CN109607742A - A kind of chemical nickle-plating wastewater reagent treatment and preparation method thereof - Google Patents
A kind of chemical nickle-plating wastewater reagent treatment and preparation method thereof Download PDFInfo
- Publication number
- CN109607742A CN109607742A CN201811568498.6A CN201811568498A CN109607742A CN 109607742 A CN109607742 A CN 109607742A CN 201811568498 A CN201811568498 A CN 201811568498A CN 109607742 A CN109607742 A CN 109607742A
- Authority
- CN
- China
- Prior art keywords
- parts
- plating wastewater
- reagent treatment
- chemical nickle
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of chemical nickle-plating wastewater reagent treatment, the raw material including following parts by weight is made: 1~5 part of sodium hypophosphite, 1~5 part of sodium hydrogensulfite, 30~50 parts of sodium hydroxide.Chemical nickle-plating wastewater reagent treatment of the invention can make available effective handle of nickel-containing waste water of the processing containing complexing agent have reached the discharge standard of country, and the committee that is used with existing many manufacturers of depressant prescription amount and cost outside handle the cost that can reduce about half;Furthermore it can simplify chemical nickle-plating wastewater processing equipment, reduce the burden of wastewater treatment producing line in factory.The present invention also provides a kind of preparation methods of chemical nickle-plating wastewater reagent treatment, and this method is easy to operate, low manufacture cost, can effectively ensure that chemical nickle-plating wastewater reagent treatment obtained is functional, prepare high yield rate.
Description
Technical field
The present invention relates to wastewater treatment reagent fields, and in particular to a kind of chemical nickle-plating wastewater reagent treatment and its preparation side
Method.
Background technique
Chemical nickle-plating wastewater is more using intermittent processing, this is because water quality pollutant fluctuation of concentration is larger, and for
The considerations of to processing cost, part factory can will scrap liquid and ejected wash water mixed processing, be diluted with the ejected wash water of low concentration highly concentrated
Degree scraps liquid, then carries out chemical precipitation, while reducing many and diverse degree of wastewater treatment, but with adding discharge standard increasingly tight
Severe, the mode of this type handles the standard for not caught up with discharge.
Due to containing a large amount of complexing agents in chemical nickel electroplate liquid formulation, the nickel in waste water exists in the form of complex state, and
Nonionic state is equally easy when this results in handling it without image of Buddha electronickelling, and in other words, the precipitation method of conventional dose cannot make
Removal.
And the concentration for scrapping liquid is too high, and service life is short, water is larger, and outer cost of entrusting is difficult to bear.
The present invention provide a kind of new chemical medicament specifically for the nickel-containing waste water containing complexing agent using redox it
Mode go brokenly or waste water in complexing agent, by the way that the functional group in organic matter is oxidized away, nickel exists in the form of ionic state, just
Nickel hydroxide precipitate is generated in conjunction with nickel ion in hydroxyl.
It based on the above situation, can be effective the invention proposes a kind of chemical nickle-plating wastewater reagent treatment and preparation method thereof
Solve problem above.
Summary of the invention
The purpose of the present invention is to provide a kind of chemical nickle-plating wastewater reagent treatments and preparation method thereof.The present invention provides one
Kind of new chemical medicament specifically for the nickel-containing waste water containing complexing agent using the mode of redox go brokenly or waste water in network
Mixture, by the way that the functional group in organic matter is oxidized away, nickel exists in the form of ionic state, convenient for hydroxyl in conjunction with nickel ion
Generate nickel hydroxide precipitate.Chemical nickle-plating wastewater reagent treatment of the invention can make nickel-containing waste water of the processing containing complexing agent can be with
Obtain effectively handling and have reached the discharge standard of country, and the committee that is used with existing many manufacturers of depressant prescription amount and cost outside
Processing can reduce the cost of about half;Furthermore it can simplify chemical nickle-plating wastewater processing equipment, reduce wastewater treatment producing line in factory
Burden.
The present invention is achieved through the following technical solutions:
A kind of chemical nickle-plating wastewater reagent treatment, the raw material including following parts by weight are made:
1~5 part of sodium hypophosphite,
1~5 part of sodium hydrogensulfite,
30~50 parts of sodium hydroxide.
The present invention provide a kind of new chemical medicament specifically for the nickel-containing waste water containing complexing agent using redox it
Mode go brokenly or waste water in complexing agent, by the way that the functional group in organic matter is oxidized away, nickel exists in the form of ionic state, just
Nickel hydroxide precipitate is generated in conjunction with nickel ion in hydroxyl.Chemical nickle-plating wastewater reagent treatment of the invention can be such that processing contains
Available effective handle of the nickel-containing waste water of complexing agent has reached the discharge standard of country, and depressant prescription amount and cost with showing
Processing can reduce the cost of about half outside the committee that many manufacturers of row use;Furthermore it can simplify chemical nickle-plating wastewater processing equipment, subtract
The burden of wastewater treatment producing line in few factory.
Sodium hypophosphite of the present invention, effect is to aoxidize complexing agent;
Sodium hydrogensulfite of the present invention, effect are to provide one catalyst of oxidation reaction;
Sodium hydroxide of the present invention gives heavy metal ion hydroxide root after oxidation.
The present invention passes through preferred raw material formula, and the ratio of reasonably combined each raw material, makes processing containing the nickeliferous of complexing agent
The available effective processing of waste water has reached the discharge standard of country.
Preferably, the chemical nickle-plating wastewater reagent treatment includes that the raw material of following parts by weight is made:
2~4 parts of sodium hypophosphite,
1.5~4.5 parts of sodium hydrogensulfite,
35~45 parts of sodium hydroxide.
Preferably, the chemical nickle-plating wastewater reagent treatment include include that the raw materials of following parts by weight is made:
2.5 parts of sodium hypophosphite,
3 parts of sodium hydrogensulfite,
42.5 parts of sodium hydroxide.
Preferably, the chemical nickle-plating wastewater reagent treatment include include that the raw materials of following parts by weight is made:
3.8 parts of sodium hypophosphite,
4.1 parts of sodium hydrogensulfite,
45.6 parts of sodium hydroxide.
The present invention also provides a kind of preparation methods of chemical nickle-plating wastewater reagent treatment, including the following steps:
A, the raw material of each parts by weight of chemical nickle-plating wastewater reagent treatment is weighed;
B, first sodium hydroxide is mixed with a certain amount of deionized water, and stirs to sodium hydroxide and is completely dissolved;
C, add sodium hydrogensulfite, stirring and dissolving again, and pass through addition deionized water condition pH, make pH value of solution 12~14;
D, it adds sodium hypophosphite, after uniform stirring, stands 20~40min, it is ensured that medicament with impurity without because that can produce
Raw reaction causes vaporization reaction to generate, and temperature drops to room temperature, is dispensed to obtain chemical nickle-plating wastewater reagent treatment.
Method of the invention is first first mixed sodium hydroxide with water when preparing with certain proportion, can accelerate to add later
The formula entered quickly dissolves;Sodium hydrogensulfite is added, must determine whether pH has at this time after sodium hydrogensulfite is added and reach 12-
Between 14, not up to this pH value or cause with the agent of activity decline come out, therefore step is particularly important;It is eventually adding sulfurous acid
Hydrogen sodium, after uniform stirring, must stand 20~40min and ensure whether medicament has causes vaporization reaction to produce because that can generate to react with impurity
It is raw, then etc. when temperature drop to room temperature, so that it may be dispensed.
Compared with prior art, the present invention have the following advantages that and the utility model has the advantages that
The present invention provide a kind of new chemical medicament specifically for the nickel-containing waste water containing complexing agent using redox it
Mode go brokenly or waste water in complexing agent, by the way that the functional group in organic matter is oxidized away, nickel exists in the form of ionic state, just
Nickel hydroxide precipitate is generated in conjunction with nickel ion in hydroxyl.
Chemical nickle-plating wastewater reagent treatment of the invention can make nickel-containing waste water of the processing containing complexing agent available effective
Processing has reached the discharge standard of country, and the committee that is used with existing many manufacturers of depressant prescription amount and cost outside handle and can reduce
The cost of about half;Furthermore it can simplify chemical nickle-plating wastewater processing equipment, reduce the burden of wastewater treatment producing line in factory.
Sodium hypophosphite of the present invention, effect is to aoxidize complexing agent;Sodium hydrogensulfite of the present invention, effect
It is to provide one catalyst of oxidation reaction;Sodium hydroxide of the present invention gives heavy metal ion hydroxide root after oxidation.The present invention
By preferred raw material formula, and the ratio of reasonably combined each raw material, make nickel-containing waste water of the processing containing complexing agent is available to have
The processing of effect has reached the discharge standard of country.
The present invention also provides a kind of preparation methods of chemical nickle-plating wastewater reagent treatment, and this method is easy to operate, is fabricated to
This is low, can effectively ensure that chemical nickle-plating wastewater reagent treatment obtained is functional, prepares high yield rate.
Specific embodiment
The present invention is described in further detail below with reference to embodiment, embodiments of the present invention are not limited thereto.
Test method described in following embodiments or test method are unless otherwise specified conventional method;The reagent
And material is obtained from routine business approach, or prepare in conventional manner unless otherwise specified.
Embodiment 1:
A kind of chemical nickle-plating wastewater reagent treatment, the raw material including following parts by weight are made:
1~5 part of sodium hypophosphite,
1~5 part of sodium hydrogensulfite,
30~50 parts of sodium hydroxide.
Embodiment 2:
A kind of chemical nickle-plating wastewater reagent treatment, the raw material including following parts by weight are made:
1~5 part of sodium hypophosphite,
1~5 part of sodium hydrogensulfite,
30~50 parts of sodium hydroxide.
Preferably, the chemical nickle-plating wastewater reagent treatment includes that the raw material of following parts by weight is made:
2~4 parts of sodium hypophosphite,
1.5~4.5 parts of sodium hydrogensulfite,
35~45 parts of sodium hydroxide.
Preferably, the chemical nickle-plating wastewater reagent treatment include include that the raw materials of following parts by weight is made:
2.5 parts of sodium hypophosphite,
3 parts of sodium hydrogensulfite,
42.5 parts of sodium hydroxide.
Preferably, the chemical nickle-plating wastewater reagent treatment include include that the raw materials of following parts by weight is made:
3.8 parts of sodium hypophosphite,
4.1 parts of sodium hydrogensulfite,
45.6 parts of sodium hydroxide.
The present invention also provides a kind of preparation methods of chemical nickle-plating wastewater reagent treatment, including the following steps:
A, the raw material of each parts by weight of chemical nickle-plating wastewater reagent treatment is weighed;
B, first sodium hydroxide is mixed with a certain amount of deionized water, and stirs to sodium hydroxide and is completely dissolved;
C, add sodium hydrogensulfite, stirring and dissolving again, and pass through addition deionized water condition pH, make pH value of solution 12~14;
D, it adds sodium hypophosphite, after uniform stirring, stands 20~40min, it is ensured that medicament with impurity without because that can produce
Raw reaction causes vaporization reaction to generate, and temperature drops to room temperature, is dispensed to obtain chemical nickle-plating wastewater reagent treatment.
Embodiment 3:
A kind of chemical nickle-plating wastewater reagent treatment, the raw material including following parts by weight are made:
1 part of sodium hypophosphite,
1 part of sodium hydrogensulfite,
30 parts of sodium hydroxide.
The preparation method of the chemical nickle-plating wastewater reagent treatment of the present embodiment, including the following steps:
A, the raw material of each parts by weight of chemical nickle-plating wastewater reagent treatment is weighed;
B, first sodium hydroxide is mixed with a certain amount of deionized water, and stirs to sodium hydroxide and is completely dissolved;
C, add sodium hydrogensulfite, stirring and dissolving again, and pass through addition deionized water condition pH, make pH value of solution 12;
D, it adds sodium hypophosphite, after uniform stirring, stands 20min, it is ensured that medicament with impurity without because that can generate instead
Vaporization reaction should be caused to generate, and temperature drops to room temperature, be dispensed to obtain chemical nickle-plating wastewater reagent treatment.
Embodiment 4:
A kind of chemical nickle-plating wastewater reagent treatment, the raw material including following parts by weight are made:
5 parts of sodium hypophosphite,
5 parts of sodium hydrogensulfite,
50 parts of sodium hydroxide.
The preparation method of the chemical nickle-plating wastewater reagent treatment of the present embodiment, including the following steps:
A, the raw material of each parts by weight of chemical nickle-plating wastewater reagent treatment is weighed;
B, first sodium hydroxide is mixed with a certain amount of deionized water, and stirs to sodium hydroxide and is completely dissolved;
C, add sodium hydrogensulfite, stirring and dissolving again, and pass through addition deionized water condition pH, make pH value of solution 14;
D, it adds sodium hypophosphite, after uniform stirring, stands 40min, it is ensured that medicament with impurity without because that can generate instead
Vaporization reaction should be caused to generate, and temperature drops to room temperature, be dispensed to obtain chemical nickle-plating wastewater reagent treatment.
Embodiment 5:
A kind of chemical nickle-plating wastewater reagent treatment, the raw material including following parts by weight are made:
2 parts of sodium hypophosphite,
1.5 parts of sodium hydrogensulfite,
35 parts of sodium hydroxide.
The preparation method of the chemical nickle-plating wastewater reagent treatment of the present embodiment, including the following steps:
A, the raw material of each parts by weight of chemical nickle-plating wastewater reagent treatment is weighed;
B, first sodium hydroxide is mixed with a certain amount of deionized water, and stirs to sodium hydroxide and is completely dissolved;
C, add sodium hydrogensulfite, stirring and dissolving again, and pass through addition deionized water condition pH, make pH value of solution 12.8;
D, it adds sodium hypophosphite, after uniform stirring, stands 28min, it is ensured that medicament with impurity without because that can generate instead
Vaporization reaction should be caused to generate, and temperature drops to room temperature, be dispensed to obtain chemical nickle-plating wastewater reagent treatment.
Embodiment 6:
A kind of chemical nickle-plating wastewater reagent treatment, the raw material including following parts by weight are made:
4 parts of sodium hypophosphite,
4.5 parts of sodium hydrogensulfite,
45 parts of sodium hydroxide.
The preparation method of the chemical nickle-plating wastewater reagent treatment of the present embodiment, including the following steps:
A, the raw material of each parts by weight of chemical nickle-plating wastewater reagent treatment is weighed;
B, first sodium hydroxide is mixed with a certain amount of deionized water, and stirs to sodium hydroxide and is completely dissolved;
C, add sodium hydrogensulfite, stirring and dissolving again, and pass through addition deionized water condition pH, make pH value of solution 13.6;
D, it adds sodium hypophosphite, after uniform stirring, stands 35min, it is ensured that medicament with impurity without because that can generate instead
Vaporization reaction should be caused to generate, and temperature drops to room temperature, be dispensed to obtain chemical nickle-plating wastewater reagent treatment.
Embodiment 7:
A kind of chemical nickle-plating wastewater reagent treatment, the raw material including following parts by weight are made:
2.5 parts of sodium hypophosphite,
3 parts of sodium hydrogensulfite,
42.5 parts of sodium hydroxide.
The preparation method of the chemical nickle-plating wastewater reagent treatment of the present embodiment, including the following steps:
A, the raw material of each parts by weight of chemical nickle-plating wastewater reagent treatment is weighed;
B, first sodium hydroxide is mixed with a certain amount of deionized water, and stirs to sodium hydroxide and is completely dissolved;
C, add sodium hydrogensulfite, stirring and dissolving again, and pass through addition deionized water condition pH, make pH value of solution 12.9;
D, it adds sodium hypophosphite, after uniform stirring, stands 32min, it is ensured that medicament with impurity without because that can generate instead
Vaporization reaction should be caused to generate, and temperature drops to room temperature, be dispensed to obtain chemical nickle-plating wastewater reagent treatment.
Embodiment 8:
A kind of chemical nickle-plating wastewater reagent treatment, the raw material including following parts by weight are made:
3.8 parts of sodium hypophosphite,
4.1 parts of sodium hydrogensulfite,
45.6 parts of sodium hydroxide.
The preparation method of the chemical nickle-plating wastewater reagent treatment of the present embodiment, including the following steps:
A, the raw material of each parts by weight of chemical nickle-plating wastewater reagent treatment is weighed;
B, first sodium hydroxide is mixed with a certain amount of deionized water, and stirs to sodium hydroxide and is completely dissolved;
C, add sodium hydrogensulfite, stirring and dissolving again, and pass through addition deionized water condition pH, make pH value of solution 13.5;
D, it adds sodium hypophosphite, after uniform stirring, stands 30min, it is ensured that medicament with impurity without because that can generate instead
Vaporization reaction should be caused to generate, and temperature drops to room temperature, be dispensed to obtain chemical nickle-plating wastewater reagent treatment.
Comparative example 1:
The sodium hydroxide solution that pH is 13.5.
Comparative example 2:
The sodium hydroxide solution that pH is 12.9.
Using control variate method, the resulting chemical nickle-plating wastewater reagent treatment of embodiment 3 to 8 and comparative example 1 to 2 are carried out
Performance test, the results are shown in Table 1.
Table 1
As it can be seen from table 1 chemical nickle-plating wastewater reagent treatment of the invention can be effectively reduced the nickel in nickel-containing waste water
Content reaches the discharge standard of country, and good more many than common lye precipitating removal nickel effect.
The above is only presently preferred embodiments of the present invention, not does limitation in any form to the present invention, it is all according to
According to technical spirit any simple modification to the above embodiments of the invention, equivalent variations, protection of the invention is each fallen within
Within the scope of.
Claims (5)
1. a kind of chemical nickle-plating wastewater reagent treatment, it is characterised in that: the raw material including following parts by weight is made:
1~5 part of sodium hypophosphite,
1~5 part of sodium hydrogensulfite,
30~50 parts of sodium hydroxide.
2. chemical nickle-plating wastewater reagent treatment according to claim 1, it is characterised in that: the raw material including following parts by weight
It is made:
2~4 parts of sodium hypophosphite,
1.5~4.5 parts of sodium hydrogensulfite,
35~45 parts of sodium hydroxide.
3. chemical nickle-plating wastewater reagent treatment according to claim 1, it is characterised in that: the raw material including following parts by weight
It is made:
2.5 parts of sodium hypophosphite,
3 parts of sodium hydrogensulfite,
42.5 parts of sodium hydroxide.
4. chemical nickle-plating wastewater reagent treatment according to claim 1, it is characterised in that: the raw material including following parts by weight
It is made:
3.8 parts of sodium hypophosphite,
4.1 parts of sodium hydrogensulfite,
45.6 parts of sodium hydroxide.
5. a kind of such as a kind of described in any item preparation methods of chemical nickle-plating wastewater reagent treatment of Claims 1-4, feature
It is, including the following steps:
A, the raw material of each parts by weight of chemical nickle-plating wastewater reagent treatment is weighed;
B, first sodium hydroxide is mixed with a certain amount of deionized water, and stirs to sodium hydroxide and is completely dissolved;
C, add sodium hydrogensulfite, stirring and dissolving again, and pass through addition deionized water condition pH, make pH value of solution 12~14;
D, it adds sodium hypophosphite, after uniform stirring, stands 20~40min, it is ensured that medicament with impurity without because that can generate instead
Vaporization reaction should be caused to generate, and temperature drops to room temperature, be dispensed to obtain chemical nickle-plating wastewater reagent treatment.