CN109722042A - Cde(硅藻复合)沥青改性剂及其硅改沥青制备方法 - Google Patents
Cde(硅藻复合)沥青改性剂及其硅改沥青制备方法 Download PDFInfo
- Publication number
- CN109722042A CN109722042A CN201711371215.4A CN201711371215A CN109722042A CN 109722042 A CN109722042 A CN 109722042A CN 201711371215 A CN201711371215 A CN 201711371215A CN 109722042 A CN109722042 A CN 109722042A
- Authority
- CN
- China
- Prior art keywords
- asphalt
- cde
- road
- pitch
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是一种用于道路的CDE(硅藻复合)沥青改性剂及其硅改沥青制备方法。这种改性方法是由路用普通沥青加温到160~170℃之后,添加硅藻复合沥青改性剂搅拌20min使沥青与改性剂混合均匀而制得。将此改性沥青加入到拌合沥青混凝土的混合料之中,加温到160~170℃即可成为改性沥青混凝土,可用于各种道路沥青路面摊铺施工。本发明CDE(硅藻复合)改性沥青用于道路沥青路面能使沥青路面70℃高温不泛油、不软化,‑37℃低温不脆变,高温稳定性、低温抗裂性显著改善,提高抗水害能力、避免早期损坏,使道路耐磨、抗滑、亚光,从而提高道路使用寿命和加强行车安全。本发明产品,价格低廉、工艺简单、操作方便,是一种经济实用的完全本土资源、国产化的改性沥青。
Description
技术领域
本发明涉及一种用于道路的国内本土资源高性能改性沥青。
背景技术
沥青是一种典型的粘弹性材料,其温度敏感性的好坏和对于集料配入的适应性能,直接影响其路用效果。为了降低沥青的温度敏感性和提高其对集料的适应性,提高沥青的高温稳定性、低温抗裂性、以及水稳性、抗疲劳、抗老化性能,通常采用沥青改性技术,其中应用最广的是用SBS(苯乙烯—丁二烯—苯乙烯嵌段共聚物)做沥青改性剂,或加工为SBS改性沥青。用SBS改性沥青虽然能显著提高沥青的高温稳定性和低温抗裂性及水稳性,但价格昂贵,改性工艺复杂,设备投资大,且易发生离折,对沥青混凝土集料配伍的适应性有所受限,因此推广应用受到限制。
发明内容
本发明的目的是:提供一种原料来源广、价格低、工艺简单,路用效果好的、以廉价无机矿替代昂贵高分子聚合物制备的改性沥青。用此复合CDE硅改沥青,沥青的粘附性特别好,SiO2>85%~90%的酸性集料,不必使用抗剥落剂,可避免沥青早期疲劳老化,粘附性可达到5级,并且高温70℃不软化,低气温-37℃不脆变、耐久性好,能大幅延长沥青路面使用寿命。
本发明是这样实现的:它是用未经改性的普通路用沥青加温至160~170℃掺入硅藻复合沥青改性剂在相应容器内适宜搅拌而成。
本发明改性沥青的制备方法是:用未经改性的路用普通沥青经试验检测确认合格,将所需普通沥青在一般沥青加温容器内加温至160~170℃后加入硅藻复合沥青改性剂(沥青用量)10%~15%,其中改性剂含煅烧提纯硅藻土30%~52%,偏高岭石12%~15%,硫磺15%~25%,氢氧化钙20%~30%,硅酸盐5%~10%,天然岩沥青30%~48%。
本CDE(硅藻复合)沥青改性剂及其硅改沥青制备方法是:路用普通沥青必须经试验检验合格,改性剂必须烘干使水分≤2%,可现场加工随制随用,不能在温度≤120℃长时停放,用时必须在达到高温≥160℃~170℃时搅拌均匀。制备改性沥青混凝土必须经过配合比设计试验,取最佳油石比和最佳掺配量再进行试验检测,以免发生配合比不佳而影响改性沥青实际效果。
用本发明制得的改性沥青有如下优点:(1)原料来源广,价格低于SBS约50%,全是国内本土就地取材廉价资源,生产和应用工艺都较为简单,不需要增添设备,符合中国国情;(2)可取代等量沥青,降低生产成本;(3)复配的硅藻土吸附性极好,能吸附沥青加热过程中散发出的有毒、有害气体,有利于工人身体健康和环境保护;(4)用CDE改性沥青铺的路面抗滑、耐磨、亚光、吸热量降低20%~35%,导热系数下降40%~50%,因此温度敏感性大大降低,致使路面夏天不泛油,冬天不脆变,能大大提高公路使用寿命和行车安全;(5)主要路用功能技术指标动稳定度可达到4000~6400次/mm,可高于国家《规范》(JTGF40-2004)要求1~2倍以上。
Claims (4)
1.一种用于道路的CDE(硅藻复合)沥青改性剂及其硅改沥青制备方法,其特征在于这种改性沥青由普通沥青加入经过煅烧提纯的硅藻土(Diatomite Earth简称DE)经过复合(complex简称c)配入偏高岭石、硫磺、氢氧化钙、硅酸盐、天然岩沥青五种矿物,制成沥青改性剂(简称改性剂),在将未经改性的普通路用沥青加温至160~170℃时,添加入改性剂适宜搅拌后即制成CDE(硅藻复合)硅改沥青,简称CDE改性沥青。
2.根据权利1所述的一种用于道路的CDE(硅藻复合)沥青改性剂及其硅改沥青制备方法,其特征在于普通沥青88%,配入改性剂12%,改性剂含硅藻土30%~52%、偏高岭石12%~15%、硫磺15%~25%、氢氧化钙20%~30%、硅酸盐5%~10%、天然岩沥青30%~48%。
3.根据权利1所述的一种用于道路的CDE(硅藻复合)沥青改性剂及其硅改沥青制备方法,其特征在于普通沥青加入改性剂制成CDE改性沥青后,沥青的马歇尔稳定度、浸水残留稳定度、冻融劈裂、抗疲劳性能都有显著提高,动稳定度技术指标提高100%~500%。
4.根据权利1所述的一种用于道路的CDE(硅藻复合)沥青改性剂及其硅改沥青制备方法,其特征在于可以在施工现场配制使用,也可以在工厂加工快速冷却降温至100℃以下远距离运输储备使用。