CN109627861A - Interiro wall latex paint - Google Patents
Interiro wall latex paint Download PDFInfo
- Publication number
- CN109627861A CN109627861A CN201811586855.1A CN201811586855A CN109627861A CN 109627861 A CN109627861 A CN 109627861A CN 201811586855 A CN201811586855 A CN 201811586855A CN 109627861 A CN109627861 A CN 109627861A
- Authority
- CN
- China
- Prior art keywords
- parts
- latex paint
- wall latex
- interiro wall
- interiro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of interiro wall latex paints, including following parts by weight of component: 10-17.5 parts of deionized water；0.5-0.7 parts of dispersing agent；0.15-0.2 parts of wetting agent；0.3-0.4 parts of defoaming agent；1.5-2.0 parts of propylene glycol；0.5-1.0 parts of alcohol ester-12；18-20 parts of titanium dioxide；10-12.8 parts of dicalcium powder；Functional lotion 38-40 parts；1-1.2 parts of thickener；The pH value of interiro wall latex paint is 8-9.Interiro wall latex paint of the present invention has the hydrophobic effect of similar lotus leaf, and recoatability is good, and paint film richness is high, has excellent water-fast and spot-resistant performance.
Description
Technical field
The present invention relates to paint field, in particular to a kind of interiro wall latex paint with lotus leaf effect.
Background technique
Interiro wall latex paint is one of indoor wall, ceiling primary decoration material, and feature is good decorating effect, easy for construction,
Environmental pollution is small, at low cost, and application range is extremely wide.Wherein, the interiro wall latex paint with hydrophobic effect is relatively strong because having
Hydrophobic self-cleaning function and have more and more wide application prospect.
At present, it is common to use the interiro wall latex paint with hydrophobic effect be on the basis of common interiro wall latex paint lead to
Crossing addition, there is the auxiliary agent of hydrophobic function to synthesize to obtain, the additive amount of coalescing agent is larger, cause this kind of with hydrophobic effect
The production cost of interiro wall latex paint is higher, in addition, coalescing agent contains a certain amount of volatile organic compounds (VOC), also leads
Causing the environmental friendliness of this kind of hydrophobicity interiro wall latex paint reduces, specifically, this interior wall cream containing additional hydrophobic auxiliary agent
Shellac varnish recoatability is poor, the twice that can not construct finishing coat, is not able to satisfy JGJ/T29-2015 " construction of building coating engineering and receiving gauge
Journey " in requirement to flat painting interior wall coating construction twice finishing coat, therefore that there is also films is plentiful for this kind of hydrophobicity interiro wall latex paint
Spend poor, feel difference defect.
Summary of the invention
In view of the deficiencies of the prior art, it is an object of the present invention to provide a kind of environment-friendly type inner wall emulsion paints, have similar lotus
The hydrophobic effect of leaf, recoatability is good, and paint film richness is high, has excellent water-fast and spot-resistant performance.
The technical scheme is that a kind of interiro wall latex paint, including following parts by weight of component:
10-17.5 parts of deionized water；
0.5-0.7 parts of dispersing agent；
0.15-0.2 parts of wetting agent；
0.3-0.4 parts of defoaming agent；
1.5-2.0 parts of propylene glycol；
0.5-1.0 parts of alcohol ester-12；
18-20 parts of titanium dioxide；
10-12.8 parts of dicalcium powder；
Functional lotion 38-40 parts；
1-1.2 parts of thickener；
The pH value of interiro wall latex paint is 8-9.
Preferably, interiro wall latex paint includes following parts by weight of component:
10-15 parts of deionized water；
0.6-0.7 parts of dispersing agent；
0.18-0.2 parts of wetting agent；
0.4 part of defoaming agent；
1.8-2.0 parts of propylene glycol；
0.8-1.0 parts of alcohol ester-12；
20 parts of titanium dioxide；
12-12.8 parts of dicalcium powder；
Functional lotion 38-40 parts；
1 part of thickener；
The pH value of interiro wall latex paint is 8-9.
It further include the preservative of 0.15-0.2 parts by weight.
The partial size of the dicalcium powder is 1250 mesh.
By adding 2-amino-2-methyl-1-propanol, pH value is adjusted.
The functionality lotion is ACRONAL ECO702ap.
The preparation method of above-mentioned interiro wall latex paint, has follow steps:
1) feeding in proportion；
2) it takes 80% deionized water to be added in blender, dispersion is sequentially added under the speed conditions of 400-600r/min
Agent, wetting agent, defoaming agent, propylene glycol and alcohol ester-12 stir 10-20min；
3) titanium dioxide, dicalcium powder are continuously added, adjustment revolving speed to 800-1200r/min is rushed with remaining 20% deionized water
Blender inner wall is washed, 20-40min is stirred, until fineness≤50 μm；
4) revolving speed is reduced to 400-600r/min, and functional lotion is added, stirs 10-20min；
5) thickener is added under 400-800r/min speed conditions, until viscosity is 100 ± 2KU, obtains interiro wall latex paint.
Preferably, fineness is 30-50 μm in step 3).
Preferably, step 5) stirring to viscosity is 100KU.
It has the advantages that by adopting the above technical scheme
1, interiro wall latex paint of the present invention,
Propylene glycol, which has, adjusts paint film rate of drying and antifreeze effect, if content of propylene glycol is too low, antifreezing effect is poor, if
Content of propylene glycol is excessively high, then causes paint film rate of drying excessively slow.
Alcohol ester-12 plays the role of coalescing agent, if the content of alcohol ester-12 is too low, is easy to cause film forming bad, if content
It is excessively high, lead to increased costs, and paint film rate of drying is excessively slow.
Titanium dioxide is used as pigment to play the role of improving covering power, if titanium white powder content is too low, interior wall in the present invention
The covering power of emulsion paint is deteriorated, and brushing surface reduces, if titanium dioxide too high levels, lead to increased costs.
Dicalcium powder is used as filler to play filling effect in the present invention, reduces the cost of interiro wall latex paint, if dicalcium powder
Content is too low, then interiro wall latex paint solid content of the present invention is lower, if the too high levels of dicalcium powder, interiro wall latex paint specific gravity increases
Add, is unfavorable for the increase of brushing surface.
Functional lotion is important film forming matter in the present invention, keeps lacquer painting hydrophobic effect, anti-pollution characteristic and excellent
Recoating performance.
The pH value of interiro wall latex paint is set as 8-9, if pH value is lower than 8, interiro wall latex paint of the present invention is invaded vulnerable to mould etc.
Erosion, causes shelf life of products to shorten, if pH value is higher than 9, contains 2-amino-2-methyl-1-propanol in interiro wall latex paint of the present invention
Measure excessively high, product odour is strong.
2, the paint film of interiro wall latex paint of the present invention, brushing has lotus leaf hydrophobic effect, shows excellent water-fast and resistant
Stain performance, especially water resistance pollutant performance.In addition, interiro wall latex paint recoatability of the present invention is good, the paint film hair after pollution
Towel wiping can eliminate spot, carry out secondary brushing, also greatly increase the time interval of old-wall renewing, be beneficial to energy conservation and subtract
Row.
3, the paint film richness of interiro wall latex paint brushing of the present invention is high, good hand touch, and is free of formaldehyde and alkyl phenol polyoxy second
Alkene ether compound (APEO) belongs to environmentally friendly machine.
With reference to the accompanying drawing and specific embodiment is further described.
Detailed description of the invention
The effect picture of one draining test of Fig. 1 embodiment (in figure, is followed successively by common interiro wall latex paint dry film from left to right, passes
System lotus leaf effect interior wall paint dry film, interiro wall latex paint dry film of the present invention)；
The effect picture that Fig. 2 a, Fig. 2 b are embodiment one, two anti-pollution characteristic of embodiment is tested (in figure, is followed successively by from left to right
Common interiro wall latex paint dry film, traditional lotus leaf effect interior wall paint dry film, interiro wall latex paint dry film of the present invention)；
Fig. 3 is that spot erases effect；
Fig. 4 is the effect picture that traditional lotus leaf effect interior wall paint recoats performance；
Fig. 5 is the effect picture that interiro wall latex paint of the present invention recoats performance.
Specific embodiment
In the present invention, dispersing agent, wetting agent, defoaming agent, thickener are common auxiliary agent in emulsion paint field, wherein
Dispersing agent, wetting agent, thickener, 2-amino-2-methyl-1-propanol (AMP-95) are purchased from Chengdu Bo Chuan Chemical Co., Ltd., disappear
Infusion, alcohol ester-12, titanium dioxide are purchased from Chongqing Heng Ye Chemical Co., Ltd., and propylene glycol uses commercial product, and dicalcium powder is purchased from Sichuan
Baoxing calcium carbonate factory, fineness are 1250 mesh, and whiteness >=85%, functional lotion is purchased from BASF AG.
Embodiment one
1) it takes the deionized water of 80mL to be added in blender, dispersion is sequentially added under the speed conditions of 400-600r/min
Agent 6g, wetting agent 2g, defoaming agent 3g, propylene glycol 15g and alcohol ester-12 5g stir 10-20min；
2) titanium dioxide 180g, dicalcium powder 100g are continuously added, adjusts revolving speed to 800-1200r/min, with 20mL deionization
Water rinses blender inner wall, 20-40min is stirred, until fineness≤50 μm；
3) revolving speed is reduced to 400-600r/min, and functional lotion 380g is added, stirs 10-20min；
4) thickener 10g is added under 400-800r/min speed conditions, until viscosity is 100 ± 2KU, obtains interior wall latex
Paint.
Embodiment two
1) it takes the deionized water of 100mL to be added in blender, is sequentially added under the speed conditions of 400-600r/min point
Powder 7g, wetting agent 2g, defoaming agent 4g, propylene glycol 20g and alcohol ester-12 7g stir 10-20min；
2) titanium dioxide 190g, dicalcium powder 110g are continuously added, adjusts revolving speed to 800-1200r/min, with 30mL deionization
Water rinses blender inner wall, 20-40min is stirred, until fineness≤50 μm；
3) revolving speed is reduced to 400-600r/min, and functional lotion 390g is added, stirs 10-20min；
4) thickener 10g is added under 400-800r/min speed conditions, until viscosity is 100 ± 2KU, obtains interior wall latex
Paint.
Embodiment three
1) it takes the deionized water of 100mL to be added in blender, is sequentially added under the speed conditions of 400-600r/min point
Powder 7g, wetting agent 2g, defoaming agent 4g, propylene glycol 20g and alcohol ester-12 10g stir 10-20min；
2) titanium dioxide 200g, dicalcium powder 120g are continuously added, adjusts revolving speed to 800-1200r/min, with 20mL deionization
Water rinses blender inner wall, 20-40min is stirred, until fineness≤50 μm；
3) revolving speed is reduced to 400-600r/min, and functional lotion 400g is added, stirs 10-20min；
4) thickener 10g is added under 400-800r/min speed conditions, until viscosity is 100 ± 2KU, obtains interior wall latex
Paint.
The test of example IV hydrophobic effect
Common interiro wall latex paint is taken, traditional lotus leaf effect interior wall paint (common interiro wall latex paint+hydrophobing agent) is used as reference examples,
The interior emulsion paint of Example one is as test example.
Execution conditions: temperature be 25 DEG C, humidity 50-60%, according to conventional construction mode, spraying or roller coating are such as
PVC board, has been scraped on the calcium silicate board of putty the cement gypsum plate for having scraped putty, until thickness of dry film is 50-70 μm.
Respectively to common interiro wall latex paint dry film, traditional lotus leaf effect interior wall paint dry film, interiro wall latex paint dry film of the present invention
Upper sprinkling 5-10g pure water, hydrophobic effect figure (in each figure, are followed successively by common interiro wall latex paint as shown in Figure 1 respectively from left to right
Dry film, traditional lotus leaf effect interior wall paint dry film, interiro wall latex paint dry film of the present invention).
It will be seen from figure 1 that interiro wall latex paint of the present invention and common interiro wall latex paint, traditional lotus leaf effect interior wall paint phase
Than showing higher hydrophobicity.
The test of five anti-pollution characteristic of embodiment
Common interiro wall latex paint is taken, traditional lotus leaf effect interior wall paint (common interiro wall latex paint+hydrophobing agent) is used as reference examples,
The interior emulsion paint of Example one, two is as test example.
Execution conditions: temperature be 25 DEG C, humidity 50-60%, according to conventional construction mode, spraying or roller coating are such as
PVC board, has been scraped on the calcium silicate board of putty the cement gypsum plate for having scraped putty, until thickness of dry film is 50-70 μm.
Respectively to common interiro wall latex paint dry film, traditional lotus leaf effect interior wall paint dry film, interiro wall latex paint dry film of the present invention
Upper dropwise addition ink, soy sauce, vinegar, tea (from left to right), anti-pollution characteristic respectively as shown in Fig. 2 a, Fig. 2 b (in each figure, from left to right
It is followed successively by common interiro wall latex paint dry film, traditional lotus leaf effect interior wall paint dry film, interiro wall latex paint dry film of the present invention).
It can be seen that interiro wall latex paint of the present invention and common interiro wall latex paint, traditional lotus leaf effect interior wall from Fig. 2 a, Fig. 2 b
Paint is compared, and superior anti-pollution characteristic is shown, and the pollutants such as ink are splashed on interiro wall latex paint dry film of the present invention, ink
It can not adhere to, can be erased with rag in drops.
Common interiro wall latex paint dry film, traditional lotus leaf effect interior wall paint dry film, the dirt on interiro wall latex paint dry film of the present invention
It is as shown in Figure 3 that stain (ink, soy sauce, vinegar, tea) rag wipes effect picture clear.
From figure 3, it can be seen that interiro wall latex paint of the present invention and common interiro wall latex paint, traditional lotus leaf effect interior wall paint phase
Than the spot being adhered on interiro wall latex paint dry film of the present invention can be erased completely.
Embodiment sixfold applies performance test
Take traditional lotus leaf effect interior wall paint (common interiro wall latex paint+hydrophobing agent) as reference examples, Example one it is interior
Emulsion paint is as test example.
Execution conditions: temperature be 25 DEG C, humidity 50-60%, according to conventional construction mode, spraying or roller coating are such as
PVC board, cement gypsum plate, on plank, until thickness of dry film is 50-70 μm.
Respectively on traditional lotus leaf effect interior wall paint dry film, interiro wall latex paint dry film of the present invention according to common form of construction work weight
Overcoating brush tradition lotus leaf effect interior wall paint, interiro wall latex paint of the present invention, recoating performance difference are as shown in Figure 4 and Figure 5.
As can be seen from Figure 4 and Figure 5, the recoatability of interiro wall latex paint of the present invention is good, and paint film richness is high, when lacquer painting quilt
When scratch needs to repair, interiro wall latex paint directly directly can be coated on the lacquer painting of damage, be beneficial to energy conservation emission reduction.
Claims (9)
1. a kind of interiro wall latex paint, which is characterized in that including following parts by weight of component:
10-17.5 parts of deionized water；
0.5-0.7 parts of dispersing agent；
0.15-0.2 parts of wetting agent；
0.3-0.4 parts of defoaming agent；
1.5-2.0 parts of propylene glycol；
0.5-1.0 parts of alcohol ester-12；
18-20 parts of titanium dioxide；
10-12.8 parts of dicalcium powder；
Functional lotion 38-40 parts；
1-1.2 parts of thickener；
The pH value of interiro wall latex paint is 8-9.
2. interiro wall latex paint according to claim 1, which is characterized in that including following parts by weight of component:
10-15 parts of deionized water；
0.6-0.7 parts of dispersing agent；
0.18-0.2 parts of wetting agent；
0.4 part of defoaming agent；
1.8-2.0 parts of propylene glycol；
0.8-1.0 parts of alcohol ester-12；
20 parts of titanium dioxide；
12-12.8 parts of dicalcium powder；
Functional lotion 38-40 parts；
1 part of thickener；
The pH value of interiro wall latex paint is 8-9.
3. interiro wall latex paint according to claim 1 or 2, which is characterized in that further include the anti-corrosion of 0.15-0.2 parts by weight
Agent.
4. interiro wall latex paint according to claim 1 or 2, it is characterised in that: the partial size of the dicalcium powder is 1250 mesh.
5. interiro wall latex paint according to claim 1 or 2, it is characterised in that: by adding 2- amino-2-methyl -1- third
Alcohol (AMP-95) adjusts pH value.
6. interiro wall latex paint according to claim 1 or 2, it is characterised in that: the functionality lotion is ACRONAL
ECO702ap。
7. the preparation method of any interiro wall latex paint of claim 1-6, has follow steps:
1) feeding in proportion；
2) take 80% deionized water be added blender in, sequentially added under the speed conditions of 400-600r/min dispersing agent,
Wetting agent, defoaming agent, propylene glycol and alcohol ester-12 stir 10-20min；
3) titanium dioxide, dicalcium powder are continuously added, adjustment revolving speed to 800-1200r/min is stirred with the flushing of remaining 20% deionized water
Device inner wall is mixed, 20-40min is stirred, until fineness≤50 μm；
4) revolving speed is reduced to 400-600r/min, and functional lotion is added, stirs 10-20min；
5) thickener is added under 400-800r/min speed conditions, until viscosity is 100 ± 2KU, obtains interiro wall latex paint.
8. preparation method according to claim 7, it is characterised in that: fineness is 30-50 μm in step 3).
9. preparation method according to claim 7, it is characterised in that: step 5) stirring to viscosity is 100 ± 2KU.