CN109650849A - A kind of flame retardant type wall brick and its production method - Google Patents
A kind of flame retardant type wall brick and its production method Download PDFInfo
- Publication number
- CN109650849A CN109650849A CN201910148680.4A CN201910148680A CN109650849A CN 109650849 A CN109650849 A CN 109650849A CN 201910148680 A CN201910148680 A CN 201910148680A CN 109650849 A CN109650849 A CN 109650849A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame retardant
- wall brick
- type wall
- retardant type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of flame retardant type wall brick, the flame retardant type wall brick includes the raw material being equipped with according to following number: 10-15 parts of flyash, 10-15 parts of feldspar, 5-10 parts of perlite, 10-15 parts of laterite, 10-15 parts of glass fibre, 4-9 parts of nano zine oxide, 8-15 parts of nano silica, 6-12 parts of bamboo charcoal powder, 5-10 parts of steel slag, 5-15 parts of glass dregs, 3-7 parts of acrylic acid series elastic resin, 1-3 parts of grinding aid, 3-5 parts of fire retardant, 1.5-3 parts of antioxidant, 1.5-2.5 parts of heat stabilizer and water.The invention also discloses a kind of production methods of flame retardant type wall brick.The present invention improves anti-flammability, and environmental protection.
Description
Technical field
The present invention relates to a kind of technical field of wall brick, especially a kind of flame retardant type wall brick and its production method.
Background technique
Wall brick is suitable for the places such as kitchen, parlor, toilet, plays the work of protection and decoration as a kind of construction material
With, but current wall brick is easily broken off, it is therefore desirable to improve since fire-type is not strong after pre- high temperature.
Summary of the invention
A kind of flame retardant type wall brick and its production are provided the purpose of the present invention is to solve above-mentioned the deficiencies in the prior art
Method.
To achieve the goals above, the present invention designed by a kind of flame retardant type wall brick, the flame retardant type wall brick include according to
The raw material that following number is equipped with: 10-15 parts of flyash, 10-15 parts of feldspar, 5-10 parts of perlite, 10-15 parts of laterite, glass fibers
Tie up 10-15 parts, 4-9 parts of nano zine oxide, 8-15 parts of nano silica, 6-12 parts of bamboo charcoal powder, 5-10 parts of steel slag, glass dregs 5-
15 parts, 3-7 parts of acrylic acid series elastic resin, 1-3 parts of grinding aid, 3-5 parts of fire retardant, 1 .5-3 parts of antioxidant, heat stabilizer 1
.5-2 .5 parts and water.
Further, the flame retardant type wall brick further includes 5-10 parts of antibacterial agent.
Further, the flame retardant type wall brick further includes 5-10 parts of anti-blushing agent.
Further, the flame retardant type wall brick further includes 3-9 parts of smectite powder.
Further, the raw material including being equipped with according to following number: 12 parts of flyash, 12 parts of feldspar, 8 parts of perlite, laterite
12 parts, 12 parts of glass fibre, 8 parts of nano zine oxide, 12 parts of nano silica, 11 parts of bamboo charcoal powder, 8 parts of steel slag, glass dregs 8
Part, 5 parts of acrylic acid series elastic resin, 2 parts of grinding aid, 4 parts of fire retardant, 2 parts of antioxidant, 2 parts of heat stabilizer and water.
Further, the smectite powder is 5 parts.
Further, the fire retardant is ammonium polyphosphate, phosphoric acid narrows base urea, phosphate, melamine phosphate, melamine
One of pyrophosphate or a variety of combinations.
Further, the heat stabilizer is the combination of 2 ethyl hexanoic acid salt, Ding Xinji ZDDP and N- phenyl-α-naphthylamine.
The invention also discloses a kind of production methods of flame retardant type wall brick, specifically includes the following steps:
1) flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag are subjected to primary filter;
2) then by filtered flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag and nano oxidized
Zinc, nano silica, bamboo charcoal powder, acrylic acid series elastic resin, grinding aid, fire retardant, antioxidant, heat stabilizer and water mixing
And it grinds and slurry is made, and the ratio of the water is adjusted in real time in grinding, ultimately becomes relatively sticky slurry;
3) painting oil processing is carried out to mold, then slurry is sent into the mold of oiling and carries out platen composition embryo material;
4) it after embryo material being carried out the pre-heat treatment cooling, calcined, cooled down and constitute flame retardant type wall brick after being demoulded processing;
Wherein, the calcination temperature is to be warming up to 500-700 degrees Celsius from 20-30 degrees Celsius with 7-9 centigrade per minute
Primary calcining 1.5 hours is carried out, then proceedes to be warming up to 1300-1400 degrees Celsius of lower secondary clacining, calcination time is that 0.5-1 is small
When.
Further, it is additionally added antibacterial agent in step 2.
A kind of flame retardant type wall brick and its production method that the present invention obtains, all raw materials environmental protection that the present invention uses, can return
It receives, finally reduces production cost, it is environmentally protective, while flame retardant type being provided.
Specific embodiment
Innovation and creation are described further below with reference to embodiment.
Embodiment 1:
A kind of flame retardant type wall brick provided in this embodiment, the flame retardant type wall brick include the raw material being equipped with according to following number: powder
10-15 parts of coal ash, 10-15 parts of feldspar, 5-10 parts of perlite, 10-15 parts of laterite, 10-15 parts of glass fibre, nano zine oxide 4-
9 parts, 8-15 parts of nano silica, 6-12 parts of bamboo charcoal powder, 5-10 parts of steel slag, 5-15 parts of glass dregs, acrylic acid series elastic resin
3-7 parts, 1-3 parts of grinding aid, 3-5 parts of fire retardant, 1 .5-3 parts of antioxidant .5 parts of 1 .5-2 of heat stabilizer and water.
Further, the flame retardant type wall brick further includes 5-10 parts of anti-blushing agent.5 parts of the anti-blushing agent.
Further, the raw material including being equipped with according to following number: 12 parts of flyash, 12 parts of feldspar, 8 parts of perlite, laterite
12 parts, 12 parts of glass fibre, 8 parts of nano zine oxide, 12 parts of nano silica, 11 parts of bamboo charcoal powder, 8 parts of steel slag, glass dregs 8
Part, 5 parts of acrylic acid series elastic resin, 2 parts of grinding aid, 4 parts of fire retardant, 2 parts of antioxidant, 2 parts of heat stabilizer and water.
Further, the smectite powder is 5 parts.
Further, the fire retardant is ammonium polyphosphate, phosphoric acid narrows base urea, phosphate, melamine phosphate, melamine
One of pyrophosphate or a variety of combinations.
Further, the heat stabilizer is the combination of 2 ethyl hexanoic acid salt, Ding Xinji ZDDP and N- phenyl-α-naphthylamine.
The present embodiment also discloses a kind of production method of flame retardant type wall brick, specifically includes the following steps:
1) flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag are subjected to primary filter;
2) then by filtered flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag and nano oxidized
Zinc, nano silica, bamboo charcoal powder, acrylic acid series elastic resin, grinding aid, fire retardant, antioxidant, anti-blushing agent, heat stabilizer
It mixes and grinds with water and slurry is made, and the ratio of the water is adjusted in real time in grinding, ultimately becomes relatively sticky
Slurry;
3) painting oil processing is carried out to mold, then slurry is sent into the mold of oiling and carries out platen composition embryo material;
4) it after embryo material being carried out the pre-heat treatment cooling, calcined, cooled down and constitute flame retardant type wall brick after being demoulded processing;
Wherein, the calcination temperature be from 20-30 degrees Celsius with 8 centigrade per minutes be warming up to 500-700 degrees Celsius into
The primary calcining of row 1.5 hours then proceedes to be warming up to 1350 degrees Celsius of lower secondary clacinings, and calcination time is 0.8 hour.
All raw materials environmental protection that the present embodiment uses, can be recycled, finally reduce production cost, environmentally protective, mention simultaneously
For flame retardant type.
Calcination temperature is to be warming up to 520 degrees Celsius of progress just with 8 centigrade per minutes from 21 degrees Celsius in the present embodiment
Grade calcining 1.5 hours then proceedes to be warming up to 1350 degrees Celsius of lower secondary clacinings, and calcination time is 0.8 hour.
Embodiment 2:
A kind of flame retardant type wall brick provided in this embodiment, the flame retardant type wall brick include the raw material being equipped with according to following number: powder
13 parts of coal ash, 13 parts of feldspar, 8 parts of perlite, 13 parts of laterite, 13 parts of glass fibre, 7 parts of nano zine oxide, nano silica
13 parts, it is 10 parts of bamboo charcoal powder, 8 parts of steel slag, 11 parts of glass dregs, 5 parts of acrylic acid series elastic resin, 2 parts of grinding aid, 4 parts of fire retardant, anti-
2 parts of oxygen agent, 1 .8 parts of heat stabilizer and water.
Further, the flame retardant type wall brick further includes 5-10 parts of anti-blushing agent.
Further, 5 parts of the anti-blushing agent.
Further, the fire retardant is ammonium polyphosphate, phosphoric acid narrows base urea.
Further, the heat stabilizer is the combination of 2 ethyl hexanoic acid salt, Ding Xinji ZDDP and N- phenyl-α-naphthylamine.
The present embodiment also discloses a kind of production method of flame retardant type wall brick, specifically includes the following steps:
1) flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag are subjected to primary filter;
2) then by filtered flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag and nano oxidized
Zinc, nano silica, bamboo charcoal powder, acrylic acid series elastic resin, grinding aid, fire retardant, antioxidant, heat stabilizer and water mixing
And it grinds and slurry is made, and the ratio of the water is adjusted in real time in grinding, ultimately becomes relatively sticky slurry;
3) painting oil processing is carried out to mold, then slurry is sent into the mold of oiling and carries out platen composition embryo material;
4) it after embryo material being carried out the pre-heat treatment cooling, calcined, cooled down and constitute flame retardant type wall brick after being demoulded processing;
Wherein, the calcination temperature is to be forged from 22 degrees Celsius with the 500 degrees Celsius of progress primary that are warming up to of 7 centigrade per minutes
It burns 1.5 hours, then proceedes to be warming up to 1300 degrees Celsius of lower secondary clacinings, calcination time is 0.5 hour.
Embodiment 3:
A kind of flame retardant type wall brick provided in this embodiment, the flame retardant type wall brick include the raw material being equipped with according to following number: powder
13 parts of coal ash, 13 parts of feldspar, 7 parts of perlite, 12 parts of laterite, 12 parts of glass fibre, 7 parts of nano zine oxide, nano silica
14 parts, it is 11 parts of bamboo charcoal powder, 8 parts of steel slag, 14 parts of glass dregs, 5 parts of acrylic acid series elastic resin, 2 parts of grinding aid, 4 parts of fire retardant, anti-
2.5 parts of oxygen agent, 2 parts of heat stabilizer and water.
Further, the flame retardant type wall brick further includes 5-10 parts of anti-blushing agent.7 parts of the anti-blushing agent.
Further, the fire retardant is ammonium polyphosphate, phosphoric acid narrows base urea, phosphate, melamine phosphate, melamine
Pyrophosphate.
Further, the heat stabilizer is the combination of 2 ethyl hexanoic acid salt, Ding Xinji ZDDP and N- phenyl-α-naphthylamine.
The present embodiment also discloses a kind of production method of flame retardant type wall brick, specifically includes the following steps:
1) flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag are subjected to primary filter;
2) then by filtered flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag and nano oxidized
Zinc, nano silica, bamboo charcoal powder, acrylic acid series elastic resin, grinding aid, fire retardant, antioxidant, heat stabilizer, anti-blushing agent
It mixes and grinds with water and slurry is made, and the ratio of the water is adjusted in real time in grinding, ultimately becomes relatively sticky
Slurry;
3) painting oil processing is carried out to mold, then slurry is sent into the mold of oiling and carries out platen composition embryo material;
4) it after embryo material being carried out the pre-heat treatment cooling, calcined, cooled down and constitute flame retardant type wall brick after being demoulded processing;
Wherein, the calcination temperature is to be warming up to 590 degrees Celsius of progress primary from 26 degrees Celsius with 7.9 centigrade per minutes
Calcining 1.5 hours then proceedes to be warming up to 1360 degrees Celsius of lower secondary clacinings, and calcination time is 0.7 hour.
Embodiment 4:
A kind of flame retardant type wall brick provided in this embodiment, the flame retardant type wall brick include the raw material being equipped with according to following number: powder
10-15 parts of coal ash, 10-15 parts of feldspar, 5-10 parts of perlite, 10-15 parts of laterite, 10-15 parts of glass fibre, nano zine oxide 4-
9 parts, 8-15 parts of nano silica, 6-12 parts of bamboo charcoal powder, 5-10 parts of steel slag, 5-15 parts of glass dregs, acrylic acid series elastic resin
3-7 parts, 1-3 parts of grinding aid, 3-5 parts of fire retardant, 1 .5-3 parts of antioxidant .5 parts of 1 .5-2 of heat stabilizer and water.
Further, the flame retardant type wall brick further includes 5-10 parts of antibacterial agent.
Further, the flame retardant type wall brick further includes 5-10 parts of anti-blushing agent.
Further, the flame retardant type wall brick further includes 3-9 parts of smectite powder.
Further, the fire retardant is melamine phosphate, melamine pyrophosphate.
Further, the heat stabilizer is the combination of 2 ethyl hexanoic acid salt, Ding Xinji ZDDP and N- phenyl-α-naphthylamine.
The present embodiment also discloses a kind of production method of flame retardant type wall brick, specifically includes the following steps:
1) flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag are subjected to primary filter;
2) then by filtered flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag and nano oxidized
Zinc, nano silica, bamboo charcoal powder, acrylic acid series elastic resin, grinding aid, fire retardant, antioxidant, heat stabilizer and water mixing
And it grinds and slurry is made, and the ratio of the water is adjusted in real time in grinding, ultimately becomes relatively sticky slurry;
3) painting oil processing is carried out to mold, then slurry is sent into the mold of oiling and carries out platen composition embryo material;
4) it after embryo material being carried out the pre-heat treatment cooling, calcined, cooled down and constitute flame retardant type wall brick after being demoulded processing;
Wherein, the calcination temperature is to be forged from 28 degrees Celsius with the 600 degrees Celsius of progress primary that are warming up to of 8 centigrade per minutes
It burns 1.5 hours, then proceedes to be warming up to 1390 degrees Celsius of lower secondary clacinings, calcination time is 0.8 hour.
Further, it is additionally added 8 parts of the antibacterial agent, 8 parts of anti-blushing agent, 7 parts of smectite powder in step 2.
Embodiment 5:
A kind of flame retardant type wall brick provided in this embodiment, the flame retardant type wall brick include the raw material being equipped with according to following number: powder
15 parts of coal ash, 15 parts of feldspar, 10 parts of perlite, 15 parts of laterite, 15 parts of glass fibre, 9 parts of nano zine oxide, nano silica
15 parts, 12 parts of bamboo charcoal powder, 10 parts of steel slag, 15 parts of glass dregs, 7 parts of acrylic acid series elastic resin, 3 parts of grinding aid, 5 parts of fire retardant,
3 parts of antioxidant, 2 .5 parts of heat stabilizer and water.
Further, the flame retardant type wall brick further includes 5-10 parts of antibacterial agent.
Further, the flame retardant type wall brick further includes 5-10 parts of anti-blushing agent.
Further, the flame retardant type wall brick further includes 3-9 parts of smectite powder.Antibacterial agent 10 described in the present embodiment
Part, 10 parts of anti-blushing agent, 9 parts of smectite powder.
Further, the fire retardant is ammonium polyphosphate, phosphoric acid narrows base urea, phosphate, melamine phosphate, melamine
One of pyrophosphate or a variety of combinations.
Further, the heat stabilizer is the combination of 2 ethyl hexanoic acid salt, Ding Xinji ZDDP and N- phenyl-α-naphthylamine.
The present embodiment also discloses a kind of production method of flame retardant type wall brick, specifically includes the following steps:
1) flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag are subjected to primary filter;
2) then by filtered flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag and nano oxidized
Zinc, nano silica, bamboo charcoal powder, acrylic acid series elastic resin, grinding aid, fire retardant, antioxidant, heat stabilizer and water mixing
And it grinds and slurry is made, and the ratio of the water is adjusted in real time in grinding, ultimately becomes relatively sticky slurry;
3) painting oil processing is carried out to mold, then slurry is sent into the mold of oiling and carries out platen composition embryo material;
4) it after embryo material being carried out the pre-heat treatment cooling, calcined, cooled down and constitute flame retardant type wall brick after being demoulded processing;
Wherein, the calcination temperature is to be forged from 30 degrees Celsius with the 700 degrees Celsius of progress primary that are warming up to of 9 centigrade per minutes
It burns 1.5 hours, then proceedes to be warming up to 1400 degrees Celsius of lower secondary clacinings, calcination time is 1 hour.
Further, it is additionally added antibacterial agent, anti-blushing agent and smectite powder in step 2.
The common wall brick of flame retardant type wall brick made from embodiment 1-5 and the prior art is tested for the property, final result
It is as follows, it is shown in Table 1:
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for those skilled in the art
For member, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from spirit of the invention or substantially
In the case where feature, the present invention can be realized in other specific forms.Therefore, in all respects, should all will implement
Example regards exemplary as, and is non-limiting, and the scope of the present invention is by appended claims rather than above description limits
It is fixed, it is intended that including all changes that fall within the meaning and scope of the equivalent elements of the claims in the present invention.To the greatest extent
The embodiment of the present invention has been shown and described in pipe, for the ordinary skill in the art, it is possible to understand that is not taking off
A variety of change, modification, replacement and modification, this hair can be carried out to these embodiments in the case where from the principle and spirit of the invention
Bright range is defined by the appended claims and the equivalents thereof.
Claims (10)
1. a kind of flame retardant type wall brick, which is characterized in that the flame retardant type wall brick includes the raw material being equipped with according to following number: fine coal
10-15 parts grey, 10-15 parts of feldspar, 5-10 parts of perlite, 10-15 parts of laterite, 10-15 parts of glass fibre, nano zine oxide 4-9
Part, 8-15 parts of nano silica, 6-12 parts of bamboo charcoal powder, 5-10 parts of steel slag, 5-15 parts of glass dregs, acrylic acid series elastic resin 3-
7 parts, 1-3 parts of grinding aid, 3-5 parts of fire retardant, 1 .5-3 parts of antioxidant .5 parts of 1 .5-2 of heat stabilizer and water.
2. a kind of flame retardant type wall brick according to claim 1, which is characterized in that the flame retardant type wall brick further includes antibacterial agent
5-10 parts.
3. a kind of flame retardant type wall brick according to claim 1 or 2, which is characterized in that the flame retardant type wall brick further includes preventing
Damp agent 5-10 parts.
4. a kind of flame retardant type wall brick according to claim 1 or 2, which is characterized in that the flame retardant type wall brick further includes changing
3-9 parts of montmorillonite powder of property.
5. a kind of flame retardant type wall brick according to claim 1 or 2, which is characterized in that including what is be equipped with according to following number
Raw material: 12 parts of flyash, 12 parts of feldspar, 8 parts of perlite, 12 parts of laterite, 12 parts of glass fibre, 8 part, nanometer two of nano zine oxide
12 parts of silica, 11 parts of bamboo charcoal powder, 8 parts of steel slag, 8 parts of glass dregs, 5 parts of acrylic acid series elastic resin, 2 parts of grinding aid, fire retardant 4
Part, 2 parts of antioxidant, 2 parts of heat stabilizer and water.
6. a kind of flame retardant type wall brick according to claim 3, which is characterized in that the smectite powder is 5 parts.
7. a kind of flame retardant type wall brick according to claim 1 or 2, which is characterized in that the fire retardant is ammonium polyphosphate, phosphorus
Acid narrows one of base urea, phosphate, melamine phosphate, melamine pyrophosphate or a variety of combinations.
8. a kind of flame retardant type wall brick according to claim 1 or 2, which is characterized in that the heat stabilizer is 2- ethyl hexyl
The combination of hydrochlorate, Ding Xinji ZDDP and N- phenyl-α-naphthylamine.
9. a kind of production method of flame retardant type wall brick, it is characterised in that specifically includes the following steps:
Flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag are subjected to primary filter;
Then by filtered flyash, feldspar, perlite, laterite, glass fibre, glass dregs and steel slag and nano oxidized
Zinc, nano silica, bamboo charcoal powder, acrylic acid series elastic resin, grinding aid, fire retardant, antioxidant, heat stabilizer and water mixing
And it grinds and slurry is made, and the ratio of the water is adjusted in real time in grinding, ultimately becomes relatively sticky slurry;
Painting oil processing is carried out to mold, then slurry is sent into the mold of oiling and carries out platen composition embryo material;
After embryo material is carried out the pre-heat treatment cooling, is calcined, cooled down and constitute flame retardant type wall brick after being demoulded processing;
Wherein, the calcination temperature is to be warming up to 500-700 degrees Celsius from 20-30 degrees Celsius with 7-9 centigrade per minute
Primary calcining 1.5 hours is carried out, then proceedes to be warming up to 1300-1400 degrees Celsius of lower secondary clacining, calcination time is that 0.5-1 is small
When.
10. a kind of production method of flame retardant type wall brick according to claim 9, it is characterised in that: be additionally added in step 2
Antibacterial agent.