CN110981221A - Surface treating agent for light bottle and using method thereof - Google Patents
Surface treating agent for light bottle and using method thereof Download PDFInfo
- Publication number
- CN110981221A CN110981221A CN201911301810.XA CN201911301810A CN110981221A CN 110981221 A CN110981221 A CN 110981221A CN 201911301810 A CN201911301810 A CN 201911301810A CN 110981221 A CN110981221 A CN 110981221A
- Authority
- CN
- China
- Prior art keywords
- bottle
- light bottle
- treating agent
- spraying
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a surface treating agent for a light bottle and a using method thereof, and the surface treating agent comprises 80-110 parts of ethanol and 3-8 parts of adhesion promoter by mass. After the surface treatment agent for the light bottle is sprayed on the surface of the light bottle, dust on the surface of the light bottle is obviously reduced, and the spraying fastness is improved.
Description
The technical field is as follows:
the invention relates to the field of glass bottle production, in particular to a light bottle surface treating agent and a using method thereof.
Background art:
in the prior art, in the spraying process, the surface has more garbage, the coating has poor fastness, and the coating can fall off after being soaked in water for 24 hours.
The invention content is as follows:
the invention aims to solve the technical problem of providing a light bottle surface treating agent capable of improving the spraying fastness, wherein dust on the surface of a light bottle is obviously reduced after the light bottle surface treating agent is sprayed on the surface of the light bottle.
The technical proposal of the invention is to provide a surface treating agent for a light bottle, which comprises the following components in parts by mass,
80-110 parts of ethanol and 3-8 parts of adhesion promoter.
Preferably, the adhesion promoter is 900A adhesion promoter.
The invention also provides a using method of the light bottle surface treating agent, which comprises the following steps of spraying the light bottle surface treating agent by using a pressure gun after the light bottle passes through a first dust removing room on a production line spraying line, drying the surface by using an air gun, volatilizing ethanol, and spraying a coating on the surface by using a spraying room.
Compared with the prior art, the invention has the following advantages after adopting the scheme: after the surface of the light bottle is sprayed with the light bottle surface treatment agent, the surface dust is obviously reduced, the fastness of the coating is obviously improved after the coating is coated, and the coating does not fall off after being soaked in water for 24 hours.
The specific implementation mode is as follows:
the invention is further illustrated with respect to specific embodiments below:
example 1
A surface treating agent for a light bottle comprises the following components in parts by weight,
100 parts of ethanol and 4 parts of adhesion promoter, wherein in the embodiment, the adhesion promoter is 900A adhesion promoter. When the polishing bottle is used, the polishing bottle is sprayed with the polishing bottle surface treating agent by a 4kg pressure gun after passing through a first dust removal room on a production line spraying line, the surface is dried by a 4kg air gun, ethanol is volatilized, and then the surface is sprayed and coated by a coating room.
After the surface of the light bottle is sprayed with the light bottle surface treatment agent, the surface dust is obviously reduced, the fastness of the subsequent coating is obviously improved after the subsequent coating is coated, and the coating does not fall off after being soaked in water for 24 hours.
The foregoing is illustrative of the preferred embodiments of the present invention only and is not to be construed as limiting the claims. All the equivalent structures or equivalent process changes made by the description of the invention are included in the scope of the patent protection of the invention.
Claims (3)
1. A surface treatment agent for a light bottle, which is characterized in that: comprises the following components in parts by mass,
80-110 parts of ethanol and 3-8 parts of adhesion promoter.
2. A light bottle surface treatment agent according to claim 1, characterized in that: the adhesion promoter is 900A adhesion promoter.
3. A method for using a light bottle surface treating agent is characterized by comprising the following steps: the method comprises the following steps of spraying a surface treatment agent on a polished bottle by a pressure gun after the polished bottle passes through a first dust removal room on a production line spraying line, drying the surface by an air gun, volatilizing ethanol, and spraying a coating on the surface by a spraying room.