CN109704618A - A kind of dregs compression strength of building block reinforcing agent and preparation method - Google Patents
A kind of dregs compression strength of building block reinforcing agent and preparation method Download PDFInfo
- Publication number
- CN109704618A CN109704618A CN201910027024.9A CN201910027024A CN109704618A CN 109704618 A CN109704618 A CN 109704618A CN 201910027024 A CN201910027024 A CN 201910027024A CN 109704618 A CN109704618 A CN 109704618A
- Authority
- CN
- China
- Prior art keywords
- dregs
- building block
- compression strength
- reinforcing agent
- block reinforcing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of dregs compression strength of building block reinforcing agent and preparation method, wherein by mass percentage, the dregs compression strength of building block reinforcing agent includes: acid polyethylene 20~30%;Polycarboxylic acids dehydragent 40~50%;Silicon powder 20~40%.The present invention has selected the raw material of acid polyethylene, polycarboxylic acids dehydragent, silicon powder as dregs compression strength of building block reinforcing agent, and the proportion of each raw material is optimized, to obtain final formula, dregs compression strength of building block reinforcing agent prepared by the present invention, it has larger improvement to the compression strength of dregs building block, and it is at low cost, preparation process is simple.
Description
Technical field
The present invention relates to the field of building materials more particularly to a kind of dregs compression strength of building block reinforcing agent and preparation methods.
Background technique
Dregs is one kind of building waste.According to alleged building waste in " urban building waste administrative provisions ", refers to and build
If unit, unit in charge of construction are newly-built, renovating and enlarging and remove all kinds of buildings, structures, pipe network etc. and resident's decorations room
Spoir caused by during room, rejected material and other wastes.Dregs regeneration product, the huge market demand, governments at all levels
Various government decrees are issued, encourage and require government-works and business development engineering to use renewable building material.
Dregs regeneration product, mainstream kind has currently on the market: recycled aggregate, regenerated construction material two major classes.Wherein: again
Raw aggregate is divided into regenerated coarse aggregate and recycled fine aggregate etc..Regenerated construction material is mainly regeneration brick series, and regeneration brick develops into now
For nearly 40 kinds, be widely used in building, road, bridge construction in, building block be exactly utilize concrete, industrial waste (clinker,
Flyash etc.) or local material made of artificial bulk, outer dimension is bigger than brick, have equipment it is simple, build it is fireballing excellent
Point has met the requirement of wall reform in building industrialization development.
And in the prior art, the compression strength of dregs building block is inadequate, is unfavorable for the popularization and application of dregs building block.
Therefore, the existing technology needs to be improved and developed.
Summary of the invention
In view of above-mentioned deficiencies of the prior art, the purpose of the present invention is to provide a kind of dregs compression strength of building block reinforcing agents
And preparation method, it is intended to solve the problems, such as that dregs compression strength of building block is inadequate in the prior art.
Technical scheme is as follows:
A kind of dregs compression strength of building block reinforcing agent, wherein by mass percentage, comprising:
Acid polyethylene 20~30%;
Polycarboxylic acids dehydragent 40~50%;
Silicon powder 20~40%.
The dregs compression strength of building block reinforcing agent, wherein the polycarboxylic acids dehydragent is DH-4004 polycarboxylic acid
Water-reducing agent.
The dregs compression strength of building block reinforcing agent, wherein the mesh number of the silicon powder is 1000~1200 mesh.
The dregs compression strength of building block reinforcing agent, wherein by mass percentage, comprising:
Acid polyethylene 22~28%;
Polycarboxylic acids dehydragent 42~48%;
Silicon powder 25~35%.
The dregs compression strength of building block reinforcing agent, wherein by mass percentage, comprising:
Acid polyethylene 25%;
Polycarboxylic acids dehydragent 45%;
Silicon powder 30%.
A kind of preparation method of dregs compression strength of building block reinforcing agent as described above, wherein comprising steps of
Each component is weighed in proportion, a point stirring is mixed under room temperature, obtains the enhancing of dregs compression strength of building block after mixing evenly
Then agent dispenses.
The preparation method, wherein the revolving speed of stirring is 60~80rpm.
The preparation method, wherein the time of stirring is 20~40 minutes.
The utility model has the advantages that the present invention has selected acid polyethylene, polycarboxylic acids dehydragent, silicon powder as dregs building block pressure resistance
The raw material of reinforcing agent is spent, and the proportion of each raw material is optimized, so that final formula has been obtained, prepared by the present invention
Dregs compression strength of building block reinforcing agent has larger improvement to the compression strength of dregs building block, and at low cost, preparation process letter
It is single.
Specific embodiment
The present invention provides a kind of dregs compression strength of building block reinforcing agent and preparation method, to make the purpose of the present invention, technology
Scheme and effect are clearer, clear, and the present invention is described in more detail below.It should be appreciated that described herein specific
Embodiment is only used to explain the present invention, is not intended to limit the present invention.
A kind of dregs compression strength of building block reinforcing agent provided by the invention, by mass percentage, comprising:
Acid polyethylene 20~30%;
Polycarboxylic acids dehydragent 40~50%;
Silicon powder 20~40%.
Specifically, acid polyethylene, also referred to as polyethylene or polyvinyl resin, polyethylene (polyethylene, abbreviation PE) are
A kind of aggregated thermoplastic resin obtained of ethylene.It industrially, also include the copolymer of ethylene and a small amount of ±-alkene.Poly- second
Alkene is odorless, nontoxic, feel ceraceous, and with excellent resistance to low temperature (minimum to use reachable -100~-70 DEG C of temperature), chemistry is steady
It is qualitative good, it is resistant to the erosion of most of soda acids (intolerant to the acid with oxidizing property).Common solvent, water imbibition are not dissolved under room temperature
Small, electrical insulating property is excellent.
The present invention uses the reason of acid polyethylene is as reinforcing agent, mainly since it includes 1, high impact properties, especially
It is in low temperature environment, impact strength reaches much higher value instead.2, service life is greatly improved in high-wearing feature.3, thermophilic
Property is wide: can work under Complex Temperature environment for a long time.
Further, polycarboxylic acids dehydragent (Polycarboxylate Superplasticizer) is that a kind of high-performance subtracts
Aqua is one of cement concrete utilization cement dispersants.It is widely used in highway, bridge, dam, tunnel, high level to build
The engineerings such as build.
Polycarboxylate water-reducer product can be divided into two major classes according to the difference of its backbone structure: one kind is with acrylic acid or first
Base acrylic acid is main chain, is grafted the polyethers of different side chain lengths.Another kind of is long using maleic anhydride as main link branch difference side chain
The polyethers of degree.
Polycarboxylic acids dehydragent overcomes some drawbacks of conventional water reducing agents, with volume is low, function of slump protection is good, concrete is received
Shrinkage is low, adjustability is strong on molecular structure, high performance potentiality are big, outstanding advantages of not using formaldehyde in production process.
Polycarboxylic acids dehydragent designs effective molecular structure according to the dispersion cement mechanism of action due to being truly realized,
With ultra-dispersed type, concrete slump loss can be prevented without causing obvious slow setting, higher plasticizing effect is played under low-dosage
Fruit, mobility retentivity is good, cement adapts to that freedom degree in wide molecular configuration is big, synthetic technology is more, the leeway of high performance is very big,
It is significant to concrete reinforcing effect, concrete shrinkage can be reduced, the technical performances feature such as harmful substance contents are extremely low imparts mixed
The outstanding construction workability of solidifying soil, good strength development, excellent durability, have good comprehensive technical performance advantage and
Environmentally friendly feature meets the needs of modernization concrete works.
The polycarboxylic acids dehydragent is DH-4004 polycarboxylic acids dehydragent.The water-reducing agent is more suitable for as the present invention
Reinforcing agent raw material, do not only reach water-reducing effect, while being also able to cooperate acid polyethylene and silicon powder, improve enhancing compression strength
Performance.
Silicon powder is a kind of nontoxic, tasteless, free of contamination inorganic non-metallic material.Have good temperature tolerance, acid-alkali-corrosive-resisting,
The excellent performances such as thermal coefficient is high, high insulation, low bulk, stable chemical performance, hardness are big.Fineness is micro- less than 1 in silicon powder
Rice accounts for 80% or more, and average grain diameter is at 0.1~0.3 micron, specific surface area are as follows: 20~28m2/g.Its fineness and specific surface area
About 80~100 times of cement, 50~70 times of flyash.SILICA FUME can the intergranular hole of filling concrete, while and water
Change product and generates gelinite.
In the concrete, mortar and refractory material casting material of cement base, suitable silicon powder is mixed, can be played the role that
1, resistance to compression, anti-folding, impervious, anti-corrosion, shock resistance and wear-resisting property are significantly improved.2, there is water conservation, prevent isolation, bleeding, substantially
Reduce the effect of concrete pumping resistance.3, significantly extend the service life of concrete.4, the landing of jetting cement and castable is greatly lowered
Ash improves single jetting thickness.5, product compression strength is improved.6, have effects that about 5 times of cement, in ordinary concrete and low cement
Application can reduce cost in castable, improve durability.7, it effectively prevent that concrete alkali-aggregate reaction occurs.8, casting type fire resisting is improved
The compactness of material.That is, being added to after silicon powder in the present invention, dregs compression strength of building block can not only be improved, together
When can also improve in other respects.
Further, the mesh number of the silicon powder is 1000~1200 mesh, in this way, the granular size of silicon powder is more moderate, and
Granular size is stablized, and can guarantee that product compression strength is maintained in claimed range.
Further, the dregs compression strength of building block reinforcing agent, by mass percentage, comprising:
Acid polyethylene 22~28%;
Polycarboxylic acids dehydragent 42~48%;
Silicon powder 25~35%.
Above-mentioned specific formula, obtained dregs compression strength of building block reinforcing agent to the improvement effect of compression strength more
It is good.
Further, the dregs compression strength of building block reinforcing agent, by mass percentage, comprising:
Acid polyethylene 25%;
Polycarboxylic acids dehydragent 45%;
Silicon powder 30%.
Above-mentioned more specific formula, obtained dregs compression strength of building block reinforcing agent to the improvement effect of compression strength more
It is good.
The present invention also provides a kind of preparation methods of dregs compression strength of building block reinforcing agent as described above comprising step
It is rapid:
Each component is weighed in proportion, a point stirring is mixed under room temperature, obtains the enhancing of dregs compression strength of building block after mixing evenly
Then agent dispenses.
In the present invention, first weigh each raw material in proportion, then each raw material is stirred, stirring be under normal temperature conditions into
Row, can impact to avoid to material property in this way, after fully mixed, obtain final dregs compression strength of building block
Reinforcing agent.
Further, mixing time is 20~40 minutes.Mixing time is too long, and material performance can be degenerated, and is not achieved most
Good effect, and mixing time is too short, raw material is difficult to play synergistic effect, and each raw material only individually plays a role, and is difficult to mix
Uniformly, it so currently preferred mixing time is 20~40 minutes, to make each raw material influence each other, maximally plays respective
Performance.
Further, the revolving speed of stirring is 60~80rpm.Speed of agitator is too fast, and the property of raw material can change, stirring
Obtained product can not play original performance, and speed of agitator is excessively slow, and raw material is unable to fully mix, so currently preferred revolving speed
It is 60~80rpm.
In following embodiment, the mesh number of the silicon powder is 1100 mesh, and the polycarboxylic acids dehydragent is preferably DH-4004
Polycarboxylic acids dehydragent.
Embodiment 1
A kind of dregs compression strength of building block reinforcing agent, by mass percentage, comprising: acid polyethylene 20%;Polycarboxylic acid
Water-reducing agent 50%;Silicon powder 30%.
The preparation method is as follows:
Each component is weighed in proportion, a point stirring is mixed under room temperature, obtains the enhancing of dregs compression strength of building block after mixing evenly
Then agent dispenses, wherein mixing time is 20 minutes, speed of agitator 80rpm.
Embodiment 2
A kind of dregs compression strength of building block reinforcing agent, by mass percentage, comprising: acid polyethylene 30%;Polycarboxylic acid
Water-reducing agent 40%;Silicon powder 30%.
The preparation method is as follows:
Each component is weighed in proportion, a point stirring is mixed under room temperature, obtains the enhancing of dregs compression strength of building block after mixing evenly
Then agent dispenses, wherein mixing time is 40 minutes, speed of agitator 60rpm.
Embodiment 3
A kind of dregs compression strength of building block reinforcing agent, by mass percentage, comprising: acid polyethylene 22%;Polycarboxylic acid
Water-reducing agent 48%;Silicon powder 30%.
The preparation method is as follows:
Each component is weighed in proportion, a point stirring is mixed under room temperature, obtains the enhancing of dregs compression strength of building block after mixing evenly
Then agent dispenses, wherein mixing time is 25 minutes, speed of agitator 75rpm.
Embodiment 4
A kind of dregs compression strength of building block reinforcing agent, by mass percentage, comprising: acid polyethylene 25%;Polycarboxylic acid
Water-reducing agent 45%;Silicon powder 30%.
The preparation method is as follows:
Each component is weighed in proportion, a point stirring is mixed under room temperature, obtains the enhancing of dregs compression strength of building block after mixing evenly
Then agent dispenses, wherein mixing time is 30 minutes, speed of agitator 70rpm.
Embodiment 5
A kind of dregs compression strength of building block reinforcing agent, by mass percentage, comprising: acid polyethylene 28%;Polycarboxylic acid
Water-reducing agent 42%;Silicon powder 30%.
The preparation method is as follows:
Each component is weighed in proportion, a point stirring is mixed under room temperature, obtains the enhancing of dregs compression strength of building block after mixing evenly
Then agent dispenses, wherein mixing time is 35 minutes, speed of agitator 65rpm.
Embodiment 6
A kind of dregs compression strength of building block reinforcing agent, by mass percentage, comprising: acid polyethylene 30%;Polycarboxylic acid
Water-reducing agent 50%;Silicon powder 20%.
The preparation method is as follows:
Each component is weighed in proportion, a point stirring is mixed under room temperature, obtains the enhancing of dregs compression strength of building block after mixing evenly
Then agent dispenses, wherein mixing time is 28 minutes, speed of agitator 72rpm.
Embodiment 7
A kind of dregs compression strength of building block reinforcing agent, by mass percentage, comprising: acid polyethylene 20%;Polycarboxylic acid
Water-reducing agent 40%;Silicon powder 40%.
The preparation method is as follows:
Each component is weighed in proportion, a point stirring is mixed under room temperature, obtains the enhancing of dregs compression strength of building block after mixing evenly
Then agent dispenses, wherein mixing time is 36 minutes, speed of agitator 64rpm.
Then the dregs compression strength of building block reinforcing agent that various embodiments of the present invention obtain is added in dregs, and prepares slag
Earth building blocks.Dregs compression strength of building block reinforcing agent is not added in blank expression.
Dregs building block according to GBJ129-90 " Standard for test methods of basic mechincal properties of masonry " build, masonry with a thickness of
Building block width, the width of masonry are main specification building block length.In the building process of dregs building block, should mortar check at any time it is full
Degree.After dregs building block conserves 28d under natural conditions indoors, while being tested.Dregs block tops are with a thickness of 10mm's
1:3 cement mortar screeding, and its flatness should be checked using horizontal ruler.
Compression strength performance test (compression strength compression test) carries out on YE-200A pressure testing machine, maximum pressure
2000kN.On the vertical middle line of test specimen (dregs building block test specimen) two broad side surfaces, by being adhered to the gauge stand of surface of test piece, pacify
Fill the axial deformation of amesdial measurement test specimen.Distance between measuring point adds a gray seam thickness multiple for a block thickness.In width
Instrument is installed, the distance at measuring point and test specimen edge is no less than 50mm, measures the transversely deforming of test specimen on the horizontal central line of side.
When estimating the 5% of failing load for test specimen application, the sensitivity of instrument and the fixing of installation are checked.It is estimating
In 5% to 20% section of failing load, Ying Fanfu precompressed 3~5 times.The relative error of the axial deformation value of two broad side surfaces,
It is not to be exceeded 10%.Every grade of load should be and estimate the 10% of failing load value, and should uniformly add in 1~1.5min;It is permanent
Apply next stage load after carrying 1~2min.When being further applied load, must not impact test piece, and deformation values should be recorded simultaneously.When loading extremely
When estimating the 80% of payload values, instrument should be removed, then by the continuous loading of test specimen to destruction.
By the dregs compression strength of building block reinforcing agent of each embodiment, the compression strength performance of prepared dregs building block is such as
Shown in following table one.
Table one
Wherein compression strength is higher, represents that resistance to compression higher grade, and elasticity modulus is bigger, and compressive property is better.As it can be seen that this hair
Bright dregs compression strength of building block reinforcing agent can improve the compressive property of dregs building block.
The embodiment of the present invention 4, obtained dregs compression strength of building block reinforcing agent change the compressive property of dregs building block
Kind effect is better than other embodiments, and is apparently higher than blank group.
It should be understood that the application of the present invention is not limited to the above for those of ordinary skills can
With improvement or transformation based on the above description, all these modifications and variations all should belong to the guarantor of appended claims of the present invention
Protect range.
Claims (8)
1. a kind of dregs compression strength of building block reinforcing agent, which is characterized in that by mass percentage, comprising:
Acid polyethylene 20~30%;
Polycarboxylic acids dehydragent 40~50%;
Silicon powder 20~40%.
2. dregs compression strength of building block reinforcing agent according to claim 1, which is characterized in that the polycarboxylic acids dehydragent
For DH-4004 polycarboxylic acids dehydragent.
3. dregs compression strength of building block reinforcing agent according to claim 1, which is characterized in that the mesh number of the silicon powder is
1000~1200 mesh.
4. dregs compression strength of building block reinforcing agent according to claim 1, which is characterized in that by mass percentage, packet
It includes:
Acid polyethylene 22~28%;
Polycarboxylic acids dehydragent 42~48%;
Silicon powder 25~35%.
5. dregs compression strength of building block reinforcing agent according to claim 4, which is characterized in that by mass percentage, packet
It includes:
Acid polyethylene 25%;
Polycarboxylic acids dehydragent 45%;
Silicon powder 30%.
6. a kind of preparation method of dregs compression strength of building block reinforcing agent as claimed in any one of claims 1 to 5, feature exist
In, comprising steps of
Each component is weighed in proportion, a point stirring is mixed under room temperature, obtains dregs compression strength of building block reinforcing agent after mixing evenly, so
After dispense.
7. preparation method according to claim 6, which is characterized in that the revolving speed of stirring is 60~80rpm.
8. preparation method according to claim 6, which is characterized in that the time of stirring is 20~40 minutes.