CN109627899A - A kind of paint composite - Google Patents

A kind of paint composite Download PDF

Info

Publication number
CN109627899A
CN109627899A CN201811524034.5A CN201811524034A CN109627899A CN 109627899 A CN109627899 A CN 109627899A CN 201811524034 A CN201811524034 A CN 201811524034A CN 109627899 A CN109627899 A CN 109627899A
Authority
CN
China
Prior art keywords
parts
uniformly mixed
paint
modified additive
oil resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811524034.5A
Other languages
Chinese (zh)
Inventor
折伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201811524034.5A priority Critical patent/CN109627899A/en
Publication of CN109627899A publication Critical patent/CN109627899A/en
Pending legal-status Critical Current

Abstract

The invention belongs to paint process technical fields, a kind of paint composite is specifically disclosed, the components such as polyamide, phenolic resin, acrylic resin, rosin resin, phthalic anhydride, chlorinated paraffin, nano silica, calcium carbonate powder, tartaric acid, diacetanilide, ammonium polyphosphate, pentaerythrite, chitosan, oil resistant modified additive, antibacterial modified auxiliary agent are included；The oil resistivity modified additive and antibiotic property modified additive are mutually compounded with other auxiliary elements, generate synergistic effect, and the paint is made to have oil resistant antibacterial action；Paint of the present invention is applied to body surface, can effectively prevent bacteria breed, prevents damage of the oil smoke to utensil, and also not easily to fall off or colour fading can form one layer of thin and tough and tensile protective film in tool face, extend utensil service life；In addition, paint of the present invention is non-hazardous to environment and human body, environmental protection.

Description

A kind of paint composite
Technical field
The invention belongs to paint process technical fields, and in particular to a kind of paint composite.
Background technique
Paint be it is a kind of can securely be covered on body surface, the chemistry for playing protection, decoration, mark and other specific uses is mixed Close object coating.Coating is a kind of material, and this material can be coated in object surface with different construction technologies, form adherency Securely, there is some strength, continuous solid film.The film common name film formed in this way, also known as paint film or coating.
In existing paint, many paint have used stupid class, ketone and lipid equal solvent in process of production, these Solvent highly volatile can cause environmental pollution in production and in, can also cause not to the health of the worker of construction site With the harm of degree.But although in the prior art paint meets the requirement of environmental-protecting performance, since environment protection oil paint is big It is chiefly used in daily life, this just has a higher requirement to the antibacterial of environment protection oil paint and oil resistance, but oil resistant and antibacterial Performance is unable to satisfy demand in actual use, it is difficult to be applied to having on the implements of ecological requirements for oil smoke weight easily growth bacterium.
Summary of the invention
The present invention provides a kind of paint composite, the paint has excellent oil resistant, anti-microbial property, is applied to simultaneously Coating on surface of article has preferable protective effect to utensil.
Specific technical solution of the present invention is as follows:
A kind of paint composite, it is characterised in that: include following components:
Polyamide, phenolic resin, acrylic resin, rosin resin, phthalic anhydride, chlorinated paraffin, nanometer titanium dioxide Silicon, bentonite, cellulose acetate, diatomite, glycerol, tributyl citrate, tartaric acid, diacetanilide, gathers calcium carbonate powder Ammonium phosphate, pentaerythrite, chitosan, oil resistant modified additive, antibacterial modified auxiliary agent；
The component is weighed by following mass parts:
3 ~ 7 parts of polyamide, 13 ~ 18 parts of phenolic resin, 10 ~ 20 parts of acrylic resin, 5 ~ 12 parts of rosin resin, O-phthalic 5 ~ 12 parts of acid anhydrides, 6 ~ 13 parts of chlorinated paraffin, 1 ~ 5 part of nano silica, 14 ~ 23 parts of calcium carbonate powder, 7 ~ 15 parts of bentonite, vinegar 7 ~ 15 parts of acid cellulose, 2 ~ 6 parts of diatomite, 3 ~ 7 parts of glycerol, 12 ~ 20 parts of tributyl citrate, 13 ~ 17 parts of tartaric acid, biacetyl 5 ~ 12 parts of aniline, 5 ~ 13 parts of ammonium polyphosphate, 6 ~ 14 parts of pentaerythrite, 7 ~ 15 parts of chitosan, 3 ~ 7 parts of oil resistant modified additive, antibacterial 5 ~ 10 parts of modified additive.
Preferably, the ingredient is weighed by following mass parts:
4 parts of polyamide, 15 parts of phenolic resin, 17 parts of acrylic resin, 9 parts of rosin resin, 9 parts of phthalic anhydride, chlorine 10 parts of fossil waxes, 3 parts of nano silica, 18 parts of calcium carbonate powder, 12 parts of bentonite, 13 parts of cellulose acetate, diatomite 4 Part, 5 parts of glycerol, 17 parts of tributyl citrate, 14 parts of tartaric acid, 7 parts of diacetanilide, 8 parts of ammonium polyphosphate, pentaerythrite 12 Part, 8 parts of chitosan, 5 parts of oil resistant modified additive, 7 parts of antibacterial modified auxiliary agent.
Preferably, the oil resistant modified additive the preparation method comprises the following steps: octylisothiazolinone is uniformly mixed with water, keep Constant temperature is added nano-titanium dioxide, zinc stearate, magnesium stearate and carborundum powder and is uniformly mixed, continues to heat up, constant temperature stirring, Zeolite powder is added after cooling down again and nitrocotton is uniformly mixed, grinding, silane coupling agent is then added and is uniformly mixed, stirs, drying, Grinding, sieving, obtains mix products；The mix products are mixed with 4-dimethylaminopyridine, dicyclohexylcarbodiimide Even, heating, stirred under nitrogen atmosphere removes supernatant liquor, washs, and filters, and freeze-drying obtains oil resistant modified additive.
Preferably, the octylisothiazolinone, nano-titanium dioxide, zinc stearate, magnesium stearate and carborundum powder with And 4-dimethylaminopyridine, dicyclohexylcarbodiimide are weighed by following mass parts: 4 ~ 9 parts of octylisothiazolinone is received Rice 5 ~ 12 parts of titanium dioxide, 7 ~ 15 parts of zinc stearate, 1 ~ 5 part of magnesium stearate, 4 ~ 9 parts of carborundum powder, 4-dimethylaminopyridine 1 ~ 4 Part, 7 ~ 18 parts of dicyclohexylcarbodiimide.
Preferably, the antibacterial modified auxiliary agent the preparation method comprises the following steps: hydroxyethyl cellulose, attapulgite, sodium chloride solution It is uniformly mixed, is stirred after heating, filtering means dehydration, dry, then roast, be then placed in lanthanum chloride solution, stir, filtering is de- Water, drying, then roasts, is subsequently placed in silver nitrate solution, stirs, obtains mix products after drying；By the mix products It is uniformly mixed, stirs, vacuum filter with ethyl orthosilicate, vinyltriethoxysilane, then it is fine that acetate butyrate is added in washing It after dimension element mixing, heats up, stirring is dry to constant weight, is cooled to room temperature to obtain antibacterial modified auxiliary agent.
Preferably, the hydroxyethyl cellulose, attapulgite, sodium chloride solution, ethyl orthosilicate, vinyl triethoxyl Silane is weighed by following mass parts: 10 ~ 18 parts of hydroxyethyl cellulose, 5 ~ 12 parts of attapulgite, sodium chloride solution 20 ~ 28 Part, 7 ~ 15 parts of ethyl orthosilicate, 12 ~ 23 parts of vinyltriethoxysilane.
The invention has the advantages that:
The invention discloses a kind of paint composite, the oil resistivity modified additive and antibiotic property modified additive and other auxiliary at Split-phase mutually compounds, and generates synergistic effect, and the paint is made to have oil resistant antibacterial action；Paint of the present invention is applied to object table Face, it can be effectively prevent bacteria breed, prevent damage of the oil smoke to utensil, also not easily to fall off or colour fading can be in tool face shape At one layer of thin and tough and tensile protective film, extend utensil service life；In addition, paint of the present invention is to environment and human body without danger Evil, environmental protection.
Specific embodiment
Technical solution of the present invention is further illustrated below by specific embodiment.
A kind of paint composite, it is characterised in that: include following components:
Polyamide, phenolic resin, acrylic resin, rosin resin, phthalic anhydride, chlorinated paraffin, nanometer titanium dioxide Silicon, bentonite, cellulose acetate, diatomite, glycerol, tributyl citrate, tartaric acid, diacetanilide, gathers calcium carbonate powder Ammonium phosphate, pentaerythrite, chitosan, oil resistant modified additive, antibacterial modified auxiliary agent；
The component is weighed by following mass parts:
3 parts of polyamide, 13 parts of phenolic resin, 10 parts of acrylic resin, 5 parts of rosin resin, 5 parts of phthalic anhydride, chlorine It is 6 parts of fossil waxes, 1 part of nano silica, 14 parts of calcium carbonate powder, 7 parts of bentonite, 7 parts of cellulose acetate, 2 parts of diatomite, sweet 3 parts of oil, 12 parts of tributyl citrate, 13 parts of tartaric acid, 5 parts of diacetanilide, 5 parts of ammonium polyphosphate, 6 parts of pentaerythrite, shell are poly- Sugared 7 parts, 3 parts of oil resistant modified additive, 5 parts of antibacterial modified auxiliary agent；
The oil resistant modified additive the preparation method comprises the following steps: octylisothiazolinone is uniformly mixed with water, keep constant temperature, addition is received Rice titanium dioxide, zinc stearate, magnesium stearate and carborundum powder are uniformly mixed, and continue to heat up, constant temperature stirring, then are added after cooling down Zeolite powder and nitrocotton are uniformly mixed, grinding, and silane coupling agent is then added and is uniformly mixed, stirs, dries, grinds, and sieving obtains To mix products；The mix products are uniformly mixed with 4-dimethylaminopyridine, dicyclohexylcarbodiimide, are heated up, nitrogen The lower stirring of protection, removes supernatant liquor, washs, filter, freeze-drying obtains oil resistant modified additive；The Octylisothiazoline Ketone, nano-titanium dioxide, zinc stearate, magnesium stearate and carborundum powder and 4-dimethylaminopyridine, dicyclohexyl carbon two are sub- Amine is weighed by following mass parts: 4 parts of octylisothiazolinone, 5 parts of nano-titanium dioxide, 7 parts of zinc stearate, magnesium stearate 1 part, 4 parts of carborundum powder, 1 part of 4-dimethylaminopyridine, 7 parts of dicyclohexylcarbodiimide；
The antibacterial modified auxiliary agent the preparation method comprises the following steps: hydroxyethyl cellulose, attapulgite, sodium chloride solution be uniformly mixed, rise It is stirred after temperature, filtering means dehydration, dries, then roast, be then placed in lanthanum chloride solution, stirred, filtering means dehydration, drying, then Roasting, is subsequently placed in silver nitrate solution, stirs, obtains mix products after drying；By the mix products and ethyl orthosilicate, Vinyltriethoxysilane is uniformly mixed, stirring, vacuum filter, washing, after acetylbutyrylcellulose mixing is then added, is risen Temperature, stirring is dry to constant weight, is cooled to room temperature to obtain antibacterial modified auxiliary agent；The hydroxyethyl cellulose, attapulgite, chlorination Sodium solution, ethyl orthosilicate, vinyltriethoxysilane are weighed by following mass parts: 10 parts of hydroxyethyl cellulose, recessed Convex stick native 5 parts, 20 parts of sodium chloride solution, 7 parts of ethyl orthosilicate, 12 parts of vinyltriethoxysilane.
Embodiment 2
A kind of paint composite, it is characterised in that: include following components:
Polyamide, phenolic resin, acrylic resin, rosin resin, phthalic anhydride, chlorinated paraffin, nanometer titanium dioxide Silicon, bentonite, cellulose acetate, diatomite, glycerol, tributyl citrate, tartaric acid, diacetanilide, gathers calcium carbonate powder Ammonium phosphate, pentaerythrite, chitosan, oil resistant modified additive, antibacterial modified auxiliary agent；
The component is weighed by following mass parts:
7 parts of polyamide, 18 parts of phenolic resin, 20 parts of acrylic resin, 12 parts of rosin resin, 12 parts of phthalic anhydride, 13 parts of chlorinated paraffin, 5 parts of nano silica, 23 parts of calcium carbonate powder, 15 parts of bentonite, 15 parts of cellulose acetate, diatomite 6 Part, 7 parts of glycerol, 20 parts of tributyl citrate, 17 parts of tartaric acid, 12 parts of diacetanilide, 13 parts of ammonium polyphosphate, pentaerythrite 14 Part, 15 parts of chitosan, 7 parts of oil resistant modified additive, 10 parts of antibacterial modified auxiliary agent；
The oil resistant modified additive the preparation method comprises the following steps: octylisothiazolinone is uniformly mixed with water, keep constant temperature, addition is received Rice titanium dioxide, zinc stearate, magnesium stearate and carborundum powder are uniformly mixed, and continue to heat up, constant temperature stirring, then are added after cooling down Zeolite powder and nitrocotton are uniformly mixed, grinding, and silane coupling agent is then added and is uniformly mixed, stirs, dries, grinds, and sieving obtains To mix products；The mix products are uniformly mixed with 4-dimethylaminopyridine, dicyclohexylcarbodiimide, are heated up, nitrogen The lower stirring of protection, removes supernatant liquor, washs, filter, freeze-drying obtains oil resistant modified additive；The Octylisothiazoline Ketone, nano-titanium dioxide, zinc stearate, magnesium stearate and carborundum powder and 4-dimethylaminopyridine, dicyclohexyl carbon two are sub- Amine is weighed by following mass parts: 9 parts of octylisothiazolinone, 12 parts of nano-titanium dioxide, 15 parts of zinc stearate, stearic acid 5 parts of magnesium, 9 parts of carborundum powder, 4 parts of 4-dimethylaminopyridine, 18 parts of dicyclohexylcarbodiimide；
The antibacterial modified auxiliary agent the preparation method comprises the following steps: hydroxyethyl cellulose, attapulgite, sodium chloride solution be uniformly mixed, rise It is stirred after temperature, filtering means dehydration, dries, then roast, be then placed in lanthanum chloride solution, stirred, filtering means dehydration, drying, then Roasting, is subsequently placed in silver nitrate solution, stirs, obtains mix products after drying；By the mix products and ethyl orthosilicate, Vinyltriethoxysilane is uniformly mixed, stirring, vacuum filter, washing, after acetylbutyrylcellulose mixing is then added, is risen Temperature, stirring is dry to constant weight, is cooled to room temperature to obtain antibacterial modified auxiliary agent；The hydroxyethyl cellulose, attapulgite, chlorination Sodium solution, ethyl orthosilicate, vinyltriethoxysilane are weighed by following mass parts: 18 parts of hydroxyethyl cellulose, recessed Convex stick native 12 parts, 28 parts of sodium chloride solution, 15 parts of ethyl orthosilicate, 23 parts of vinyltriethoxysilane.
Embodiment 3
A kind of paint composite, it is characterised in that: include following components:
Polyamide, phenolic resin, acrylic resin, rosin resin, phthalic anhydride, chlorinated paraffin, nanometer titanium dioxide Silicon, bentonite, cellulose acetate, diatomite, glycerol, tributyl citrate, tartaric acid, diacetanilide, gathers calcium carbonate powder Ammonium phosphate, pentaerythrite, chitosan, oil resistant modified additive, antibacterial modified auxiliary agent；
The ingredient is weighed by following mass parts:
4 parts of polyamide, 15 parts of phenolic resin, 17 parts of acrylic resin, 9 parts of rosin resin, 9 parts of phthalic anhydride, chlorine 10 parts of fossil waxes, 3 parts of nano silica, 18 parts of calcium carbonate powder, 12 parts of bentonite, 13 parts of cellulose acetate, diatomite 4 Part, 5 parts of glycerol, 17 parts of tributyl citrate, 14 parts of tartaric acid, 7 parts of diacetanilide, 8 parts of ammonium polyphosphate, pentaerythrite 12 Part, 8 parts of chitosan, 5 parts of oil resistant modified additive, 7 parts of antibacterial modified auxiliary agent；
The oil resistant modified additive the preparation method comprises the following steps: octylisothiazolinone is uniformly mixed with water, keep constant temperature, addition is received Rice titanium dioxide, zinc stearate, magnesium stearate and carborundum powder are uniformly mixed, and continue to heat up, constant temperature stirring, then are added after cooling down Zeolite powder and nitrocotton are uniformly mixed, grinding, and silane coupling agent is then added and is uniformly mixed, stirs, dries, grinds, and sieving obtains To mix products；The mix products are uniformly mixed with 4-dimethylaminopyridine, dicyclohexylcarbodiimide, are heated up, nitrogen The lower stirring of protection, removes supernatant liquor, washs, filter, freeze-drying obtains oil resistant modified additive；The Octylisothiazoline Ketone, nano-titanium dioxide, zinc stearate, magnesium stearate and carborundum powder and 4-dimethylaminopyridine, dicyclohexyl carbon two are sub- Amine is weighed by following mass parts: 7 parts of octylisothiazolinone, 9 parts of nano-titanium dioxide, 13 parts of zinc stearate, stearic acid 4 parts of magnesium, 6 parts of carborundum powder, 3 parts of 4-dimethylaminopyridine, 14 parts of dicyclohexylcarbodiimide；
The antibacterial modified auxiliary agent the preparation method comprises the following steps: hydroxyethyl cellulose, attapulgite, sodium chloride solution be uniformly mixed, rise It is stirred after temperature, filtering means dehydration, dries, then roast, be then placed in lanthanum chloride solution, stirred, filtering means dehydration, drying, then Roasting, is subsequently placed in silver nitrate solution, stirs, obtains mix products after drying；By the mix products and ethyl orthosilicate, Vinyltriethoxysilane is uniformly mixed, stirring, vacuum filter, washing, after acetylbutyrylcellulose mixing is then added, is risen Temperature, stirring is dry to constant weight, is cooled to room temperature to obtain antibacterial modified auxiliary agent；The hydroxyethyl cellulose, attapulgite, chlorination Sodium solution, ethyl orthosilicate, vinyltriethoxysilane are weighed by following mass parts: 15 parts of hydroxyethyl cellulose, recessed Convex stick native 8 parts, 25 parts of sodium chloride solution, 13 parts of ethyl orthosilicate, 19 parts of vinyltriethoxysilane.

Claims (6)

1. a kind of paint composite, it is characterised in that: include following components:
Polyamide, phenolic resin, acrylic resin, rosin resin, phthalic anhydride, chlorinated paraffin, nanometer titanium dioxide Silicon, bentonite, cellulose acetate, diatomite, glycerol, tributyl citrate, tartaric acid, diacetanilide, gathers calcium carbonate powder Ammonium phosphate, pentaerythrite, chitosan, oil resistant modified additive, antibacterial modified auxiliary agent；
The component is weighed by following mass parts:
3 ~ 7 parts of polyamide, 13 ~ 18 parts of phenolic resin, 10 ~ 20 parts of acrylic resin, 5 ~ 12 parts of rosin resin, O-phthalic 5 ~ 12 parts of acid anhydrides, 6 ~ 13 parts of chlorinated paraffin, 1 ~ 5 part of nano silica, 14 ~ 23 parts of calcium carbonate powder, 7 ~ 15 parts of bentonite, vinegar 7 ~ 15 parts of acid cellulose, 2 ~ 6 parts of diatomite, 3 ~ 7 parts of glycerol, 12 ~ 20 parts of tributyl citrate, 13 ~ 17 parts of tartaric acid, biacetyl 5 ~ 12 parts of aniline, 5 ~ 13 parts of ammonium polyphosphate, 6 ~ 14 parts of pentaerythrite, 7 ~ 15 parts of chitosan, 3 ~ 7 parts of oil resistant modified additive, antibacterial 5 ~ 10 parts of modified additive.
2. paint composite according to claim 1, it is characterised in that the ingredient is weighed by following mass parts:
4 parts of polyamide, 15 parts of phenolic resin, 17 parts of acrylic resin, 9 parts of rosin resin, 9 parts of phthalic anhydride, chlorine 10 parts of fossil waxes, 3 parts of nano silica, 18 parts of calcium carbonate powder, 12 parts of bentonite, 13 parts of cellulose acetate, diatomite 4 Part, 5 parts of glycerol, 17 parts of tributyl citrate, 14 parts of tartaric acid, 7 parts of diacetanilide, 8 parts of ammonium polyphosphate, pentaerythrite 12 Part, 8 parts of chitosan, 5 parts of oil resistant modified additive, 7 parts of antibacterial modified auxiliary agent.
3. paint composite according to claim 1, it is characterised in that the oil resistant modified additive the preparation method comprises the following steps: by pungent Base isothiazolinone is uniformly mixed with water, keeps constant temperature, and nano-titanium dioxide, zinc stearate, magnesium stearate and silicon carbide is added Powder is uniformly mixed, and continues to heat up, constant temperature stirring, then zeolite powder is added after cooling down and nitrocotton is uniformly mixed, then grinding is added Silane coupling agent is uniformly mixed, and is stirred, and is dried, and is ground, and sieving obtains mix products；By the mix products and 4- diformazan ammonia Yl pyridines, dicyclohexylcarbodiimide are uniformly mixed, heating, and stirred under nitrogen atmosphere removes supernatant liquor, washs, and filters, cold Jelly is dried to obtain oil resistant modified additive.
4. paint composite according to claim 3, it is characterised in that the octylisothiazolinone, nano-titanium dioxide, Zinc stearate, magnesium stearate and carborundum powder and 4-dimethylaminopyridine, dicyclohexylcarbodiimide are by following mass parts It is weighed: 4 ~ 9 parts of octylisothiazolinone, 5 ~ 12 parts of nano-titanium dioxide, 7 ~ 15 parts of zinc stearate, 1 ~ 5 part of magnesium stearate, carbon 4 ~ 9 parts of SiClx powder, 1 ~ 4 part of 4-dimethylaminopyridine, 7 ~ 18 parts of dicyclohexylcarbodiimide.
5. paint composite according to claim 1, it is characterised in that the antibacterial modified auxiliary agent the preparation method comprises the following steps: hydroxyl second Base cellulose, attapulgite, sodium chloride solution are uniformly mixed, and are stirred after heating, filtering means dehydration, are dried, are then roasted, then set In lanthanum chloride solution, stirring, filtering means dehydration dries, then roasts, be subsequently placed in silver nitrate solution, stirs, after drying To mix products；The mix products are uniformly mixed with ethyl orthosilicate, vinyltriethoxysilane, are stirred, vacuum mistake Filter, washing heat up after acetylbutyrylcellulose mixing is then added, and stirring is dry to constant weight, are cooled to room temperature to obtain antibacterial Modified additive.
6. paint composite according to claim 5, it is characterised in that the hydroxyethyl cellulose, attapulgite, sodium chloride Solution, ethyl orthosilicate, vinyltriethoxysilane are weighed by following mass parts: 10 ~ 18 parts of hydroxyethyl cellulose, recessed 5 ~ 12 parts of convex stick soil, 20 ~ 28 parts of sodium chloride solution, 7 ~ 15 parts of ethyl orthosilicate, 12 ~ 23 parts of vinyltriethoxysilane.
CN201811524034.5A 2018-12-13 2018-12-13 A kind of paint composite Pending CN109627899A (en)