CN109719418A - 核电20控铬钢专用焊丝 - Google Patents

核电20控铬钢专用焊丝 Download PDF

Info

Publication number
CN109719418A
CN109719418A CN201811651223.9A CN201811651223A CN109719418A CN 109719418 A CN109719418 A CN 109719418A CN 201811651223 A CN201811651223 A CN 201811651223A CN 109719418 A CN109719418 A CN 109719418A
Authority
CN
China
Prior art keywords
content
chromium steel
core wire
nuclear power
surplus
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811651223.9A
Other languages
English (en)
Inventor
徐亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Xinpu New Material Technology Co Ltd
Original Assignee
Suzhou Xinpu New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Xinpu New Material Technology Co Ltd filed Critical Suzhou Xinpu New Material Technology Co Ltd
Priority to CN201811651223.9A priority Critical patent/CN109719418A/zh
Publication of CN109719418A publication Critical patent/CN109719418A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种核电20控铬钢专用焊丝，包括焊芯和涂覆在所述焊芯上的药皮，以质量分数表示，所述焊芯的组成成分及含量为：C含量0.0%5~0.08%、Si含量0.75%~0.8%、Mn含量1%~1.2%、P含量0.001%~0.01%、S含量0.001%~0.015%、Ni含量0.1%~0.18%、Cr含量0.2%~0.35%、Mo含量0.001%~0.01%、Cu含量0.001%~0.2%、Ti含量0.18%~0.22%、Mg含量0.03%~0.04%，余量为Fe；所述药皮组成成分及含量为：大理石30%~35%、萤石15%~25%、电解锰5%~10%、海藻酸钠0.5%~1.2%、铜粉0.1%~0.3%、钛白粉0.1%~0.5%、余量为铁粉。通过上述方式，本发明能够满足核电20控铬钢焊接的要求，使用其完成20控铬钢焊缝的抗FAC性能有显著提高。

Description

核电20控铬钢专用焊丝
技术领域
本发明涉及焊接材料技术领域，特别是涉及一种核电20控铬钢专用焊丝。
背景技术
20控铬钢是CPR1000压谁堆核电站国产化过程中开发的钢种，在碳素钢中加入一定含量的铬元素提高管道的抗流体加速腐蚀性能（即抗FAC性能），是CPR1000型核电站常规的主要使用钢材之一。
根据现有的研究资料，碳钢中FAC的腐蚀速率取决于介质温度、流速、pH值、电极电位、管材合金元素、热力学等因素，其中管材合金元素是可以通过选择钢种成分来解决的。经研究表明，在碳钢中增加Cr含量可以明显降低FAC的腐蚀速率。20控铬钢就是在此背景下开发的具有较高抗FAC性能的新钢种。
发明内容
本发明主要解决的技术问题是提供一种核电20控铬钢专用焊丝，能够保证核电项目中20控铬钢的焊接要求。
为解决上述技术问题，本发明采用的一个技术方案是：
提供一种核电20控铬钢专用焊丝，包括焊芯和涂覆在所述焊芯上的药皮，以质量分数表示，所述焊芯的组成成分及含量为：C含量0.0%5~0.08%、Si含量0.75%~0.8%、Mn含量1%~1.2%、P含量0.001%~0.01%、S含量0.001%~0.015%、Ni含量0.1%~0.18%、Cr含量0.2%~0.35%、Mo含量0.001%~0.01%、Cu含量0.001%~0.2%、Ti含量0.18%~0.22%、Mg含量0.03%~0.04%，余量为Fe；
所述药皮组成成分及含量为：大理石30%~35%、萤石15%~25%、电解锰5%~10%、海藻酸钠0.5%~1.2%、铜粉0.1%~0.3%、钛白粉0.1%~0.5%、余量为铁粉。
在本发明一个较佳实施例中，所述焊芯与所述药皮之间的质量比为2:1~7:3。
在本发明一个较佳实施例中，所述焊丝的规格为φ1.0~2.0。
在本发明一个较佳实施例中，一种核电20控铬钢专用焊丝，包括焊芯和涂覆在所述焊芯上的药皮，以质量分数表示，所述焊芯的组成成分及含量为：C含量0.06%、Si含量0.75%、Mn含量1.1%、P含量0.0051%、S含量0.001%、Ni含量0.12%、Cr含量0.28%、Mo含量0.005%、Cu含量0.0015%、Ti含量0.18%、Mg含量0.03%，余量为Fe；
所述药皮组成成分及含量为：大理石32%、萤石18%、电解锰8%、海藻酸钠0.8%、铜粉0.15%、钛白粉0.3%、余量为铁粉。
在本发明一个较佳实施例中，一种核电20控铬钢专用焊丝，包括焊芯和涂覆在所述焊芯上的药皮，以质量分数表示，所述焊芯的组成成分及含量为：C含量 0.08%、Si含量0.78%、Mn含量1.2%、P含量0.005%、S含量0.0013%、Ni含量0.18%、Cr含量0.28%、Mo含量0.005%、Cu含量0.2%、Ti含量0.2%、Mg含量0.04%，余量为Fe；
所述药皮组成成分及含量为：大理石35%、萤石20%、电解锰8%、海藻酸钠0.8%、铜粉0.3%、钛白粉0.3%、余量为铁粉。
本发明的有益效果是：本发明核电20控铬钢专用焊丝，能够满足核电20控铬钢焊接的要求，使用其完成20控铬钢焊缝的抗FAC性能有显著提高，确保了核电站中20控铬钢焊缝在运营过程中的质量，对核电机组的安全运行有重要意义。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例1：一种核电20控铬钢专用焊丝，包括焊芯和涂覆在所述焊芯上的药皮，以质量分数表示，所述焊芯的组成成分及含量为：C含量0.06%、Si含量0.75%、Mn含量1.1%、P含量0.0051%、S含量0.001%、Ni含量0.12%、Cr含量0.28%、Mo含量0.005%、Cu含量0.0015%、Ti含量0.18%、Mg含量0.03%，余量为Fe；
所述药皮组成成分及含量为：大理石32%、萤石18%、电解锰8%、海藻酸钠0.8%、铜粉0.15%、钛白粉0.3%、余量为铁粉。
实施例2：一种核电20控铬钢专用焊丝，包括焊芯和涂覆在所述焊芯上的药皮，以质量分数表示，所述焊芯的组成成分及含量为：C含量 0.08%、Si含量0.78%、Mn含量1.2%、P含量0.005%、S含量0.0013%、Ni含量0.18%、Cr含量0.28%、Mo含量0.005%、Cu含量0.2%、Ti含量0.2%、Mg含量0.04%，余量为Fe；
所述药皮组成成分及含量为：大理石35%、萤石20%、电解锰8%、海藻酸钠0.8%、铜粉0.3%、钛白粉0.3%、余量为铁粉。
实施例3：一种核电20控铬钢专用焊丝，包括焊芯和涂覆在所述焊芯上的药皮，以质量分数表示，所述焊芯的组成成分及含量为：C含量0.05%~0.08%、Si含量0.8%、Mn含量1.2%、P含量0.008%、S含量0.012%、Ni含量0.15%、Cr含量0.3%、Mo含量0.005%、Cu含量0.002%、Ti含量0.2%、Mg含量0.04%，余量为Fe；
所述药皮组成成分及含量为：大理石32%、萤石18%、电解锰10%、海藻酸钠1.0%、铜粉0.2%、钛白粉0.5%、余量为铁粉。
下表为实施例1-3焊丝熔敷金属的力学性能。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (5)

1.一种核电20控铬钢专用焊丝，其特征在于，包括焊芯和涂覆在所述焊芯上的药皮，以质量分数表示，所述焊芯的组成成分及含量为：C含量0.05%~0.08%、Si含量0.75%~0.8%、Mn含量1%~1.2%、P含量0.001%~0.01%、S含量0.001%~0.015%、Ni含量0.1%~0.18%、Cr含量0.2%~0.35%、Mo含量0.001%~0.01%、Cu含量0.001%~0.2%、Ti含量0.18%~0.22%、Mg含量0.03%~0.04%，余量为Fe；
所述药皮组成成分及含量为：大理石30%~35%、萤石15%~25%、电解锰5%~10%、海藻酸钠0.5%~1.2%、铜粉0.1%~0.3%、钛白粉0.1%~0.5%、余量为铁粉。
2.根据权利要求1所述的核电20控铬钢专用焊丝，其特征在于，所述焊芯与所述药皮之间的质量比为2:1~7:3。
3.根据权利要求1所述的核电20控铬钢专用焊丝，其特征在于，所述焊丝的规格为φ1.0~2.0。
4.根据权利要求1所述的核电20控铬钢专用焊丝，其特征在于，以质量分数表示，所述焊芯的组成成分及含量为：C含量0.06%、Si含量0.75%、Mn含量1.1%、P含量0.0051%、S含量0.001%、Ni含量0.12%、Cr含量0.28%、Mo含量0.005%、Cu含量0.0015%、Ti含量0.18%、Mg含量0.03%，余量为Fe；
所述药皮组成成分及含量为：大理石32%、萤石18%、电解锰8%、海藻酸钠0.8%、铜粉0.15%、钛白粉0.3%、余量为铁粉。
5.根据权利要求1所述的核电20控铬钢专用焊丝，其特征在于，以质量分数表示，所述焊芯的组成成分及含量为：C含量 0.08%、Si含量0.78%、Mn含量1.2%、P含量0.005%、S含量0.0013%、Ni含量0.18%、Cr含量0.28%、Mo含量0.005%、Cu含量0.2%、Ti含量0.2%、Mg含量0.04%，余量为Fe；
所述药皮组成成分及含量为：大理石35%、萤石20%、电解锰8%、海藻酸钠0.8%、铜粉0.3%、钛白粉0.3%、余量为铁粉。
CN201811651223.9A 2018-12-31 2018-12-31 核电20控铬钢专用焊丝 Pending CN109719418A (zh)