CN109719154A - A kind of processing technology of band steel - Google Patents
A kind of processing technology of band steel Download PDFInfo
- Publication number
- CN109719154A CN109719154A CN201711022483.5A CN201711022483A CN109719154A CN 109719154 A CN109719154 A CN 109719154A CN 201711022483 A CN201711022483 A CN 201711022483A CN 109719154 A CN109719154 A CN 109719154A
- Authority
- CN
- China
- Prior art keywords
- steel
- cold
- drawn
- band steel
- saponification process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses processing steps such as a kind of processing technologys of band steel, including storage, heat treatment, ball blast, cold rolling, phosphorus saponification process, cold-drawn, secondary heat treatment, secondary cold-drawn and packaging, the phosphorus content of steel is no more than 1.5%;Band steel of the invention is uniform in material, with a thickness of 10-30mm, yield strength >=310, tensile strength 400-430, elongation percentage >=25%.
Description
Technical field
The invention belongs to steel processing technique field, the processing technology of specifically a kind of band steel.
Background technique
Band steel is finger beam 12-300mm, thickness 4-60mm, section for rectangle and slightly with the steel of root face.The material of band steel
Mainly there are structural carbon steel, carbon constructional quality steel, low-alloy high-tensile structural steel.Band steel can be finished steel, can also be with
Do the blank of welded tube and the sheet billet of pack-rolled sheet.Band steel, which can be used as to become a useful person, can be used for hoop-iron, tool and machine components processed,
It is used as room frame structural member, staircase in building.
Summary of the invention
It is an object of the invention to provide a kind of processing technologys of band steel.
A kind of processing technology of band steel of the invention, comprising the following steps:
(1) it is put in storage: checking steel, and by qualified material storage;
(2) be heat-treated: control hardening heat is 860-890 DEG C, and 480-500 DEG C of tempering temperature, quenching oil temperature control is in 20-60
℃;
(3) ball blast: carrying out Shot Blasting to the oxide layer of steel surface, and the bullet that diameter is 0.2~3.0mm is thrown to workpiece
Surface makes the surface of workpiece reach certain roughness;
(4) cold rolling: successively carrying out pickling, rolling, degreasing, annealing and finishing to steel, steel with a thickness of 10- after cold rolling
30mm;
(5) phosphorus saponification process: by the steel elder generation phosphatization after cold rolling, then carrying out saponification process, is washed after the completion of saponification process with clear water
And it is dry, it takes the lead after dry;
(6) cold-drawn: steel are cooled to room temperature, and carry out drawing using drawbench, modification amount must not exceed the 10% of raw material;
(7) secondary heat treatment: control hardening heat is 600-630 DEG C, and 300-320 DEG C of tempering temperature, quenching oil temperature control exists
30-50℃;
(8) secondary cold-drawn: steel are cooled to room temperature, and carry out redraing using drawbench, modification amount must not exceed raw material
5%;
(9) pack: the band steel after secondary cold-drawn is cut off, is aligned, packaging.
Preferably, the phosphorus content of heretofore described steel is no more than 1.5%.
Band steel of the invention is uniform in material, and with a thickness of 10-30mm, yield strength >=310, tensile strength 400-430 prolongs
Stretch rate >=25%.
Specific embodiment
Embodiment 1
A kind of processing technology of the band steel of the present embodiment, comprising the following steps:
(1) it is put in storage: checking steel, and by qualified material storage;
(2) be heat-treated: control hardening heat is 880 DEG C, and 490 DEG C of tempering temperature, quenching oil temperature control is at 50 DEG C;
(3) ball blast: carrying out Shot Blasting to the oxide layer of steel surface, the bullet that diameter is 1.8mm thrown to the surface of workpiece,
The surface of workpiece is set to reach certain roughness;
(4) cold rolling: successively carrying out pickling, rolling, degreasing, annealing and finishing to steel, steel with a thickness of 26mm after cold rolling;
(5) phosphorus saponification process: by the steel elder generation phosphatization after cold rolling, then carrying out saponification process, is washed after the completion of saponification process with clear water
And it is dry, it takes the lead after dry;
(6) cold-drawn: steel are cooled to room temperature, and carry out drawing using drawbench, modification amount must not exceed the 10% of raw material;
(7) secondary heat treatment: control hardening heat is 620 DEG C, and 310 DEG C of tempering temperature, quenching oil temperature control is at 40 DEG C;
(8) secondary cold-drawn: steel are cooled to room temperature, and carry out redraing using drawbench, modification amount must not exceed raw material
5%;
(9) pack: the band steel after secondary cold-drawn is cut off, is aligned, packaging.
The phosphorus content of steel described in the present embodiment is 1.36%.
Embodiment 2
A kind of processing technology of the band steel of the present embodiment, comprising the following steps:
(1) it is put in storage: checking steel, and by qualified material storage;
(2) be heat-treated: control hardening heat is 860 DEG C, and 480 DEG C of tempering temperature, quenching oil temperature control is at 20 DEG C;
(3) ball blast: carrying out Shot Blasting to the oxide layer of steel surface, the bullet that diameter is 0.2mm thrown to the surface of workpiece,
The surface of workpiece is set to reach certain roughness;
(4) cold rolling: successively carrying out pickling, rolling, degreasing, annealing and finishing to steel, steel with a thickness of 10mm after cold rolling;
(5) phosphorus saponification process: by the steel elder generation phosphatization after cold rolling, then carrying out saponification process, is washed after the completion of saponification process with clear water
And it is dry, it takes the lead after dry;
(6) cold-drawn: steel are cooled to room temperature, and carry out drawing using drawbench, modification amount must not exceed the 10% of raw material;
(7) secondary heat treatment: control hardening heat is 600 DEG C, and 300 DEG C of tempering temperature, quenching oil temperature control is at 30 DEG C;
(8) secondary cold-drawn: steel are cooled to room temperature, and carry out redraing using drawbench, modification amount must not exceed raw material
5%;
(9) pack: the band steel after secondary cold-drawn is cut off, is aligned, packaging.
The phosphorus content of steel described in the present embodiment is 1.28%.
Embodiment 3
A kind of processing technology of the band steel of the present embodiment, comprising the following steps:
(1) it is put in storage: checking steel, and by qualified material storage;
(2) be heat-treated: control hardening heat is 890 DEG C, and 500 DEG C of tempering temperature, quenching oil temperature control is at 60 DEG C;
(3) ball blast: carrying out Shot Blasting to the oxide layer of steel surface, the bullet that diameter is 3.0mm thrown to the surface of workpiece,
The surface of workpiece is set to reach certain roughness;
(4) cold rolling: successively carrying out pickling, rolling, degreasing, annealing and finishing to steel, steel with a thickness of 30mm after cold rolling;
(5) phosphorus saponification process: by the steel elder generation phosphatization after cold rolling, then carrying out saponification process, is washed after the completion of saponification process with clear water
And it is dry, it takes the lead after dry;
(6) cold-drawn: steel are cooled to room temperature, and carry out drawing using drawbench, modification amount must not exceed the 10% of raw material;
(7) secondary heat treatment: control hardening heat is 630 DEG C, and 320 DEG C of tempering temperature, quenching oil temperature control is at 50 DEG C;
(8) secondary cold-drawn: steel are cooled to room temperature, and carry out redraing using drawbench, modification amount must not exceed raw material
5%;
(9) pack: the band steel after secondary cold-drawn is cut off, is aligned, packaging.
The phosphorus content of steel described in the present embodiment is 1.07%.
Claims (2)
1. a kind of processing technology of band steel, it is characterised in that the following steps are included:
(1) it is put in storage: checking steel, and by qualified material storage;
(2) be heat-treated: control hardening heat is 860-890 DEG C, and 480-500 DEG C of tempering temperature, quenching oil temperature control is in 20-60
℃;
(3) ball blast: carrying out Shot Blasting to the oxide layer of steel surface, and the bullet that diameter is 0.2~3.0mm is thrown to workpiece
Surface makes the surface of workpiece reach certain roughness;
(4) cold rolling: successively carrying out pickling, rolling, degreasing, annealing and finishing to steel, steel with a thickness of 10- after cold rolling
30mm;
(5) phosphorus saponification process: by the steel elder generation phosphatization after cold rolling, then carrying out saponification process, is washed after the completion of saponification process with clear water
And it is dry, it takes the lead after dry;
(6) cold-drawn: steel are cooled to room temperature, and carry out drawing using drawbench, modification amount must not exceed the 10% of raw material;
(7) secondary heat treatment: control hardening heat is 600-630 DEG C, and 300-320 DEG C of tempering temperature, quenching oil temperature control exists
30-50℃;
(8) secondary cold-drawn: steel are cooled to room temperature, and carry out redraing using drawbench, modification amount must not exceed raw material
5%;
(9) pack: the band steel after secondary cold-drawn is cut off, is aligned, packaging.
2. a kind of processing technology of band steel according to claim 1, it is characterised in that: the phosphorus content of the steel is no more than
1.5%。