CN109701197A - A kind of glue composite fire extinguishing agent - Google Patents
A kind of glue composite fire extinguishing agent Download PDFInfo
- Publication number
- CN109701197A CN109701197A CN201811524364.4A CN201811524364A CN109701197A CN 109701197 A CN109701197 A CN 109701197A CN 201811524364 A CN201811524364 A CN 201811524364A CN 109701197 A CN109701197 A CN 109701197A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire extinguishing
- extinguishing agent
- water
- composite fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of glue composite fire extinguishing agents, using water as base-material, add a variety of auxiliary reagents such as ammonium dihydrogen phosphate, expansible graphite, silica, hydroxyethyl cellulose, xanthan gum, by improving formula and preparation process, it is made to have the advantages that fire extinguishing effectiveness height, good flame retardation effect, anti-re-ignition effect are good compared to common extinguishing chemical.Meanwhile the ingredient safety non-pollution of extinguishing chemical of the invention, and removed conveniently after use, attachment can be removed with water.
Description
Technical field
The invention belongs to extinguishing chemical preparation technical fields, and in particular to glue composite fire extinguishing agent.
Background technique
Fire is arch enemy of man, no matter superficial fire or underground fire, not only result in a large amount of casualties, also
It will cause the heavy losses of property and natural resources.How fast and effeciently to stamp out a fire, reduces loss to the maximum extent, always
It is the research topic being of great significance.
Extinguishing chemical refers to effectively destroying burning condition, make the substance of fire end, extinguishing mechanism is mainly
Cooling, asphyxia, isolation and Chemical Inhibition.Currently, extinguishing chemical can substantially be divided into two major classes: physics according to the difference of extinguishing mechanism
Extinguishing chemical and chemical.Physical extinguishant includes water, foam, carbon dioxide, nitrogen, argon gas and other inert gases, it
In fire extinguishing procedure while reducing combustion mixture temperature, combustible is isolated, to play the role of fire extinguishing in dilution oxygen;
Chemical includes that halon extinguishing agent, dry powder fire extinguishing agent etc. are a variety of, it is the chain reaction by cutting off living radical
And inhibit burning.
Up to the present, water is still most-often used extinguishing chemical, and it is excellent that it has, and source is wide, cheap, fire extinguishing property is strong
Point.But water is also clearly present, be easy to run off the disadvantages of big including mobility.Water-based extinguishing agent is to be increased using water as base-material by addition
Thick dose, initiator, the additives such as antifreeze, change the performance of water, to improve a series of extinguishing chemicals of extinguishing ability.However mesh
There is some shortcomingss for preceding water-based extinguishing agent, and such as applicable fire phases are not comprehensive, fire-fighting efficiency is low, fire re-ignition is high
Deng.Therefore, it is badly in need of the applied widely, high-effect fire-extinguishing of one kind in the market and prevents the fire-extinguishing agent of fire re-ignition.
Summary of the invention
The purpose of the present invention is to provide a kind of glue composite fire extinguishing agents, for solving the shortcomings of the prior art.
The technical scheme is that
A kind of glue composite fire extinguishing agent, which is characterized in that by weight include following component: ammonium dihydrogen phosphate 8~
12 parts, 30~50 parts of expansible graphite, 2~6 parts of silica, 2~6 parts of sodium metasilicate, 3~6 parts of aluminium hydroxide, sodium pyrophosphate 2
~6 parts, 8~12 parts of antifreeze, 3~6 parts of hydroxyethyl cellulose, 3~6 parts of carboxymethyl cellulose, 8~12 parts of xanthan gum, gelatin 3
~6 parts, 1~3 part of Sodium Polyacrylate, 3~6 parts of ammonium polyacrylate, 3~6 parts of anionic polyacrylamide, water-absorbing resin 3~6
Part, 3~6 parts of thickener, 80~120 parts of water.
It by weight include following component: phosphoric acid as a kind of above-mentioned further improvement of glue composite fire extinguishing agent
It is 10 parts of ammonium dihydrogen, 40 parts of expansible graphite, 4 parts of silica, 4 parts of sodium metasilicate, 5 parts of aluminium hydroxide, 3 parts of sodium pyrophosphate, freeze proof
10 parts of agent, 5 parts of hydroxyethyl cellulose, 5 parts of carboxymethyl cellulose, 10 parts of xanthan gum, 5 parts of gelatin, 2 parts of Sodium Polyacrylate, poly- third
5 parts of olefin(e) acid ammonium, 5 parts of anionic polyacrylamide, 5 parts of water-absorbing resin, 5 parts of thickener, 100 parts of water.
As a kind of above-mentioned further improvement of glue composite fire extinguishing agent, antifreeze is selected from sodium chloride, potassium carbonate, chlorination
Magnesium, calcium chloride, ethylene glycol, propylene glycol, the one of which of glycerol.
As a kind of above-mentioned further improvement of glue composite fire extinguishing agent, thickener is selected from polyvinyl alcohol, guar gum, first
The one of which of shell amine.
When selecting expansible graphite, need to consider that the granularity effect of expansible graphite is dispersed and flame retardant property to it
It influences.The small expansible graphite expansion multiplying power of mesh number is high, and the big expansible graphite of mesh number disperses more uniform in system.As
A kind of further improvement of above-mentioned glue composite fire extinguishing agent, the mesh number of expansible graphite are 100~200 mesh.
As a kind of above-mentioned further improvement of glue composite fire extinguishing agent, the mesh number of water-absorbing resin is 100~200 mesh.
As a kind of above-mentioned further improvement of glue composite fire extinguishing agent, water-absorbing resin includes cellulose graft acryloyl
Amine, starch graft acrylamide, the one of which in POLYPROPYLENE GLYCOL grafted propylene hydrochlorate.
As a kind of above-mentioned further improvement of glue composite fire extinguishing agent, the extinguishing chemical the preparation method comprises the following steps:
1) ammonium dihydrogen phosphate, expansible graphite, silica, sodium metasilicate, hydrogen are added in mixed once tank according to formula
Aluminium oxide, sodium pyrophosphate and antifreeze mix;
2) material that step 1) is stirred is transferred to secondary blending tank, and water, hydroxyethyl cellulose, carboxylic first is added according to formula
Base vitamin, xanthan gum, gelatin, Sodium Polyacrylate, ammonium polyacrylate, anionic polyacrylamide, water-absorbing resin, thickener,
It mixes;
3) after all material addition, further it is uniformly mixed so as to obtain glue composite fire extinguishing agent.
As a kind of above-mentioned further improvement of glue composite fire extinguishing agent, secondary stir is carried out after water is added in step 2)
It mixes, hydroxyethyl cellulose, carboxymethyl vitamin, xanthan gum, gelatin, Sodium Polyacrylate, polyacrylic acid is added after 20~30 minutes
Ammonium, anionic polyacrylamide, water-absorbing resin, thickener, stirring 3 after every kind of material is added~add lower one kind after ten minutes
Material.
As a kind of above-mentioned further improvement of glue composite fire extinguishing agent, after all material adds in step 3), into one
The method that step mixes is to be repeated 3 times in the way of standing 12~36 hours after stirring 12~36 hours.
The beneficial effects of the present invention are:
Glue composite fire extinguishing agent of the invention, using water as base-material, reasonable selection additive is auxiliary reagent, improves preparation
Technique makes it have following characteristics:
1. not influenced by fire stage, any time of fire can be used;
2. the silica constituents added in glue composite fire extinguishing agent of the invention have porosity, burning can be adsorbed
Particle in the smog of generation, achievees the effect that smoke elimination;
3. flowability is low, adhesive capacity is splendid, and time overlength, anti-re-ignition ability with super strength can be adhered;
4. ingredient non-toxic and safe selected by glue composite fire extinguishing agent of the invention, non-environmental-pollution in use process,
It is convenient to remove after use, can remove attachment with water.
Detailed description of the invention
Fig. 1 is the finished product figure of the glue composite fire extinguishing agent of the application;
Fig. 2 is the partial result that the glue composite fire extinguishing agent flame-retarded efficiency of the application is tested.
Specific embodiment
The present invention is described in detail With reference to embodiment.
Embodiment 1
The present embodiment discloses a kind of glue composite fire extinguishing agent, and formula meter includes: 10 parts of ammonium dihydrogen phosphate,
40 parts of expansible graphite, 4 parts of silica, 4 parts of sodium metasilicate, 5 parts of aluminium hydroxide, 3 parts of sodium pyrophosphate, 10 parts of antifreeze, hydroxyl second
5 parts of base cellulose, 5 parts of carboxymethyl cellulose, 10 parts of xanthan gum, 5 parts of gelatin, 2 parts of Sodium Polyacrylate, 5 parts of ammonium polyacrylate, yin
5 parts of cationic polyacrylamide, 5 parts of water-absorbing resin, 5 parts of thickener, 100 parts of water.
Wherein, antifreeze is sodium chloride, and thickener is polyvinyl alcohol, and the mesh number of expansible graphite is 100 mesh, water-absorbing resin
For the cellulose graft acrylamide of 100 mesh.
The preparation method of the glue composite fire extinguishing agent of the present embodiment are as follows:
1) ammonium dihydrogen phosphate, expansible graphite, silica, sodium metasilicate, hydrogen are added in mixed once tank according to formula
Aluminium oxide, sodium pyrophosphate and antifreeze, uniform stirring 30 minutes;
2) material that step 1) is stirred is transferred to secondary blending tank, is added after water according to formula and carries out secondary agitation, and 20
Hydroxyethyl cellulose, carboxymethyl vitamin, xanthan gum, gelatin, Sodium Polyacrylate, ammonium polyacrylate, yin is once added after minute
Cationic polyacrylamide, water-absorbing resin, thickener, every kind of material stir after being added and add a kind of lower material after five minutes;
3) after all material addition, according to stirring 24 hours, 24 hours modes is stood and are repeated 3 times, that is, complete a batch
Glue composite fire extinguishing agent product preparation.
Obtained finished product is as shown in Figure 1.
Embodiment 2
The present embodiment discloses a kind of glue composite fire extinguishing agent, and formula meter includes: 8 parts of ammonium dihydrogen phosphate,
40 parts of expansible graphite, 5 parts of silica, 5 parts of sodium metasilicate, 5 parts of aluminium hydroxide, 3 parts of sodium pyrophosphate, 10 parts of antifreeze, hydroxyl second
4 parts of base cellulose, 4 parts of carboxymethyl cellulose, 12 parts of xanthan gum, 5 parts of gelatin, 2 parts of Sodium Polyacrylate, 4 parts of ammonium polyacrylate, yin
6 parts of cationic polyacrylamide, 6 parts of water-absorbing resin, 5 parts of thickener, 100 parts of water.
Wherein, antifreeze is ethylene glycol, and thickener is chitosan, and the mesh number of expansible graphite is 100 mesh, and water-absorbing resin is
The cellulose graft acrylamide of 100 mesh.
The preparation method of the glue composite fire extinguishing agent of the present embodiment are as follows:
1) ammonium dihydrogen phosphate, expansible graphite, silica, sodium metasilicate, hydrogen are added in mixed once tank according to formula
Aluminium oxide, sodium pyrophosphate and antifreeze, uniform stirring 50 minutes;
2) material that step 1) is stirred is transferred to secondary blending tank, is added after water according to formula and carries out secondary agitation, and 20
Hydroxyethyl cellulose, carboxymethyl vitamin, xanthan gum, gelatin, Sodium Polyacrylate, ammonium polyacrylate, yin is once added after minute
Cationic polyacrylamide, water-absorbing resin, thickener, every kind of material stir after being added and add a kind of lower material after five minutes;
3) after all material addition, according to stirring 24 hours, 24 hours modes is stood and are repeated 3 times, that is, complete a batch
Glue composite fire extinguishing agent product preparation.
Comparative example 1
Compared with Example 1, difference is only that the present embodiment, and ammonium polyacrylate is not added in the present embodiment.
Particle dispersion is uneven in the finished product being prepared in the present embodiment, occurs reuniting and precipitate, is not suitable for storage tank
It saves.
Comparative example 2
Compared with Example 1, difference is only that the present embodiment, and water-absorbing resin is not added in the present embodiment.
Embodiment 3
Flame-retarded efficiency test is carried out to the glue composite fire extinguishing agent that above-described embodiment 1 obtains:
It the use of the rectangular haystack of 4 heap 1m × 1m × 0.15m is one group of test haystack, it is rectangular using 1m × 0.2m × 0.1m
Haystack+150mL gasoline is oxidizer, and any extinguishing chemical is not added in uniform spraying fire-extinguishing agent, setting on test haystack in advance
Blank control.Down wind makes oxidizer intersect 0.1m with test haystack, is then uniformly spilled into 150mL gasoline, refires.Repeat three
Secondary test.Test to obtain 27~30 DEG C of live temperature, humidity 70%, 1~2.7m/s of wind speed.Test result is as shown in table 1.Wherein,
Blank control over-fires burning quickly, the completely burned time be 1 point 40 seconds 55 seconds to 2 points.
The partial result of the flame-retarded efficiency test of embodiment 1 is as shown in Figure 2.
Table 1, extinguishing chemical flame-retarded efficiency test and comparison
Embodiment 4
Flame-retarded efficiency test is carried out to the glue composite fire extinguishing agent that above-described embodiment 2 obtains:
It the use of the rectangular haystack of 4 heap 1m × 1m × 0.15m is one group of test haystack, it is rectangular using 1m × 0.2m × 0.1m
Haystack+150mL gasoline is oxidizer, and any extinguishing chemical is not added in uniform spraying fire-extinguishing agent, setting on test haystack in advance
Blank control.3 hours are first stood in air, then down wind makes oxidizer intersect 0.1m with test haystack, is then uniformly spilled into
150mL gasoline, refires.It tests in triplicate.Test to obtain 26~30 DEG C of live temperature, humidity 73%, 1.5~2.5m/ of wind speed
s.Test result is as shown in table 2.Wherein, blank control over-fires burning quickly, the completely burned time be 1 point 33 seconds 45 seconds to 2 points.
Table 2, extinguishing chemical flame-retarded efficiency test and comparison
Embodiment 5
Fire extinguishing effectiveness and resistance re-ignition performance are carried out to the glue composite fire extinguishing agent that above-described embodiment 1 and comparative example 2 obtain
Test:
The squarer of 1m high is superimposed as using 3cm × 3cm × 1m square wood strip, every 3 heap is one group, is tested for totally 4 groups.?
Uniformly sprinkling 300mL gasoline, column foot are surrounded with the cloth of sprinkling 200ml gasoline in four directions on each squarer, light distance after 10min
3m is put out a fire using water, dry powder and glue composite fire extinguishing agent around wood pagoda respectively;After extinguishing completely after standing 120min again
Sprinkling 300mL gasoline carries out re-ignition and lights test, test resistance re-ignition performance.Retest 3 times.Test result is as shown in table 3.
Table 3, extinguishing chemical fire extinguishing effectiveness and resistance re-ignition performance test are compared
It can be seen that by embodiment test result, glue composite fire extinguishing agent of the invention has compared to common extinguishing chemical to go out
The good advantage of fiery efficiency height, good flame retardation effect, anti-re-ignition effect.
Enumerating for above embodiments is to allow those skilled in the art that technical solution of the present invention is more clearly understood.
It should be noted that above embodiments are not construed as limiting protection scope of the presently claimed invention.
Claims (10)
1. a kind of glue composite fire extinguishing agent, which is characterized in that by weight include following component: ammonium dihydrogen phosphate 8~12
Part, 30~50 parts of expansible graphite, 2~6 parts of silica, 2~6 parts of sodium metasilicate, 3~6 parts of aluminium hydroxide, sodium pyrophosphate 2~6
Part, 8~12 parts of antifreeze, 3~6 parts of hydroxyethyl cellulose, 3~6 parts of carboxymethyl cellulose, 8~12 parts of xanthan gum, gelatin 3~6
Part, 1~3 part of Sodium Polyacrylate, 3~6 parts of ammonium polyacrylate, 3~6 parts of anionic polyacrylamide, 3~6 parts of water-absorbing resin, increase
Thick dose 3~6 parts, 80~120 parts of water.
2. a kind of glue composite fire extinguishing agent according to claim 1, which is characterized in that by weight include such as the following group
Part: 10 parts of ammonium dihydrogen phosphate, 40 parts of expansible graphite, 4 parts of silica, 4 parts of sodium metasilicate, 5 parts of aluminium hydroxide, sodium pyrophosphate 3
Part, 10 parts of antifreeze, 5 parts of hydroxyethyl cellulose, 5 parts of carboxymethyl cellulose, 10 parts of xanthan gum, 5 parts of gelatin, Sodium Polyacrylate 2
Part, 5 parts of ammonium polyacrylate, 5 parts of anionic polyacrylamide, 5 parts of water-absorbing resin, 5 parts of thickener, 100 parts of water.
3. a kind of glue composite fire extinguishing agent according to claim 1, which is characterized in that antifreeze is selected from sodium chloride, carbon
Sour potassium, magnesium chloride, calcium chloride, ethylene glycol, propylene glycol, the one of which of glycerol.
4. a kind of glue composite fire extinguishing agent according to claim 1, which is characterized in that thickener be selected from polyvinyl alcohol,
The one of which of guar gum, chitosan.
5. a kind of glue composite fire extinguishing agent according to claim 1, which is characterized in that the mesh number of expansible graphite is
100~200 mesh.
6. a kind of glue composite fire extinguishing agent according to claim 1, which is characterized in that the mesh number of water-absorbing resin is 100
~200 mesh.
7. a kind of glue composite fire extinguishing agent according to claim 1, which is characterized in that water-absorbing resin includes that cellulose connects
Branch acrylamide, starch graft acrylamide, the one of which in POLYPROPYLENE GLYCOL grafted propylene hydrochlorate.
8. a kind of glue composite fire extinguishing agent according to claim 1, which is characterized in that the preparation step of the extinguishing chemical
Are as follows:
1) ammonium dihydrogen phosphate, expansible graphite, silica, sodium metasilicate, hydroxide are added in mixed once tank according to formula
Aluminium, sodium pyrophosphate and antifreeze mix;
2) material that step 1) is stirred is transferred to secondary blending tank, and water, hydroxyethyl cellulose, carboxymethyl is added according to formula and ties up
Raw element, xanthan gum, gelatin, Sodium Polyacrylate, ammonium polyacrylate, anionic polyacrylamide, water-absorbing resin, thickener, mix;
3) after all material addition, further it is uniformly mixed so as to obtain glue composite fire extinguishing agent.
9. a kind of glue composite fire extinguishing agent according to claim 8, which is characterized in that carried out after water is added in step 2)
Secondary agitation is added hydroxyethyl cellulose, carboxymethyl vitamin, xanthan gum, gelatin, Sodium Polyacrylate, gathers after 20~30 minutes
Ammonium acrylate, anionic polyacrylamide, water-absorbing resin, thickener, stirring 3 after every kind of material is added~add after ten minutes
A kind of lower material.
10. a kind of glue composite fire extinguishing agent according to claim 8, which is characterized in that all material adds in step 3)
After adding, the method further mixed is to be repeated 3 times in the way of standing 12~36 hours after stirring 12~36 hours.