CN109625566A - A kind of carton break-resistance processing method - Google Patents
A kind of carton break-resistance processing method Download PDFInfo
- Publication number
- CN109625566A CN109625566A CN201910140172.1A CN201910140172A CN109625566A CN 109625566 A CN109625566 A CN 109625566A CN 201910140172 A CN201910140172 A CN 201910140172A CN 109625566 A CN109625566 A CN 109625566A
- Authority
- CN
- China
- Prior art keywords
- silicon oxide
- carton
- oxide layer
- solidify
- degrees celsius
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of carton processing methods, and in particular to a kind of carton break-resistance processing method includes the following steps: to be coated with one layer of silica in the paperboard surface of carton；When coating, the temperature of silica is 800 degrees Celsius；Solidify silica, first solidify 5-10 minutes under 400-500 degrees Celsius, then 100-200 degrees Celsius solidification 2-5 minutes, finally solidify 10 minutes under 20-30 degrees Celsius, formation silicon oxide layer；Surface evening processing is carried out to silicon oxide layer；One layer of protection paint is coated on the surface of silicon oxide layer.The invention has the beneficial effects that: multistep curing method is used, so that silicon oxide layer hardness is high, carton is enable to have preferable anticollision fragility；Surface evening processing is carried out to silicon oxide layer, makes surfacing.
Description
Technical field
The present invention relates to a kind of carton processing methods, and in particular to a kind of carton break-resistance processing method.
Background technique
Carton is easy to be knocked and cut occur in transport, preserving process.
Summary of the invention
To solve the deficiencies in the prior art, it is an object of the invention to overcome the deficiencies of existing technologies, provides a kind of
Carton break-resistance processing method, this method can prevent from being knocked and cut occur.
In order to achieve the above objectives, the present invention adopts the following technical scheme that:
A kind of carton break-resistance processing method, which comprises the steps of:
(1) one layer of silica is coated in the paperboard surface of carton；When coating, the temperature of silica is 800 degrees Celsius；
(2) solidify silica, first solidify under 400-500 degrees Celsius 5-10 minutes, then solidify at 100-200 degrees centigrade
2-5 minutes, finally solidify 10 minutes under 20-30 degrees Celsius, forms silicon oxide layer；
(3) surface evening processing is carried out to silicon oxide layer；
(4) one layer of protection paint is coated on the surface of silicon oxide layer.
Further include following steps (5): leveling processing is carried out to protection painted surface.
The silica with a thickness of 2mm-5mm, preferably 4mm.The protection paint thickness is 2mm-5mm.
In step (2), first solidifies under 450 degrees Celsius 6 minutes, then solidify 3 minutes at 100 degrees centigrade, finally exist
Solidify 10 minutes under 25 degrees Celsius, forms silicon oxide layer.
The invention has the beneficial effects that: multistep curing method is used, so that silicon oxide layer hardness is high, there is carton preferably
Anticollision fragility energy；Surface evening processing is carried out to silicon oxide layer, makes surfacing.
Specific embodiment
Embodiment 1
(1) one layer of silica is coated in the paperboard surface of carton；When coating, the temperature of silica is 800 degrees Celsius；
(2) solidify silica, first solidify 10 minutes under 400 degrees Celsius, then 200 degrees centigrade solidification 4 minutes, finally
Solidify 10 minutes under 25 degrees Celsius, forms silicon oxide layer；
(3) surface evening processing is carried out to silicon oxide layer；
(4) one layer of protection paint is coated on the surface of silicon oxide layer.
(5): leveling processing is carried out to protection painted surface.
Comparative example 1
(1) in the paperboard surface coating protection paint of carton；
(2): leveling processing is carried out to protection painted surface.
Respectively to the carton of embodiment 1 and comparative example 1 upper, preceding, left three faces of cardboard same position with same
Strength carry out 1 shock respectively, impact force 10-15N/cm2, the shocks duration is 0.5s, and research can obtain, embodiment 1
Cardboard do not occur broken hole, then there are 2 face breakages to the cardboard of comparative example 1 in 3 faces.The bending of embodiment 1 and comparative example 1 is strong
Degree is 52MPa and 40MPa.
The basic principles, main features and advantages of the invention have been shown and described above.The technical staff of the industry should
Understand, the above embodiments do not limit the invention in any form, all obtained by the way of equivalent substitution or equivalent transformation
Technical solution is fallen within the scope of protection of the present invention.
Claims (6)
1. a kind of carton break-resistance processing method, which comprises the steps of:
One layer of silica is coated in the paperboard surface of carton；When coating, the temperature of silica is 800 degrees Celsius；
Solidify silica, first solidifies under 400-500 degrees Celsius 5-10 minutes, then in 100-200 degrees centigrade solidification 2-5
Minute, finally solidify 10 minutes under 20-30 degrees Celsius, forms silicon oxide layer；
Surface evening processing is carried out to silicon oxide layer；
(4) one layer of protection paint is coated on the surface of silicon oxide layer.
2. a kind of carton break-resistance processing method according to claim 1, which is characterized in that further include following steps (5):
Leveling processing is carried out to protection painted surface.
3. a kind of carton break-resistance processing method according to claim 1, which is characterized in that the thickness of the silica
For 2mm-5mm.
4. a kind of carton break-resistance processing method according to claim 3, which is characterized in that the thickness of the silicon oxide layer
Degree is 4mm.
5. the wrinkle resistant processing method of a kind of packed in cases according to claim 1, which is characterized in that the protection is painted thick
Degree is 2mm-5mm.
6. a kind of carton break-resistance processing method according to claim 1, which is characterized in that in step (2), first 450
Solidify under degree Celsius 6 minutes, then solidify 3 minutes at 100 degrees centigrade, finally solidify 10 minutes under 25 degrees Celsius, is formed
Silicon oxide layer.