except oxygen layer
It is prepared, wherein adsorption layer is prepared by nano material, except oxygen layer is prepared by sponge iron；
(8) the modified silicon rubber bonding agent of deployed viscosity is made on the second gluing oxidant layer covering toughening layer.
Embodiment three
A kind of comprehensive performance emphasis article gummed tape, including bracing ring 1 and be wound on bracing ring 1 narrow tape body 2,
Wide tape body 3, the narrow tape body 2,3 structure of wide tape body are identical, the narrow tape body 2 include set gradually substrate layer 4,
Antistatic backing 5, the first barrier layer 6, the first adhesive layer 7, the second barrier layer 8, flame-retardant layer 9, toughening layer 10, the second adhesive
Layer 12,7 two sides of the first gluing oxidant layer are additionally provided with polynorbornene sheet layer 11.
As the present embodiment preferred embodiment, the substrate layer 4 is composite layer, by PET and foam Material cladding
It forms.
As the present embodiment preferred embodiment, the toughening layer 10 include set gradually pure metal layer 10.1,
Adsorption layer 10.2 removes oxygen layer 10.3.
As the present embodiment preferred embodiment, the gluing oxidant layer 7 is modified silicon rubber adhesive layer.
As the present embodiment preferred embodiment, the adhesive layer 7 with a thickness of 0.2mm.
As the present embodiment preferred embodiment, the pure metal layer 10.1 is with a thickness of 0.3mm.
As the present embodiment preferred embodiment, the bracing ring 1 with a thickness of 0.4mm.
As the present embodiment preferred embodiment, the toughening layer 10 with a thickness of 0.8mm.
Its production method, comprising the following steps:
(1) be PET by ingredient, the base of foam material expects that machine-shaping forms substrate layer；
(2) by ingredient be from antistatic acrylic film or antistatic polychloroethylene film or antistatic polycarbonate membrane or
The antistatic material of antistatic polyethylene terephthalate's film is processed into antistatic backing and is covered on substrate layer；
(3) it is covered on the antistatic backing on the first barrier layer；
(4) the first gluing oxidant layer is made in the modified silicon rubber bonding agent of deployed viscosity to be covered on the first barrier layer,
Wherein, the first gluing oxidant layer two sides are also covered with polynorbornene sheet layer respectively；
(5) the second barrier layer is covered in the first gluing oxidant layer；
(6) flame-retardant layer is covered on the second barrier layer；
(7) toughening layer is covered on flame-retardant layer, wherein toughening layer includes metal layer, adsorption layer, except oxygen layer, and metal layer is adopted
It is arranged on flame-retardant layer with the mode of metal spraying or hot dip metal coating, adsorption layer is all made of hot pressing technique except oxygen layer
It is prepared, wherein adsorption layer is prepared by nano material, except oxygen layer is prepared by sponge iron；
(8) the modified silicon rubber bonding agent of deployed viscosity is made on the second gluing oxidant layer covering toughening layer.
The gummed tape of Examples 1 to 3 prepared by the present invention is tested for the property:
1, the tearing toughness of vertical and horizontal is measured according to detection method JIS-P-8116, test result is as follows:
1 tearing toughness performance test of table
Test result can be seen that adhesive tape of the present invention and have good tear-resistant strength character, Ke Yibao from table
Card gummed tape can resist the damaging problem in transportation environment.
2, peel strength tested according to detection method GB/T 2792-2014, tested according to detection method GB/T 4851-84
Hold viscosity energy tests initial cohesiveness according to examination criteria GB/T 4852-2002 (rolling ball method), and test result is as follows:
2 gluing performance test of table
From test result as can be seen that the initial cohesiveness of comprehensive performance emphasis article gummed tape of the invention is than general glue
Band wants high 2~3 ball numbers and hold viscosity energy to be all larger than 24 hours, illustrates to can be good at binder in packaging applications
Product simultaneously keep tacky state for a long time, and 180 ° of peel strengths belong to adhesive viscosity peel strength in 16N/25mm or so,
It can tear easily when unloading packaging.
3, according to testing standard method GB/T 33375-2016 test tape antistatic property, test result is as follows shown in table:
3 antistatic performance test of table
| Project | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Surface electrostatic pressure (unit: KV) | 5.1 | 5.3 | 5.4 |
It can be seen that comprehensive performance emphasis article gummed tape of the invention, surface electrostatic voltage from test result above
In 5.3KV or so, indicate that there is good antistatic property.
The present invention and its embodiments have been described above, this description is no restricted, shown in the drawings
Only one of embodiments of the present invention, actual structure is not limited to this.All in all if the ordinary skill of this field
Personnel are enlightened by it, without departing from the spirit of the invention, are not inventively designed and the technical solution phase
As frame mode and embodiment, be within the scope of protection of the invention.
Claims (9)
1. a kind of comprehensive performance emphasis article gummed tape, it is characterised in that: including bracing ring and be wound in narrow on bracing ring
Tape body, wide tape body, the narrow tape body, wide tape body structure are identical, and the narrow tape body includes the substrate set gradually
Layer, antistatic backing, the first barrier layer, the first adhesive layer, the second barrier layer, flame-retardant layer, toughening layer, the second adhesive layer, institute
It states the first gluing oxidant layer two sides and is additionally provided with polynorbornene sheet layer.
2. a kind of comprehensive performance emphasis article gummed tape according to claim 1, it is characterised in that: the substrate layer is
Composite layer is combined by PET and foam material.
3. a kind of comprehensive performance emphasis article gummed tape according to claim 1, it is characterised in that: the toughening layer packet
Include the pure metal layer set gradually, adsorption layer, except oxygen layer.
4. a kind of comprehensive performance emphasis article gummed tape according to claim 1, it is characterised in that: the gluing oxidant layer
For modified silicon rubber adhesive layer.
5. a kind of comprehensive performance emphasis article gummed tape according to claim 1, it is characterised in that: the adhesive layer
With a thickness of 0.1-0.3mm.
6. a kind of comprehensive performance emphasis article gummed tape according to claim 2, it is characterised in that: the pure metal layer
With a thickness of 0.2-0.4mm.
7. a kind of comprehensive performance emphasis article gummed tape according to claim 1, it is characterised in that: the bracing ring
With a thickness of 0.2-0.5mm.
8. a kind of comprehensive performance emphasis article gummed tape according to claim 1, it is characterised in that: the toughening layer
With a thickness of 0.6-1mm.
9. a kind of comprehensive performance emphasis article gummed tape according to claim 1, production method, including following step
It is rapid:
(1) be PET by ingredient, the base of foam material expects that machine-shaping forms substrate layer；
It (2) is from antistatic acrylic film or antistatic polychloroethylene film or antistatic polycarbonate membrane or to prevent quiet by ingredient
The antistatic material of voltolisation diethyl terephthalate film is processed into antistatic backing and is covered on substrate layer；
(3) it is covered on the antistatic backing on the first barrier layer；
(4) the first gluing oxidant layer is made in the modified silicon rubber bonding agent of deployed viscosity to be covered on the first barrier layer, wherein
First gluing oxidant layer two sides are also covered with polynorbornene sheet layer respectively；
(5) the second barrier layer is covered in the first gluing oxidant layer；
(6) flame-retardant layer is covered on the second barrier layer；
(7) toughening layer is covered on flame-retardant layer, wherein toughening layer includes metal layer, adsorption layer, except oxygen layer, and metal layer is using gold
The mode for belonging to spraying or hot dip metal coating is arranged on flame-retardant layer, and adsorption layer is all made of hot pressing technique preparation except oxygen layer
It forms, wherein adsorption layer is prepared by nano material, except oxygen layer is prepared by sponge iron；
(8) the modified silicon rubber bonding agent of deployed viscosity is made on the second gluing oxidant layer covering toughening layer.