CN109626921A - A kind of benefit waste concrete hollow partition board and preparation method thereof - Google Patents
A kind of benefit waste concrete hollow partition board and preparation method thereof Download PDFInfo
- Publication number
- CN109626921A CN109626921A CN201811620405.XA CN201811620405A CN109626921A CN 109626921 A CN109626921 A CN 109626921A CN 201811620405 A CN201811620405 A CN 201811620405A CN 109626921 A CN109626921 A CN 109626921A
- Authority
- CN
- China
- Prior art keywords
- slag
- cement
- building waste
- small furnace
- hollow partition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of sharp waste concrete hollow partition boards and preparation method thereof, and by weight percentage, siccative component includes: cement: 12-15%；Slag powders: 5-8%；Small furnace ferronickel slag: 50-60%；Building waste: 20-30%.The present invention replaces part of cement using the potential volcano ash effect of slag powders, not only reduces production cost, and can reduce the heat of hydration of cement；The utilization new way of small furnace ferronickel slag and building waste has been expanded again, economic benefit and social benefit has been promoted, has saved natural resources, is met national recycling economy and is utilized policy, it is contemplated that there is apparent social economy and environmental benefit.
Description
Technical field
The present invention relates to a kind of concrete hollow partition plate and its method of preparation, in particular to a kind of sharp waste concrete is empty
Septum cordis wallboard and preparation method thereof field.
Background technique
With the propulsion of country's building housing industrialization, as precast light wall matched with skyscraper, frame structure
Plate is increasingly becoming the chief component of current materials for wall and the development trend of certainty.Concrete hollow partition plate can be used as filling
Internal partition wall with formula building uses, and has from heavy and light, good heat preservation performance, and shock resistance is good, construction and installation are convenient and efficient, increases interior makes
With area, labor intensity is reduced, improves construction quality, the advantages that cost is moderate.
With accelerating for Chinese Urbanization, building waste, in the trend risen, but generally existing is at present built in China
The not high phenomenon of building refuse utilization rate, nowadays building waste processing mode mainly keeps in stacking and landfill stabilization.To old mixed
The recycling for coagulating soil does not cause enough attention also, with the sharp increase of China's building waste quantity, building waste resource
Change processing is extremely urgent.The water quenching waste residue that small furnace ferronickel slag generates when being smelting ferronickel, activity is low compared with slag,
Admixture dosage as cement is seldom, and utilization rate is low, causes bulk deposition, pollutes environment.But due to small furnace ferronickel slag
Itself specific gravity is lighter, can be used as construction material aglite carry out using.
Currently, industrial residue is in hollow partition board using being broadly divided into following a few classes: (1) big, light weight, work by particle
The low waste residue of property is utilized in concrete hollow partition plate as light-weight aggregate；(2) the high waste residue of activity is then milled, and utilizes it
The volcano ash effect that has as gelling material carry out using；(3) small waste residue is then used as filler to be filled out to the low, particle of activity again
It fills, plays humidification.In addition then haydite can also be carried out to prepare concrete hollow partition as lightweight aggregate with precast ceramsite
Plate.Such as: CN1194929C " production method of mechanically from industrial cinder, ceramsite concrete light-weight partition board ": what is involved is utilize industry ash
Slag and haydite are the method that light aggregate prepares partition plate, belong to waste utilization；CN1207441A " machine-made compound light partition item
Plate ": what is involved is the methods for preparing light partition board with perlite, clinker, slag etc. for primary raw material；CN101759402A
" a kind of concrete fireproof hollow lath ": what is involved is be main with fire-proof cement, flyash, fire resistant infilling, expanded perlite
The method that raw material prepares concrete fireproof hollow lath.But these wallboards are generally existing at high cost, complex process, and intensity is low etc.
Disadvantage.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of sharp waste concrete hollow partition board and preparation method thereof, gram
At high cost in the prior art, complex process is taken, the low defect of intensity, the invention is using small furnace ferronickel slag and building waste as bone
Material prepares concrete hollow partition plate, has expanded the utilization new way of small furnace ferronickel slag and building waste.
A kind of concrete composition of the present invention, by weight percentage, siccative component includes: cement: 12-15%；Slag powders:
5-8%；Small furnace ferronickel slag: 50-60%；Building waste: 20-30%.
Preferably, by weight percentage, the siccative component are as follows: 15% cement, 5% slag powders, 50% small furnace ferronickel
Slag, 30% building waste.
Preferably, by weight percentage, the siccative component are as follows: 12% cement, 8% slag powders, 50% small furnace ferronickel
Slag, 30% building waste.
Preferably, by weight percentage, the siccative component are as follows: 15% cement, 5% slag powders, 60% small furnace ferronickel
Slag, 20% building waste.
Preferably, by weight percentage, the siccative component are as follows: 12% cement, 8% slag powders, 60% small furnace ferronickel
Slag, 20% building waste.
Preferably, by weight percentage, the siccative group is divided into 13.5% cement, 6.5% slag powders, 55% small furnace nickel
Iron-ore Slag, 25% building waste.
Preferably, the cement is portland cement；Slag powders: water-granulated slag is made by levigate, and specific surface area >=
400m2/kg；Small furnace ferronickel slag: partial size 0-5mm；Building waste: partial size 0-10mm.
It further include water in the composition, water: being 0.3-0.4 with siccative ratio.
The present invention provides a kind of preparation method of concrete hollow partition plate, comprising:
After being measured respectively using the composition siccative component, then the uniform stirring 0.5-2min in blender is added
Water uniform stirring 2-3min, then after extrusion forming, natural curing is to get hollow partition board.
The extrusion forming is to be transported into ground mould extrusion moulding machine to carry out extrusion forming through dumper.
It is put in storage after the concrete hollow partition plate cutting conserved, starting board, detection, number.
The present invention also provides a kind of applications of concrete composition, are such as applicable to heat preservation, sound insulation and fire proofing wood
The light building materials such as material.
Beneficial effect
Performance advantage of the invention is utilized industrial solid castoff and building waste as aggregate, is squeezed using ground mould
The concrete hollow partition plate intensity of moulding process production reaches 10 megapascal or more, the standard of 5 megapascal universal higher than industry.
It is characteristic of the invention that being raw material using solid waste, the solids such as small furnace ferronickel slag, building waste are given up
Gurry is main aggregate, is gelling material with cement, slag powders, prepares concrete hollow partition plate by ground model extrusion, should
Concrete hollow partition plate compression strength height and bending resistance carrying are big, while having light, heat preservation, sound insulation, prevent fires, be easily installed
Feature.
The present invention is the potential volcano ash effect using slag powders to replace part of cement, not only reduces production cost,
And the heat of hydration of cement can be reduced；The utilization new way of small furnace ferronickel slag and building waste has been expanded again, promotes warp
Benefit of helping and social benefit, have saved natural resources, meet national recycling economy and utilize policy, it is contemplated that have apparent society's warp
Ji and environmental benefit.
The present invention prepares concrete using small furnace ferronickel slag and building waste as aggregate using ground model extrusion technique
Hollow partition board, and each performance indicator of concrete hollow partition plate prepared meets standard GB/T/T23449-2009 " ash
Slag concrete hollow partition plate " requirement.
The present invention with the solid waste such as small furnace ferronickel slag, building waste be main aggregate, be with cement, slag powders
Be gelled material, prepares concrete hollow partition plate by ground model extrusion, belongs to the recycling of solid waste, is applicable to protect
The light building materials such as temperature, sound insulation and fire proofing material.
Specific embodiment
Present invention will be further explained below with reference to specific examples.It should be understood that these embodiments are merely to illustrate the present invention
Rather than it limits the scope of the invention.In addition, it should also be understood that, after reading the content taught by the present invention, those skilled in the art
Member can make various changes or modifications the present invention, and such equivalent forms equally fall within the application the appended claims and limited
Range.
Cement is 42.5 grades of ordinary portland cements；
Slag powders: water-granulated slag is made by levigate, specific surface area >=400m2/ kg, species abundance in Baosteel in Shanghai company；
Small furnace ferronickel slag: partial size 0-5mm, Fujian Desheng iron company；
Building waste: partial size 0-10mm, Shanghai urban construction company.
Embodiment 1
The present embodiment specific formula is by weight are as follows: the cement of 15wt%, the slag powders of 5wt%, 50wt%0-5mm it is small
Blast-furnace cinder, 30wt%0-10mm building waste measure respectively after, then uniform stirring 1 minute in blender is added dry
Water uniform stirring 3 minutes for expecting weight 40wt%；The material mixed is transported into extrusion forming in single lead screw ex truding briquetting machine through dumper；At
Natural curing 7 days or more after type, then it is put in storage after cutting, starting board, detection, number.
It is required according in GB/T23449-2009 " ash slag concrete hollow partition plate ", detects the concrete hollow partition plate
With a thickness of 120mm, width 600mm, per unit aerial density 115kg/m2, compression strength 11.5MPa, bending resistance is carried as
1.5。
Embodiment 2
Specific formula of the present invention is by weight are as follows: the cement of 12wt%, the slag powders of 8wt%, 50wt%0-5mm small height
Furnace slag, 30wt%0-10mm building waste measure respectively after, uniform stirring 1 minute, is then added siccative in blender
The water uniform stirring of weight 40wt% 3 minutes；The material mixed is transported into extrusion forming in single lead screw ex truding briquetting machine through dumper；Molding
It natural curing 7 days or more afterwards, is then put in storage after cutting, starting board, detection, number.
It is required according in GB/T23449-2009 " ash slag concrete hollow partition plate ", detects the concrete hollow partition plate
With a thickness of 120mm, width 600mm, per unit aerial density 114kg/m2, compression strength 13.7MPa, bending resistance is carried as
1.6。
Embodiment 3
Specific formula of the present invention is by weight are as follows: the cement of 15wt%, the slag powders of 5wt%, 60wt%0-5mm small height
Furnace slag, 20wt%0-10mm building waste measure respectively after, uniform stirring 1 minute, is then added siccative in blender
The water uniform stirring of weight 30wt% 3 minutes；The material mixed is transported into extrusion forming in single lead screw ex truding briquetting machine through dumper；Molding
It natural curing 7 days or more afterwards, is then put in storage after cutting, starting board, detection, number.
It is required according in GB/T23449-2009 " ash slag concrete hollow partition plate ", detects the concrete hollow partition plate
With a thickness of 120mm, width 600mm, per unit aerial density 106kg/m2, compression strength 10.9MPa, bending resistance is carried as
1.4。
Embodiment 4
Specific formula of the present invention is by weight are as follows: the cement of 12wt%, the slag powders of 8wt%, 60wt%0-5mm small height
Furnace slag, 20wt%0-10mm building waste measure respectively after, uniform stirring 1 minute, is then added siccative in blender
The water uniform stirring of weight 30wt% 3 minutes；The material mixed is transported into extrusion forming in single lead screw ex truding briquetting machine through dumper；Molding
It natural curing 7 days or more afterwards, is then put in storage after cutting, starting board, detection, number.
It is required according in GB/T23449-2009 " ash slag concrete hollow partition plate ", detects the concrete hollow partition plate
With a thickness of 120mm, width 600mm, per unit aerial density 109kg/m2, compression strength 10.1MPa, bending resistance is carried as
1.3。
Embodiment 5
Specific formula of the present invention is by weight are as follows: the cement of 13.5wt%, the slag powders of 6.5wt%, 55wt%0-5mm
Small furnace slag, 25wt%0-10mm building waste measure respectively after, uniform stirring 1 minute, is then added in blender
The water uniform stirring of siccative weight 35wt% 3 minutes；The material mixed is transported into extrusion forming in single lead screw ex truding briquetting machine through dumper；
Natural curing 7 days or more after molding, then it is put in storage after cutting, starting board, detection, number.
It is required according in GB/T23449-2009 " ash slag concrete hollow partition plate ", detects the concrete hollow partition plate
With a thickness of 120mm, width 600mm, per unit aerial density 110kg/m2, compression strength 10.7MPa, bending resistance is carried as
1.3。
Claims (10)
1. a kind of concrete composition, which is characterized in that by weight percentage, siccative component includes: cement: 12-15%；Slag
Powder: 5-8%；Small furnace ferronickel slag: 50-60%；Building waste: 20-30%.
2. composition according to claim 1, which is characterized in that the siccative component are as follows: 15% cement, 5% slag powders,
50% small furnace ferronickel slag, 30% building waste.
3. composition according to claim 1, which is characterized in that the siccative component are as follows: 12% cement, 8% slag powders,
50% small furnace ferronickel slag, 30% building waste.
4. composition according to claim 1, which is characterized in that the siccative component are as follows: 15% cement, 5% slag powders,
60% small furnace ferronickel slag, 20% building waste.
5. composition according to claim 1, which is characterized in that the siccative component are as follows: 12% cement, 8% slag powders,
60% small furnace ferronickel slag, 20% building waste.
6. composition according to claim 1, which is characterized in that the siccative group is divided into 13.5% cement, 6.5% slag
Powder, 55% small furnace ferronickel slag, 25% building waste.
7. composition according to claim 1, which is characterized in that the cement is portland cement；Slag powders: water-granulated slag
It is made by levigate, specific surface area >=400m2/kg；Small furnace ferronickel slag: partial size 0-5mm；Building waste: partial size 0-
10mm。
8. composition according to claim 1, which is characterized in that further include water in the composition, water: be with siccative ratio
0.3-0.4。
9. a kind of preparation method of concrete hollow partition plate, comprising:
After being measured respectively using composition described in claim 1, then it is equal that water is added in the uniform stirring 0.5-2min in blender
Even stirring 2-3min, then after extrusion forming, natural curing is to get hollow partition board.
10. a kind of application of concrete composition described in claim 1.