CN109705374A - A kind of preparation method of liquid xanthan gum - Google Patents
A kind of preparation method of liquid xanthan gum Download PDFInfo
- Publication number
- CN109705374A CN109705374A CN201811551989.XA CN201811551989A CN109705374A CN 109705374 A CN109705374 A CN 109705374A CN 201811551989 A CN201811551989 A CN 201811551989A CN 109705374 A CN109705374 A CN 109705374A
- Authority
- CN
- China
- Prior art keywords
- xanthan gum
- liquid
- selection
- preparation
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the applied technical fields of xanthan gum, disclose a kind of preparation method of liquid xanthan gum, and selection (2) raw material including (1) raw material weighs and three steps of preparation of (3) liquid xanthan gum.The present invention utilizes the emulsifiability of xanthan gum itself, adds it in mixed solvent system, prepares good fluidity, finely dispersed liquid xanthan gum.The present invention overcomes the problems such as slow solid powder xanthan gum dissolution, easy to knot groups, and shortens the setup time of xanthan gum solution, and entire preparation and use process time-consuming are short, convenient and efficient.The liquid xanthan gum that the present invention prepares shows its huge development potentiality and good application effect as a kind of novel oilfield chemical assistant, also widens application of the xanthan gum in China's oilfield chemistry operation.
Description
Technical field
The invention belongs to the applied technical fields of xanthan gum, and in particular to a kind of preparation method of liquid xanthan gum.
Background technique
Xanthan gum (Xanthan Gum) is that integrate emulsification, thickening, the microorganism of suspending stabilized superior performance high
Molecular polysaccharide.Since it is in polyanion state in aqueous solution, can be dissolved in hot water or cold water;And its conformation is also
It is diversified, it can express different characteristics at different conditions, there is unique physicochemical property, therefore in food, medicine, stone
Multiple industries such as oily industry and cosmetics, are widely used.However existing xanthan gum is solid powder substance, is made
It is long with dissolution time in the process, it is easy to produce conglomeration, operation is relatively complicated, and the scene for being not easy to be well adapted for oil drilling is answered
With also resulting in the problems such as recovery ratio recovered the oil in application process is low in this way.Therefore these problems are directed to, we are badly in need of developing one
Kind of liquid xanthan gum, with its dissolution sufficiently, without flake, temperature tolerance is good, the strong excellent performance of suspending power, using oil as carrier, more
It is mixed with well-drilling waste water, rejected well drilling liquid and drilling cuttings etc. well, is applied to drilling fluid, to solve the problems, such as in drilling well, improved and bore
Well efficiency.
The improvement that Many researchers all carry out different modes to xanthan gum at present is explored, to overcome some of itself to lack
It falls into, improves application.Chinese patent literature CN106833562A discloses a kind of xanthan gum liquid dispersion and preparation method thereof:
When using xanthan gum liquid dispersion, it is mixed with water, xanthan gum can rapid dispersion in water, it is existing that conglomeration will not be generated
As, the time of configuration xanthan gum solution is significantly shortened, it is convenient and efficient;And fugitive dust will not be led to the problem of, pollution-free, healthy ring
It protects.The preparation method process of this xanthan gum liquid dispersion is short, at low cost, efficient quick.In addition, liquid xanthan gum is probed into selection
To a variety of brills such as diesel oil-clear water system, crude oil-polymer drilling fluid system and crude oil-sulphonated polymer mud oil-in-water drilling fluids
The influence of well liquid system performance, prepares liquid xanthan gum polysulfonate oil-in-water drilling fluid system formulation, which compares
Good, site construction technology is relatively simple, and has heatproof, antiacid alkali, excellent tackifying, and play certain filtrate reducing
With good compatibility.Deep-well and ultradeep well downhole formation situation are complicated at present, and bottom hole temperature (BHT) is high, therefore are suitble to yellow using liquid
Virgin rubber handles drilling fluid.Liquid xanthan gum is widely used, but the application in China Petroleum also needs more, deeper time
Exploration and research (normal Gansu Province is tight, liquid xanthan gum oil-in-water drilling fluid research, mineral exploration engineering;2015,42(8): 6-12).
Chinese patent literature CN101270166B discloses a kind of preparation method of liquid xanthan gum.Utilize xanthan gum itself
Emulsibility, xanthan gum solid matter is added to prepare liquid xanthan gum in the mixture of both diesel oil and paraffin oil.
This liquid xanthan gum stability is good, and simple process, easy to operate, and can solve ordinary xanthan gums cannot be directly used to petroleum drilling
The problem of oil-base mud, is with a wide range of applications in well.
Although many documents all do improvement to xanthan gum and probe into, to achieve the purpose that Properties of Optimization, expand application range,
But still there are many problems in the liquid xanthan gum of improvement, as stability is poor, poor fluidity etc. deficiency.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides the preparation method and application of a kind of liquid xanthan gum.
Technical scheme is as follows:
A kind of preparation method of liquid xanthan gum, which is characterized in that described method includes following steps: (1) selection of raw material,
(2) raw material weighs, the preparation of (3) liquid xanthan gum.
Further, described method includes following steps:
(1) selection of raw material
The following one or more kinds of substances of main solvent selection: mineral oil, diesel oil, kerosene, C6-C12Alcohol, vegetable oil;
The following one or more kinds of substances of suspending agent selection: hydroxypropyl methyl cellulose, hydroxy butyl methyl cellulose, organic glutinous
Soil;
Dispersing agent selects polyalcohol ethers;
Optionally, thinner;
(2) raw material weighs
Xanthan gum 20-75%, main solvent 30-65%, suspending agent 0.10-1.20%, dispersing agent 0.50-1.50%, thinner 0.10-
0.80%, the sum of weight percentage of the above component is 100%;
(3) preparation of liquid xanthan gum
Suspending agent and main solvent are mixed, dispersing agent is added in whipping process, is mixed evenly, by weighed xanthan
Glue is uniformly mixed with above-mentioned system, forms the liquid xanthan gum, and xanthan gum additive amount is the 20- of entire mixed system quality
75%。
Further, described method includes following steps:
(1) selection of raw material
The following one or more kinds of substances of main solvent selection: mineral oil, diesel oil, kerosene, C6-C12Alcohol, vegetable oil;
The following one or more kinds of substances of suspending agent selection: hydroxypropyl methyl cellulose, hydroxy butyl methyl cellulose, organic glutinous
Soil;
The following one or more kinds of substances of dispersing agent selection: polyalcohol ethers;
And thinner;
(2) raw material weighs
Xanthan gum 30-55%, main solvent 30-65%, suspending agent 0.10-1.20%, dispersing agent 0.50-1.50%, thinner 0.10-
0.80%, the sum of weight percentage of the above component is 100%;
(3) preparation of liquid xanthan gum
Suspending agent and main solvent are mixed, dispersing agent is added in whipping process, thinner is added after being uniformly dispersed, is mixed
It stirs evenly, weighed xanthan gum is uniformly mixed with above-mentioned system, form the liquid xanthan gum, xanthan gum additive amount is whole
The 30-55% of a mixed system quality.
Preferably,
The organic clay is selected from the mixture of bentonite, montmorillonite, bentonite or above-mentioned any the two or more.
Preferably,
The polyalcohol ethers is selected from ethylene glycol, polyethylene glycol, glycerine, ethylene glycol monobutyl ether or above-mentioned any the two or more
Mixture.
Preferably,
The thinner is selected from lecithin or lignosulfonates.
Preferably,
The main solvent is the mixture of mineral oil, diesel oil, octanol, ethyl alcohol or above-mentioned any the two or more.
Preferably,
The polyalcohol ethers is selected from the mixture of glycerine, ethylene glycol monobutyl ether or said two devices.
Preferably,
The partial size of the xanthan gum is 200 mesh or more.
Main solvent plays the role of dispersing xanthan gum in the present invention, and dispersing agent can increase solubility property, and suspending agent guarantees to produce
The stability of product prevents from precipitating;Whole system guarantees Product Status stable homogeneous, and the holding time is long, can reach 12 months or more.
This product can be applied in the field that various aspects need aqueous polymers, be particularly suitable in field use.Liquid xanthan gum
Dosage and formula determined according to the final usage amount in required environment.When using high concentration polymer slurries, in stirring bar
It is mixed into water and uses under part.
Compared with prior art, beneficial effects of the present invention mainly include but is not limited to the following aspects:
1, the present invention prepares the good liquid xanthan gum of stability using the emulsifiability of xanthan gum itself, system stable homogeneous,
Good flowing properties solve the problems, such as that xanthan gum of the existing technology cannot be directly used to oil-base mud in oil drilling, system
Standby process is simple.
2, the existing way of xanthan gum of the present invention is the liquid condition that mass percentage is 30-55%, in use, liquid
Xanthan gum is mixed with water, and water solubility improves obviously, can rapidly dissolve in water, will not lead to the problem of conglomeration flake, convenient fast
It is prompt;Process is easily controllable.
3, the formula that the present invention selects can't change the double-spiral structure of xanthan gum, additionally it is possible between xanthan molecules
Electrostatic attraction is formed, viscosity is also promoted, prompts have preferable synergistic effect between recipe ingredient of the invention.
4, the present invention have simple process, easy to operate, manufacturing cost is cheap, less cost of power.
Detailed description of the invention
Fig. 1: the state effect picture for the liquid xanthan gum that the present invention synthesizes.
Fig. 2: the mobile performance effect picture of liquid xanthan gum in the present invention.
Specific embodiment
Those skilled in the art can use for reference present disclosure, be suitably modified realization of process parameters.In particular, it should be pointed out that
All similar substitutions and modifications are apparent to those skilled in the art, they are considered as being included in this hair
It is bright.Product and method of the invention is described by preferred embodiment, and related personnel can obviously not depart from this hair
Product as described herein and method are modified in bright content, spirit and scope or appropriate changes and combinations, to realize and answer
Use the technology of the present invention.For a further understanding of the present invention, the following describes the present invention in detail with reference to examples.
The raw materials used in the present invention is conventional raw material, commercial products.Xanthan gum derives from the limited public affairs of Shandong Fu Feng biofermentation
Department.
Embodiment 1
A kind of preparation method of liquid xanthan gum, steps are as follows:
(1) selection of raw material
Select mineral oil for main solvent and ethyl alcohol;Organic clay is suspending agent;Glycerine is dispersing agent;Thinner is lecithin.
(2) raw material weighs
Xanthan gum 45%, main solvent mineral oil 48%, suspending agent organic clay 1.0%, dispersing agent glycerine 1.2%, thinner lecithin
Rouge 0.12%, surplus are ethyl alcohol, and the sum of weight percent content of the above component is 100%.
(3) preparation of liquid xanthan gum
Selected suspending agent and main solvent are mixed, quantitative dispersing agent is added in whipping process, after being uniformly dispersed
Weighed thinner is added, is mixed evenly, weighed xanthan gum is uniformly mixed with above-mentioned system, it is yellow to form the liquid
Virgin rubber, xanthan gum additional amount are the 45% of entire mixed system quality.
Embodiment 2
A kind of preparation method of liquid xanthan gum, steps are as follows:
(1) selection of raw material
Select octanol and ethyl alcohol for main solvent;Hydroxypropyl methyl cellulose is suspending agent;Ethylene glycol monobutyl ether is dispersing agent;Viscosity reduction
Agent is lecithin.
(2) raw material weighs
Xanthan gum 45%, main solvent octanol 48%, suspending agent hydroxypropyl methyl cellulose 0.12%, dispersing agent ethylene glycol monobutyl ether are
0.6%, thinner lecithin 0.12%, surplus is ethyl alcohol.The sum of weight percentage of the above component is 100%.
(3) preparation of liquid xanthan gum
Selected suspending agent and main solvent are mixed, quantitative dispersing agent is added in whipping process, after being uniformly dispersed
Weighed thinner is added, is mixed evenly, weighed xanthan gum is uniformly mixed with above-mentioned system, it is yellow to form the liquid
Virgin rubber, xanthan gum additional amount are the 45% of entire mixed system quality.
Embodiment 3
A kind of preparation method of liquid xanthan gum, steps are as follows:
(1) selection of raw material
Select octanol and ethyl alcohol for main solvent;Hydroxypropyl methyl cellulose is suspending agent;Glycerine and ethylene glycol monobutyl ether are point
Powder;Thinner is lecithin.
(2) raw material weighs
Xanthan gum 43.0%, main solvent octanol 35.0%, ethyl alcohol 21.0%, suspending agent hydroxypropyl methyl cellulose 0.15%, dispersing agent
Glycerine 0.25%, ethylene glycol monobutyl ether 0.5%, thinner lecithin 0.1%.The sum of the weight percentage of the above component is
100% 。
(3) preparation of liquid xanthan gum
Selected suspending agent and main solvent are mixed, quantitative dispersing agent is added in whipping process, after being uniformly dispersed
Weighed thinner is added, is mixed evenly, weighed xanthan gum is uniformly mixed with above-mentioned system, it is yellow to form the liquid
Virgin rubber, xanthan gum additional amount are the 43% of entire mixed system quality.
Embodiment 4
A kind of preparation method of liquid xanthan gum, steps are as follows:
(1) selection of raw material
Select diesel oil for main solvent, organic clay is suspending agent;Glycerine and ethylene glycol monobutyl ether are dispersing agent;Thinner is preferred
Lecithin.
(2) raw material weighs
Xanthan gum 46%, main solvent diesel oil 52.35%, suspending agent organic clay 0.90%, dispersing agent glycerine 0.2%, ethylene glycol list
Butyl ether 0.55%.The sum of weight percentage of the above component is 100%.
(3) preparation of liquid xanthan gum
Selected suspending agent and main solvent are mixed, quantitative dispersing agent is added in whipping process, by weighed Huang
Virgin rubber is uniformly mixed with above-mentioned system, forms the liquid xanthan gum, and xanthan gum additional amount is entire mixed system quality
46%。
Embodiment 5
A kind of preparation method of liquid xanthan gum, steps are as follows:
(1) selection of raw material
Select diesel oil and ethyl alcohol for main solvent;Hydroxypropyl methyl cellulose is suspending agent;Polyethylene glycol-400 and ethylene glycol only son
Ether is dispersing agent;Thinner is lecithin.
(2) raw material weighs
Xanthan gum 48%, main solvent diesel oil 28%, ethyl alcohol 22.64%, suspending agent are hydroxypropyl methyl cellulose 0.25%, and dispersing agent is poly-
Ethylene glycol -400 is 0.35%, ethylene glycol monobutyl ether 0.3%;Thinner lecithin is 0.46%.The weight percent of the above component contains
The sum of amount is 100%.
(3) preparation of liquid xanthan gum
Selected suspending agent and main solvent are mixed, quantitative dispersing agent is added in whipping process, after being uniformly dispersed
Weighed thinner is added, is mixed evenly, weighed xanthan gum is uniformly mixed with above-mentioned system, it is yellow to form the liquid
Virgin rubber, xanthan gum additional amount are the 48% of entire mixed system quality.
Embodiment 6
The liquid xanthan gum of embodiment 1-5 is put into water respectively, is configured to the solution that xanthan gum concentration is 0.8wt%;Simultaneously
Setting control group: directly putting into xanthan gum in water, is configured to the solution that xanthan gum concentration is 0.8wt%;Specific each performance ginseng
Number is shown in Table 1:
Table 1
Group | Appearance | Viscosity Pa.S(steady-flow experiment) | Complex viscosity (strain sweep) |
Embodiment 1 | Without flake, dissolution is completed in 30s | 1.923 | 4.34 |
Embodiment 2 | Without flake, dissolution is completed in 30s | 1.912 | 4.29 |
Embodiment 3 | Without flake, dissolution is completed in 30s | 1.905 | 4.24 |
Embodiment 4 | Without flake, dissolution is completed in 30s | 1.896 | 4.31 |
Embodiment 5 | Without flake, dissolution is completed in 30s | 1.901 | 4.18 |
Control group | There are a large amount of flakes, dissolution time is 30min or more | 1.875 | 4.12 |
Conclusion: xanthan gum is directly appended in water, since xanthan gum absorbs water rapidly, will form flake structure;The present invention passes through
Liquid xanthan gum is added in water, not will form flake structure, and viscosity will not be reduced;This is because what the present invention selected
Formula can't change the double-spiral structure of xanthan gum, electrostatic attraction can be formed between xanthan molecules, also to viscosity
It is promoted, prompts have preferable synergistic effect between recipe ingredient of the invention.
Finally, it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although
Present invention has been described in detail with reference to the aforementioned embodiments, those skilled in the art should understand that: it still may be used
To modify to technical solution documented by previous embodiment or equivalent replacement of some of the technical features;And
These are modified or replaceed, the spirit and model of technical solution of the embodiment of the present invention that it does not separate the essence of the corresponding technical solution
It encloses.
Claims (9)
1. a kind of preparation method of liquid xanthan gum, which is characterized in that described method includes following steps: (1) selection of raw material,
(2) raw material weighs, the preparation of (3) liquid xanthan gum.
2. the method according to claim 1, wherein described method includes following steps:
(1) selection of raw material
The following one or more kinds of substances of main solvent selection: mineral oil, diesel oil, kerosene, C6-C12Alcohol, vegetable oil;
The following one or more kinds of substances of suspending agent selection: hydroxypropyl methyl cellulose, hydroxy butyl methyl cellulose, organic glutinous
Soil;
Dispersing agent selects polyalcohol ethers;
(2) raw material weighs
Xanthan gum 20-75%, main solvent 30-65%, suspending agent 0.10-1.20%, dispersing agent 0.50-1.50%, the weight of the above component
Measuring the sum of percentage composition is 100%;
(3) preparation of liquid xanthan gum
Suspending agent and main solvent are mixed, dispersing agent is added in whipping process, is mixed evenly, by weighed xanthan
Glue is uniformly mixed with above-mentioned system, forms the liquid xanthan gum, and xanthan gum additive amount is the 20- of entire mixed system quality
75%。
3. method according to claim 1 or 2, which is characterized in that described method includes following steps:
(1) selection of raw material
The following one or more kinds of substances of main solvent selection: mineral oil, diesel oil, kerosene, C6-C12Alcohol, vegetable oil;
The following one or more kinds of substances of suspending agent selection: hydroxypropyl methyl cellulose, hydroxy butyl methyl cellulose, organic glutinous
Soil;
The following one or more kinds of substances of dispersing agent selection: polyalcohol ethers;
And thinner;
(2) raw material weighs
Xanthan gum 30-55%, main solvent 30-65%, suspending agent 0.10-1.20%, dispersing agent 0.50-1.50%, thinner 0.10-
0.80%, the sum of weight percentage of the above component is 100%;
(3) preparation of liquid xanthan gum
Suspending agent and main solvent are mixed, dispersing agent is added in whipping process, thinner is added after being uniformly dispersed, is mixed
It stirs evenly, weighed xanthan gum is uniformly mixed with above-mentioned system, form the liquid xanthan gum, xanthan gum additive amount is whole
The 30-55% of a mixed system quality.
4. according to the method in claim 2 or 3, which is characterized in that the organic clay is selected from bentonite, montmorillonite, soap
Mixture more than native or above-mentioned any the two.
5. according to the method in claim 2 or 3, which is characterized in that the polyalcohol ethers is selected from ethylene glycol, poly- second two
Mixture more than alcohol, glycerine, ethylene glycol monobutyl ether or above-mentioned any the two.
6. according to the method in claim 2 or 3, which is characterized in that the thinner is selected from lecithin or lignin sulfonic acid
Salt.
7. according to the method in claim 2 or 3, which is characterized in that the main solvent is mineral oil, diesel oil, octanol, second
Mixture more than alcohol or above-mentioned any the two.
8. according to the method in claim 2 or 3, which is characterized in that the polyalcohol ethers is selected from glycerine, ethylene glycol list
The mixture of butyl ether or said two devices.
9. according to the method in claim 2 or 3, which is characterized in that the partial size of the xanthan gum is 200 mesh or more.