CN109645578A - A kind of seamless Briefs and its manufacture craft - Google Patents
A kind of seamless Briefs and its manufacture craft Download PDFInfo
- Publication number
- CN109645578A CN109645578A CN201910065411.1A CN201910065411A CN109645578A CN 109645578 A CN109645578 A CN 109645578A CN 201910065411 A CN201910065411 A CN 201910065411A CN 109645578 A CN109645578 A CN 109645578A
- Authority
- CN
- China
- Prior art keywords
- parts
- yarn
- underpants
- auxiliary agent
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of seamless Briefs, the pouch that hot pressing is formed including underpants ontology and on underpants ontology, and the diameter of yarn its yarn for being woven into pocket areas is greater than the yarn diameter for being woven into underpants ontology.Upper hot pressing has one layer of anti-bacteria cloth bed of material on the inside of the pocket areas, the antibacterial cloth is woven by silver fiber and cotton, the cotton is handled by the first auxiliary agent, and first auxiliary agent includes the component of following parts by weight: 10-15 parts of nano-titanium dioxide, 3-5 parts of nano silver particles, 20-30 parts of zirconium dioxide, 50-80 parts of water.The present invention increases the thickness of pocket areas after having the effect of hot pressing pocket areas and increases underpants antibiotic health care.
Description
Technical field
The present invention relates to the technical fields of clothing making, more particularly, to a kind of seamless Briefs and its manufacture craft.
Background technique
Underpants are the necessitys in daily life, for protection privacy places of human body and maintain daily exercise it is comfortable
Degree.With the development of science and technology, the manufacture craft of underpants is also gradually being improved, human body dress and have to produce to be more suitable
The underpants of healthcare function.
Existing underpants manufacturing process, which mainly first passes through loom, will produce the seamless cylindric cloth of one, then lead to again
It crosses working cut and goes out underpants prototype.And Briefs usually also need to go out pouch by hot pressing on underpants, so that Briefs
It is more bonded skin, is worn more comfortable.
Prior art among the above has the following deficiencies: when Briefs generate pouch by hot pressing on underpants
When, fabric fibre at pouch is due to thinning by hot pressing and compared with other fibers, so that the cloth at pouch is more fragile,
Underpants are easy to be damaged during use.
Summary of the invention
In view of the deficiencies of the prior art, the present invention intends to provide a kind of underpants man Multifunctional underpants production
Technique, by the way that the yarn of pocket areas is used thicker yarn, to increase the wearability of pocket areas.
Above-mentioned purpose of the invention has the technical scheme that
A kind of seamless Briefs, the pouch that hot pressing is formed including underpants ontology and on underpants ontology are described to be woven into
The diameter of its yarn of the yarn of pocket areas is greater than the yarn diameter for being woven into underpants ontology.
By using above-mentioned technical proposal, diameter is greater than braiding underpants ontology to the yarn of pocket areas in the weaving process
Yarn diameter so that pocket areas still can keep after in hot pressing, yarn is extruded it is identical as underpants body yam diameter or
The diameter being not much different is not easy so that pocket areas still can keep certain intensity after hot-pressing in use process
In be worn.
The present invention is further arranged to: upper hot pressing has one layer of anti-bacteria cloth bed of material, the anti-bacteria cloth on the inside of the pocket areas
Material is woven by silver fiber and cotton, and the cotton is handled by the first auxiliary agent, and first auxiliary agent includes following heavy
Measure the component of number: 10-15 parts of nano-titanium dioxide, 3-5 parts of nano silver particles, 20-30 parts of zirconium dioxide, 50-80 parts of water.
By using above-mentioned technical proposal, zirconium dioxide forms metal oxide sol, Nano titanium dioxide in water
It is incorporated in metal oxide sol with nano silver particles, cotton passes through the first auxiliary agent again and handled, so that gluing on cotton
Titanium dioxide and silver particles are enclosed, titanium dioxide and silver particles have effects that certain antibiotic and sterilizing, so that cotton obtains
Antibacterial ability centainly, while it is blended together with cotton have silver fiber, silver fiber is further such that the antibacterial being woven into
Cloth has certain antibacterial ability.So that having the function of certain antibacterial bacteriostatic on the pocket areas of underpants, so that interior
Trousers relatively sanitary health when in use.
The present invention is further arranged to: the partial size of the nano silver particles and nano-titanium dioxide is not more than 15 nanometers.
By using above-mentioned technical proposal, when the partial size of nano silver particles is greater than 15 nanometers, nano silver particles are in colloidal sol
Poor dispersion, can not be uniformly distributed in colloidal sol, to can not equably cover on cotton.
The present invention is further arranged to: it is connected by adhesive with the anti-bacteria cloth bed of material on the inside of the pocket areas, it is described
The side of antibacterial cloth is arranged in adhesive;The silk thread of anti-bacteria cloth bed of material composition is handled by the second auxiliary agent, and described second
Auxiliary agent includes the component of following parts by weight: 20-30 parts of chitin, 10-15 parts of glutaraldehyde, 10-15 parts of N- hydroxy amide, pH tune
Agent 3-5 parts of section, 5-8 parts of buffer, 5-8 parts of coupling agent and 60-80 parts of water.
By using above-mentioned technical proposal, reaction is crosslinked by glutaraldehyde between chitin and fiber, so that composition
The silk thread of pouch is by overstriking, and chitin has certain anti-microbial property, so that pocket areas has certain antibiotic property, lemon
Not only the solvent as the crosslinking agent of chitin but also as dissolution chitin can make acid when citric acid and chitin are used in mixed way
Crease resistance is obtained to increase.
The present invention is further arranged to: described adhesive is by including that the group of following parts by weight is grouped as: methyl acrylate
30-60 parts, 20 parts -30 parts of isoamyl acetate, 10-20 parts of acetone, 10-13 parts of phenolic resin, 100-200 parts of deionized water.
By using above-mentioned technical proposal, methyl acrylate, phenolic resin under the action of acetone and isoamyl acetate
The solvent that colloid, acetone and isoamyl acetate are formed in water as dissolution has the dissolution of methyl acrylate, phenolic resin
Certain solubilization, methyl acrylate and phenolic resin can bond cloth, and the two molding rear surface is smooth, and has
Certain pliability when in use for underpants increases the comfort property of underpants.
A kind of manufacture craft of seamless Briefs, comprising the following steps:
S1: yarn is imported in large circle machine and carries out being compiled into semi-finished product underpants;
S2: hot pressing goes out pocket areas on semi-finished product underpants;
S3: method 1: the upper hot pressing anti-bacteria cloth bed of material on the inside of the pocket areas;
Method 2: the anti-bacteria cloth bed of material is bonded on the inside of pouch by adhesive on the inside of the pocket areas;
By above 3 steps, finished product man's Multifunctional underpants are obtained.
By using above-mentioned technical proposal, yarn first passes through large circle machine integrated woven and forms underpants ontology, then passes through heat
It is pressed in hot pressing on underpants ontology to go out to form pocket areas, then passes through hot pressing or adhesive for anti-bacteria cloth in the inside of pocket areas
Material is in conjunction with the cloth of pocket areas, to increase the antibacterial comfort of underpants.
The present invention is further arranged to: the cotton of the anti-bacteria cloth bed of material is at through the first auxiliary agent in the method 1
When reason the following steps are included:
(1) zirconium dioxide is mixed with water, is then heated to 60 to 80 degrees Celsius, stirred 20-30 minutes;
(2) nano-titanium dioxide and nano silver particles are added in above-mentioned mixed colloidal solution, and stirred evenly;
(3) staple line is immersed in above-mentioned solution, is kept for 30-40 degrees Celsius, impregnate 1-2h.
By using above-mentioned technical proposal, zirconium dioxide heating is lower and water can generate metal oxide sol, is lower than 60 DEG C
Relatively stable sol solution can not be all formed with being higher than 80 DEG C, if then titanium dioxide and Nano silver grain in colloidal sol again
It is mixed with colloidal sol, then yarn is impregnated, temperature is controlled at 30-40 degrees Celsius, and when being lower than 30 DEG C, colloidal sol is easy to happen cohesion and makes
The adhesion effect variation that yarn impregnates colloidal sol is obtained, when temperature is higher than 40 DEG C, colloidal sol can not largely be coated cotton.
It can be applied on cotton after yarn immersion 1-2h and be covered with most colloidal sol.
The present invention is further arranged to: when the yarn of the anti-bacteria cloth bed of material in the method two is handled with the second auxiliary agent
The following steps are included:
(1) first by yarn into the water, add pH adjusting agent adjust pH be 6-8;
(2) chitin and glutaraldehyde are added to the water, and are stirred;
(3) N- hydroxy amide, buffer and coupling agent are added to the water, are stirred;
(4) it maintains temperature at 40-60 DEG C, handles 30-60min.
By using above-mentioned technical proposal, pH is less than 6 and when being greater than 8, solution peracid or excessively alkali, so that the chitin being added
It can not be crosslinked in yarn fibers well with glutaraldehyde.First shell adding polysaccharide and glutaraldehyde, so that chitin and glutaraldehyde
It is first crosslinked on fiber, thickening fibre, chitin has certain antibiotic property, so that cloth has certain antibacterial
Ability.And the fibrous layer after being crosslinked thickens, so that fabric thickness made of braiding thickens, to increase the wear-resistant of cloth
Ability improves durability.
Compared with prior art, the beneficial effects of the present invention are:
1, the diameter for being greater than underpants ontology braided silk by the way that the wire diameter of pouch layer will be formed, thus hot-forming
When pouch, the thickness of pouch layer will not become too thin and be easy breakage;
2, by bonding antibacterial cloth on the inner sidewall of pouch layer, so that pouch layer has the guarantor of certain antibacterial bacteriostatic
Strong effect.
Detailed description of the invention
Fig. 1 is the perspective view of underpants of the present invention.
Appended drawing reference: 1, underpants ontology;2, pouch.
Specific embodiment
With reference to the accompanying drawings and examples, the present invention will be described in detail.
Embodiment one:
Referring to Fig.1, a kind of seamless Briefs disclosed by the invention, including underpants ontology 1 and the hot pressing on underpants ontology 1
The pouch 2 of formation, the diameter for being woven into the yarn in 2 region of pouch its yarn are greater than the yarn diameter for being woven into underpants ontology 1.
Manufacture craft the following steps are included:
A kind of manufacture craft of seamless Briefs, comprising the following steps:
S1: yarn is imported in large circle machine and carries out being compiled into semi-finished product underpants;
S2: hot pressing goes out pouch on semi-finished product underpants;
S3: the upper hot pressing anti-bacteria cloth bed of material on the inside of the pocket areas;Yarn on the anti-bacteria cloth bed of material passes through the first auxiliary agent
Processing:
(1) 20 parts of zirconium dioxide are mixed with 50 parts of water, is then heated to 60 to 80 degrees Celsius, stirred 20-30 minutes;
(2) 10 parts and 3 parts of nano silver particles of nano-titanium dioxide are added in above-mentioned mixed colloidal solution, and stirred
Uniformly;The partial size of nano silver particles and nano-titanium dioxide is not more than 15 nanometers.
(3) staple line is immersed in above-mentioned solution, is kept for 30 degrees Celsius, impregnate 1h.
By above 3 steps, finished product man's Multifunctional underpants are obtained.
Embodiment 2 is not all to embodiment 5 and embodiment 1: the parts by weight of each component are calculated as in first auxiliary agent
Following table.
Embodiment 6 to 9 the difference from embodiment 1 is that: first auxiliary agent processing when step (1) treatment temperature it is as follows
Table.
Embodiment | Temperature |
Embodiment 6 | 65 |
Embodiment 7 | 70 |
Embodiment 8 | 75 |
Embodiment 9 | 80 |
Embodiment 10 to 13 the difference from embodiment 1 is that: first auxiliary agent processing when step (1) mixing time such as
Following table.
Embodiment | Mixing time |
Embodiment 10 | 22.5 |
Embodiment 11 | 25 |
Embodiment 12 | 27.5 |
Embodiment 13 | 30 |
Embodiment 14 to 17 the difference from embodiment 1 is that: first auxiliary agent processing when step (3) treatment temperature such as
Following table.
Embodiment | Temperature |
Embodiment 14 | 32.5 |
Embodiment 15 | 35 |
Embodiment 16 | 37.5 |
Embodiment 17 | 40 |
Embodiment 14 to 17 the difference from embodiment 1 is that: first auxiliary agent processing when step (3) soaking time such as
Following table.
Embodiment | Soaking time |
Embodiment 18 | 1.25 |
Embodiment 19 | 1.5 |
Embodiment 20 | 1.75 |
Embodiment 21 | 2 |
Embodiment 22:
Referring to Fig.1, a kind of seamless Briefs disclosed by the invention, including underpants ontology 1 and the hot pressing on underpants ontology 1
The pouch 2 of formation, the diameter for being woven into the yarn in 2 region of pouch its yarn are greater than the yarn diameter for being woven into underpants ontology 1.
The configuration of adhesive: 30 parts of methyl acrylate, 20 parts of isoamyl acetate, 10 parts of acetone, 10 parts of phenolic resin, go from
100 parts of sub- water are uniformly mixed.
A kind of manufacture craft of seamless Briefs, comprising the following steps:
S1: yarn is imported in large circle machine and carries out being compiled into semi-finished product underpants;
S2: hot pressing goes out pouch on semi-finished product underpants;
S3: the anti-bacteria cloth bed of material is bonded on the inside of pouch by adhesive on the inside of the pocket areas;Antibacterial cloth
When yarn on layer passes through the processing of the second auxiliary agent the following steps are included:
(1) first by yarn into the water, add pH adjusting agent adjust pH be 6;
(2) 20 parts and 10 parts of glutaraldehyde of chitin are added to the water, and be stirred;
(3) it by 10 parts of N- hydroxy amide, 5 parts of buffer and 5 parts of coupling agent, 60 parts of water of addition, is stirred;
(4) it maintains temperature at 40 DEG C, handles 30min;
By above 3 steps, finished product man's Multifunctional underpants are obtained.
Embodiment 23-3 and the difference of embodiment 22 are: the parts by weight of each component are calculated as down in second auxiliary agent
Table.
Embodiment 31 to 34 and the difference of embodiment 22 are: the pH maintained in step (1) when second auxiliary agent processing
For following table.
Embodiment | pH |
Embodiment 31 | 6 |
Embodiment 32 | 6 |
Embodiment 33 | 7 |
Embodiment 34 | 8 |
Embodiment 35 to 38 and the difference of embodiment 22 are: the temperature maintained when second auxiliary agent processing is following table.
Embodiment | Temperature |
Embodiment 35 | 45 |
Embodiment 36 | 50 |
Embodiment 37 | 55 |
Embodiment 38 | 60 |
Embodiment 39 to 42 the difference from embodiment 1 is that: second auxiliary agent processing time is following table.
Embodiment | Time |
Embodiment 39 | 40 |
Embodiment 40 | 45 |
Embodiment 41 | 50 |
Embodiment 42 | 60 |
Embodiment 43 to 46 the difference from embodiment 1 is that: in the binder each component parts by weight be following table.
Comparative example
Comparative example 1 and comparative example 2 are the difference from embodiment 1 is that on the inside of pouch first used in the silk thread of antibacterial cloth composition
Auxiliary agent includes following parts by weight at being grouped as:
Comparative example 3-5 and the difference of embodiment 22 are that each component contained in the second auxiliary agent is as follows:
Detection method
Antibiotic property test
Anti-microbial property test: AATCC-90 test method(s): inoculation test bacterium (mould) on agar medium, then be close to try
Sample, after being cultivated for 24 hours at 37 DEG C, with the haloing size of aseptic area around amplification sem observation mushroom breeding situation and sample.It prevents
Bandwidth is successively increased by 1 grade to 10 grades.Bandwidth is prevented to represent the size of antibacterial efficacy.
Conclusion: the width of preventing belt can be seen that as the increase of nano-titanium dioxide and nano silver becomes by upper table
The anti-microbial property of width, the more wide then cloth of the width of preventing belt is better, it was demonstrated that nano-titanium dioxide and nano silver particles enhance really
The anti-microbial property of cloth.The prevention bandwidth of second auxiliary agent treated cloth is also apparently higher than comparative example 2, it was demonstrated that second helps
Agent increases the anti-microbial property of cloth.
Wearability test
Under certain load, sample is that the movement of Lissajous curve plane rubs with abrasive material with track in fixture,
Total Rubbing number, determines the wear-resisting property of fabric when occurring damaged with sample.Rub material selection: No.600 waterproof abrasive paper;Sampling: at least
Three pieces are taken, and the area of every group of cloth is identical, test result is averaged.
Group | Rubbing number |
Embodiment 23 | 5 times |
Embodiment 24 | 5 times |
Embodiment 25 | 6 times |
Embodiment 26 | 8 times |
Embodiment 27 | 4 times |
Embodiment 28 | 4 times |
Embodiment 29 | 5 times |
Embodiment 30 | 6 times |
Comparative example 3 | 1 time |
Comparative example 4 | 1 time |
Comparative example 5 | 3 times |
Conclusion: by upper table, the obvious Rubbing number than comparative example 3-5 of the Rubbing number of embodiment 22 to embodiment 29
It is more, it was demonstrated that the yarn fibers of chitin and glutaraldehyde and pouch layer produce crosslinking so that the thickness of cloth further adds really
Slightly.Embodiment 22-25 can be seen that the increase with chitin and glutaraldehyde, and the crosslinking degree of fiber increases, so that surveying
Rubbing number in test result increases.Embodiment 26-29 then proves that N- hydroxy amide has certain change for chitin crosslinking
Property effect, so that the degree of cross linking of chitin is strengthened to a certain extent, so that the wear-resisting property of cloth obtains certain increase.
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (8)
- It is special including underpants ontology (1) and hot pressing is formed on underpants ontology (1) pouch (2) 1. a kind of seamless Briefs Sign is: the diameter of yarn its yarn for being woven into pouch (2) region be greater than be woven into underpants ontology (1) yarn it is straight Diameter.
- 2. a kind of seamless Briefs according to claim 1, it is characterised in that: there is upper hot pressing on the inside of the pocket areas One layer of anti-bacteria cloth bed of material, the antibacterial cloth are woven by silver fiber and cotton, and the cotton passes through at the first auxiliary agent Reason, first auxiliary agent includes the component of following parts by weight: 10-15 parts of nano-titanium dioxide, 3-5 parts of nano silver particles, two 20-30 parts of zirconium oxide, 50-80 parts of water.
- 3. a kind of seamless Briefs according to claim 1, it is characterised in that: the nano silver particles and nano-silica The partial size for changing titanium is not more than 15 nanometers.
- 4. a kind of seamless Briefs according to claim 1, it is characterised in that: by viscous on the inside of the pocket areas Mixture is connected with the anti-bacteria cloth bed of material, and the side of antibacterial cloth is arranged in described adhesive;The silk thread of anti-bacteria cloth bed of material composition passes through Second auxiliary agent is handled, and second auxiliary agent includes the component of following parts by weight: 20-30 parts of chitin, glutaraldehyde 10-15 Part, 10-15 parts of N- hydroxy amide, 3-5 parts of pH adjusting agent, 5-8 parts of buffer, 5-8 parts of coupling agent and 60-80 parts of water.
- 5. a kind of seamless Briefs according to claim 1, it is characterised in that: described adhesive is by including following weight The group of number is grouped as: 30-60 parts of methyl acrylate, 20 parts -30 parts of isoamyl acetate, 10-20 parts of acetone, phenolic resin 10- 13 parts, 100-200 parts of deionized water.
- 6. a kind of manufacture craft of seamless Briefs, it is characterised in that the following steps are included:S1: the pretreated yarn in yarn and step 1 is imported in large circle machine and carries out being compiled into semi-finished product underpants;S2: hot pressing goes out pouch on semi-finished product underpants;S3: method 1: the upper hot pressing anti-bacteria cloth bed of material on the inside of the pocket areas;Method 2: the anti-bacteria cloth bed of material is bonded on the inside of pouch by adhesive on the inside of the pocket areas;By above 3 steps, finished product man's Multifunctional underpants are obtained.
- 7. a kind of seamless Briefs according to claim 1, it is characterised in that: the anti-bacteria cloth bed of material in the method 1 Cotton when being handled by the first auxiliary agent the following steps are included:(1) zirconium dioxide is mixed with water, is then heated to 60 to 80 degrees Celsius, stirred 20-30 minutes;(2) nano-titanium dioxide and nano silver particles are added in above-mentioned mixed colloidal solution, and stirred evenly;(3) staple line is immersed in above-mentioned solution, is kept for 30-40 degrees Celsius, impregnate 1-2h.
- 8. a kind of seamless Briefs according to claim 1, it is characterised in that: the anti-bacteria cloth bed of material in the method two Yarn when being handled with the second auxiliary agent the following steps are included:(1) first by yarn into the water, add pH adjusting agent adjust pH be 6-8;(2) chitin and glutaraldehyde are added to the water, and are stirred;(3) N- hydroxy amide, buffer and coupling agent are added to the water, are stirred;(4) it maintains temperature at 40-60 DEG C, handles 30-60min.