CN109627929A - A kind of red enamel polyester paint of China - Google Patents
A kind of red enamel polyester paint of China Download PDFInfo
- Publication number
- CN109627929A CN109627929A CN201811277632.7A CN201811277632A CN109627929A CN 109627929 A CN109627929 A CN 109627929A CN 201811277632 A CN201811277632 A CN 201811277632A CN 109627929 A CN109627929 A CN 109627929A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- agent
- ingredient
- red
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of red enamel polyester paint of China, including step 1 weigh polyester resin, cyclohexanone, solvent naphtha, high boiling solvent, 912 dispersing agents, anti-settling agent, red pigment by formula；High-speed stirred is ground to 15 μm or less and is made into slurry after above-mentioned ingredient is mixed；Step 2 weighs defoaming agent by formula, levelling agent, polyester resin, catalyst, amino resins, Amino resin, epoxy resin, above-mentioned ingredient is added sequentially to continue to stir and be added adjusting adhesive in the slurry in step 1, allotment is completed to be made.The red enamel polyester paint of China produced has the characteristics that glossiness is high, adhesive force is good, buckling performance is good, consumption is low.
Description
Technical field
The present invention relates to a kind of baking vanish, especially a kind of red enamel polyester paint of China.
Background technique
Coating is that one kind can be coated in object surface with different construction technologies, and formation is sticked securely, with centainly strong
Degree, continuous solid film.The film common name film formed in this way, also known as paint film or coating.It is divided into liquid coating by coating form
(solution-type, emulsion-type, dispersing type, no-solvent type), solids coating (powdery paints) etc.；By coating applications be divided into building coating,
Industrial coating, universal lacquer, sapecial coating；It is divided into water paint, solvent based coating, no-solvent type coating etc. by decentralized medium；
It is divided into antirusting paint, anticorrosive paint, heat-resistant coating, fireproof coating, coatings, antifouling paint etc. by functional coating film；By film
Function is divided into antirusting paint, anticorrosive paint, heat-resistant coating, fireproof coating, coatings, antifouling paint etc.；By construction method point
For spray painting, dipping lacquer, electrophoretic paint, certainly swimming paint, roller coating etc..
Coating has reflected light, shines, absorbs and reflect infrared ray, absorbs the light such as solar energy, shielding ray, flag colors
Learn the effect of aspect of performance；There are also various different roles such as antinoise, vibration damping, disinfecting, anti-condensation, anti-freeze etc..Coating
It is strong to ground or to the adhesive force of old paint film the features such as appearance gloss, color is fine and smooth with protecting light colour retention, there is hardness, punching
It hits, the characteristics such as flexibility.
Coating Industry in Our Country faces huge challenge at present, and the competition of Coating Market will be unprecedented, domestic enterprise
To occupy a tiny space in the market, the exploitation of new technology, new product is crucial.The exploitation of sapecial coating will become 21 century
The exploitation hot spot of Chinese Coating Market.The various functional paints in China --- waterproof material, fireproof coating, floor coatings, fluorine carbon
Coating, nano composite dope, camouflage paint, antifouling paint, anticorrosive paint, coil coating, aqueous polyurethane coating and heat-insulated
Coating etc..Coating is just towards low pollutions such as Water-borne modification, powdered, solvent free, high solid and radiation curing, nuisanceless simultaneously
Direction develop.These low pollutions, nuisanceless coating account for 70% or more of whole coating at present, have accounted for the 93% of coating within 2015
More than.Water paint is the main force of the following coating, accounts for 30% or more of world's coating total amount at present, coatings industry 2 most
It has overwhelming superiority in the building coating of one of big application field, especially in industrially developed country.In another maximum application
Field --- in industrial coating, water paint has accounted for the 20% of world industry coating, is up to 30% or more by 2010.
Summary of the invention
The technical problems to be solved in view of the defects of the present invention is to propose a kind of glossiness height, adhesive force
The red enamel polyester paint of China good, buckling performance is good, consumption is low.
The technical problem to be solved by the present invention is to what is be achieved through the following technical solutions, a kind of red enamel polyester paint of China,
Its main feature is that:
Including step 1,
Ingredient:
20 ~ 40 parts by weight of polyester resin, 1 ~ 5 parts by weight of cyclohexanone,
0.8 ~ 1.5 parts by weight of solvent naphtha, 0.5 ~ 1.0 parts by weight of high boiling solvent,
912 dispersing agent, 0.1 ~ 0.8 parts by weight, 0.1 ~ 0.8 parts by weight of anti-settling agent,
4 ~ 10 parts by weight of red pigment；
After above-mentioned ingredient is weighed by formula, high-speed stirred is ground to 15 μm or less and is made into slurry after mixing,
Step 2,
Ingredient:
0.1 ~ 0.3 parts by weight of defoaming agent, 0.3 ~ 0.8 parts by weight of levelling agent, 28 ~ 40 parts by weight of polyester resin, catalyst 0.2 ~ 0.6
Parts by weight, 2 ~ 6 parts by weight of amino resins, 12 ~ 18 parts by weight of Amino resin, 1 ~ 3 parts by weight of epoxy resin,
Continue to stir and be added 1 ~ 3 parts by weight in the slurry being added sequentially in step 1 after above-mentioned ingredient is weighed by formula
Adjusting adhesive, allotment are completed to be made.
The technical problem to be solved in the present invention can also further realize by the following technical programs, matching in step 1
Expect to be 30 parts by weight of polyester resin, 3 parts by weight of cyclohexanone, 1.25 parts by weight of solvent naphtha, 0.75 parts by weight of high boiling solvent, 912
0.4 parts by weight of dispersing agent, 0.5 parts by weight of anti-settling agent, 6 parts by weight of red pigment.
The technical problem to be solved in the present invention can also further realize by the following technical programs, matching in step 1
Material also contains the carbon black of 3 ~ 6 parts by weight.
The technical problem to be solved in the present invention can also further realize by the following technical programs, matching in step 2
Material is 0.2 parts by weight of defoaming agent, 0.5 parts by weight of levelling agent, 34 parts by weight of polyester resin, 0.5 parts by weight of catalyst, amino resins
4 parts by weight, 16 parts by weight of Amino resin, 2 parts by weight of epoxy resin.
The technical problem to be solved in the present invention can also further realize by the following technical programs, and the anti-settling agent is
Fumed silica.
The technical problem to be solved in the present invention can also further realize by the following technical programs, and the attachment is made every effort to promote
It is without polysiloxane non-ionic compound into agent.
The technical problem to be solved in the present invention can also further realize by the following technical programs, and defoaming agent is silicon oxygen
The twin body structure surface active agent of alkane type.
The technical problem to be solved in the present invention can also further realize by the following technical programs, and levelling agent is fluorine carbon
Modification acrylate.
Compared with prior art, the present invention mainly using polyester resin and Amino resin and by being added solely
Special formula and technique, the red enamel polyester paint of China produced is high with glossiness, adhesive force is good, buckling performance is good, consumption is low
The characteristics of.
Specific embodiment
The specific technical solution of the present invention described further below, in order to which those skilled in the art is further understood that
The present invention, without constituting the limitation to its right.
A kind of red enamel polyester paint of China, including step 1,
Ingredient:
20 ~ 40 parts by weight of polyester resin, 1 ~ 5 parts by weight of cyclohexanone,
0.8 ~ 1.5 parts by weight of solvent naphtha, 0.5 ~ 1.0 parts by weight of high boiling solvent,
912 dispersing agent, 0.1 ~ 0.8 parts by weight, 0.1 ~ 0.8 parts by weight of anti-settling agent,
4 ~ 10 parts by weight of red pigment；
After above-mentioned ingredient is weighed by formula, high-speed stirred is ground to 15 μm or less and is made into slurry after mixing,
Step 2,
Ingredient:
0.1 ~ 0.3 parts by weight of defoaming agent, 0.3 ~ 0.8 parts by weight of levelling agent, 28 ~ 40 parts by weight of polyester resin, catalyst 0.2 ~ 0.6
Parts by weight, 2 ~ 6 parts by weight of amino resins, 12 ~ 18 parts by weight of Amino resin, 1 ~ 3 parts by weight of epoxy resin,
Continue to stir and be added 1 ~ 3 parts by weight in the slurry being added sequentially in step 1 after above-mentioned ingredient is weighed by formula
Adjusting adhesive, allotment are completed to be made.
Recently the functionality of baking vanish is also had higher requirement, it is higher and higher to the requirement of product gloss, but to coating
Usage amount require it is lower and lower, the coating in market is no longer satisfied the demand of client.The red enamel polyester paint of China that I invents
Have the characteristics that glossiness is high, adhesive force is good, buckling performance is good, consumption is low.
Ingredient in specific step 1 is 30 parts by weight of polyester resin, 3 parts by weight of cyclohexanone, 1.25 weight of solvent naphtha
Part, 0.75 parts by weight of high boiling solvent, 912 dispersing agent, 0.4 parts by weight, 0.5 parts by weight of anti-settling agent, 6 parts by weight of red pigment.
Ingredient in step 1 also contains the carbon black of 3 ~ 6 parts by weight.It is preferred that the carbon black of 5 parts by weight.
Ingredient in specific step 2 is 0.2 parts by weight of defoaming agent, 0.5 parts by weight of levelling agent, 34 weight of polyester resin
Part, 0.5 parts by weight of catalyst, 4 parts by weight of amino resins, 16 parts by weight of Amino resin, 2 parts by weight of epoxy resin.
The anti-settling agent is fumed silica.
The adhesion promoter is without polysiloxane non-ionic compound.
Defoaming agent is the twin body structure surface active agent of silicone-type.
Levelling agent is fluorine-carbon modified acrylate.
High boiling solvent: sub-phosphono triamine (HMPT) molecular formula: C6H18N3OP molecular weight: 179.20 CAS
Number: 680-31-9 property: colorless and transparent runny liquid.
Polyester resin can be bought in market, select resin according to characteristic requirements.
Cyclohexanone is organic compound, is carbonylic carbon atom, it can dissolve coating, paint.
Solvent naphtha (s-100, s-150, s-180) using reformed arene as raw material, be chiefly used in advanced baking vanish effect higher boiling,
It is not volatile, it is the environment-friendly type solvent that smell is small at one.
912 dispersing agents have excellent pigment wetting dispersibility, are mainly added in due course with system material, its effect is to promote
Into fineness of grind, shorten milling time, composition: the mixture of polymeric carboxylic and modified polyorganosiloxane.
Anti-settling agent is a kind of fumed silica, is acted on as anti-settling pigment.
Defoaming agent is the twin body structure surface active agent of silicone-type, the requirement how much delustring spends, depending on being required according to degree
Amount.
Levelling agent, fluorine-carbon modified acrylate leveling agent promote surface levelling effect, prevent orange peel effect.
Catalyst is a kind of cationic surface active agent, can make coating catalyst, also can be used as amino-stoving varnish cooling
Catalyst.
Amino resins, height methyl-etherified, free formaldehyde are mutually dissolved in water and solvent, excellent flexibility
Epoxy resin, the main adhesive force for increasing baking vanish, corrosion resistance etc..
Adjusting adhesive is moderately adjusted according to viscosity and content requirement.
Adhesion promoter, the product can significantly improve resin and each to increase substantially the adhesive force of film layer and ground
The binding force of kind substrate, can greatly improve the ply adhesion between paint finishing coat and priming paint, hence it is evident that improve the moisture resistant of film
Performance, resistance to saltfog energy and heat resistance, minimum dosage can be obtained high-strength adhesive force and bond power.In paint systems
It is excellent storage stability and long-term effect.Composition is: being free of polysiloxane non-ionic compound, appearance supernatant liquid.City
Such product can be found on.
Testing conditions and requirement
Galvanized sheet 0.30mm is thick, and bar scrapes sample baking detection
240 DEG C of baking temperature, 60 seconds 193-216 DEG C of plate temperature of baking time
Double painting techniques: thickness of dry film, 3 μm -5 μm of priming paint, finishing coat: 13-16 μm
Surface drying, (resistance to butanone wipes 5 times and breaks) finishing coat secondary baking can reach requirement performance.
Detection performance result:
90-100 ° of gloss,
Hardness >=3H,
O grades of adhesive force (drawing lattice),
Impact force 13J,
T is curved≤and 2T do not split,
Resistance to butanone (mek) >=150 time.
Process flow and requirement
1, check whether equipment, tool are normal, safety, health；
2, labour protection articles for use is worn；
3, by formula accurate weighing ingredient；
4, high-speed stirred (pre-dispersed) is ground to fineness requirement；
5, finished product ingredient；
6, item performance inverse indicator is closed in detection；
7, toning detects performance indexes again；
8, qualified packaging.
Claims (8)
1. a kind of red enamel polyester paint of China, it is characterised in that:
Including step 1,
Ingredient:
20 ~ 40 parts by weight of polyester resin, 1 ~ 5 parts by weight of cyclohexanone,
0.8 ~ 1.5 parts by weight of solvent naphtha, 0.5 ~ 1.0 parts by weight of high boiling solvent,
912 dispersing agent, 0.1 ~ 0.8 parts by weight, 0.1 ~ 0.8 parts by weight of anti-settling agent,
4 ~ 10 parts by weight of red pigment；
After above-mentioned ingredient is weighed by formula, high-speed stirred is ground to 15 μm or less and is made into slurry after mixing,
Step 2,
Ingredient:
0.1 ~ 0.3 parts by weight of defoaming agent, 0.3 ~ 0.8 parts by weight of levelling agent, 28 ~ 40 parts by weight of polyester resin, catalyst 0.2 ~ 0.6
Parts by weight, 2 ~ 6 parts by weight of amino resins, 12 ~ 18 parts by weight of Amino resin, 1 ~ 3 parts by weight of epoxy resin,
Continue to stir and be added 1 ~ 3 parts by weight in the slurry being added sequentially in step 1 after above-mentioned ingredient is weighed by formula
Adjusting adhesive, allotment are completed to be made.
2. the red enamel polyester paint of China according to claim 1, it is characterised in that: the ingredient in step 1 is polyester resin 30
Parts by weight, 3 parts by weight of cyclohexanone, 1.25 parts by weight of solvent naphtha, 0.75 parts by weight of high boiling solvent, 912 dispersing agent, 0.4 weight
Part, 0.5 parts by weight of anti-settling agent, 6 parts by weight of red pigment.
3. the red enamel polyester paint of China according to claim 1 or 2, it is characterised in that: the ingredient in step 1 also contains 3 ~ 6
The carbon black of parts by weight.
4. the red enamel polyester paint of China according to claim 1, it is characterised in that: the ingredient in step 2 is defoaming agent 0.2
Parts by weight, 0.5 parts by weight of levelling agent, 34 parts by weight of polyester resin, 0.5 parts by weight of catalyst, 4 parts by weight of amino resins, methyl ether
Change 16 parts by weight of amino resins, 2 parts by weight of epoxy resin.
5. the red enamel polyester paint of China according to claim 1, it is characterised in that: the anti-settling agent is vapor phase method titanium dioxide
Silicon.
6. the red enamel polyester paint of China according to claim 1, it is characterised in that: the adhesion promoter is without poly- silicon
Oxygen alkane nonionic compound.
7. the red enamel polyester paint of China according to claim 1, it is characterised in that: defoaming agent is the twin structure table of silicone-type
Face activating agent.
8. the technical problem to be solved in the present invention can also further realize by the following technical programs, levelling agent is that fluorine carbon changes
Property acrylate.